CN105088104A - 一种耐海水腐蚀合金钢及其制备方法 - Google Patents

一种耐海水腐蚀合金钢及其制备方法 Download PDF

Info

Publication number
CN105088104A
CN105088104A CN201510525640.9A CN201510525640A CN105088104A CN 105088104 A CN105088104 A CN 105088104A CN 201510525640 A CN201510525640 A CN 201510525640A CN 105088104 A CN105088104 A CN 105088104A
Authority
CN
China
Prior art keywords
corrosion resistance
seawater corrosion
steel alloy
intermediate frequency
resistance steel
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510525640.9A
Other languages
English (en)
Inventor
陈程
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangxi Nanning Zhicui Technology Consulting Co Ltd
Original Assignee
Guangxi Nanning Zhicui Technology Consulting Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangxi Nanning Zhicui Technology Consulting Co Ltd filed Critical Guangxi Nanning Zhicui Technology Consulting Co Ltd
Priority to CN201510525640.9A priority Critical patent/CN105088104A/zh
Publication of CN105088104A publication Critical patent/CN105088104A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐海水腐蚀合金钢,其特征在于:由以下重量组分组成:碳0.15-0.27%、硅0.25-0.46%、硒0.12-0.18%、镍0.05-0.14%、钛0.16-0.22%、钴0.04-0.09%、锑0.5-1.2%、钨0.6-1.8%、锆0.4-1.3%、铜0.05-0.8%、复合稀土元素0.04-0.1%、磷<0.03%、硫<0.03%、余量为铁。本发明的合金钢耐海水腐蚀性大大提高,是普通合金钢的5倍以上,且脆性小、相对生产成本低。

Description

一种耐海水腐蚀合金钢及其制备方法
技术领域
本发明涉及到合金钢制造技术领域,具体地说是一种耐海水腐蚀合金钢及其制备方法。
背景技术
合金钢的发展已经有loo多年的历史了,到目前为止,多种多样的合金钢在工业上被应用,主要有以下类型:调质钢、弹簧钢、滚动轴承钢、工具钢、特殊性能钢、耐热钢、低温钢等各种性能优异的合金钢。耐腐蚀的合金钢有多种多样,技术有很大进步,但是仍有很多问题存在,如耐磨性、硬度、防锈性能、耐腐蚀性能、耐高低温性能、脆性、韧性等,在很多场合还不能满足生产的要求,还需要进一步改进,以提高生产效率,降低成本,提高安全性,为高精尖技术发展提供保障,为社会发展提供动力,任务还很艰巨。
发明内容
为解决上述技术问题,本发明提出了耐海水腐蚀合金钢及其制备方法,本发明制备的合金钢其耐海水腐蚀性能是普通合金钢的5倍以上。
本发明的方案是通过这样实现的:
一种耐海水腐蚀合金钢,由以下重量组分组成:碳0.15-0.27%、硅0.25-0.46%、硒0.12-0.18%、镍0.05-0.14%、钛0.16-0.22%、钴0.04-0.09%、锑0.5-1.2%、钨0.6-1.8%、锆0.4-1.3%、铜0.05-0.8%、复合稀土元素0.04-0.1%、磷<0.03%、硫<0.03%、余量为铁。
优选的,所述的耐海水腐蚀合金钢由以下重量组分组成:碳0.18-0.22%、硅0.35-0.42%、硒0.14-0.16%、镍0.09-0.12%、钛0.19-0.22%、钴0.06-0.09%、锑0.7-1%、钨1-1.5%、锆0.6-1.1%、铜0.35-0.6%、复合稀土元素0.06-0.9%、磷<0.03%、硫<0.03%、余量为铁。
优选的,所述的耐海水腐蚀合金钢由以下重量组分组成:碳0.19%、硅0.38%、硒0.14%、镍0.12%、钛0.21%、钴0.07%、锑0.8%、钨1.2%、锆0.9%、铜0.4%、复合稀土元素0.6%、磷<0.03%、硫<0.03%、余量为铁。
优选的,所述复合稀土元素包括铈、钕、铕、钆、铒、镥、钇中的两种以上。
制备上述耐海水腐蚀合金钢方法,包括以下步骤:
(1)冶炼:将废铁、废钢及废合金钢放入中频炉内,再向中频炉通低电流,中频炉内配料预热后全负荷送电,直至中频炉内配料熔化并进行成分初调;
(2)LF精炼:在LF炉中进行脱氧及成分微调;
(3)连铸:采用高拉速、高拉矫温度,在连铸机上浇成连铸坯;
(4)连轧:连铸坯入轧钢加热炉加热,经过连轧机组轧制,轧制成圆钢。
优选的,所述中频炉的炉衬为碱性炉衬。
优选的,所述碱性炉衬为热石灰炉衬。
优选的,所述高拉速其拉速为0.9-1.0m/min。
优选的,所述高拉矫其温度为1150-1200℃。
优选的,所述轧钢加热炉其加热温度为350-450℃。
本发明具备以下良好效果:
(1)耐海水腐蚀性是普通合金钢的5倍以上。
(2)强度高,脆性小,适合加工各种部件。
(3)大大提高成材率和生产效率,生产成本低。。
具体实施方式
以下结合实施例描述本发明的一种耐海水腐蚀合金钢及其制备方法,这些描述并不是对本发明内容作进一步的限定。
实施例1
一种耐海水腐蚀合金钢,由以下重量组分组成:碳0.19%、硅0.38%、硒0.14%、镍0.12%、钛0.21%、钴0.07%、锑0.8%、钨1.2%、锆0.9%、铜0.4%、复合稀土元素0.6%、磷<0.03%、硫<0.03%、余量为铁。
其中,复合稀土元素包括铈、钕、铕、钆、铒、镥、钇。
制备上述耐海水腐蚀合金钢方法,包括以下步骤:
(1)冶炼:将废铁、废钢及废合金钢放入中频炉内,再向中频炉通低电流,中频炉内配料预热后全负荷送电,直至中频炉内配料熔化并进行成分初调;
(2)LF精炼:在LF炉中进行脱氧及成分微调;
(3)连铸:采用高拉速、高拉矫温度,在连铸机上浇成连铸坯;
(4)连轧:连铸坯入轧钢加热炉加热,经过连轧机组轧制,轧制成圆钢。
其中,中频炉的炉衬为碱性热石灰炉衬,高拉速其拉速为0.9m/min,高拉矫其温度为1150℃,轧钢加热炉其加热温度为350℃。
实施例2
一种耐海水腐蚀合金钢,由以下重量组分组成:碳0.15%、硅0.25%、硒0.12%、镍0.05%、钛0.16%、钴0.04%、锑0.5%、钨0.6%、锆0.4%、铜0.05%、复合稀土元素0.04%、磷<0.03%、硫<0.03%、余量为铁。
其中,复合稀土元素包括铈、钕、铒、镥、钇。
制备上述耐海水腐蚀合金钢方法,包括以下步骤:
(1)冶炼:将废铁、废钢及废合金钢放入中频炉内,再向中频炉通低电流,中频炉内配料预热后全负荷送电,直至中频炉内配料熔化并进行成分初调;
(2)LF精炼:在LF炉中进行脱氧及成分微调;
(3)连铸:采用高拉速、高拉矫温度,在连铸机上浇成连铸坯;
(4)连轧:连铸坯入轧钢加热炉加热,经过连轧机组轧制,轧制成圆钢。
其中,中频炉的炉衬为碱性热石灰炉衬,高拉速其拉速为1.0m/min,高拉矫其温度为1200℃,轧钢加热炉其加热温度为450℃。
实施例3
一种耐海水腐蚀合金钢,由以下重量组分组成:碳0.27%、硅0.46%、硒0.18%、镍0.14%、钛0.22%、钴0.09%、锑1.2%、钨1.8%、锆1.3%、铜0.8%、复合稀土元素0.1%、磷<0.03%、硫<0.03%、余量为铁。
其中,复合稀土元素包括、铒、镥、钇中。
制备上述耐海水腐蚀合金钢方法,包括以下步骤:
(1)冶炼:将废铁、废钢及废合金钢放入中频炉内,再向中频炉通低电流,中频炉内配料预热后全负荷送电,直至中频炉内配料熔化并进行成分初调;
(2)LF精炼:在LF炉中进行脱氧及成分微调;
(3)连铸:采用高拉速、高拉矫温度,在连铸机上浇成连铸坯;
(4)连轧:连铸坯入轧钢加热炉加热,经过连轧机组轧制,轧制成圆钢。
其中,中频炉的炉衬为碱性热石灰炉衬,高拉速其拉速为0.95m/min,高拉矫其温度为1180℃,轧钢加热炉其加热温度为400℃。
实施例4
一种耐海水腐蚀合金钢,由以下重量组分组成:碳0.2%、硅0.33%、硒0.14%、镍0.09%、钛0.18%、钴0.07%、锑0.9%、钨0.7%、锆0.9%、铜0.06%、复合稀土元素0.08%、磷<0.03%、硫<0.03%、余量为铁。
其中,复合稀土元素包括、铒、镥、钇中。
制备上述耐海水腐蚀合金钢方法,包括以下步骤:
(1)冶炼:将废铁、废钢及废合金钢放入中频炉内,再向中频炉通低电流,中频炉内配料预热后全负荷送电,直至中频炉内配料熔化并进行成分初调;
(2)LF精炼:在LF炉中进行脱氧及成分微调;
(3)连铸:采用高拉速、高拉矫温度,在连铸机上浇成连铸坯;
(4)连轧:连铸坯入轧钢加热炉加热,经过连轧机组轧制,轧制成圆钢。
其中,中频炉的炉衬为碱性热石灰炉衬,高拉速其拉速为0.95m/min,高拉矫其温度为1180℃,轧钢加热炉其加热温度为400℃。
实施例5
一种耐海水腐蚀合金钢,由以下重量组分组成:碳0.25%、硅0.38%、硒0.16%、镍0.12%、钛0.16-0.22%、钴0.05%、锑0.7%、钨1.2%、锆0.7%、铜0.5%、复合稀土元素0.8%、磷<0.03%、硫<0.03%、余量为铁。
其中,复合稀土元素包括、铒、镥、钇中。
制备上述耐海水腐蚀合金钢方法,包括以下步骤:
(1)冶炼:将废铁、废钢及废合金钢放入中频炉内,再向中频炉通低电流,中频炉内配料预热后全负荷送电,直至中频炉内配料熔化并进行成分初调;
(2)LF精炼:在LF炉中进行脱氧及成分微调;
(3)连铸:采用高拉速、高拉矫温度,在连铸机上浇成连铸坯;
(4)连轧:连铸坯入轧钢加热炉加热,经过连轧机组轧制,轧制成圆钢。
其中,中频炉的炉衬为碱性热石灰炉衬,高拉速其拉速为1.0m/min,高拉矫其温度为1200℃,轧钢加热炉其加热温度为450℃。

Claims (10)

1.一种耐海水腐蚀合金钢,其特征在于:由以下重量组分组成:碳0.15-0.27%、硅0.25-0.46%、硒0.12-0.18%、镍0.05-0.14%、钛0.16-0.22%、钴0.04-0.09%、锑0.5-1.2%、钨0.6-1.8%、锆0.4-1.3%、铜0.05-0.8%、复合稀土元素0.04-0.1%、磷<0.03%、硫<0.03%、余量为铁。
2.根据权利要求1所述的耐海水腐蚀合金钢,其特征在于:由以下重量组分组成:碳0.18-0.22%、硅0.35-0.42%、硒0.14-0.16%、镍0.09-0.12%、钛0.19-0.22%、钴0.06-0.09%、锑0.7-1%、钨1-1.5%、锆0.6-1.1%、铜0.35-0.6%、复合稀土元素0.06-0.9%、磷<0.03%、硫<0.03%、余量为铁。
3.根据权利要求2所述的耐海水腐蚀合金钢,其特征在于:由以下重量组分组成:碳0.19%、硅0.38%、硒0.14%、镍0.12%、钛0.21%、钴0.07%、锑0.8%、钨1.2%、锆0.9%、铜0.4%、复合稀土元素0.6%、磷<0.03%、硫<0.03%、余量为铁。
4.根据权利要求1-3任一项所述的耐海水腐蚀合金钢,其特征在于:所述复合稀土元素包括铈、钕、铕、钆、铒、镥、钇中的两种以上。
5.一种耐海水腐蚀合金钢的制备方法,其特征在于,包括以下步骤:
(1)冶炼:将废铁、废钢及废合金钢放入中频炉内,再向中频炉通低电流,中频炉内配料预热后全负荷送电,直至中频炉内配料熔化并进行成分初调;
(2)LF精炼:在LF炉中进行脱氧及成分微调;
(3)连铸:采用高拉速、高拉矫温度,在连铸机上浇成连铸坯;
(4)连轧:连铸坯入轧钢加热炉加热,经过连轧机组轧制,轧制成圆钢。
6.根据权利要求5所述的耐海水腐蚀合金钢的制备方法,其特征在于:所述中频炉的炉衬为碱性炉衬。
7.根据权利要求6所述的耐海水腐蚀合金钢的制备方法,其特征在于:所述碱性炉衬为热石灰炉衬。
8.根据权利要求5所述的耐海水腐蚀合金钢的制备方法,其特征在于:所述高拉速其拉速为0.9-1.0m/min。
9.根据权利要求5所述的耐海水腐蚀合金钢的制备方法,其特征在于:所述高拉矫其温度为1150-1200℃。
10.根据权利要求5所述的耐海水腐蚀合金钢的制备方法,其特征在于:所述轧钢加热炉其加热温度为350-450℃。
CN201510525640.9A 2015-08-25 2015-08-25 一种耐海水腐蚀合金钢及其制备方法 Pending CN105088104A (zh)