CN105111706A - 一种采用玻纤增强手机外壳用塑料及其制备方法 - Google Patents

一种采用玻纤增强手机外壳用塑料及其制备方法 Download PDF

Info

Publication number
CN105111706A
CN105111706A CN201510442336.8A CN201510442336A CN105111706A CN 105111706 A CN105111706 A CN 105111706A CN 201510442336 A CN201510442336 A CN 201510442336A CN 105111706 A CN105111706 A CN 105111706A
Authority
CN
China
Prior art keywords
phone housing
polycarbonate
glass fibre
preparation
mobile phone
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510442336.8A
Other languages
English (en)
Inventor
张瑞辉
王杰
王影
戴碧城
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan City Xin Tai Communication Apparatus Co Ltd
Original Assignee
Dongguan City Xin Tai Communication Apparatus Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dongguan City Xin Tai Communication Apparatus Co Ltd filed Critical Dongguan City Xin Tai Communication Apparatus Co Ltd
Priority to CN201510442336.8A priority Critical patent/CN105111706A/zh
Publication of CN105111706A publication Critical patent/CN105111706A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种采用玻纤增强手机外壳用塑料，其原料按质量比包括：聚碳酸酯30-70，导热填料10-20，阻燃剂5-10，偶联剂1-5，玻璃纤维25-40。本发明的有益效果是：采用玻纤增强手机壳体塑料，并再配合原料中的导热填料、阻燃剂、偶联剂，结合着本发明的制备方法及参数，能够使得产品在厚度减薄的情况下，提升了壳体的整体和局部强度，从而使得该塑料能够满足手机相关性能需要。

Description

一种采用玻纤增强手机外壳用塑料及其制备方法
技术领域
本发明涉及塑料材料技术领域，特别是一种采用玻纤增强手机外壳用塑料及其制备方法。
背景技术
手机是日常生活中常见的用品。手机的使用过程中，难免会遇到掉落、磕碰、划擦等情况，轻则会造成手机壳的划伤形成划痕，重则会导致手机壳的开裂。手机壳体的强度还不能满足手机相关性能的需要。
发明内容
本发明的目的在于克服现有技术的缺点，提供一种提高手机壳强度的采用玻纤增强手机外壳用塑料及其制备方法。
本发明的目的通过以下技术方案来实现：一种采用玻纤增强手机外壳用塑料，其原料按质量比包括：
聚碳酸酯30-70，
导热填料10-20，
阻燃剂5-10，
偶联剂1-5，
玻璃纤维25-40。
所述的采用玻纤增强手机外壳用塑料的制备方法，包括以下步骤：
a、在聚碳酸酯中添加玻璃纤维并混合均匀；
b、将混合好的玻璃纤维与聚碳酸酯在干燥机内烘干，烘干温度115℃～125℃，时间3h～4h；
c、烘干好的混合材料置于注塑机内，并加入导热填料、阻燃剂、偶联剂；
d、在下述的工艺参数下将原材料塑化：料管温度295℃～340℃、树脂温度315℃～345℃、螺杆转速40rpm～60rpm；
e、产品生产：熔化的原材料从喷嘴中射出，进入手机壳体模具，射出速度为100mm/s～300mm/s，模具温度80℃～115℃。
本发明具有以下优点：
本发明采用玻纤增强手机壳体塑料，并再配合原料中的导热填料、阻燃剂、偶联剂，结合着本发明的制备方法及参数，能够使得产品在厚度减薄的情况下，提升了壳体的整体和局部强度，从而使得该塑料能够满足手机相关性能需要。
具体实施方式
下面结合实施例对本发明做进一步的描述：
实施例1：
一种采用玻纤增强手机外壳用塑料，其原料按质量比包括：
聚碳酸酯50，
导热填料15，
阻燃剂8，
偶联剂3，
玻璃纤维35。
所述的采用玻纤增强手机外壳用塑料的制备方法，包括以下步骤：
a、在聚碳酸酯中添加玻璃纤维并混合均匀；
b、将混合好的玻璃纤维与聚碳酸酯在干燥机内烘干，烘干温度120℃，时间3.5h；
c、烘干好的混合材料置于注塑机内，并加入导热填料、阻燃剂、偶联剂；
d、在下述的工艺参数下将原材料塑化：料管温度320℃、树脂温度330℃、螺杆转速50rpm；
e、产品生产：熔化的原材料从喷嘴中射出，进入手机壳体模具，射出速度为200mm/s，模具温度100℃。
实施例2：
一种采用玻纤增强手机外壳用塑料，其原料按质量比包括：
聚碳酸酯30，
导热填料20，
阻燃剂10，
偶联剂1，
玻璃纤维25。
所述的采用玻纤增强手机外壳用塑料的制备方法，包括以下步骤：
a、在聚碳酸酯中添加玻璃纤维并混合均匀；
b、将混合好的玻璃纤维与聚碳酸酯在干燥机内烘干，烘干温度115℃，时间4h；
c、烘干好的混合材料置于注塑机内，并加入导热填料、阻燃剂、偶联剂；
d、在下述的工艺参数下将原材料塑化：料管温度340℃、树脂温度345℃、螺杆转速40rpm；
e、产品生产：熔化的原材料从喷嘴中射出，进入手机壳体模具，射出速度为100mm/s，模具温度80℃。
实施例3：
一种采用玻纤增强手机外壳用塑料，其原料按质量比包括：
聚碳酸酯70，
导热填料10，
阻燃剂5，
偶联剂5，
玻璃纤维40。
所述的采用玻纤增强手机外壳用塑料的制备方法，包括以下步骤：
a、在聚碳酸酯中添加玻璃纤维并混合均匀；
b、将混合好的玻璃纤维与聚碳酸酯在干燥机内烘干，烘干温度125℃，时间3h；
c、烘干好的混合材料置于注塑机内，并加入导热填料、阻燃剂、偶联剂；
d、在下述的工艺参数下将原材料塑化：料管温度295℃、树脂温度315℃、螺杆转速60rpm；
e、产品生产：熔化的原材料从喷嘴中射出，进入手机壳体模具，射出速度为300mm/s，模具温度115℃。

Claims (2)

1.一种采用玻纤增强手机外壳用塑料，其特征在于：其原料按质量比包括：
聚碳酸酯30-70，
导热填料10-20，
阻燃剂5-10，
偶联剂1-5，
玻璃纤维25-40。
2.如权利要求1所述的一种采用玻纤增强手机外壳用塑料的其制备方法，其特征在于：包括以下步骤：
a、在聚碳酸酯中添加玻璃纤维并混合均匀；
b、将混合好的玻璃纤维与聚碳酸酯在干燥机内烘干，烘干温度115℃～125℃，时间3h～4h；
c、烘干好的混合材料置于注塑机内，并加入导热填料、阻燃剂、偶联剂；
d、在下述的工艺参数下将原材料塑化：料管温度295℃～340℃、树脂温度315℃～345℃、螺杆转速40rpm～60rpm；
e、产品生产：熔化的原材料从喷嘴中射出，进入手机壳体模具，射出速度为100mm/s～300mm/s，模具温度80℃～115℃。
CN201510442336.8A 2015-07-27 2015-07-27 一种采用玻纤增强手机外壳用塑料及其制备方法 Pending CN105111706A (zh)