CN105113092A - Antistatic woven fabric and preparation method thereof - Google Patents
Antistatic woven fabric and preparation method thereof Download PDFInfo
- Publication number
- CN105113092A CN105113092A CN201510583776.5A CN201510583776A CN105113092A CN 105113092 A CN105113092 A CN 105113092A CN 201510583776 A CN201510583776 A CN 201510583776A CN 105113092 A CN105113092 A CN 105113092A
- Authority
- CN
- China
- Prior art keywords
- antistatic
- polyester fiber
- woven fabrics
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses antistatic woven fabric and a preparation method thereof. The antistatic woven fabric comprises 50-60 parts of polyester fiber polyester yarn, 10-15 parts of wool, 10-15 parts of cashmere, 5-8 parts of cotton, 3-5 parts of mucilage glue and 0.5-1.5 parts of antistatic agents. The preparation method comprises the steps of loose wool dyeing, wool combining, carding, twisting, sheet weaving, after-finishing and the like. The woven fabric prepared through the blends of different proportions has the advantages of being stiff in appearance, good in heat stability, soft, free of pilling, free of static and the like, and compared with conventional multifunctional finished fabric, the production and aftertreatment process is greatly simplified, and production efficiency is improved.
Description
Technical field
The present invention relates to a kind of antistatic Woven Fabrics and preparation method thereof, belong to textile technology field.
Background technology
Traditional Woven Fabrics is usually by natural fabric, synthetic fiber or its blending composition, and antistatic effect is bad, easily produce electrostatic, and antiultraviolet, fire resistance property are strong, Multifunctional finishing complex process, and cost is high; And polyester fiber to have outward appearance well-pressed, the advantage of Heat stability is good, therefore, has a good application prospect in drapery, bedding, interior decoration etc.
Summary of the invention
In order to solve problems of the prior art as above, the invention provides that a kind of preparation method is simple, the antistatic Woven Fabrics of good product quality and preparation method thereof.
In order to reach the object of foregoing invention, technical scheme of the present invention is:
A kind of antistatic Woven Fabrics, is characterized in that, comprises following component and the parts by weight of each component are respectively:
Polyester fiber is lost synthetic fibre silk: 50-60 part;
Wool: 10-15 part;
Cashmere: 10-15 part;
Cotton: 5-8 part;
Viscose glue: 3-5 part;
Antistatic additive: 0.5-1.5 part.
Further, described antistatic additive is any one in ammonium salt, quaternary ammonium salt, alkyl amino acid.
Further, the be lost preparation method of synthetic fibre silk of described polyester fiber is: the terephthalic acid (TPA) of equivalent and ethylene glycol are carried out polycondensation reaction under temperature is the condition of 50-60 DEG C, reaction time is 15-20h, generate polyester stoste, then carry out spinning and obtain polyester fiber, be organized into silk thread through a point shuttle again, obtain polyester fiber and to be lost synthetic fibre silk.And described polyester fiber is lost, the length of synthetic fibre silk is greater than 60mm, and fineness is 20-25den.
A preparation method for above-mentioned antistatic Woven Fabrics, is characterized in that, comprise the following steps:
(1) dye: take polyester fiber according to the ratio of weight and number of each component and to be lost synthetic fibre silk, wool, cashmere, cotton, viscose glue, and carry out a point cylinder flock dyeing, COLOR FASTNESS controls more than 3.5 grades;
(2) and hair: raw material step (1) processed adds the wool lubricant of corresponding amount, water and antistatic additive by spinning process requirement and mixes;
(3) spin, close and twist with the fingers: use combing machine for fur, carry out combing slivering to the raw material that step (2) processed, single thread made by rear upper fine spining machine, then each component single thread is closed and twist with the fingers, carry out doubling twisting and become blended yarn;
(4) upper woven: utilization is spun cloth machine and knitted sheet process to the yarn after step (3) conjunction sth. made by twisting, forms Woven Fabrics, and carries out washing and soft post processing.
And in upper woven step, knitting sheet density is: 126*22.
The invention has the beneficial effects as follows: utilize raw material of the present invention to form and the Woven Fabrics that obtains of preparation method to have outward appearance well-pressed, Heat stability is good, softness, not balling-up, without advantages such as electrostatic, and simplify production technology, improve production efficiency.
Detailed description of the invention
Below in conjunction with specific embodiment, concrete introduction is carried out to the present invention.
embodiment 1:
(1) terephthalic acid (TPA) of equivalent and ethylene glycol are carried out polycondensation reaction under temperature is the condition of 50 DEG C, the reaction time is 20h, generates polyester stoste, then carries out spinning and obtain polyester fiber, then is organized into silk thread through a point shuttle, obtains polyester fiber and to be lost synthetic fibre silk.And described polyester fiber is lost, the length of synthetic fibre silk is greater than 60mm, and fineness is 20-25den.
(2) dye: take 60 parts of polyester fibers according to the ratio of weight and number of each component and to be lost synthetic fibre silk, 10 parts of wools, 15 parts of cashmere, 5 parts of cottons, 5 parts of viscose glues, and carry out a point cylinder flock dyeing, COLOR FASTNESS controls more than 3.5 grades;
(3) and hair: raw material step (2) processed adds the wool lubricant of corresponding amount, water and 1.5 parts of ammonium salts by spinning process requirement and mixes;
(4) spin, close and twist with the fingers: use combing machine for fur, carry out combing slivering to the raw material that step (3) processed, single thread made by rear upper fine spining machine, then each component single thread is closed and twist with the fingers, carry out doubling twisting and become blended yarn;
(5) upper woven: utilization is spun cloth machine and knitted sheet process to the yarn after step (4) conjunction sth. made by twisting, and form Woven Fabrics, and carry out washing and soft post processing, finally knitting sheet density is: 126*22.
embodiment 2:
(1) terephthalic acid (TPA) of equivalent and ethylene glycol are carried out polycondensation reaction under temperature is the condition of 60 DEG C, the reaction time is 15h, generates polyester stoste, then carries out spinning and obtain polyester fiber, then is organized into silk thread through a point shuttle, obtains polyester fiber and to be lost synthetic fibre silk.And described polyester fiber is lost, the length of synthetic fibre silk is greater than 60mm, and fineness is 20-25den.
(2) dye: take 50 parts of polyester fibers according to the ratio of weight and number of each component and to be lost synthetic fibre silk, 15 parts of wools, 10 parts of cashmere, 8 parts of cottons, 3 parts of viscose glues, and carry out a point cylinder flock dyeing, COLOR FASTNESS controls more than 3.5 grades;
(3) and hair: raw material step (2) processed adds the wool lubricant of corresponding amount, water and 0.5 part of quaternary ammonium salt by spinning process requirement and mixes;
(4) spin, close and twist with the fingers: use combing machine for fur, carry out combing slivering to the raw material that step (3) processed, single thread made by rear upper fine spining machine, then each component single thread is closed and twist with the fingers, carry out doubling twisting and become blended yarn;
(5) upper woven: utilization is spun cloth machine and knitted sheet process to the yarn after step (4) conjunction sth. made by twisting, and form Woven Fabrics, and carry out washing and soft post processing, finally knitting sheet density is: 126*22.
embodiment 3:
(1) terephthalic acid (TPA) of equivalent and ethylene glycol are carried out polycondensation reaction under temperature is the condition of 55 DEG C, the reaction time is 18h, generates polyester stoste, then carries out spinning and obtain polyester fiber, then is organized into silk thread through a point shuttle, obtains polyester fiber and to be lost synthetic fibre silk.And described polyester fiber is lost, the length of synthetic fibre silk is greater than 60mm, and fineness is 20-25den.
(2) dye: take 55 parts of polyester fibers according to the ratio of weight and number of each component and to be lost synthetic fibre silk, 12 parts of wools, 12 parts of cashmere, 6 parts of cottons, 4 parts of viscose glues, and carry out a point cylinder flock dyeing, COLOR FASTNESS controls more than 3.5 grades;
(3) and hair: raw material step (2) processed adds the wool lubricant of corresponding amount, water and 1.0 parts of alkyl amino acids by spinning process requirement and mixes;
(4) spin, close and twist with the fingers: use combing machine for fur, carry out combing slivering to the raw material that step (3) processed, single thread made by rear upper fine spining machine, then each component single thread is closed and twist with the fingers, carry out doubling twisting and become blended yarn;
(5) upper woven: utilization is spun cloth machine and knitted sheet process to the yarn after step (4) conjunction sth. made by twisting, and form Woven Fabrics, and carry out washing and soft post processing, finally knitting sheet density is: 126*22.
The present invention is illustrated according to above-described embodiment and should be appreciated that above-described embodiment does not limit the present invention in any form, and all employings are equal to replacement or the technical scheme that obtains of equivalent transformation mode, all drop within protection scope of the present invention.
Claims (6)
1. an antistatic Woven Fabrics, is characterized in that, comprises following component and the parts by weight of each component are respectively:
Polyester fiber is lost synthetic fibre silk: 50-60 part;
Wool: 10-15 part;
Cashmere: 10-15 part;
Cotton: 5-8 part;
Viscose glue: 3-5 part;
Antistatic additive: 0.5-1.5 part.
2. the antistatic Woven Fabrics of one according to claim 1, is characterized in that, described antistatic additive is any one in ammonium salt, quaternary ammonium salt, alkyl amino acid.
3. the antistatic Woven Fabrics of one according to claim 1, it is characterized in that, the be lost preparation method of synthetic fibre silk of described polyester fiber is: the terephthalic acid (TPA) of equivalent and ethylene glycol are carried out polycondensation reaction under temperature is the condition of 50-60 DEG C, reaction time is 15-20h, generate polyester stoste, then carry out spinning and obtain polyester fiber, then be organized into silk thread through a point shuttle, obtain polyester fiber and to be lost synthetic fibre silk.
4. the antistatic Woven Fabrics of one according to claim 3, is characterized in that, the be lost length of synthetic fibre silk of described polyester fiber is greater than 60mm, and fineness is 20-25den.
5. a preparation method for antistatic Woven Fabrics according to claim 1, is characterized in that, comprise the following steps:
(1) dye: take polyester fiber according to the ratio of weight and number of each component and to be lost synthetic fibre silk, wool, cashmere, cotton, viscose glue, and carry out a point cylinder flock dyeing, COLOR FASTNESS controls more than 3.5 grades;
(2) and hair: raw material step (1) processed adds the wool lubricant of corresponding amount, water and antistatic additive by spinning process requirement and mixes;
(3) spin, close and twist with the fingers: use combing machine for fur, carry out combing slivering to the raw material that step (2) processed, single thread made by rear upper fine spining machine, then each component single thread is closed and twist with the fingers, carry out doubling twisting and become blended yarn;
(4) upper woven: utilization is spun cloth machine and knitted sheet process to the yarn after step (3) conjunction sth. made by twisting, forms Woven Fabrics, and carries out washing and soft post processing.
6. the preparation method of a kind of antistatic Woven Fabrics according to claim 5, is characterized in that, in upper woven step, knitting sheet density is: 126*22.