CN105086783B - A kind of imitative electrodeposition-type powdery paints and preparation method thereof - Google Patents
A kind of imitative electrodeposition-type powdery paints and preparation method thereof Download PDFInfo
- Publication number
- CN105086783B CN105086783B CN201510532570.XA CN201510532570A CN105086783B CN 105086783 B CN105086783 B CN 105086783B CN 201510532570 A CN201510532570 A CN 201510532570A CN 105086783 B CN105086783 B CN 105086783B
- Authority
- CN
- China
- Prior art keywords
- powdery paints
- electrodeposition
- imitative
- saturated polyester
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of imitative electrodeposition-type powdery paints and preparation method thereof, raw material components percentage:End carboxyl saturated polyester resin 80 90%, isocyanuric acid three-glycidyl ester 6 10%, terminal hydroxy group saturated polyester resin 7 9%, isophorone 2 2.5%, levelling agent 0.8 1%, silver powder 1 1.5%, pure fluorine wax 0.5 0.7%, the percetage by weight sum of each component is 100%.Coating gloss >=100% of the powdery paints, silver powder are aligned on melting high viscosity powdery paints surface, produced in film coated surface reflective as the metal effect of chromium plating minute surface;Technique is simple, raw material is easy to get, and is advantageous to popularization and application, possesses significant economic and social benefit.
Description
Technical field
The invention belongs to art of powder coatings, and in particular to a kind of imitative electrodeposition-type powdery paints and preparation method thereof.
Background technology
Powdery paints is a kind of new without solvent, 100% solid powdery coating, have it is solvent-free, pollution-free, can
Recovery, environmental protection, save the energy and resource, reduce labor intensity with coating machinery intensity it is high the features such as.There is the binding of metal appearance
Powdery paints, the expensive goods being generally recognised as by people in art of powder coatings, by market segments such as household electrical appliances, furniture and automobiles
Favorable comment, slowly promote and come in every field.The coating of high imitative electrosilvering powdery paints therein has excellent minute surface
Effect and beautiful outward appearance, by pursuing for people.
The content of the invention
It is an object of the invention to provide a kind of imitative electrodeposition-type powdery paints and preparation method thereof, the coating of the powdery paints
Gloss >=100%, silver powder are aligned on melting high viscosity powdery paints surface, and reflective picture chromium plating mirror is produced in film coated surface
The metal effect in face;Technique is simple, raw material is easy to get, and is advantageous to popularization and application, possesses significant economic and social benefit.
To achieve the above object, the present invention adopts the following technical scheme that:
A kind of imitative electrodeposition-type powdery paints, raw material components percentage:End carboxyl saturated polyester resin 80-90%,
Isocyanuric acid three-glycidyl ester 6-10%, terminal hydroxy group saturated polyester resin 7-9%, isophorone 2-2.5%, levelling agent 0.8-1%,
Silver powder 1-1.5%, pure fluorine wax 0.5-0.7%, the percetage by weight sum of each component is 100%.
Preparation method:Each component is put into bonding machines successively, is passed through protective gas, 500-900rpm bondings 3- at room temperature
6min, obtain imitative electrodeposition-type powdery paints.
The remarkable advantage of the present invention is:Coating gloss >=100% of the powdery paints, silver powder align high in melting
Viscosity powdery paints surface, the metal effect of chromium minute surface is crossed in the reflective picture of film coated surface generation;Technique is simple, raw material is easy to get,
Be advantageous to popularization and application, possess significant economic and social benefit.
Embodiment
Embodiment 1
A kind of imitative electrodeposition-type powdery paints, raw material components percentage:It is end carboxyl saturated polyester resin 80%, different
It is cyanuric acid three-glycidyl ester 7.3%, terminal hydroxy group saturated polyester resin 7%, isophorone 2.5%, levelling agent 1%, silver powder 1.5%, pure
Fluorine wax 0.7%.
Preparation method:Each component is put into bonding machines successively, is passed through protective gas at room temperature, 500rpm bonding 3min,
Obtain imitative electrodeposition-type powdery paints.
Embodiment 2
A kind of imitative electrodeposition-type powdery paints, raw material components percentage:End carboxyl saturated polyester resin 80.7%,
Isocyanuric acid three-glycidyl ester 6%, terminal hydroxy group saturated polyester resin 9%, isophorone 2%, levelling agent 0.8%, silver powder 1%, pure fluorine
Wax 0.5%.
Preparation method:Each component is put into bonding machines successively, is passed through protective gas at room temperature, 900rpm bonding 6min,
Obtain imitative electrodeposition-type powdery paints.
Embodiment 3
A kind of imitative electrodeposition-type powdery paints, raw material components percentage:End carboxyl saturated polyester resin 80.9%,
Isocyanuric acid three-glycidyl ester 6.3%, terminal hydroxy group saturated polyester resin 8%, isophorone 2.1%, levelling agent 0.9%, silver powder
1.2%th, pure fluorine wax 0.6%.
Preparation method:Each component is put into bonding machines successively, is passed through protective gas at room temperature, 700rpm bonding 5min,
Obtain imitative electrodeposition-type powdery paints.
Obtained imitative electrodeposition-type powdery paints, plate is sprayed with electrostatic gun, the film coated surface obtained after baking produces reflective
As the metal effect of chromium plating minute surface.
Detection project:
The foregoing is only presently preferred embodiments of the present invention, all equivalent changes done according to scope of the present invention patent with
Modification, it should all belong to the covering scope of the present invention.
Claims (1)
- A kind of 1. imitative electrodeposition-type powdery paints, it is characterised in that:Raw material components percentage:End carboxyl saturated polyester tree Fat 80.7%, isocyanuric acid three-glycidyl ester 6%, terminal hydroxy group saturated polyester resin 9%, isophorone 2%, levelling agent 0.8%, silver Powder 1%, pure fluorine wax 0.5%;Preparation method:Each component is put into bonding machines successively, protective gas is passed through at room temperature, 900rpm bonding 6min, obtains Imitative electrodeposition-type powdery paints.