CN105088503A - Thin-type blended knitted sweater and processing method for preventing shrinkage and resisting pilling - Google Patents
Thin-type blended knitted sweater and processing method for preventing shrinkage and resisting pilling Download PDFInfo
- Publication number
- CN105088503A CN105088503A CN201510405025.4A CN201510405025A CN105088503A CN 105088503 A CN105088503 A CN 105088503A CN 201510405025 A CN201510405025 A CN 201510405025A CN 105088503 A CN105088503 A CN 105088503A
- Authority
- CN
- China
- Prior art keywords
- sweater
- knitted
- maleic anhydride
- slim
- blended
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a thin-type blended knitted sweater and a processing method for preventing shrinkage and resisting pilling, which belong to the technical field of knitted fabric. In the thin-type blended knitted sweater of the invention, viscose fiber and protein fiber are blended as first yarns; wool and micro-denier polypropylene fiber are blended as second yarns; the first yarns are respectively used as warp yarns and weft yarns to knit to be an inner layer; the second yarns are respectively used as warp yarns and weft yarns to knit to be a face player; and the quality density of the blended knitted sweater is within the range of 80 percent to 100 percent/ square meter. The knitted sweater provided by the invention has the thin and flat properties through blending; at the same time, the knitted sweater also has the properties of preserving heat, ventilating, absorbing moisture and discharging sweat, and resisting shrinkage and pilling; and the knitted sweater is a collection of heat preservation, health care and comfort, thus the knitted sweater provided herein has wide market prospect.
Description
Technical field
The present invention relates to the technical field of knit fabric, more particularly, the present invention relates to a kind of slim blended knitted sweater and shrinkproof ANTIPILLING processing method.
Background technology
Along with the growing of economy and the raising of living standards of the people, professional awareness and the consumer psychology of consumer also reach its maturity.The Functional Requirement of people to clothes is also more and more higher, particularly also constantly improves the health care of clothes, the requirement of the aspect such as feel and quality, also will have comfortableness and aesthetic property concurrently simultaneously.
Summary of the invention
In order to solve the technical problem existed in prior art, the object of the present invention is to provide slim blended knitted sweater and shrinkproof ANTIPILLING processing method.
In order to realize foregoing invention object of the present invention, the invention provides following technical scheme:
A kind of slim blended knitted sweater, is characterized in that: be the first yarn with viscose and protein fibre blending, is the second yarn with wool and fine denier polypropylene fibers; Be made into nexine using the first yarn as warp thread and weft yarn, be made into surface layer using the second yarn as warp thread and weft yarn; And the mass density of described blended knitted sweater is 80 ~ 100g/m
2.
Wherein, the blending rate of described viscose and protein fibre is 4:1; The blending rate of described wool and fine denier polypropylene fibers is 1:1.
Wherein, described nexine accounts for 20 ~ 25wt% of sweater knitted quality, and described surface layer accounts for 75 ~ 80wt% of sweater knitted quality.
Wherein, described viscose is Modal fibre, and its line density is 1.31 ~ 1.53dtex, and average length is about 45mm.Described protein fibre is soybean fiber, and its line density is 3.21 ~ 3.53dtex, and averag density is about 50mm.
Wherein, the line density of described fine denier polypropylene fibers is 0.6 ~ 0.8dtex, and average length is about 40mm.The quality count of described wool is 78 ~ 80, and average length is 50mm.
Wherein, described sweater knitted through shrinkproof ANTIPILLING process, it is process 15 ~ 20min under the condition of 42 DEG C in temperature by the described sweater knitted treatment fluid that is placed in; Wherein, described sweater knitted be 1:15 ~ 20 with the mass ratio for the treatment of fluid, described treatment fluid contains: (EO) of 0.20 ~ 0.25g/L
2the H of the dihydroxyethylglycin of lauryl amino ether dicarboxylate, 0.12 ~ 0.15g/L, 3-hydroxyl-2, the 2 '-iminodisuccinic acid of 0.12 ~ 0.15g/L, 0.3 ~ 0.5g/L
2o
2, the diethanol amine of 3.0 ~ 5.0g/L, the maleic anhydride modified Chlorinated Polypropylene Emulsions of 0.5 ~ 0.8wt%, the alkyl glycoside of 0.3 ~ 0.5g/L, the poly-alkoxylation terpenes of 0.8 ~ 1.0g/L, and the water of surplus.
Wherein, in described maleic anhydride modified Chlorinated Polypropylene Emulsions, the content of maleic anhydride modified chlorinated polypropylene is 30wt%; In maleic anhydride modified chlorinated polypropylene, the content of maleic anhydride is 1.6%, and chlorinity is 15%, and molecular weight is 60000 ~ 80000.
Wherein, the molecular formula of poly-alkoxylation terpenes is: two rings [2,2,1] heptene-OCH
2cH
2o-[PO]
n-[EO]
p-[PO] q-R, wherein, n is 2 ~ 4, p be 10 ~ 20, q is 10 ~ 20, and R is C1-C6 alkyl.
Compared with prior art, the present invention has following beneficial effect:
Of the present invention sweater knittedly not only have slim, smooth characteristic by blending, imparts the character such as warming, ventilative, moisture absorbing and sweat releasing, nonshrink ANTIPILLING simultaneously, integrate warming, health care and comfortable, has wide market prospects.
Detailed description of the invention
Embodiment 1
Slim blended knitted sweater described in the present embodiment, with line density be 1.31 ~ 1.53dtex, the average length Modal fibre that is 45mm, with line density be 3.21 ~ 3.53dtex, the averag density soybean protein fibre blending that is about 50mm is the first yarn, and the blending rate of described Modal fibre and soybean protein fibre is 4:1.With quality count for 78 ~ 80, average length is the wool of 50mm, and line density be 0.6 ~ 0.8dtex, the average length polypropylene fibre that is about 40mm is the second yarn, and the blending rate of described wool and fine denier polypropylene fibers is 1:1; Be made into nexine using the first yarn as warp thread and weft yarn, be made into surface layer using the second yarn as warp thread and weft yarn; And the mass density of described blended knitted sweater is 80 ~ 100g/m
2, described nexine accounts for 20 ~ 25wt% of sweater knitted quality, and described surface layer accounts for 75 ~ 80wt% of sweater knitted quality.
Slim blended knitted sweater described in the present embodiment, pastes skin mask have good hygroscopicity, gas permeability by soybean protein fibre and modal fiber blended being imparted nexine, and can antistatic, eliminates the feeling of oppression and heat of dress; And by fine denier polypropylene fibers and wool blendedly not only remain warming, soft, that outward appearance is good characteristic, and by after shrinkproof ANTIPILLING process, shrinkproof and anti-pilling property is good, not only quality is light, and comfortable and easy to wear.
Embodiment 2
Shrinkproof ANTIPILLING process is carried out to the slim blended knitted sweater of embodiment 1.By sweater knitted be 1:20 with the mass ratio for the treatment of fluid, be process 20min under the condition of 42 DEG C in temperature.Wherein, described treatment fluid contains: (EO) of 0.20g/L
2the H of the dihydroxyethylglycin of lauryl amino ether dicarboxylate, 0.15g/L, 3-hydroxyl-2, the 2 '-iminodisuccinic acid of 0.12g/L, 0.5g/L
2o
2, the diethanol amine of 5.0g/L, the maleic anhydride modified Chlorinated Polypropylene Emulsions of 0.8wt%, the alkyl glycoside of 0.3g/L, the poly-alkoxylation terpenes of 1.0g/L, and the water of surplus.Wherein, in described maleic anhydride modified Chlorinated Polypropylene Emulsions, the content of maleic anhydride modified chlorinated polypropylene is 30wt%; In described maleic anhydride modified chlorinated polypropylene, the content of maleic anhydride is 1.6%, and chlorinity is 15%, and molecular weight is about 60000.The molecular formula of described poly-alkoxylation terpenes is: two rings [2,2,1] heptene-OCH
2cH
2o-[PO]
n-[EO]
p-[PO] q-R, wherein, n is 2 ~ 4, p be 10 ~ 20, q is 10 ~ 20, and R is C1-C6 alkyl.After shrinkproof ANTIPILLING process, carry out conventional soft sofening treatment, then wash oven dry, tentering, preshrunk, wholely to scald, pack.
Embodiment 3
Shrinkproof ANTIPILLING process is carried out to the slim blended knitted sweater of embodiment 1.By sweater knitted be 1:15 with the mass ratio for the treatment of fluid, be process 20min under the condition of 42 DEG C in temperature.Wherein, described treatment fluid contains: (EO) of 0.25g/L
2the H of the dihydroxyethylglycin of lauryl amino ether dicarboxylate, 0.12g/L, 3-hydroxyl-2, the 2 '-iminodisuccinic acid of 0.12g/L, 0.5g/L
2o
2, the diethanol amine of 3.0g/L, the maleic anhydride modified Chlorinated Polypropylene Emulsions of 0.5wt%, the alkyl glycoside of 0.3g/L, the poly-alkoxylation terpenes of 0.8g/L, and the water of surplus.Wherein, in described maleic anhydride modified Chlorinated Polypropylene Emulsions, the content of maleic anhydride modified chlorinated polypropylene is 30wt%; In described maleic anhydride modified chlorinated polypropylene, the content of maleic anhydride is 1.6%, and chlorinity is 15%, and molecular weight is 60000 ~ 80000.The molecular formula of described poly-alkoxylation terpenes is: two rings [2,2,1] heptene-OCH
2cH
2o-[PO]
n-[EO]
p-[PO] q-R, wherein, n is 2 ~ 4, p be 10 ~ 20, q is 10 ~ 20, and R is C1-C6 alkyl.After shrinkproof ANTIPILLING process, carry out conventional soft sofening treatment, then wash oven dry, tentering, preshrunk, wholely to scald, pack.
Comparative example 1
Shrinkproof ANTIPILLING process is carried out to the slim blended knitted sweater of embodiment 1.By sweater knitted be 1:15 with the mass ratio for the treatment of fluid, be process 20min under the condition of 42 DEG C in temperature.Described treatment fluid contains: the penetrating agent JFC of 1.0wt%, anti-piping compound KJ-2,2.0wt% of 2.0wt% (EO)
2the crosslinking agent CS-260 of lauryl amino ether dicarboxylate, 1.0wt%, and the water of surplus.After shrinkproof ANTIPILLING process, carry out conventional soft sofening treatment, then wash oven dry, tentering, preshrunk, wholely to scald, pack.
Comparative example 2
Shrinkproof ANTIPILLING process is carried out to the slim blended knitted sweater of embodiment 1.By sweater knitted be 1:15 with the mass ratio for the treatment of fluid, be process 20min under the condition of 42 DEG C in temperature.Wherein, described treatment fluid contains: (EO) of 0.25g/L
2the H of compound protease B, 0.5g/L of lauryl amino ether dicarboxylate, 0.25g/L
2o
2, the diethanol amine of 3.0g/L, the maleic anhydride modified Chlorinated Polypropylene Emulsions of 0.5wt%, the alkyl glycoside of 0.3g/L, the poly-alkoxylation terpenes of 0.8g/L, and the water of surplus.Wherein, in described maleic anhydride modified Chlorinated Polypropylene Emulsions, the content of maleic anhydride modified chlorinated polypropylene is 30wt%; In described maleic anhydride modified chlorinated polypropylene, the content of maleic anhydride is 1.6%, and chlorinity is 15%, and molecular weight is 60000 ~ 80000.The molecular formula of described poly-alkoxylation terpenes is: two rings [2,2,1] heptene-OCH
2cH
2o-[PO]
n-[EO]
p-[PO] q-R, wherein, n is 2 ~ 4, p be 10 ~ 20, q is 10 ~ 20, and R is C1-C6 alkyl.After shrinkproof ANTIPILLING process, carry out conventional soft sofening treatment, then wash oven dry, tentering, preshrunk, wholely to scald, pack.
Comparative example 3
Shrinkproof ANTIPILLING process is carried out to the slim blended knitted sweater of embodiment 1.By sweater knitted be 1:15 with the mass ratio for the treatment of fluid, be process 20min under the condition of 42 DEG C in temperature.Wherein, described treatment fluid contains: (EO) of 0.25g/L
2the dihydroxyethylglycin of lauryl amino ether dicarboxylate, 0.12g/L, the 3-hydroxyl-2,2 of 0.12g/L
,the H of-iminodisuccinic acid, 0.5g/L
2o
2, the diethanol amine of 3.0g/L, the alkyl glycoside of anti-piping compound KJ-2,0.3g/L of 1.0wt%, the poly-alkoxylation terpenes of 0.8g/L, and the water of surplus.The molecular formula of wherein said poly-alkoxylation terpenes is: two rings [2,2,1] heptene-OCH
2cH
2o-[PO]
n-[EO]
p-[PO] q-R, wherein, n is 2 ~ 4, p be 10 ~ 20, q is 10 ~ 20, and R is C1-C6 alkyl.After shrinkproof ANTIPILLING process, carry out conventional soft sofening treatment, then wash oven dry, tentering, preshrunk, wholely to scald, pack.
To the sweater knitted standard method of test of pressing IWS after embodiment 2 ~ 3 and comparative example 1 ~ 3 process, wash 3 times and measure percentage reduction of area, test anti-pilling according to GB/T4802.1, its result is as shown in table 1.
Table 1
| Fabric | Percentage reduction of area (%) | Anti-pilling (level) | Feel (level) |
| Embodiment 2 | 7.8 | 3.5～4.0 | 4.0 |
| Embodiment 3 | 8.1 | 3.5～4.0 | 4.0 |
| Comparative example 1 | 12.1 | 2.5～3.0 | 4.0 |
| Comparative example 2 | 13.5 | 2.5～3.0 | 4.0 |
| Comparative example 3 | 11.2 | 2.5～3.0 | 4.0 |
For the ordinary skill in the art, protection scope of the present invention is not limited to the specific embodiment of detailed description of the invention part, as long as no the embodiment departing from invention essence, within the protection domain being all interpreted as having dropped on application claims.
Claims (10)
1. a slim blended knitted sweater, is characterized in that: be the first yarn with viscose and protein fibre blending, is the second yarn with wool and fine denier polypropylene fibers; Be made into nexine using the first yarn as warp thread and weft yarn, be made into surface layer using the second yarn as warp thread and weft yarn; And the mass density of described blended knitted sweater is 80 ~ 100g/m
2.
2. slim blended knitted sweater according to claim 1, is characterized in that: the blending rate of described viscose and protein fibre is 4:1; The blending rate of described wool and fine denier polypropylene fibers is 1:1.
3. slim blended knitted sweater according to claim 1, it is characterized in that: described nexine accounts for 20 ~ 25wt% of sweater knitted quality, described surface layer accounts for 75 ~ 80wt% of sweater knitted quality.
4. slim blended knitted sweater according to claim 1, is characterized in that: described viscose is Modal fibre, and its line density is 1.31 ~ 1.53dtex, and average length is about 45mm; Described protein fibre is soybean fiber, and its line density is 3.21 ~ 3.53dtex, and averag density is about 50mm.
5. slim blended knitted sweater according to claim 1, is characterized in that: the line density of described fine denier polypropylene fibers is 0.6 ~ 0.8dtex, and average length is about 40mm; The quality count of described wool is 78 ~ 80, and average length is 50mm.
6. slim blended knitted sweater according to claim 1, is characterized in that: described sweater knitted through shrinkproof ANTIPILLING process, and it is process 15 ~ 20min under the condition of 42 DEG C in temperature by the described sweater knitted treatment fluid that is placed in; Wherein, described sweater knitted be 1:15 ~ 20 with the mass ratio for the treatment of fluid, described treatment fluid contains: (EO) of 0.20 ~ 0.25g/L
2the dihydroxyethylglycin of lauryl amino ether dicarboxylate, 0.12 ~ 0.15g/L, the 3-hydroxyl-2,2 of 0.12 ~ 0.15g/L
,the H of-iminodisuccinic acid, 0.3 ~ 0.5g/L
2o
2, the diethanol amine of 3.0 ~ 5.0g/L, the maleic anhydride modified Chlorinated Polypropylene Emulsions of 0.5 ~ 0.8wt%, the alkyl glycoside of 0.3 ~ 0.5g/L, the poly-alkoxylation terpenes of 0.8 ~ 1.0g/L, and the water of surplus.
7. slim blended knitted sweater according to claim 6, is characterized in that: in described maleic anhydride modified Chlorinated Polypropylene Emulsions, the content of maleic anhydride modified chlorinated polypropylene is 30wt%; In maleic anhydride modified chlorinated polypropylene, the content of maleic anhydride is 1.6%, and chlorinity is 15%, and molecular weight is 60000 ~ 80000.
8. slim blended knitted sweater according to claim 6, is characterized in that: the molecular formula of poly-alkoxylation terpenes is: two rings [2,2,1] heptene-OCH
2cH
2o-[PO]
n-[EO]
p-[PO] q-R, wherein, n is 2 ~ 4, p be 10 ~ 20, q is 10 ~ 20, and R is C1-C6 alkyl.
9. the shrinkproof ANTIPILLING processing method of slim blended knitted sweater according to claim 1, is characterized in that: described processing method refers to that by the described sweater knitted treatment fluid that is placed in be process 15 ~ 20min under the condition of 42 DEG C in temperature; Wherein, described sweater knitted be 1:15 ~ 20 with the mass ratio for the treatment of fluid, described treatment fluid contains: (EO) of 0.20 ~ 0.25g/L
2the dihydroxyethylglycin of lauryl amino ether dicarboxylate, 0.12 ~ 0.15g/L, the 3-hydroxyl-2,2 of 0.12 ~ 0.15g/L
,the H of-iminodisuccinic acid, 0.3 ~ 0.5g/L
2o
2, the diethanol amine of 3.0 ~ 5.0g/L, the maleic anhydride modified Chlorinated Polypropylene Emulsions of 0.5 ~ 0.8wt%, the alkyl glycoside of 0.3 ~ 0.5g/L, the poly-alkoxylation terpenes of 0.8 ~ 1.0g/L, and the water of surplus.
10. shrinkproof ANTIPILLING processing method according to claim 9, is characterized in that: in described maleic anhydride modified Chlorinated Polypropylene Emulsions, the content of maleic anhydride modified chlorinated polypropylene is 30wt%; In maleic anhydride modified chlorinated polypropylene, the content of maleic anhydride is 1.6%, and chlorinity is 15%, and molecular weight is 60000 ~ 80000; The molecular formula of described poly-alkoxylation terpenes is: two rings [2,2,1] heptene-OCH
2cH
2o-[PO]
n-[EO]
p-[PO] q-R, wherein, n is 2 ~ 4, p be 10 ~ 20, q is 10 ~ 20, and R is C1-C6 alkyl.