CN110014494A - A kind of fire-proof doors and windows combo box plate and its synthetic method - Google Patents
A kind of fire-proof doors and windows combo box plate and its synthetic method Download PDFInfo
- Publication number
- CN110014494A CN110014494A CN201910297404.4A CN201910297404A CN110014494A CN 110014494 A CN110014494 A CN 110014494A CN 201910297404 A CN201910297404 A CN 201910297404A CN 110014494 A CN110014494 A CN 110014494A
- Authority
- CN
- China
- Prior art keywords
- fire
- combo box
- parts
- box plate
- proof doors
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fire-proof doors and windows combo box plate of window technology field and its synthetic method, fire-proof doors and windows combo box plate compositions are as follows: log: 35~40 parts；Logging residue: 15~20 parts；Industrial wood waste: 10~13 parts；Adhesive: 6~9 parts；Core material: 9~15 parts；Fire retardant: 8~14 parts；Packing material: 12~14 parts, the fire-proof doors and windows combo box plate, it can be before the deckle board of door and window be formed, fire retardant is built among material, pass through the fusion of fire retardant and packing material, the uniformity of fire retardant is ensured that when mating formation, after cooperating precompressed and hot pressing, the plate that makes to mat formation has flame-retarding characteristic, the increase of glass fibre, so that anti-flammability and bonding strength get a promotion, the amalgamation of door and window moulding material is strong, and overall flame is excellent, not against external skin, flame-retarding characteristic is lasting, will not generate loss.
Description
Technical field
The invention discloses a kind of fire-proof doors and windows combo box plate and its synthetic methods, specially window technology field.
Background technique
Door and window is divided into fender member or partition member by the location of its difference, has different design requirements to have respectively
There are the functions such as heat preservation, heat-insulated, sound insulation, waterproof, fire prevention.
And door and window combo box plate, it is the raw material of cooperation compression door and window combo box production, is divided into log board and compression plate
Two kinds of material.
When cooperating door and window production, especially deckle board made of compress mode, lack has existing door and window combo box plate
The fire-retardant mode of effect, only progress outer armor or spray coated flame retardant material, the mode difficulty of processing of armouring is big, low efficiency, and
The mode of spray coated flame retardant material will receive the influence of solarization rainwater and gradually peel off, substantially reduces flame retardant effect, directly influence
The service life of door and window deckle board and intensity.
Summary of the invention
The purpose of the present invention is to provide a kind of fire-proof doors and windows combo box plate and its synthetic methods, to solve above-mentioned background
When cooperating door and window production, especially deckle board made of compress mode lacks the existing door and window combo box plate proposed in technology
Few effective fire-retardant mode, only progress outer armor or spray coated flame retardant material, the mode difficulty of processing of armouring is big, efficiency
It is low, and the mode of spray coated flame retardant material, will receive the influence of solarization rainwater gradually peels off, and substantially reduces flame retardant effect, direct shadow
Ring the problem of having arrived service life and the intensity of door and window deckle board.
To achieve the above object, the invention provides the following technical scheme: a kind of fire-proof doors and windows combo box plate, the fire resistant doorsets
Window combo box plate composition are as follows:
Log: 35~40 parts；
Logging residue: 15~20 parts；
Industrial wood waste: 10~13 parts；
Adhesive: 6~9 parts；
Core material: 9~15 parts；
Fire retardant: 8~14 parts；
Packing material: 12~14 parts.
Preferably, the log is small diameter grade log, tears two kinds in plate log, wood-fiber board and elm plate open.
Preferably, the logging residue is one of brush wood and root timber.
Preferably, the industrial wood waste is three kinds in slab, end, broken veneer and sawdust.
Preferably, the adhesive is one of phenol glue, melamine glue, MR glue and UF glue.
Preferably, the core material is two kinds in glued board, small juggle and bark.
Preferably, the fire retardant is one of antimony oxide and aluminium hydroxide.
Preferably, the packing material is three kinds in glass fibre, stalk, rice husk, sawdust and Plant Powder disintegrating slag.
A kind of synthetic method of fire-proof doors and windows combo box plate, the synthetic method of the fire-proof doors and windows combo box plate are as follows:
Step 1: log is sawed-off and boiling: the sawed-off length of log is controlled as 13mm -26mm, the waste material of the generation of log
If small juggle, butt and sawdust are recycled, the proportion of goods damageds are controlled 3% -10%, and cooperate thermophilic digestion, boiling liquid
According to 3:0.5 ratio be placed in thimerosal, digestion time 30min, temperature be 80 DEG C -120 DEG C；
Step 2: wood shavings preparation: wood shavings slenderness ratio is sheet wood shavings S=L/t, rod-shaped wood shavings S=L/d, and wherein L is plane
Flower length, d are wood shavings diameter, and t is wood shavings thickness, guarantees that S is greater than 10mm -12mm, wood shavings length-width ratio J=L/W, and wherein W is plane
Flower width, oriented shaving J are greater than 10, width-thickness ratio K=W/t；
Step 3: dry: to be dried using contact heating rotary formula roller dryer, drying time is 100min-
120min, drying temperature are 100 DEG C -130 DEG C；
Step 4: mixing: fire retardant and packing material use mechanical mixture mode, and the revolving speed of mixing machine motor is 2600r/
Min, mixed time are 25min, and temperature when mixing is 50 DEG C~75 DEG C；
Step 5: mat formation: using mechanical spreading machine, utilizing the density and measurement at isotopic number densimeter measurement slab each point
The falling amount of wood shavings, the density and thickness deviation on surface are as small as possible, using plate thickness center as symmetrical plane；
Step 6: continous way precompressed, compression measurement 1/2-1/3, pressure 1.5Mpa-1.7Mpa, when precompressed precompressed: are used
Between 10s-30s, rebound degree is maintained at 15%-25%；
Step 7: hot pressing: using the multi-daylight press of periodic, with board briquette and water-cut variation, slab thickness
It gradually decreases, hot pressing temperature is 110 DEG C -140 DEG C；
Step 8: cutting edge sanding: using plate shearing machine, and the good hair plates of hot pressing is cut into deckle board material, and to frame panel surface into
Row sanding makes the bright and clean beauty in deckle board flitch face.
It compared with prior art, can be in the deckle board of door and window the beneficial effects of the present invention are: the fire-proof doors and windows combo box plate
Before being formed, fire retardant is built among material, by the fusion of fire retardant and packing material, the increase of glass fibre,
So that anti-flammability and bonding strength get a promotion, the uniformity of fire retardant is ensured that when mating formation, after cooperating precompressed and hot pressing,
The plate that makes to mat formation has flame-retarding characteristic, and the amalgamation of door and window moulding material is strong, and overall flame is excellent, not against external skin, resistance
It is lasting to fire characteristic, loss will not be generated.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
The present invention provides a kind of technical solution: a kind of fire-proof doors and windows combo box plate, the fire-proof doors and windows combo box plate group
Become:
Log: 35~40 parts；
Logging residue: 15~20 parts；
Industrial wood waste: 10~13 parts；
Adhesive: 6~9 parts；
Core material: 9~15 parts；
Fire retardant: 8~14 parts；
Packing material: 12~14 parts.
Wherein, log is small diameter grade log, tears two kinds in plate log, wood-fiber board and elm plate open, and logging residue is
One of brush wood and intermediate cutting residue, industrial wood waste are three kinds in slab, end, broken veneer and sawdust, adhesive
For one of phenol glue, melamine glue, MR glue and UF glue, core material is two kinds in glued board, small juggle and bark, fire-retardant
Agent is one of antimony oxide and aluminium hydroxide, and packing material is three in stalk, rice husk, sawdust and Plant Powder disintegrating slag
Kind.
A kind of synthetic method of fire-proof doors and windows combo box plate, the synthetic method of the fire-proof doors and windows combo box plate are as follows:
Step 1: log is sawed-off and boiling: the sawed-off length of log is controlled as 13mm -26mm, the waste material of the generation of log
If small juggle, butt and sawdust are recycled, the proportion of goods damageds are controlled 3% -10%, and cooperate thermophilic digestion, boiling liquid
According to 3:0.5 ratio be placed in thimerosal, digestion time 30min, temperature be 80 DEG C -120 DEG C；
Step 2: wood shavings preparation: wood shavings slenderness ratio is sheet wood shavings S=L/t, rod-shaped wood shavings S=L/d, and wherein L is plane
Flower length, d are wood shavings diameter, and t is wood shavings thickness, guarantees that S is greater than 10mm -12mm, wood shavings length-width ratio J=L/W, and wherein W is plane
Flower width, oriented shaving J are greater than 10, width-thickness ratio K=W/t；
Step 3: dry: to be dried using contact heating rotary formula roller dryer, drying time is 100min-
120min, drying temperature are 100 DEG C -130 DEG C；
Step 4: mixing: fire retardant and packing material use mechanical mixture mode, and the revolving speed of mixing machine motor is 2600r/
Min, mixed time are 25min, and temperature when mixing is 50 DEG C~75 DEG C；
Step 5: mat formation: using mechanical spreading machine, utilizing the density and measurement at isotopic number densimeter measurement slab each point
The falling amount of wood shavings, the density and thickness deviation on surface are as small as possible, using plate thickness center as symmetrical plane；
Step 6: continous way precompressed, compression measurement 1/2-1/3, pressure 1.5Mpa-1.7Mpa, when precompressed precompressed: are used
Between 10s-30s, rebound degree is maintained at 15%-25%；
Step 7: hot pressing: using the multi-daylight press of periodic, with board briquette and water-cut variation, slab thickness
It gradually decreases, hot pressing temperature is 110 DEG C -140 DEG C；
Step 8: cutting edge sanding: using plate shearing machine, and the good hair plates of hot pressing is cut into deckle board material, and to frame panel surface into
Row sanding makes the bright and clean beauty in deckle board flitch face.
Embodiment
Step 1: raw material is chosen: 37 parts of logs, 17 parts of logging residues, 11 parts of industrial wood wastes, 7 parts of adhesives are pressed
According to sequentially being weighed respectively, material is weighed, log is first cut into staple fiber, raw material first adds specific gravity small, rear to add than great
, adhesive finally adds, and log staple fiber is used and is added portionwise；
Step 2: log is sawed-off and boiling: the sawed-off length of log is controlled as 17mm, for example small wood of the waste material of the generation of log
Section, butt and sawdust are recycled, and the proportion of goods damageds cooperate thermophilic digestion 7%, according to the ratio of 3:0.5 in boiling liquid
Example merging thimerosal, digestion time 30min, temperature are 100 DEG C；
Step 3: wood shavings preparation: wood shavings slenderness ratio is sheet wood shavings S=L/t, rod-shaped wood shavings S=L/d, and wherein L is plane
Flower length, d are wood shavings diameter, and t is wood shavings thickness, guarantees that S is greater than 11mm, wood shavings length-width ratio J=L/W, and wherein W is that wood shavings are wide
Degree, oriented shaving J are greater than 10, width-thickness ratio K=W/t；
Step 4: dry: to be dried using contact heating rotary formula roller dryer, drying time 110min is done
Dry temperature is 115 DEG C；
Step 5: mixing: fire retardant and packing material use mechanical mixture mode, and the revolving speed of mixing machine motor is 2600r/
Min, mixed time are 25min, and temperature when mixing is 65 DEG C；
Step 6: mat formation: using mechanical spreading machine, utilizing the density and measurement at isotopic number densimeter measurement slab each point
The falling amount of wood shavings, the density and thickness deviation on surface are as small as possible, using plate thickness center as symmetrical plane；
Step 7: precompressed: using continous way precompressed, and compression measurement 1/2-1/3, pressure 1.6Mpa, squeeze time 25s are returned
Bullet rate is maintained at 20%；
Step 8: hot pressing: using the multi-daylight press of periodic, with board briquette and water-cut variation, slab thickness
It gradually decreases, hot pressing temperature is 130 DEG C；
Step 9: cutting edge sanding: using plate shearing machine, and the good hair plates of hot pressing is cut into deckle board material, and to frame panel surface into
Row sanding makes the bright and clean beauty in deckle board flitch face.
Now a kind of made fire-proof doors and windows combo box plate is often tested with deckle board material with certain market through the invention
Comparison, test process are as follows；
1, cooperate breaking plant such as ram, embodiment is crushed.
2, after embodiment places natural temperature, dry tack free is carried out, a section surface is taken to prick hole, then open fire is lighted, burning
After stopping, burning time is calculated.
3, it weighs to the embodiment after burning, to determine the weight of remaining deckle board material.
Test data is as follows:
Through Experimental comparison, a kind of fire-proof doors and windows combo box plate made by the present invention has outstanding flame retardant property, combustion
The burning time is short, and burning degree is low, and intensity is big, and stronger for door and window protection, applied widely, overall performance is excellent, convenient for general
And production.
Although hereinbefore invention has been described by reference to embodiment, the scope of the present invention is not being departed from
In the case where, various improvement can be carried out to it and can replace component therein with equivalent.Especially, as long as being not present
Structural conflict, the various features in presently disclosed embodiment can be combined with each other use by any way,
The description for not carrying out exhaustive to the case where these combinations in this specification is examined merely for the sake of omission length with what is economized on resources
Consider.Therefore, the invention is not limited to specific embodiments disclosed herein, but the institute including falling within the scope of the appended claims
There is technical solution.
Claims (9)
1. a kind of fire-proof doors and windows combo box plate, it is characterised in that: fire-proof doors and windows combo box plate composition are as follows:
Log: 35~40 parts；
Logging residue: 15~20 parts；
Industrial wood waste: 10~13 parts；
Adhesive: 6~9 parts；
Core material: 9~15 parts；
Fire retardant: 8~14 parts；
Packing material: 12~14 parts.
2. a kind of fire-proof doors and windows combo box plate according to claim 1, it is characterised in that: the log is that small diameter grade is former
Wood tears two kinds in plate log, wood-fiber board and elm plate open.
3. a kind of fire-proof doors and windows combo box plate according to claim 1, it is characterised in that: the logging residue is branch
One of fork material and root timber.
4. a kind of fire-proof doors and windows combo box plate according to claim 1, it is characterised in that: the industrial wood waste is plate
Three kinds in skin, end, broken veneer and sawdust.
5. a kind of fire-proof doors and windows combo box plate according to claim 1, it is characterised in that: the adhesive is phenolic aldehyde
One of glue, melamine glue, MR glue and UF glue.
6. a kind of fire-proof doors and windows combo box plate according to claim 1, it is characterised in that: the core material be glued board,
Two kinds in small juggle and bark.
7. a kind of fire-proof doors and windows combo box plate according to claim 1, it is characterised in that: the fire retardant is three oxidations
One of two antimony and aluminium hydroxide.
8. a kind of fire-proof doors and windows combo box plate according to claim 1, it is characterised in that: the packing material is glass
Three kinds in fiber, stalk, rice husk, sawdust and Plant Powder disintegrating slag.
9. a kind of synthetic method of such as fire-proof doors and windows combo box plate of any of claims 1-8, it is characterised in that:
The synthetic method of the fire-proof doors and windows combo box plate are as follows:
Step 1: log is sawed-off and boiling: the sawed-off length of log being controlled as 13mm -26mm, the waste material of the generation of log is for example small
Juggle, butt and sawdust are recycled, and the proportion of goods damageds are controlled 3% -10%, and cooperate thermophilic digestion, in boiling liquid according to
The ratio of 3:0.5 is placed in thimerosal, digestion time 30min, and temperature is 80 DEG C -120 DEG C；
Step 2: wood shavings preparation: wood shavings slenderness ratio is sheet wood shavings S=L/t, rod-shaped wood shavings S=L/d, and wherein L is wood shavings length, d
For wood shavings diameter, t is wood shavings thickness, guarantees that S is greater than 10mm -12mm, wood shavings length-width ratio J=L/W, and wherein W is wood shavings width, fixed
It is greater than 10 to wood shavings J, width-thickness ratio K=W/t；
Step 3: dry: to be dried using contact heating rotary formula roller dryer, drying time is 100min-
120min, drying temperature are 100 DEG C -130 DEG C；
Step 4: mixing: fire retardant and packing material use mechanical mixture mode, and the revolving speed of mixing machine motor is 2600r/min,
The mixed time is 25min, and temperature when mixing is 50 DEG C~75 DEG C；
Step 5: mat formation: using mechanical spreading machine, utilizing the density and measurement wood shavings at isotopic number densimeter measurement slab each point
Falling amount, the density and thickness deviation on surface are as small as possible, using plate thickness center as symmetrical plane；
Step 6: precompressed: using continous way precompressed, and 1/2-1/3, pressure 1.5Mpa-1.7Mpa, squeeze time are measured in compression
10s-30s, rebound degree are maintained at 15%-25%；
Step 7: hot pressing: using the multi-daylight press of periodic, with board briquette and water-cut variation, slab thickness is gradually
It reduces, hot pressing temperature is 110 DEG C -140 DEG C；
Step 8: cutting edge sanding: using plate shearing machine, the good hair plates of hot pressing is cut into deckle board material, and carry out sand to frame panel surface
Light makes the bright and clean beauty in deckle board flitch face.