CN105175007B - 一种轻质保温砖 - Google Patents

一种轻质保温砖 Download PDF

Info

Publication number
CN105175007B
CN105175007B CN201510533537.9A CN201510533537A CN105175007B CN 105175007 B CN105175007 B CN 105175007B CN 201510533537 A CN201510533537 A CN 201510533537A CN 105175007 B CN105175007 B CN 105175007B
Authority
CN
China
Prior art keywords
temperature
base substrate
time
light
insulating brick
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510533537.9A
Other languages
English (en)
Other versions
CN105175007A (zh
Inventor
林�智
武祯
邵俊杰
郭峰
陈全娣
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Keda Manufacturing Co., Ltd
Original Assignee
Keda Clean Energy Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Keda Clean Energy Co Ltd filed Critical Keda Clean Energy Co Ltd
Priority to CN201510533537.9A priority Critical patent/CN105175007B/zh
Publication of CN105175007A publication Critical patent/CN105175007A/zh
Application granted granted Critical
Publication of CN105175007B publication Critical patent/CN105175007B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种轻质保温砖,由以下主要原料制成:工业煤渣50‑76%、泥料6‑20%、钾长石4‑20%、钠长石4‑20%、石英4‑20%、抛光渣0‑15%。本发明以工业煤渣为配方主体,加入量为50%以上,而且,本发明的整个烧成时间控制在4‑7小时即可,制得的轻质保温砖质地坚硬、比重小、气孔率高、耐火温度超过1000度,可以轻易抵抗常规火灾,导热系数小、抗压强度高,非常适合用于外墙的隔热保温以及室内的隔热隔音保温。

Description

一种轻质保温砖
技术领域
[0001] 本发明涉及保温材料领域,特别涉及一种用于外墙的隔热保温以及室内的隔热隔 音保温的轻质保温砖。
背景技术
[0002] 本发明涉及的保温材料主要用于外墙的隔热保温以及室内的隔热隔音保温,现有 的保温材料主要有以下几种:
[0003] 1、现有的外墙隔热保温材料主要以苯板为主,苯板的耐火温度为700度左右,而且 没有硬度,是类似棉质质感,所以其使用一定要有其它建筑材料作为刚性支撑,形成复合材 料进行使用。而且,火灾的温度一般为800-1000度,苯板700度的耐火温度不足以抵抗火灾, 所以就火灾而言,它并不是实际意义上的耐火材料。
[0004] 2、现有的内墙隔热隔音保温材料主要是以加气砖为主,还有使用页岩砖、粘土 砖。加气砖虽然质轻,但其最大的缺点就是易碎,强度不足,而且易呈粉状。但综合考虑到它 的轻质对建筑成本的节约,近些年还是不断的被扩大使用,代替了页岩砖及粘土砖。页岩 砖、粘土砖,强度比较高,但自重大,使建筑物的承重大大增加,而且在火灾中墙体倒塌对人 体造成的二次损伤较大,所以这类的隔墙砖已经逐渐的被取代。
[0005] 3、现有的利用工业煤渣制轻质保温砖,主要是以抛光砖生产过程中的抛光渣为主 体原料,而补充极少部分的工业煤渣作为补充原料(15%以内)。同时,现有的用抛光渣制轻 质保温材料的技术,生产成本高,烧成过程需要16-24个小时不等。
[0006] 中国专利CN200510016692. X公开的《凝石砖及空心砌块》,其原料包括:凝石11-28%、煤渣26-40%、尾矿砂32-43%,余量为水。此专利中,利用了煤渣作为原料,但煤渣的用量 较少,没有作为原料主体,而且以凝石作为粘结剂,采用胶粘工序制得砖块。
[0007] 中国专利0似00910016194.3公开的《煤渣粉环保砖》,“取60-70%的煤渣粉作主 料,用20-30% 300#水泥作凝聚剂,用10%的100目普通砂石作辅料,将三种原料混合搅拌均 匀后,加入可使砖原料用手捏成团的水即可,然后将原料运送到挤出成型机制成砖坯,成型 后的砖坯放到环境温度20 °C〜30 °C、相对湿度65 ± 20 % rh晾晒棚中,避免暴晒,自然干燥48 小时以上即可为成品。”此专利是一种煤渣粉环保砖,虽然煤渣的加入量也较大,但它不经 过烧成,只是用水泥作为一种粘结剂进行粘结。
[0008] 中国专利CN201410137770.0《一种低导热系数隔热陶瓷砖及其制备方法》,煤渣为 其中的一种原料,加入量较少,仅为8-14%,而且其烧成工艺为:5-10°C/min的速率升温至 820-860°C,保温 0.5-lh,再以 8-12°C/min 的速率升温至 1220-1280°C,保温 1.5-2h,然后以 10-15°(:/11^11的速率降温至740-780°(:,保温1-1.511,再以5-10°(:/1^11的速率升温至1060-1120°C,保温l_2h,冷却至常温。该专利的烧成工艺较为复杂,总烧成时间约10小时,耗时 长。
发明内容
[0009] 本发明所要解决的技术问题在于,提供一种轻质保温砖,以工业煤渣为配方主体, 制备工艺简单,烧成时间短,节约能源,制得的保温砖性能好。
[0010] 为达到上述技术效果,本发明提供了一种轻质保温砖,由以下主要原料制成:
[0011] 工业煤渣 50-76%
[0012] 泥料 6-20%
[0013] 钾长石 4-20%
[0014] 纳长石 4-20%
[0015] 石英 4-20%
[0016] 抛光渣 0-15%。
[0017] 作为上述方案的改进,所述轻质砖由以下主要原料制成:
[0018] 工业煤渣 60-76%
[0019] 泥料 8-20%
[0020] 钟长石 5-20%
[0021] 纳长石 5-20%
[0022] 石英 5-20%
[0023] 抛光渣 0.1-15%。
[0024] 作为上述方案的改进,所述轻质砖的原料还包括:辅助料3-10%,所述辅助料为羧 甲基纤维素、三聚磷酸钠中的一种或组合。
[0025] 作为上述方案的改进,所述工业煤渣包括发电厂煤渣、供热煤渣、煤转气煤渣。
[0026] 作为上述方案的改进,所述轻质保温砖由下述方法制得:
[0027] 将原料按配比混合、经过球磨、喷雾、压制成型、干燥、烧成、抛光、磨边,最后打包 成成品。
[0028] 作为上述方案的改进,所述轻质保温砖由下述方法制得:
[0029] 将原料按配比混合、经过球磨、喷雾、堆粉成型、干燥、烧成、切割成板、磨边,最后 打包成成品。
[0030] 作为上述方案的改进,所述烧成包括:
[0031] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层高温粉末;
[0032] (2)将坯体从常温升温至800 °C,升温时间为t;
[0033] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2 40-90min,并在温度1000°C 的条件下保温,保温时间为t3 20-30min;
[0034] (4)将坯体从1000°C升温至温度T,升温时间为t4,其中,所述温度T为1150-1250 °C;
[0035] ⑸从温度T自然降温至常温,降温时间为t5。
[0036] 作为上述方案的改进,所述ti、t2、t3、t4、t5的时间总长为4-7小时。
[0037] 作为上述方案的改进,所述高温粉末为氧化铝或二氧化硅。
[0038] 作为上述方案的改进,所述轻质保温砖的比重为0.2-0.8,耐火温度>1000°C,导 热系数为0.04〜0.1 OWAm.k)。
[0039] 实施本发明具有如下有益效果:
[0040] 一、本发明的配方为工业煤渣50-76%、泥料6-20%、钾长石4-20%、钠长石4-20%、石 英4-20%、抛光渣0-15%。本发明以工业煤渣为配方主体,加入量为50%以上,同时该类煤渣的 特性是都未完全燃烧,内部含有的碳又是在烧成过程中的起泡剂,所产生的气泡被分别单 独密闭在坯体内部,形成单孔封闭的气孔,空气在坯体内部不能形成对流,热量在坯体内部 不能形成热交换,而达到保温、隔音、隔热的作用。本发明在工业煤渣的基础上配合加入钾 长石4-20%、钠长石4-20%,可以调节高温时配方的表面张力,封闭气泡,以确保所产生的微 小气泡不会穿透溢出,也不会聚集形成大泡;加入泥料6-20%,提高坯体的可塑性,保证配方 粉料的硬度;加入石英4-20%,在高温时形成玻璃项,调节最终产品的硬度和脆性,保证抗压 强度;加入抛光渣0-15%,用于调节气孔率及气孔大小。
[0041] 二、由于本发明采用上述特定配方,因此,本发明保温砖既可以采用压制成型方法 来成型,也可以采用堆粉成型方法来成型,制备过程可以有多种选择,适用范围广。
[0042] 三、本发明的烧成工艺简单,仅仅需要控制第二升温阶段为慢升温即可,其他升温 阶段可以采用正常升温速度,这是因为第二升温阶段是气体产生的过程,而坯体的瓷化需 要时间,如果气体已经产生,而坯体还未完成瓷化,则气泡就会溢出坯体,不能形成多孔结 构。如果升温太快,内部产生气体压力过大,容易产生气体溢出穿透,而不能形成封闭独立 的气孔,生产出来的成品就达不到隔热、保温的效果。而且,本发明的整个烧成时间控制在 4-7小时即可,与现有的烧成工艺相比,大大简化烧成步骤,节省烧成时间。
[0043] 综上,本发明制得的轻质保温砖质地坚硬、比重小、气孔率高、耐火温度超过1000 度,可以轻易抵抗常规火灾,导热系数小、抗压强度高,非常适合用于外墙的隔热保温以及 室内的隔热隔首保温。
附图说明
[0044] 图1是本发明一种轻质保温砖的制备方法一实施例的流程图;
[0045] 图2是本发明一种轻质保温砖的制备方法另一实施例的流程图。
具体实施方式
[0046] 为使本发明的目的、技术方案和优点更加清楚,下面将结合附图和具体实施例对 本发明作进一步地详细描述。
[0047] 本发明提供了一种轻质保温砖,由以下主要原料制成:
[0048] 工业煤渣 50-76%
[0049] 泥料 6-20%
[0050] 钟长石 4-20%
[0051] 纳长石 4-20%
[0052] 石英 4-20%
[0053] 抛光渣 0-15%。
[0054] 其中,工业煤渣为配方主体,加入量为50%以上。所述工业煤渣包括发电厂煤渣、供 热煤渣、煤转气煤渣,该类煤渣的特性是都未完全燃烧,内部含有的碳在温烧成过程中会形 成气泡,故工业煤渣又是在烧成过程中的起泡剂,由于生产过程会对坯体的高温粘度进行 控制,工业煤渣所产生的气泡被分别单独密闭在坯体内部,形成单孔封闭的气孔,空气在坯 体内部不能形成对流,热量在坯体内部不能形成热交换,而达到保温、隔音、隔热的作用。同 时由于本发明的原料是在1200度左右烧制出来的陶瓷质材料,所以能够达到1000度以上的 耐火温度。
[0055] 本发明在工业煤渣的基础上配合加入钾长石4-20%、钠长石4-20%,可以调节高温 时配方的表面张力,封闭气泡,以确保所产生的微小气泡不会穿透溢出,也不会聚集形成大 泡;
[0056] 加入泥料6-20%,提高坯体的可塑性,保证配方粉料的硬度,保证粉料在成型过程 中的粘结性能,具体的,该泥料可以是黑泥或污泥;
[0057] 加入石英4-20%,在高温时形成玻璃项,调节最终产品的硬度和脆性,保证抗压强 度;
[0058] 加入抛光渣0-15%,用于调节气孔率及气孔大小,所述抛光渣可以加入,也可以不 加入,其加入量是按产品的性能要求来决定的。本发明主要的发泡剂是煤渣中所含有的碳, 而抛光渣为辅助的发泡剂,当需要更大量的发泡效果,成品比重更小时,可以适当按需要添 加抛光渣。需要说明的是,抛光渣是抛光砖生产过程中,抛光工序所产生的废渣,主要成分 为碳化硅、树脂及抛下来的砖坯废渣。
[0059] 需要说明的是,本发明原料配方中的%是指重量百分比。
[0060] 优选的,所述轻质砖由以下主要原料制成:
[0061] 工业煤渣 60-76%
[0062] 泥料 8-20%
[0063] 钟长石 5-20%
[0064] 纳长石 5-20%
[0065] 石英 5-20%
[0066] 抛光渣 0.1-15%。
[0067] 更佳的,所述轻质砖的原料还包括:辅助料3-10%,所述辅助料为羧甲基纤维素、 三聚磷酸钠中的一种或组合,主要用于调节浆料流动性、悬浮性。
[0068] 如图1所示,所述轻质保温砖由下述方法制得:
[0069] 将原料按配比混合、经过球磨、喷雾、压制成型、干燥、烧成、抛光、磨边,最后打包 成成品。
[0070] 其中,所述烧成包括:
[0071] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层高温粉末;
[0072] (2)将坯体从常温升温至800 °C,升温时间为t;
[0073] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2 40-90min,并在温度1000°C 的条件下保温,保温时间为t3 20-30min;
[0074] (4)将坯体从1000°C升温至温度T,升温时间为t4,其中,所述温度T为1150-1250 °C;
[0075] (5)从温度T自然降温至常温,降温时间为t5。
[0076] 具体的,步骤(1)中,所述高温粉末为氧化铝或二氧化硅。本发明需要在坯体下方 加入耐火垫板且在坯体与耐火垫板之间铺上至少一层高温粉末,这是因为整个坯体完全玻 化且膨胀,高温时呈熔融的液态,不能直接进辊道窑烧成,故需在坯体下加耐火垫板进行垫 烧;垫板与坯体间要均匀的布一层氧化铝、二氧化硅等高温粉末,以方便烧成后的产品与垫 板间的分离。
[0077] 步骤(2)中,将坯体从常温升温至800°C,此阶段为第一升温阶段,没有特别的升温 速度要求,只要正常升温即可,该升温时间为以,以约为20-60min。
[0078] 步骤(3)中,将坯体从800°C缓慢升温至1000°C,升温时间t2为40-90min,并在温度 1 〇〇〇 °C的条件下保温,保温时间t3为20-30min。升温时间t2和保温时间t3的时间总长为60-120min。此阶段为第二升温阶段,需要慢升温,因为这个阶段是气体产生的过程,且坯体的 瓷化需要时间,如果气体已经产生,而坯体还未完成瓷化,则气泡就会溢出坯体,不能形成 多孔结构。如果升温太快,内部产生气体压力过大,容易产生气体溢出穿透,不能形成封闭 独立的气孔,生产出来的材料就达不到隔热、保温的效果。
[0079] 步骤(4)中,将坯体从1000°C升温至温度T,升温时间为t4,此阶段为第三升温阶 段,没有特别的升温速度要求,只要正常升温即可,升温时间为t4为40-80min。其中,温度T 为本发明烧成的最高温度,所述温度T为1150-1250°C,其依据具体配方而定。
[0080] 步骤⑸中,从温度T自然降温至常温,降温时间为t5,降温时间t5约为2-4小时。
[0081] 本发明的整体烧成周期为4_7小时,即所述ti、t2、t3、t4、t5的时间总长为4_7小 时。
[0082] 在烧成过程中,本发明的保温时间短(只要20-30分钟),保温温度点低(低于1000 摄氏度),大大简化工艺,节约能源。
[0083] 需要说明的是,上述球磨、喷雾、压制成型、干燥、抛光、磨边等步骤采用现有技术 即可。
[0084] 如图2所示,所述轻质保温砖也可以由下述方法制得:
[0085] 将原料按配比混合、经过球磨、喷雾、堆粉成型、干燥、烧成、切割成板、磨边,最后 打包成成品。
[0086] 其中,所述烧成包括:
[0087] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层高温粉末;
[0088] (2)将坯体从常温升温至800 °C,升温时间为t;
[0089] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2 40-90min,并在温度1000°C 的条件下保温,保温时间为t3 20-30min;
[0090] (4)将坯体从1000°C升温至温度T,升温时间为t4,其中,所述温度T为1150-1250 °c;
[0091] (5)从温度T自然降温至常温,降温时间为t5。
[0092] 具体的,步骤(1)中,所述高温粉末为氧化铝或二氧化硅。本发明需要在坯体下方 加入耐火垫板且在坯体与耐火垫板之间铺上至少一层高温粉末,这是因为整个坯体完全玻 化且膨胀,高温时呈熔融的液态,不能直接进辊道窑烧成,故需在坯体下加耐火垫板进行垫 烧;垫板与坯体间要均匀的布一层氧化铝、二氧化硅等高温粉末,以方便烧成后的产品与垫 板间的分离。
[0093] 步骤(2)中,将坯体从常温升温至800°C,此阶段为第一升温阶段,没有特别的升温 速度要求,只要正常升温即可,该升温时间Stht1约为20-60min。
[0094] 步骤(3)中,将坯体从800°C缓慢升温至1000°C,升温时间t2为40-90min,并在温度 1 〇〇〇 °C的条件下保温,保温时间t3为20-30min。升温时间t2和保温时间t3的时间总长为60- 120min。此阶段为第二升温阶段,需要慢升温,因为这个阶段是气体产生的过程,且坯体的 瓷化需要时间,如果气体已经产生,而坯体还未完成瓷化,则气泡就会溢出坯体,不能形成 多孔结构。如果升温太快,内部产生气体压力过大,容易产生气体溢出穿透,不能形成封闭 独立的气孔,生产出来的材料就达不到隔热、保温的效果。
[0095] 步骤(4)中,将坯体从1000°C升温至温度T,升温时间为t4,此阶段为第三升温阶 段,没有特别的升温速度要求,只要正常升温即可,升温时间为t4为40-80min。其中,温度T 为本发明烧成的最高温度,所述温度T为1150-1250°C,其依据具体配方而定。
[0096] 步骤⑸中,从温度T自然降温至常温,降温时间为t5,降温时间t5约为2-4小时。
[0097] 本发明的整体烧成周期为4_7小时,即所述ti、t2、t3、t4、t5的时间总长为4_7小 时。
[0098] 在烧成过程中,本发明的保温时间短(只要20-30分钟),保温温度点低(低于1000 摄氏度),大大简化工艺,节约能源。
[0099] 需要说明的是,上述球磨、喷雾、堆粉成型、干燥、切割成板、磨边等步骤采用现有 技术即可。
[0100] 综上,本发明采用上述特定配方,通过上述特定的烧成工艺,制得的轻质保温砖的 比重为0.2-0.8,耐火温度> 1000°C,导热系数为0.04〜0 . IOWAm. k),抗压强度为1.0-6.5MPa 〇
[0101] 下面以具体实施例对本发明进行进一步阐述
[0102] 实施例1
[0103] 将原料按配比混合,配方为:工业煤渣60%、泥料20%、钾长石4%、钠长石4%、石英4%、 抛光渣8%;然后经过球磨、喷雾、压制成型、干燥、烧成、抛光、磨边,最后打包成成品;
[0104] 其中,烧成步骤包括:
[0105] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层氧化铝高 温粉末;
[0106] (2)将坯体从常温升温至800°C,升温时间为tFSOmin;
[0107] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2=40min,并在温度1000°C的 条件下保温,保温时间为t3 =20min;
[0108] (4)将坯体从1000°C升温至温度T,其中,所述温度T为1150°C,升温时间为t4= 40min;
[0109] ⑸从温度T自然降温至常温,降温时间为t5=2小时;
[0110] 整体烧成周期为4h。
[0111] 实施例2
[0112] 将原料按配比混合,配方为:工业煤渣65%、泥料10%、钾长石5%、钠长石5%、石英5%、 抛光渣10%;
[0113] 经过球磨、喷雾、压制成型、干燥、烧成、抛光、磨边,最后打包成成品。
[0114] 其中,烧成步骤包括:
[0115] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层二氧化硅 高温粉末;
[0116] (2)将坯体从常温升温至800°C,升温时间为tFSOmin;
[0117] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2=50min,并在温度1000°C的 条件下保温,保温时间为t3 =25min;
[0118] (4)将坯体从1000°C升温至温度T,其中,所述温度T为1200°C,升温时间为t4= 50min;
[0119] (5)从温度T自然降温至常温,降温时间为t5=2小时35分钟;
[0120] 整体烧成周期为5h。
[0121] 实施例3
[0122] 将原料按配比混合,配方为:工业煤渣70%、泥料6%、钾长石6%、钠长石6%、石英6%、 抛光渣6%;
[0123] 经过球磨、喷雾、压制成型、干燥、烧成、抛光、磨边,最后打包成成品。
[0124] 其中,烧成步骤包括:
[0125] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层氧化铝高 温粉末;
[0126] (2)将坯体从常温升温至800°C,升温时间为
[0127] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2=60min,并在温度1000°C的 条件下保温,保温时间为t3 =30min;
[0128] (4)将坯体从1000°C升温至温度T,其中,所述温度T为1180°C,升温时间为t4= 50min;
[0129] ⑸从温度T自然降温至常温,降温时间为t5=3小时;
[0130] 整体烧成周期为6h。
[0131] 实施例4
[0132] 将原料按配比混合,配方为:工业煤渣76%、泥料6%、钾长石10%、钠长石4%、石英4%;
[0133] 经过球磨、喷雾、堆粉成型、干燥、烧成、切割成板、磨边,最后打包成成品。
[0134] 其中,烧成步骤包括:
[0135] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层二氧化硅 高温粉末;
[0136] (2)将坯体从常温升温至800°C,升温时间为tfSOmin;
[0137] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2=40min,并在温度1000°C的 条件下保温,保温时间为t3 =30min;
[0138] (4)将坯体从1000°C升温至温度T,其中,所述温度T为1160°C,升温时间为t4= 60min;
[0139] ⑸从温度T自然降温至常温,降温时间为t5=2小时;
[0140] 整体烧成周期为5 h。
[0141] 实施例5
[0142] 将原料按配比混合,配方为:工业煤渣50%、泥料10%、钾长石10%、钠长石10%、石英 10%、抛光渣10%;
[0143] 经过球磨、喷雾、堆粉成型、干燥、烧成、切割成板、磨边,最后打包成成品。
[0144] 其中,烧成步骤包括:
[0145] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层氧化铝高 温粉末;
[0146] (2)将坯体从常温升温至800°C,升温时间为t^eOmin;
[0147] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2=50min,并在温度1000°C的 条件下保温,保温时间为t3 =20min;
[0148] (4)将坯体从1000°C升温至温度T,其中,所述温度T为1220°C,升温时间为t4= 60min;
[0149] ⑸从温度T自然降温至常温,降温时间为t5=3小时;
[0150] 整体烧成周期为6小时10分钟。
[0151] 实施例6
[0152] 将原料按配比混合,配方为:工业煤渣62%、泥料10%、钾长石10%、钠长石10%、石英 4%、抛光渣1 %、羧甲基纤维素2%、三聚磷酸钠1 %;
[0153] 经过球磨、喷雾、堆粉成型、干燥、烧成、切割成板、磨边,最后打包成成品。
[0154] 其中,烧成步骤包括:
[0155] (1)在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层二氧化硅 高温粉末;
[0156] (2)将坯体从常温升温至800°C,升温时间为乜=2511^11;
[0157] (3)将坯体从800°C缓慢升温至1000°C,升温时间为t2=45min,并在温度1000°C的 条件下保温,保温时间为t3 =25min;
[0158] (4)将坯体从1000°C升温至温度T,其中,所述温度T为1250°C,升温时间为t4= 65min;
[0159] (5)从温度T自然降温至常温,降温时间为t5=3小时20分钟;
[0160] 整体烧成周期为6 h。
[0161] 将实施例1-6所得的轻质保温砖做技术检测,结果如下:
[0162]
Figure CN105175007BD00111
[0163] 综上,本发明制得的轻质保温砖质地坚硬、比重小、气孔率高、耐火温度超过1000 度,可以轻易抵抗常规火灾,导热系数小、抗压强度高,非常适合用于外墙的隔热保温以及 室内的隔热隔音保温。而且,本发明以工业煤渣为配方主体,很好地回收利用了废弃资源, 制备工艺简单,烧成时间短,节约能源。
[0164] 以上所述是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员 来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也视为 本发明的保护范围。

Claims (5)

1. 一种轻质保温砖,其特征在于,由以下主要原料制成: 工业煤渣 60-76% 泥料 6-20% 钟长石 4-20% 纳长石 4-20% 石英 4-20% 抛光渣 0.1-15%; 所述工业煤渣包括发电厂煤渣、供热煤渣、煤转气煤渣; 所述轻质保温砖由下述方法制得: 将原料按配比混合、经过球磨、喷雾、压制成型、干燥、烧成、抛光、磨边,最后打包成成 品; 所述烧成包括: (1) 在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层高温粉末; (2) 将坯体从常温升温至800 °C,升温时间为t; (3) 将坯体从800 °C缓慢升温至1000 °C,升温时间为t2 40-90min,并在温度1000 °C的条 件下保温,保温时间为t3 20-30min; (4) 将坯体从1000 °C升温至温度T,升温时间为t4,其中,所述温度T为1150-1250 °C ; (5) 从温度T自然降温至常温,降温时间为t5。 ti为20_60min,t4为40_80min,t5为2_4h,ti、t2、t3、t4、t5的时间总长为4-7 h; 所述高温粉末为氧化铝或二氧化硅; 所述泥料是黑泥或污泥; 所述原料配方中的%是指重量百分比。
2. —种轻质保温砖,其特征在于,由以下主要原料制成: 工业煤渣 60-76% 泥料 6-20% 钟长石 4-20% 纳长石 4-20% 石英 4-20% 抛光渣 0.1-15%; 所述工业煤渣包括发电厂煤渣、供热煤渣、煤转气煤渣; 所述轻质保温砖由下述方法制得: 将原料按配比混合、经过球磨、喷雾、堆粉成型、干燥、烧成、切割成板、磨边,最后打包 成成品; 所述烧成包括: (1) 在坯体下方加入耐火垫板,所述坯体与耐火垫板之间铺上至少一层高温粉末; (2) 将坯体从常温升温至800 °C,升温时间为t; (3) 将坯体从800 °C缓慢升温至1000 °C,升温时间为t2 40-90min,并在温度1000 °C的条 件下保温,保温时间为t3 20-30min; (4) 将坯体从1000 °C升温至温度T,升温时间为t4,其中,所述温度T为1150-1250 °C ; (5)从温度T自然降温至常温,降温时间为t5; ti为20_60min,t4为40_80min,t5为2_4h,ti、t2、t3、t4、t5的时间总长为4-7 h; 所述高温粉末为氧化铝或二氧化硅; 所述泥料是黑泥或污泥; 所述原料配方中的%是指重量百分比。
3. 如权利要求1或2所述的轻质保温砖,其特征在于,所述轻质保温砖由以下主要原料 制成: 工业煤渣 60-76% 泥料 8-20% 钟长石 5-20% 纳长石 5-20% 石英 5-20% 抛光渣 0.1-15%; 所述原料配方中的%是指重量百分比。
4. 如权利要求1或2所述的轻质保温砖,其特征在于,所述轻质保温砖的原料还包括:辅 助料3-10%, 所述辅助料为羧甲基纤维素、三聚磷酸钠中的一种或组合;所述原料配方中的%是指重 量百分比。
5. 如权利要求1所述的轻质保温砖,其特征在于,所述轻质保温砖的比重为0.2-0.8,耐 火温度> l〇〇〇°C,导热系数为0.04〜0. l〇W(m. k)。
CN201510533537.9A 2015-08-27 2015-08-27 一种轻质保温砖 Active CN105175007B (zh)