CN105175804A - 具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物 - Google Patents
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物 Download PDFInfo
- Publication number
- CN105175804A CN105175804A CN201510496098.9A CN201510496098A CN105175804A CN 105175804 A CN105175804 A CN 105175804A CN 201510496098 A CN201510496098 A CN 201510496098A CN 105175804 A CN105175804 A CN 105175804A
- Authority
- CN
- China
- Prior art keywords
- rubber
- parts
- rubber composition
- corrosion resistant
- tire sidewall
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物及其制备方法，橡胶组合物是由以下重量份数的组分制备而成：橡胶基体100份，聚缩醛树脂10-20份，呋喃环氧树脂5-10份，碳纤维3-5份，硅烷偶联剂1-3份，环保芳烃油2-5份，促进剂1-3份，白炭黑20-30份和硫磺2-5份。本发明的树脂混合物中包括有聚缩醛树脂、呋喃环氧树脂和碳纤维，三者加入橡胶基体中，提高了橡胶组合物本体的耐腐蚀性和抗老化性，同时提高了橡胶组合物本身的机械强度和硬度，从而提高了轮胎的使用寿命。
Description
技术领域
本发明涉及轮胎生产领域，具体是一种具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物。
背景技术
制作轮胎的主要材料为橡胶，橡胶又分为天然橡胶、丁晴橡胶、丁苯橡胶、丁基橡胶等。但是这些橡胶本身的耐酸性、耐老化性较差，为了解决这个问题，在轮胎生产的时候，会在橡胶基体中加入防老化剂或其他助剂，提高轮胎的防老化性和强度。但是这种加入防老化剂的橡胶组合物本身的耐腐蚀性还是较差，由于是轮胎胎侧的部分整体形态较薄，很容易被酸碱腐蚀，使用寿命较低。
发明内容
本发明要解决的技术问题是提供一种具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其在橡胶基体中加入树脂混合物，从而提高了橡胶组合物整体的耐腐蚀性和抗老化性，从而提高了轮胎的使用寿命。
本发明的技术方案为：
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，它是由以下重量份数的组分制备而成：橡胶基体100份，聚缩醛树脂10-20份，呋喃环氧树脂5-10份，碳纤维3-5份，硅烷偶联剂1-3份，环保芳烃油2-5份，促进剂1-3份，白炭黑20-30份和硫磺2-5份。
所述的橡胶基体包括有天然橡胶、丁苯橡胶和顺丁橡胶，其中，三者的重量份比为30-50：20-40：20-30。
所述的聚缩醛树脂选用共聚聚缩醛树脂和均聚聚缩醛树脂中的至少一种。
所述的选用单环呋喃环氧树脂、双环呋喃环氧树脂或四环呋喃环氧树脂中的至少一种。
所述的碳纤维选用聚丙烯腈基碳纤维，其纤维长度为30-80μm。
所述的硅烷偶联剂选用硅烷偶联剂KH-550，KH-560，KH-570，KH-580和KH-590中至少一种。
所述的促进剂选用N-叔丁基-2-苯并噻唑次磺酰胺、N-环已基-2-苯骈噻唑次磺酰胺或2、2'-二硫代二苯并噻唑。
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物的制备方法，具体包括有以下步骤：首先按重量份比称取聚缩醛树脂、呋喃环氧树脂、碳纤维和硅烷偶联剂加入到挤出机中进行挤出造粒得到树脂混合物，然后将树脂混合物连同橡胶基体、环保芳烃油、促进剂和白炭黑加入到密炼机中进行密炼混合，密炼完后的物料连同硫磺继续密炼，最后加压硫化得橡胶组合物，然后橡胶组合物进入挤压机挤压成轮胎胎面结构。
本发明的优点：
本发明的树脂混合物中包括有聚缩醛树脂、呋喃环氧树脂和碳纤维，三者加入橡胶基体中，提高了橡胶组合物本体的耐腐蚀性和抗老化性，同时提高了橡胶组合物本身的机械强度和硬度，从而提高了轮胎的使用寿命。
具体实施方式
实施例1
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，它是由以下重量份数的组分制备而成：天然橡胶50份，丁苯橡胶30份，顺丁橡胶20份，聚缩醛树脂15份，呋喃环氧树脂10份，碳纤维5份，硅烷偶联剂3份，环保芳烃油5份，促进剂2份，白炭黑25份和硫磺2份。
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物的制备方法：首先按重量份比称取聚缩醛树脂、呋喃环氧树脂、碳纤维和硅烷偶联剂加入到挤出机中进行挤出造粒得到树脂混合物，然后将树脂混合物连同橡胶基体、环保芳烃油、促进剂和白炭黑加入到密炼机中进行密炼混合，密炼完后的物料连同硫磺继续密炼，最后加压硫化得橡胶组合物，然后橡胶组合物进入挤压机挤压成轮胎胎面结构。
实施例2
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，它是由以下重量份数的组分制备而成：天然橡胶45份，丁苯橡胶35份，顺丁橡胶20份，聚缩醛树脂20份，呋喃环氧树脂5份，碳纤维3份，硅烷偶联剂3份，环保芳烃油5份，促进剂3份，白炭黑20份和硫磺3份。
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物的制备方法同实施例1。
实施例3
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，它是由以下重量份数的组分制备而成：天然橡胶40份，丁苯橡胶35份，顺丁橡胶25份，聚缩醛树脂10份，呋喃环氧树脂10份，碳纤维5份，硅烷偶联剂3份，环保芳烃油5份，促进剂3份，白炭黑30份和硫磺5份。
具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物的制备方法同实施例1。
本发明实施例1-3制备的轮胎胎侧用橡胶组合物的测试结果见表1。
表1
| 项目 | 实施例1 | 实施例2 | 实施例3 |
| 耐腐蚀性（与腐蚀性液体接触1月） | 无开裂、变形、爆胎现象 | 无开裂、变形、爆胎现象 | 无开裂、变形、爆胎现象 |
| 抗老化性（日光下光照6个月） | 无开裂 | 无开裂 | 无开裂 |
| 硬度（邵尔A度） | 85-87 | 84-86 | 83-85 |
| 拉伸强度（MPa） | 22-24 | 22-25 | 21-24 |
| 扯断拉长率（%） | 520-550 | 510-540 | 510-540 |
| 撕裂强度（KN/m） | 70-75 | 70-75 | 70-75 |
表1数据为各实施例多次测试的范围值，从表1数据可知，本发明制备的轮胎胎侧用橡胶组合物耐腐蚀性和抗老化性能均较好，且具有更好的硬度和强度，从而进一步提高了轮胎胎侧的使用寿命。
Claims (8)
1.具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其特征在于：它是由以下重量份数的组分制备而成：橡胶基体100份，聚缩醛树脂10-20份，呋喃环氧树脂5-10份，碳纤维3-5份，硅烷偶联剂1-3份，环保芳烃油2-5份，促进剂1-3份，白炭黑20-30份和硫磺2-5份。
2.根据权利要求1所述的具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其特征在于：所述的橡胶基体包括有天然橡胶、丁苯橡胶和顺丁橡胶，其中，三者的重量份比为30-50：20-40：20-30。
3.根据权利要求1所述的具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其特征在于：所述的聚缩醛树脂选用共聚聚缩醛树脂和均聚聚缩醛树脂中的至少一种。
4.根据权利要求1所述的具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其特征在于：所述的选用单环呋喃环氧树脂、双环呋喃环氧树脂或四环呋喃环氧树脂中的至少一种。
5.根据权利要求1所述的具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其特征在于：所述的碳纤维选用聚丙烯腈基碳纤维，其纤维长度为30-80μm。
6.根据权利要求1所述的具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其特征在于：所述的硅烷偶联剂选用硅烷偶联剂KH-550，KH-560，KH-570，KH-580和KH-590中至少一种。
7.根据权利要求1所述的具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物，其特征在于：所述的促进剂选用N-叔丁基-2-苯并噻唑次磺酰胺、N-环已基-2-苯骈噻唑次磺酰胺或2、2'-二硫代二苯并噻唑。
8.根据权利要求1所述的具有高耐腐蚀老化性的含有树脂组合物的轮胎胎侧用橡胶组合物的制备方法，其特征在于：具体包括有以下步骤：首先按重量份比称取聚缩醛树脂、呋喃环氧树脂、碳纤维和硅烷偶联剂加入到挤出机中进行挤出造粒得到树脂混合物，然后将树脂混合物连同橡胶基体、环保芳烃油、促进剂和白炭黑加入到密炼机中进行密炼混合，密炼完后的物料连同硫磺继续密炼，最后加压硫化得橡胶组合物，然后橡胶组合物进入挤压机挤压成轮胎胎面结构。