CN105113729A - Rail material for building decoration and manufacturing method thereof - Google Patents
Rail material for building decoration and manufacturing method thereof Download PDFInfo
- Publication number
- CN105113729A CN105113729A CN201510556060.6A CN201510556060A CN105113729A CN 105113729 A CN105113729 A CN 105113729A CN 201510556060 A CN201510556060 A CN 201510556060A CN 105113729 A CN105113729 A CN 105113729A
- Authority
- CN
- China
- Prior art keywords
- railing
- architectural decoration
- galvanizing
- washing
- mild steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rail material for building decoration and a manufacturing method thereof. The manufacturing method comprises processing low-carbon steel as base material into semi-finished pieces; thermally zincing the semi-finished pieces, performing surface precision finishing on the thermally zinced pieces, and performing fluorocarbon spraying to finally obtain the rail material. By using the scheme above, the rail material is simple in structure and good in performance.
Description
Technical field
The invention belongs to a kind of architectural decoration railing material.
Background technology
Railing material and the production method in present architectural decoration field mainly contain two kinds:
1, use stainless steel to be materials processing, defect is as follows:
1.1 in order to make railing material in Long-Time Service process non-corrosive, do not corrode, because stainless steel cannot accomplish completely long-time non-corrosive, and Stainless Steel railing cost is very high.
1.2 stainless steel hardness are high, and welding performance is poor, process very difficult.
1.3 stainless steel colors are single, can not meet the raising of people's aesthetical standard.
2, use ordinary carbon steel to be materials processing, use cold galvanizing, surface brush is painted, and there is following defect:
2.1 paint are easy to come off, and Several Thiourea Derivatives on Zinc Plate Surface spraying adhesive power is inadequate, and spraying process is easy to foaming, and coating quality cannot ensure.
2.2 cold galvanizing zinc coats are very thin, only have 15 ~ 30 μm, and galvanizing process is formed at normal temperatures, and therefore zinc layers is thin, poor adhesive force.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of architectural decoration railing material and preparation method thereof, and in order to overcome carbon steel material for railing and architectural decoration materials, in prior art, paint is easy to come off, the shortcoming of antiseptic property difference.
It is as follows that the present invention solves the problems of the technologies described above taked technical scheme:
A preparation method for architectural decoration railing material, comprising:
Choosing mild steel as base material is processed into semi worked pieces;
Semi worked pieces is carried out galvanizing, fluorocarbon-sprayed processing after the workpiece after galvanizing is carried out special processing, final formation architectural decoration railing material.
Preferably, what described mild steel was chosen is model Q235-A mild steel.
Preferably, semi worked pieces is carried out galvanizing, and step is as follows:
------hydrotropy------------recheck in passivation in cooling in galvanizing by cleaning---go-on-go---in washing in pickling.
Preferably, processed by the surface of the work after galvanizing, step is as follows:
Dezincify knurl---precision leveling---water mill 1---water mill 2.
Preferably, the workpiece after galvanizing is carried out fluorocarbon-sprayed processing, and step is as follows:
---------------washing---is closed and---is dried---dedusting---primer spray---topcoating---spray finishing varnish---solidification in passivation in washing in degreasing in washing in pre-degreasing.
A kind of architectural decoration mild steel railing material be prepared from based on above method.
Preferably, described railing material, is followed successively by substrate layer, zinc coat, prime coat, top coat layer, Lacquer finish enamelled coating from top to bottom.
Preferably, what described substrate layer was chosen is model Q235-A mild steel.
After this invention takes such scheme, mild steel is after processing, the far super general mild steel of antiseptic property on surface, and the carbon steel material overcome after zinc-plated processing sprays paint the inadequate defect of adhesive power, thus ensure the decay resistance of railing material, solve a non-corrosive difficult problem for coastal area railing material, its structure is simple, and performance is good.
Other features and advantages of the present invention will be set forth in the following description, and, partly become apparent from manual, or understand by implementing the present invention.Object of the present invention and other advantages realize by structure specifically noted in write manual, claims and accompanying drawing and obtain.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, the present invention is described in detail, to make above-mentioned advantage of the present invention definitely.Wherein,
Fig. 1 is the structural representation of the material of architectural decoration railing of the present invention itself;
Fig. 2 is the structural representation of the railing that architectural decoration railing material of the present invention is made.
Detailed description of the invention
Describe embodiments of the present invention in detail below with reference to drawings and Examples, to the present invention, how application technology means solve technical problem whereby, and the implementation procedure reaching technique effect can fully understand and implement according to this.It should be noted that, only otherwise form conflict, each embodiment in the present invention and each feature in each embodiment can be combined with each other, and the technical scheme formed is all within protection scope of the present invention.
As shown in Figure 1, it is the structural representation of the material of architectural decoration railing of the present invention itself, it mainly comprises: be followed successively by substrate layer 5, zinc coat 4, prime coat 3, top coat layer 2, Lacquer finish enamelled coating 1 from top to bottom, wherein, in an embodiment, adopt Q235-A mild steel as substrate layer, it makes railing and is easy to processing, in general, and Q235, also being carbon structural steel or general plate, is a kind of material of steel.
Q representative be the surrender of this material, below 235, just refer to the yield value of this material, about 235.And its yield value can be reduced along with the increase of the thickness of material.
Q235-A level is containing C0.14 ~ 0.22%Mn0.30 ~ 0.65Si≤0.30S≤0.050P≤0.045.
Wherein, its preparation method mainly comprises the steps:
Choosing mild steel as base material is processed into semi worked pieces;
Semi worked pieces is carried out galvanizing, the workpiece after galvanizing is carried out fluorocarbon-sprayed processing, final formation architectural decoration railing material.
Preferably, what described mild steel was chosen is model Q235-A mild steel.
Preferably, semi worked pieces is carried out galvanizing, and step is as follows:
------hydrotropy---------------recheck in passivation in fine finishining in cooling in galvanizing by cleaning---go-on-go---in washing in pickling.
Preferably, processed by the surface of the work after galvanizing, step is as follows:
Dezincify knurl---precision leveling---water mill 1---water mill 2.
Preferably, the workpiece after galvanizing is carried out fluorocarbon-sprayed processing, and step is as follows:
---------------washing---is closed and---is dried---dedusting---primer spray---topcoating---spray finishing varnish---solidification in passivation in washing in degreasing in washing in pre-degreasing.
Fig. 2 is the structural representation of the railing that architectural decoration railing material of the present invention is made.
Effect of the present invention:
1, adopt Q235-A mild steel to make railing as base material and be easy to processing.
2, adopt the antirust corrosive nature of putting of hot dip galvanizing process good.
3, adopt and fluorocarbon-sprayedly make product color variation, can improve that railing is antirust, Corrosion Protection further.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (7)
1. a preparation method for architectural decoration railing material, is characterized in that, comprising:
Choosing mild steel as base material is processed into semi worked pieces;
Semi worked pieces is carried out galvanizing, the workpiece after galvanizing is carried out retrofit surface and carries out fluorocarbon-sprayed processing, final formation architectural decoration railing material.
2. the preparation method of architectural decoration railing material according to claim 1, is characterized in that, what described mild steel was chosen is model Q235-A mild steel.
3. the preparation method of architectural decoration railing according to claim 1 and 2, is characterized in that, semi worked pieces is carried out galvanizing, and step is as follows:
---------------------go-on-go---rechecks---removing surface list edge---finishing smoothing---thick water mill---smart water mill to hydrotropy in cleaning in passivation in cooling in galvanizing in washing in pickling.
4. the preparation method of architectural decoration railing material according to claim 1 and 2, it is characterized in that, the workpiece after galvanizing is carried out fluorocarbon-sprayed processing, and step is as follows:
---------------washing---dries---surface-sealing---primer spray---topcoating---spray finishing varnish---solidification in passivation in washing in degreasing in washing in pre-degreasing.
5. the architectural decoration railing material be prepared from based on Claims 1 to 4 either method.
6. architectural decoration railing material according to claim 5, is characterized in that, described railing material is followed successively by substrate layer, zinc coat, prime coat, top coat layer, Lacquer finish enamelled coating from top to bottom.
7. the architectural decoration railing material according to claim 5 or 6, what it is characterized in that described substrate layer chooses is model Q235-A mild steel.