CN103789615B - 一种高强度低碳钢材料及其制备方法 - Google Patents
一种高强度低碳钢材料及其制备方法 Download PDFInfo
- Publication number
- CN103789615B CN103789615B CN201410034542.0A CN201410034542A CN103789615B CN 103789615 B CN103789615 B CN 103789615B CN 201410034542 A CN201410034542 A CN 201410034542A CN 103789615 B CN103789615 B CN 103789615B
- Authority
- CN
- China
- Prior art keywords
- powder
- high strength
- carbon
- hour
- insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种高强度低碳钢材料，其含有的化学元素成分及其质量百分比为：碳0.2-0.4、硅0.05-0.15、Mo3.2-3.5、Ni1.7-2.2、Mn4.1-4.3、Co0.03-0.05、Nb0.4-0.6、V0.004-0.008、P≤0.030、S≤0.030、余量为铁。本发明通过使用锰、镍、铌、钒等原料组合，合理设置配比和生产工艺，合理设置投放次序，形成的低碳钢不仅具有低碳钢的优异韧性和可塑性，还具有高强度、硬度高、耐磨性好的特点；并使用部分废铁作为原料，提高合金的质量稳定均一；本发明适用于多种部件，机械加工性能好，使用寿命长，安全系数高。通过加入精炼剂，气孔度降低1-2度。
Description
技术领域
本发明涉及金属材料制备领域，尤其涉及一种高强度低碳钢材料及其制备方法。
背景技术
合金钢的发展已经有100多年的历史了，到目前为止，多种多样的合金钢在工业上被应用，主要有以下类型：调质钢、弹簧钢、工具钢、高速钢、模具钢、高中低碳合金钢等，目前为止，虽然合金钢技术得到很大发展，但是，仍有很多问题存在，如耐磨度、硬度、防锈性能、耐腐蚀性能、耐高低温性能、脆性、韧性、成本等不能兼顾，在很多场合还不能满足生产的要求，还需要进一步改进，以提高生产效率，降低成本，提高安全性，为高精尖技术发展提供保障，为社会发展提供动力，任务还很艰巨。
发明内容
本发明的目的在于提供一种高强度低碳钢材料及其制备方法，该合金材料具有良好的韧性、可塑性，较高的强度和硬度的特点。
本发明的技术方案如下：
一种高强度低碳钢材料，其特征在于：其含有的化学元素成分及其质量百分比为：碳0.2-0.4、硅0.05-0.15、Mo3.2-3.5、Ni1.7-2.2、Mn4.1-4.3、Co0.03-0.05、Nb0.4-0.6、V0.004-0.008、P≤0.030、S≤0.030、余量为铁。
所述的高强度低碳钢材料的生产方法，其特征在于：
（1）、将生铁与废铁按1：2比例投入炉中熔化作为铁基质来源；进行脱硫、脱氧、合金化、采用精炼剂精炼、浇铸、铸后热处理等；
（2）、合金化过程中向炉内投入合金元素的批次顺序为：（1）硅、Mn；（2）Mo、Ni、Co；（3）其它剩余成分；各批次投入元素的时间间隔为10-12分钟，投料后搅拌均匀。
所述的铸后热处理是：先由室温以180-200℃/小时速率升温至900-915℃，保温3-4小时；再以140-160℃/小时速率降温至600-615℃，保温40-60分钟；再以100-120℃/小时速率降温至320-340℃，保温2-3小时；再以150-170℃/小时速率升温至500-520℃，保温2-3小时，取出空冷即得。
所述的精炼剂由下列重量份的原料制成：工具钢粉3-4、粘土9-12、氧化镁3-4、氯化锌2-3、氟铝酸钠5-6、氧化铝1-2、铝矾土5-6、硼化钒1-2、二甲基氧化锡1-2、氢氧化铝8-10、玉石粉3-4、蒙脱石1-2；制备方法是将各原料混合，加热至熔融状态，然后，浇注入纯净水中激冷，再粉碎成100-200目粉末；将所得粉末加入相当于粉末重量2-3%的硅烷偶联剂KH-550、1-2%的纳米碳粉，混合均匀后，在8-15Mpa下压制成坯，然后，在900-950℃下煅烧3-4小时，冷却后，再粉碎成150-250目粉末，即得。
本发明的有益效果
本发明通过使用锰、镍、铌、钒等原料组合，合理设置配比和生产工艺，合理设置投放次序，形成的低碳钢不仅具有低碳钢的优异韧性和可塑性，还具有高强度、硬度高、耐磨性好的特点；并使用部分废铁作为原料，提高合金的质量稳定均一；本发明适用于多种部件，机械加工性能好，使用寿命长，安全系数高。本发明精炼剂用于铸造生产，明显提高成品率，特别是铸件中的气孔度降低1-2度，得到有效的控制，不会在铸件表面产生气孔，夹杂氧化物也明显降低，氧化夹杂物在2级左右。
具体实施方式
一种高强度低碳钢材料，其含有的化学元素成分及其质量百分比为：碳0.2-0.4、硅0.05-0.15、Mo3.2-3.5、Ni1.7-2.2、Mn4.1-4.3、Co0.03-0.05、Nb0.4-0.6、V0.004-0.008、P≤0.030、S≤0.030、余量为铁。
所述的高强度低碳钢材料的生产方法：
（1）、将生铁与废铁按1：2比例投入炉中熔化作为铁基质来源；进行脱硫、脱氧、合金化、采用精炼剂精炼、浇铸、铸后热处理等；
（2）、合金化过程中向炉内投入合金元素的批次顺序为：（1）硅、Mn；（2）Mo、Ni、Co；（3）其它剩余成分；各批次投入元素的时间间隔为11分钟，投料后搅拌均匀。
所述的铸后热处理是：先由室温以190℃/小时速率升温至910℃，保温3.6小时；再以150℃/小时速率降温至610℃，保温50分钟；再以110℃/小时速率降温至330℃，保温2.5小时；再以160℃/小时速率升温至510℃，保温2.5小时，取出空冷即得。
所述的精炼剂由下列重量份(公斤)的原料制成：工具钢粉3、粘土9、氧化镁3、氯化锌2、氟铝酸钠6、氧化铝1、铝矾土5、硼化钒1、二甲基氧化锡1、氢氧化铝8、玉石粉4、蒙脱石1；制备方法是将各原料混合，加热至熔融状态，然后，浇注入纯净水中激冷，再粉碎成100-200目粉末；将所得粉末加入相当于粉末重量2-3%的硅烷偶联剂KH-550、1-2%的纳米碳粉，混合均匀后，在8-15Mpa下压制成坯，然后，在900-950℃下煅烧3-4小时，冷却后，再粉碎成150-250目粉末，即得。
本发明高强度低碳钢材料的机械性能为：拉伸强度1198MPa，屈服强度934MPa，延伸率15.2％，断面收缩率28.9％，冲击吸收功53.6J，冲击韧性63.5J/cm2，硬度286.4HB。
Claims (1)
1.一种高强度低碳钢材料，其特征在于：其含有的化学元素成分及其质量百分比为：碳0.2-0.4、硅0.05-0.15、Mo3.2-3.5、Ni1.7-2.2、Mn4.1-4.3、Co0.03-0.05、Nb0.4-0.6、V0.004-0.008、P≤0.030、S≤0.030、余量为铁；
所述的高强度低碳钢材料的生产方法，其特征在于：
（1）、将生铁与废铁按1：2比例投入炉中熔化作为铁基质来源；进行脱硫、脱氧、合金化、采用精炼剂精炼、浇铸、铸后热处理；
（2）、合金化过程中向炉内投入合金元素的批次顺序为：（a）硅、Mn；（b）Mo、Ni、Co；（c）其它剩余成分；各批次投入元素的时间间隔为10-12分钟，投料后搅拌均匀；
所述的铸后热处理是：先由室温以180-200℃/小时速率升温至900-915℃，保温3-4小时；再以140-160℃/小时速率降温至600-615℃，保温40-60分钟；再以100-120℃/小时速率降温至320-340℃，保温2-3小时；再以150-170℃/小时速率升温至500-520℃，保温2-3小时，取出空冷即得；
所述的精炼剂由下列重量份的原料制成：工具钢粉3-4、粘土9-12、氧化镁3-4、氯化锌2-3、氟铝酸钠5-6、氧化铝1-2、铝矾土5-6、硼化钒1-2、二甲基氧化锡1-2、氢氧化铝8-10、玉石粉3-4、蒙脱石1-2；制备方法是将各原料混合，加热至熔融状态，然后，浇注入纯净水中激冷，再粉碎成100-200目粉末；将所得粉末加入相当于粉末重量2-3%的硅烷偶联剂KH-550、1-2%的纳米碳粉，混合均匀后，在8-15MPa下压制成坯，然后，在900-950℃下煅烧3-4小时，冷却后，再粉碎成150-250目粉末，即得。