CN201494233U - Anti-scratching anti-abrasion color coating steel plate - Google Patents
Anti-scratching anti-abrasion color coating steel plate Download PDFInfo
- Publication number
- CN201494233U CN201494233U CN2009202222684U CN200920222268U CN201494233U CN 201494233 U CN201494233 U CN 201494233U CN 2009202222684 U CN2009202222684 U CN 2009202222684U CN 200920222268 U CN200920222268 U CN 200920222268U CN 201494233 U CN201494233 U CN 201494233U
- Authority
- CN
- China
- Prior art keywords
- layer
- steel plate
- zinc
- steel strip
- scratching
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to an anti-scratching anti-abrasion color coating steel plate, which uses a galvanization or aluminum-zinc alloy substrate as a base material, and comprises a substrate layer, a galvanization or an aluminum-zinc alloy layer, a chemical conversion layer and a color painting layer from the core to outside in turn, wherein the coarse surfaces of the galvanization or the aluminum-zinc alloy layer and the chemical conversion layer are contacted. The anti-scratching anti-abrasion color coating steel plate greatly improves the adhesive force of the coating layer through improving the structure of the steel plate of the color coating layer, and has the advantages that firstly, the anti-scratching anti-abrasion color coating steel plate has excellent anti-scratching and anti-abrasion property, the service span of products manufactured by the anti-scratching anti-abrasion color coating steel plate is obviously higher than a normal color coating steel plate under the use environment of repeated folding and mutual friction, secondly, the anti-scratching anti-abrasion color coating steel plate has excellent bending and processing property, the coating layer is not cracked and stripped under various complex processing conditions, and thirdly, the surface has excellent sand surface visual effects.
Description
Technical field
The utility model relates to the material technology field, specifically, relates to a kind of scratch-resistant and wear-resistant color coat steel plate.
Background technology
Color painted steel strip is meant the steel plate that has organic coating on substrate, generally abbreviates Coil Coating Products as, and its substrate commonly used is a cold-rolled substrate, hot dip galvanizing substrate and electrogalvanizing substrate; Coating commonly used has polyester, silicon modified polyester, poly-partially difluoroethylene and plastisol etc.It is good that color painted steel strip has corrosion resistance, bright in luster, appearance looks elegant, machine-shaping is convenient, the intensity height, advantage such as cost is lower is widely used in industries such as building household electrical appliances and communications and transportation, building industry particularly mainly is used as the roof wall surface of industry such as steel-structure factory building, airport, storehouse and freezer and commercial building and door etc.
Through the developing history of two more than ten years, the color painted steel strip industry is greatly developed in China, and its output is with the speed increment in every year average 40%, and China has become world color painted steel strip big producing country.But the quality of the color product made from steel of China also is in low side, and its durability, apparent property and functional and external like product also have a certain distance.
The tradition color painted steel strip is to be base material with zinc-plated or aluminum-zinc alloy substrate, through the preliminary treatment degreasing, be coated with chemical composition coating, linging back of the body lacquer, be coated with finish paint after secondary baking form.The common color coated steel sheet is with epoxy or polyester or the polyurethane resin main film forming substance as priming paint, with polyester or silicon modified resin or other resins main film forming substance as finish paint.Difference according to product purpose is coated with lacquer the corresponding collocation of paint ingredient to satisfy the performance requirement of different use occasions to filming to the bottom surface.It is long-term serviceability that factory building requires paint film to have good weatherability with color painted steel strip, and higher hardness is to avoid processing the scuffing in the use, and physical performance index commonly used is: pencil hardness 〉=2H; T bends≤3T; MEK 〉=100 time; Salt spray resistance meets the respective country standard; And the coated steel sheet that tame electroplax uses requires paint film to have good Bending Processing performance and pliability, good paint film adhesion, and physical performance index commonly used is: T is curved≤and 1T; 0 grade of adhesive force (cross-hatching); More than the pencil hardness F level; MEK 〉=50 time.This two classes color painted steel strip is at present the most frequently used and typical application example, and the former is a color painted steel strip for building, and when it need to be used to the bending machining product, because of the curved poor-performing of its T, hardness of paint film was higher and the cracking and the quick-fried lacquer of paint film easily take place; The latter is the household electrical appliances color painted steel strips, when it is used for that needs are antifriction, during anti-scratch product, very easily damage in processing or use because of its paint film is softer.
Along with expanding economy and growth in the living standard, the application of color painted steel strip constantly enlarges, and present high-grade color painted steel strip is more and more by employings such as building material industry such as high clean room, freezer, multi-storied garages; Also be used to part electrical equipment such as STB, part household electrical appliances plate such as refrigerator refrigerator dorsal plate, solar water heater header tank etc., and boats and ships decoration, interior decoration and furniture industry etc.In these application scenarios, not only require color painted steel strip to have the excellent in vending workability energy, require it to have good anti-scratching wearproof performance, good long-term serviceability and beautiful appearance simultaneously.
Therefore, be necessary to provide a kind of color painted steel strip of anti-scratching wearproof.
The utility model content
The purpose of this utility model is to overcome the deficiency of above-mentioned color painted steel strip, provide a kind of and can satisfy the complicated bend processing characteristics and require simultaneously that paint film has remarkable anti-scratching wearproof characteristic again, and have the good long-term serviceability and the color painted steel strip of beautiful outward appearance.
The color painted steel strip of anti-scratching wearproof described in the utility model, be to be base material with zinc-plated or aluminum-zinc alloy substrate, from its core to the outside, comprise substrate layer, zinc-plated or aluminum-zinc alloy layer, chemical conversion layer and colour coating successively, wherein, described zinc-plated or aluminum-zinc alloy layer is that matsurface contacts with described chemical conversion layer.
The contact of described matsurface is meant that on the surface of zinc-plated or aluminum-zinc alloy substrate be rough surface, then chemical conversion layer is coated in this rough surface, with improve described zinc-plated or aluminum-zinc alloy layer, and described chemical conversion layer between adhesion.
Described colour coating comprises priming coat and back coating, is the coating that is made of amino modified epoxy resin, and described priming coat and back coating lay respectively at the outer surface and the inner surface of color painted steel strip;
The thickness of described back coating is 5～12 μ m, and it has formed the colour coating of color painted steel strip inner surface;
The thickness of described priming coat is 4～6 μ m;
Described colour coating also comprises finishing coat, and it is positioned at the outer surface of described priming coat;
Described finishing coat is the coating that is made of polyamide modified mylar, and itself and described priming coat are formed the described colour coating of color painted steel strip outer surface jointly.
The thickness of described finishing coat is 15～20 μ m;
Described rough surface can make by this area preparation method commonly used, as burn into frosted processing etc., the preferred mode that adopts brush roll to grind, remove the passivation layer and the plate face greasy dirt spot of zinc-plated or aluminum-zinc alloy laminar surface fully, and zinc layer outermost top layer slightly ground, so that expose nascent state zinc layer or aluminium zinc layer; On apparent, remove yellow passivation layer fully, expose zinc white look (nascent state zinc layer or aluminium zinc layer), apply chemical conversion layer then, improve the adhesive force of chemical conversion layer greatly.
Specifically, select for use nylon yarn as the hairbrush material, brush roll is made backward rotation by motor-driven and steel plate traffic direction, nylon yarn slightly contacts with steel plate, contact force is not to destroy zinc-plated or the aluminum-zinc alloy layer is as the criterion, until the passivation layer of removing zinc-plated or aluminum-zinc alloy laminar surface fully and plate face greasy dirt spot, and zinc layer outermost top layer slightly ground, so that expose nascent state zinc layer or aluminium zinc layer.
The color painted steel strip of anti-scratching wearproof described in the utility model is a base material with zinc-plated or aluminum-zinc alloy substrate, adopts the following steps preparation: 1) spray degreasing; 2) brush roll is ground; 3) coating chemical composition coating, oven dry; 4) roller coat priming paint, back of the body lacquer, baking; 5) roller coat finish paint, baking molding.
In described step 2) afterwards, before the described step 3), also comprise ii) degreasing;
Step I i) described degreasing is for the grease that will may introduce in processing procedure on the substrate cleans up fully, can adopt this area method commonly used to carry out, and also can adopt spray process.
For guaranteeing the cleaning of substrate, at described step I i) afterwards, before the described step 3), also comprise iii) washing;
The ii) described washing of step I can be carried out repeatedly, preferred 3-4 time.
It is the surface of the zinc-plated or aluminum-zinc alloy substrate after placing spray degreasing to handle brush roll that described brush roll is ground, driving and driving direction are opposite with the substrate motion direction, grind, until the passivation layer of removing zinc-plated or aluminum-zinc alloy laminar surface fully and plate face greasy dirt spot, and zinc layer outermost top layer slightly ground, so that expose nascent state zinc layer or aluminium zinc layer; On apparent, remove yellow passivation layer fully, expose zinc white look (nascent state zinc layer or aluminium zinc layer), improve the adhesive force of chemical conversion layer greatly.
The employing brush roll is ground, the one, can remove the purpose that remaining greasy dirt reaches the cleaned base material surface, the 2nd, the passivation layer that can destroy zinc-plated substrate surface exposes initial state zinc layer, because the existence of passivation layer will reduce the adhesive force of chemical composition coating and priming paint and base material greatly.Slightly grind back coating one deck chemical composition coating through brush roll and be coated with one deck priming paint again, the adhesion of priming paint and base material will be greatly improved.
Described brush roll can select for use nylon yarn as the hairbrush material, and nylon yarn slightly contacts with steel plate, and contact force is a standard not destroy the zinc layer.Should be noted that: " overmastication " phenomenon can occur when excessive or nylon yarn is because of ageing hardening when brush roll pressure, the wire cut can appear in promptly zinc-plated substrate surface.Should in time regulate brush roll pressure this moment or change brush roll.
Described priming paint and back of the body lacquer adopt amino modified epoxy resin, baking temperature is PMT224～232 ℃, and film thickness is priming paint 4～6 μ m, back of the body lacquer 5～12 μ m, both keep good closure property of epoxy resin and good adhesive force, had the pliability that adopts amino modified back resin again;
Described finish paint adopts polyamide modified mylar, and it is PMT216～224 ℃ that face is coated with the baking temperature, and film thickness is 15～20 μ m, and this resin has higher hardness and sand face effect, so topcoat has good anti-scratching wearproof effect.
The spray pressure of the described spray degreasing of step 1) can be according to crossing plate length and flow different choice, preferred 1.5～2.5kg/cm
2Effectively spray time is 8～12 seconds; Used tank liquor temperature is controlled at 55 ± 5 ℃;
Described chemical composition coating adopts this area chromate epithelium commonly used (chromate and zinc form metallo-chelate), and its bake out temperature is 80～100 ℃;
The utility model has improved adhesive force of coatings greatly by the architecture advances to color painted steel strip; In conjunction with to being used of finish paint and priming paint, prepare described scratch-resistant and wear-resistant color coat steel plate, its advantage mainly contains:
1. has good anti-scratching wearproof characteristic.Adopt product that this colored steel makes under the environment for use of folding, mutual friction, be significantly higher than the common color coated steel sheet its service life;
2. has the excellent in vending workability energy.Under various complicated processing conditions, coating does not ftracture, does not peel off;
3. the surface has good sand facial vision effect.
And preparation method of the present utility model is simply effective, the equipment less investment, and cost is low, is very suitable for continuous roller coat production.
Description of drawings
Fig. 1 scratch-resistant and wear-resistant color coat steel plate cross-sectional view, 1: substrate; 2,2 ': zinc-plated or aluminum-zinc alloy layer; 3,3 ': chemical conversion layer; 4: priming coat; 5: back coating; 6: finishing coat.
Fig. 2 brush roll is ground schematic diagram.
The specific embodiment
Following examples are used to illustrate utility model, but are not used for limiting the scope of utility model.
Adopting the aluminum-zinc alloy substrate is base material, and the continuous automatic production process flow process of scratch-resistant and wear-resistant color coat steel plate is as follows:
Uncoiling → spray degreasing I → brush roll grinding → degreasing II → three road washing → chemical composition coating → oven dry → primary coat/back ofs the body are coated with → toast → and the I → face that cools off is coated with → toasts → cool off II → check → rolling.
Spray degreasing I adopts alkaline degreasing method, and main component is that NaOH, sodium carbonate, tertiary sodium phosphate, sodium metasilicate etc. and surfactant are formed, and tank liquor temperature is controlled at 55 ± 5 ℃; Spray pressure 2.0kg/cm
2Effectively spray time is 10 seconds; Degreasing II washes sheet material with alkali lye;
In the washing of three roads, first and second road adopts demineralized water, and the washing of the 3rd road adopts deionized water to guarantee the substrate surface cleannes;
It is the surface of the zinc-plated or aluminum-zinc alloy substrate after placing spray degreasing to handle brush roll that brush roll is ground, driving and driving direction are opposite with the substrate motion direction, grind, until removing yellow passivation layer and plate face greasy dirt spot fully, and zinc layer outermost top layer slightly ground, so that expose the zinc white look, process is seen shown in Figure 2.
Brush roll selects for use nylon yarn as the hairbrush material, and nylon yarn slightly contacts with steel plate, and contact force is standard (zinc-plated substrate surface the wire cut can not occur) not destroy the zinc layer.
Chemical composition coating adopts the chromate epithelium, and bake out temperature is 100 ℃;
The baking temperature that is coated with of control primary coat/back of the body is PMT224～232 ℃, and film thickness is primary coat 5 ± 1 μ m, and carrying on the back and being coated with thickness is 8 ± 1 μ m; It is PMT216～224 ℃ that face is coated with the baking temperature, and film thickness is 18 ± 1 μ m, and its structure chart is seen shown in Figure 1, to the outside, obtains comprising substrate 1 from its core; Zinc-plated or aluminum-zinc alloy layer 2,2 '; Chemical conversion layer 3,3 '; Priming coat 4; Back coating 5; The anti-scratching wearproof colour coating steel plate of finishing coat 6.With table 1 Listed Items this scratch-resistant and wear-resistant color coat steel plate being carried out performance indications detects:
Table 1 color painted steel strip performance indications detect
The results are shown in Table 2: obviously, through after the coarse processing of brush roll, adhesive force of coatings increases greatly.
Table 2 scratch-resistant and wear-resistant color coat steel plate The performance test results
Adopting uses the same method measures the correlated performance of the color steel of the recoat oil that grinds without brush roll or the zinc-plated substrate preparation after the passivation, compares with the color steel index after hairbrush grinds, and the curved performance of its adhesive force and T is obviously relatively poor, and concrete outcome sees Table 3:
Table 3 grinds and does not grind the contrast of color coating properties of product through brush roll
Adopt amino modified epoxy coating to make the anti-scratching wearproof color steel that priming paint and polyamide modified Polyester resin lacquer are made as finish paint, its every performance indications and ordinary epoxy resin coating are done that priming paint, Polyester resin lacquer are made finish paint or are that priming paint, polyester coating are that the color steel that finish paint is made carries out performance comparison with polyester (or polyurethane) coating, the results are shown in Table 4:
The different coating color steel of table 4 performance comparison
Wang: (1) amino modified epoxy primer, polyamide modified polyester finish coat
(2) epoxy primer, polyester finish coat
(3) polyester (polyurethane) priming paint, polyester finish coat
Can find out that from table 4 when the bottom surface lacquer adopted upward table (2) combination, colored steel T bent poor-performing, hardness is not high enough; When adopting (3) combination, paint film adhesion is relatively poor, and hardness is on the low side equally, obviously, adopts amino modified epoxy coating to make the anti-scratching wearproof color steel that priming paint and polyamide modified Polyester resin lacquer are made as finish paint, and its every performance indications are more superior.
Claims (7)
1. the color painted steel strip of an anti-scratching wearproof, with zinc-plated or aluminum-zinc alloy substrate is base material, to the outside, comprises substrate layer, zinc-plated or aluminum-zinc alloy layer, chemical conversion layer and colour coating from its core successively, wherein, described zinc-plated or aluminum-zinc alloy layer is that matsurface contacts with described chemical conversion layer.
2. color painted steel strip as claimed in claim 1 is characterized in that, described matsurface contact is meant that the outer surface at zinc-plated or aluminum-zinc alloy layer is a rough surface, then chemical conversion layer is coated in this rough surface.
3. color painted steel strip as claimed in claim 1 is characterized in that described colour coating comprises priming coat and back coating, and described priming coat and back coating lay respectively at the outer surface and the inner surface of color painted steel strip, is the coating that is made of amino modified epoxy resin;
4. color painted steel strip as claimed in claim 3 is characterized in that, the thickness of described back coating is 5～12 μ m.
5. color painted steel strip as claimed in claim 3 is characterized in that, the thickness of described priming coat is 4～6 μ m.
6. color painted steel strip as claimed in claim 3 is characterized in that described colour coating also comprises finishing coat, and it is positioned at the outer surface of described priming coat;
Described finishing coat is the coating that is made of polyamide modified mylar, and itself and described priming coat are formed the described colour coating of color painted steel strip outer surface jointly.
7. color painted steel strip as claimed in claim 6 is characterized in that, the thickness of described finishing coat is 15～20 μ m.