CN105131709A - Water-soluble gravure ink and preparation method thereof - Google Patents
Water-soluble gravure ink and preparation method thereof Download PDFInfo
- Publication number
- CN105131709A CN105131709A CN201510545417.0A CN201510545417A CN105131709A CN 105131709 A CN105131709 A CN 105131709A CN 201510545417 A CN201510545417 A CN 201510545417A CN 105131709 A CN105131709 A CN 105131709A
- Authority
- CN
- China
- Prior art keywords
- water
- ink
- solvent
- agent
- agents
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses water-soluble gravure ink and a preparation method thereof. The water-soluble gravure ink is prepared from, by mass, 40-60% of acrylic emulsion, 5-15% of polyurethane emulsion, 10-15% of pigment, 2-3% of solvent, 0.2-1% of defoaming agents, 0.5-1.5% of dispersing agents, 0.2-1% of flatting agents, 12-21% of water and 1-3% of curing agents. The acrylic emulsion, the polyurethane emulsion and the defoaming agents are stirred and dispersed to be prepared into pre-emusion, then the pigment, the dispersing agents, the flatting agents, the solvent and the water are added, the mixture is stirred evenly, before the ink is used, the curing agents are added, the ink is stirred and dispersed, and then the ink can be used. According to the water-soluble gravure ink and the preparation method thereof, the significant advantages of being safe, free of poison and harm, non-ignitable, non-explosive and the like are achieved, and human body health and environment safety are facilitated; when the ink is used, the ink is good in stability on an ink machine, rapid to dry, clear in patterns of printed products and capable of simultaneously suitable for multiple substrates such as paper and plastic.
Description
Technical field
The present invention relates to ink area, specifically water-soluble base gravure ink and preparation method thereof.
Background technology
The ink of present stage China's intaglio printing, be still Chlorinated Polypropylene III class about half, Chlorinated Polypropylene III class contains the VOC such as a large amount of toluene, butanone, mibk, but due to cheap, so share of market is still very high.Traditional soft packaging intaglio printing, main or employing Chlorinated Polypropylene III is that the benzene that has of Primary resins has ketone solvent type ink.Carving intaglio printing ink due to routine contains a large amount of vegetables oil, oil-soluble polymers tackiness agent is (as plant oil modified alkyd resin adhesiver agent, urethane resin adhesives, rosin and derivative polyol ester resin glue thereof, rosin modified phenolic resin tackiness agent, oil soluble pure phenolic resin tackiness agent, epoxy resin binder etc.), tensio-active agent, wax, siccative, solvent (if #200 solvent oil and/or 210 Dormant oils and/or boiling range are at 170-190 DEG C lower without boiling points such as aromatic hydrocarbons Dormant oils or solvent that boiling range is narrower) etc., harm is existed to environment and the person, be not suitable for printing printings such as the strict packagings of health conditions requiring, and in the carving intaglio printing ink production process of routine and there is certain combustibility in use procedure, ink smell is large and printing aftertreatment cost is high, and environmental pollution is serious, brings inconvenience, such as CN1390897A to safe and secret typography, CN1392203A, CN1563221A, CN1560145A, the plate engraving ink of these routines has the advantage of not adding a cover paper print money, is generally latter 24 hours of printing time of drying, because time of drying is longer, give the product after printing deposit process bands together with lower in typography come inconvenient, in plate engraving ink, solvent is volatile, and in printing process, wiping version liquid contains sodium hydroxide and alizarin assistant is many, after being completed for printing, brings severe contamination to environment.
Summary of the invention
The object of the present invention is to provide safety, nontoxic water-soluble base gravure ink and preparation method thereof, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
Water-soluble base gravure ink, is grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 40-60%, polyaminoester emulsion 5-15%, pigment 10-15%, solvent 2-3%, defoamer 0.2-1%, dispersion agent 0.5-1.5%, flow agent 0.2-1%, water 12-21%, solidifying agent 1-3%.
As the further scheme of the present invention: water-soluble base gravure ink, be grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 56%, polyaminoester emulsion 10%, pigment 12.5%, solvent 2.5%, defoamer 0.5%, dispersion agent 1%, flow agent 0.5%, water 15%, solidifying agent 2%.
The preparation method of described water-soluble base gravure ink, first ACRYLIC EMULSION, polyaminoester emulsion and defoamer dispersed with stirring are made pre-emulsion, then add pigment, dispersion agent, flow agent, solvent, water, stir, add solidifying agent dispersed with stirring before using, can use.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention is not containing the ink composite of benzophenone class, esters solvent, have safe, nontoxic, do not fire the distinguishing features such as not quick-fried, be conducive to HUMAN HEALTH and environmental safety, during use, good at ink machine stability, ink setting is fast, and printing figure line is clear, solves the deficiency of aqueous ink composition at machine stability and ink setting aspect of performance; By selecting special construction resin, solve the binding strength of aqueous ink composition on base material and the problem in printing materialization patience, this ink composite can be applicable to the multiple base material such as paper and plastics simultaneously.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, water-soluble base gravure ink, is grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 60%, polyaminoester emulsion 5%, pigment 10%, solvent 2%, defoamer 1%, dispersion agent 1%, flow agent 1%, water 19%, solidifying agent 1%.
The preparation method of water-soluble base gravure ink, first ACRYLIC EMULSION, polyaminoester emulsion and defoamer dispersed with stirring are made pre-emulsion, then add pigment, dispersion agent, flow agent, solvent, water, stir, add solidifying agent dispersed with stirring before using, can use.
Embodiment 2
In the embodiment of the present invention, water-soluble base gravure ink, is grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 40%, polyaminoester emulsion 15%, pigment 15%, solvent 3%, defoamer 1%, dispersion agent 1.5%, flow agent 1%, water 20.5%, solidifying agent 3%.
Preparation process as described in Example 1.
Embodiment 3
In the embodiment of the present invention, water-soluble base gravure ink, is grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 56%, polyaminoester emulsion 10%, pigment 12.5%, solvent 2.5%, defoamer 0.5%, dispersion agent 1%, flow agent 0.5%, water 15%, solidifying agent 2%.
Preparation process as described in Example 1.
Embodiment 4
In the embodiment of the present invention, water-soluble base gravure ink, is grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 60%, polyaminoester emulsion 12.1%, pigment 12%, solvent 2%, defoamer 0.2%, dispersion agent 0.5%, flow agent 0.2%, water 12%, solidifying agent 1%.
Preparation process as described in Example 1.
Embodiment 5
In the embodiment of the present invention, water-soluble base gravure ink, is grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 55%, polyaminoester emulsion 10%, pigment 12%, solvent 2%, defoamer 0.5%, dispersion agent 1.5%, flow agent 0.2-1%, water 17%, solidifying agent 1%.
Preparation process as described in Example 1.
Embodiment 6
In the embodiment of the present invention, water-soluble base gravure ink, is grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 50%, polyaminoester emulsion 15%, pigment 15%, solvent 2%, defoamer 1%, dispersion agent 1%, flow agent 1%, water 14%, solidifying agent 11%.
Preparation process as described in Example 1.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should by specification sheets integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.
Claims (3)
1. water-soluble base gravure ink, it is characterized in that, be grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 40-60%, polyaminoester emulsion 5-15%, pigment 10-15%, solvent 2-3%, defoamer 0.2-1%, dispersion agent 0.5-1.5%, flow agent 0.2-1%, water 12-21%, solidifying agent 1-3%.
2. water-soluble base gravure ink according to claim 1, it is characterized in that, be grouped into by the following one-tenth according to mass percent: ACRYLIC EMULSION 56%, polyaminoester emulsion 10%, pigment 12.5%, solvent 2.5%, defoamer 0.5%, dispersion agent 1%, flow agent 0.5%, water 15%, solidifying agent 2%.
3. the preparation method of the water-soluble base gravure ink as described in as arbitrary in claim 1-2, it is characterized in that, first ACRYLIC EMULSION, polyaminoester emulsion and defoamer dispersed with stirring are made pre-emulsion, add pigment, dispersion agent, flow agent, solvent, water again, stir, add solidifying agent dispersed with stirring before using, can use.