CN105110652A - 一种手机屏幕用疏水剂 - Google Patents
一种手机屏幕用疏水剂 Download PDFInfo
- Publication number
- CN105110652A CN105110652A CN201510525751.XA CN201510525751A CN105110652A CN 105110652 A CN105110652 A CN 105110652A CN 201510525751 A CN201510525751 A CN 201510525751A CN 105110652 A CN105110652 A CN 105110652A
- Authority
- CN
- China
- Prior art keywords
- parts
- mobile phone
- zine oxide
- nano zine
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种手机屏幕用疏水剂,包括水、异丙醇、聚四氟乙烯、硅油、纳米氧化锌、稀释剂、氟化聚乙烯、硅烷偶联剂,各组分的质量份数为:水50-80、异丙醇30-60、聚四氟乙烯20-30、硅油25-30、纳米氧化锌10-20、稀释剂20-25、氟化聚乙烯8-10、硅烷偶联剂5-16。本发明疏水表面因具有疏水、防污、防腐蚀以及抗氧化等特性,在很多领域有着广阔的应用前景,疏水剂可隔绝环境中的水、灰尘、酸、碱、盐、微生物及其代谢产物、生活污染物等腐蚀介质,防止腐蚀介质渗透到手机屏幕等固体表面而造成腐蚀,以及降低光和其它微粒子对固体性能的影响。
Description
技术领域
本发明涉及一种疏水剂技术领域,具体地讲,本发明涉及一种手机屏幕用疏水剂。
背景技术
近年来,随着人们对生活质量要求的不断提高以及环保和节能意识的不断增强,具有自清洁功能的表面得到了迅速的发展。自清洁表面是指表面的污染物或灰尘在重力或雨水、风力等外力作用下能够自动脱落或被降解的一种表面。超疏水表面因具有疏水、防污、防腐蚀以及抗氧化等特性,使得其在很多领域有着广阔的应用前景。疏水剂可隔绝环境中的水、灰尘、酸、碱、盐、微生物及其代谢产物、生活污染物等腐蚀介质,防止腐蚀介质渗透到金属、玻璃(手机屏幕等)、混凝土、陶瓷等固体表面而造成腐蚀,以及降低光和其它微粒子对固体性能的影响。
发明内容
针对现有技术中存在的上述不足,本发明所要解决的技术问题是提供一种效果好的手机屏幕用疏水剂。
本发明解决其技术问题所采用的技术方案是:提供一种手机屏幕用疏水剂,包括水、异丙醇、聚四氟乙烯、硅油、纳米氧化锌、稀释剂、氟化聚乙烯、硅烷偶联剂,各组分的质量份数为:水50-80、异丙醇30-60、聚四氟乙烯20-30、硅油25-30、纳米氧化锌10-20、稀释剂20-25、氟化聚乙烯8-10、硅烷偶联剂5-16。
作为优选,所述手机屏幕用疏水剂各组分的质量份数为:水80、异丙醇50、聚四氟乙烯20、硅油25、纳米氧化锌18、稀释剂25、氟化聚乙烯8、硅烷偶联剂16。
作为优选,所述纳米氧化锌的颗粒度为1220-1500目,进一步优选1335目。
作为优选,其特征在于:所述水为去离子水。
具体制备步骤:
①、将异丙醇、聚四氟乙烯和去离子水混合均匀得到混合物A;
②、然后将纳米氧化锌与去离子水混合搅拌配制质量浓度为10%的纳米氧化锌水溶液;
③、接着依次向反应器中加入氟化聚乙烯、硅烷偶联剂以及硅油于50℃温度下搅拌30min,得到混合物B;
④、然后将混合物A以及纳米氧化锌水溶液加入到混合物B中,混合均匀,搅拌55min,得到混合物C;
⑤、最后将稀释剂加入到混合物C中,在60℃,保温反应0.5h;停止加热,冷却至室温即得。
本发明疏水表面因具有疏水、防污、防腐蚀以及抗氧化等特性,在很多领域有着广阔的应用前景,疏水剂可隔绝环境中的水、灰尘、酸、碱、盐、微生物及其代谢产物、生活污染物等腐蚀介质,防止腐蚀介质渗透到手机屏幕等固体表面而造成腐蚀,以及降低光和其它微粒子对固体性能的影响。
具体实施方式
本发明提供的一种手机屏幕用疏水剂,包括水、异丙醇、聚四氟乙烯、硅油、纳米氧化锌、稀释剂、氟化聚乙烯、硅烷偶联剂,各组分的质量份数为:水50-80、异丙醇30-60、聚四氟乙烯20-30、硅油25-30、纳米氧化锌10-20、稀释剂20-25、氟化聚乙烯8-10、硅烷偶联剂5-16。
作为优选,所述手机屏幕用疏水剂各组分的质量份数为:水80、异丙醇50、聚四氟乙烯20、硅油25、纳米氧化锌18、稀释剂25、氟化聚乙烯8、硅烷偶联剂16。
作为优选,所述纳米氧化锌的颗粒度为1220-1500目,进一步优选1335目。
作为优选,其特征在于:所述水为去离子水。
具体制备步骤:
①、将异丙醇、聚四氟乙烯和去离子水混合均匀得到混合物A;
②、然后将纳米氧化锌与去离子水混合搅拌配制质量浓度为10%的纳米氧化锌水溶液;
③、接着依次向反应器中加入氟化聚乙烯、硅烷偶联剂以及硅油于50℃温度下搅拌30min,得到混合物B;
④、然后将混合物A以及纳米氧化锌水溶液加入到混合物B中,混合均匀,搅拌55min,得到混合物C;
⑤、最后将稀释剂加入到混合物C中,在60℃,保温反应0.5h;停止加热,冷却至室温即得。
为了更清楚、完整说明本发明的内容,下面提供具体实施方式来说明本发明构思。当然,所提供的是实施例旨在说明本发明的构思,并不是本发明设计方案的全部,更不应该视为本发明设计内容的局限。在所提供的实施方式的启示下,所作出的任何方案均属于本发明的保护范围。
Claims (5)
1.一种手机屏幕用疏水剂,其特征在于:包括水、异丙醇、聚四氟乙烯、硅油、纳米氧化锌、稀释剂、氟化聚乙烯、硅烷偶联剂,各组分的质量份数为:水50-80、异丙醇30-60、聚四氟乙烯20-30、硅油25-30、纳米氧化锌10-20、稀释剂20-25、氟化聚乙烯8-10、硅烷偶联剂5-16。
2.根据权利要求1所述的手机屏幕用疏水剂,其特征在于:所述手机屏幕用疏水剂各组分的质量份数为:水80、异丙醇50、聚四氟乙烯20、硅油25、纳米氧化锌18、稀释剂25、氟化聚乙烯8、硅烷偶联剂16。
3.根据权利要求2所述的手机屏幕用疏水剂,其特征在于:所述纳米氧化锌的颗粒度为1220-1500目,进一步优选1335目。
4.根据权利要求1所述的手机屏幕用疏水剂,其特征在于:所述水为去离子水。
5.具体制备步骤:
①、将异丙醇、聚四氟乙烯和去离子水混合均匀得到混合物A;
②、然后将纳米氧化锌与去离子水混合搅拌配制质量浓度为10%的纳米氧化锌水溶液;
③、接着依次向反应器中加入氟化聚乙烯、硅烷偶联剂以及硅油于50℃温度下搅拌30min,得到混合物B;
④、然后将混合物A以及纳米氧化锌水溶液加入到混合物B中,混合均匀,搅拌55min,得到混合物C;
⑤、最后将稀释剂加入到混合物C中,在60℃,保温反应0.5h;停止加热,冷却至室温即得。