CN103540224A - Anti-corrosion paint for switch cabinet and preparation method thereof - Google Patents
Anti-corrosion paint for switch cabinet and preparation method thereof Download PDFInfo
- Publication number
- CN103540224A CN103540224A CN201310514972.8A CN201310514972A CN103540224A CN 103540224 A CN103540224 A CN 103540224A CN 201310514972 A CN201310514972 A CN 201310514972A CN 103540224 A CN103540224 A CN 103540224A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- paint
- stir
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-corrosion paint for a switch cabinet. The anti-corrosion paint is characterized in that the anti-corrosion paint is prepared from the following raw materials in parts by weight: 45-50 parts of E-12 epoxy resin, 30-40 parts of amino resin, 40-50 parts of epoxy phenolic resin, 20-24 parts of polyester acrylate, 6-8 parts of 2-methyl dimethacrylate, 1-2 parts of monobutyl tin oxide, 2-3 parts of montmorillonite powder, 12-14 parts of bentonite, 1-2 parts of anti-aging agent OD, 4-5 parts of bamboo charcoal powder, 10-12 parts of ethyl acetate, 2-3 parts of vinyl acetate, 2-3 parts of sodium bicarbonate, 4-5 parts of di-dodecanol ester and 4-5 parts of auxiliaries. The auxiliaries can improve the optical performance of the anti-corrosion paint, enable the dispersion of the paint to be uniform, further maintain the stability of the paint and improve the film-forming effect. The anti-corrosion paint provided by the invention has the advantages of great insulation property, weather resistance, smooth paint surface, luster and good leveling property, can be used for the switch cabinet in a corrosive environment, and has a relatively good protection effect.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly a kind of switching cabinet antifouling paste and preparation method thereof.
Background technology
Electric, switch, instrument cabinet (switch cabinet) are a kind of electric equipment, and outside line is introduced into master switch in cabinet, then enters sub-control switch, and each needs to arrange by it along separate routes.As instrument, automatic control, electric motor magnetic switch, various alternating current contactors etc., what have also establishes pressurizing chamber and low-pressure chamber switching cabinet, is provided with high voltage bus, and as power station etc., what have is also provided with as protecting the low-frequency load reduction of major equipment.Switching cabinet Working environment diversity, some environment are severe, need be coated with enamelled coating on cabinet surface, and with high temperature resistant, cold-resistant, UV resistant, corrosion-resistant etc., but that existing paint cannot meet is electric, the different requirements of switch, instrument cabinet.
Summary of the invention
The object of this invention is to provide a kind of switching cabinet antifouling paste and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
An antifouling paste, is characterized in that being made by the raw material of following weight part: E-12 epoxy resin 45-50, aminoresin 30-40, epoxy phenolics 40-50, polyester acrylate 20-24,2-methyl diacrylate methyl esters 6-8, Mono-n-butyltin 1-2, montmorillonite powder 2-3, wilkinite 12-14, anti-aging agent OD 1-2, bamboo charcoal powder 4-5, ethyl acetate 10-12, vinyl acetate 2-3, sodium bicarbonate 2-3, two Lauryl Alcohol ester 4-5, auxiliary agent 4-5; Auxiliary agent is made by the raw material of following weight part: attapulgite 100-110, jade powder 12-13, sepiolite 20-23, manganous sulfate 6-8, zinc oxide 3-4, zinc sulfate 2-3, Zinc Stearate 2-3, xitix 1-2, Radix Angelicae Sinensis oil 0.1-0.2, linking agent TAC1-2; Preparation method is pulverized and mixed attapulgite, jade powder, sepiolite, manganous sulfate, grinds and obtains 200-300 order powder, will in mixed powder, add Zinc Stearate, stir, briquetting material under 30-40Mpa, sends in 950-980 ℃ of calcining furnace, calcining 3-4 hour, after cooling, take out pulverizing and obtain 300-400 order powder, add zinc sulfate, xitix to continue grinding distribution 1-2 hour in the powder of gained, finally add other remaining component, grind 2-3 hour, obtain.
The preparation method of described switching cabinet antifouling paste, it is characterized in that: by epoxy phenolics, polyester acrylate, 2-methyl diacrylate methyl esters, Mono-n-butyltin, montmorillonite powder, wilkinite adds in ethyl acetate, be warming up to 55-60 ℃, stir 30-40 minute, be warming up to again 80-85 ℃, within interval 5-8 minute, add successively vinyl acetate, sodium bicarbonate, two Lauryl Alcohol esters, auxiliary agent, while feeding in raw material, stir, continue to stir 40-45 minute, add again other remaining component, after 1600-1800 rev/min of high speed dispersion 15-20 minute, proceed to grinding, obtain 20-50 μ m slurry, obtain.
Auxiliary agent of the present invention has improved optical property, and paint is uniformly dispersed, and has maintained stability, the raising film-formation result of paint; The present invention has good insulativity, weathering resistance, and lacquer painting is smooth, glossy, and good leveling property is used in corrosive environment for switching cabinet, has better protecting effect.
Embodiment
An antifouling paste, by following weight part (kilogram) raw material make: E-12 epoxy resin 45, aminoresin 30, epoxy phenolics 40, polyester acrylate 24,2-methyl diacrylate methyl esters 8, Mono-n-butyltin 2, montmorillonite powder 2, wilkinite 12, anti-aging agent OD 2, bamboo charcoal powder 5, ethyl acetate 10, vinyl acetate 3, sodium bicarbonate 2, two Lauryl Alcohol ester 4, auxiliary agent 4;
Described auxiliary agent by following weight part (kilogram) raw material make: attapulgite 100, jade powder 12, sepiolite 20, manganous sulfate 6, zinc oxide 3, zinc sulfate 2, Zinc Stearate 3, xitix 1, Radix Angelicae Sinensis oil 0.1, linking agent TAC1; Preparation method is pulverized and mixed attapulgite, jade powder, sepiolite, manganous sulfate, grinds and obtains 200-300 order powder, will in mixed powder, add Zinc Stearate, stir, briquetting material under 30-40Mpa, sends in 950-980 ℃ of calcining furnace, calcining 3-4 hour, after cooling, take out pulverizing and obtain 300-400 order powder, add zinc sulfate, xitix to continue grinding distribution 1-2 hour in the powder of gained, finally add other remaining component, grind 2-3 hour, obtain.
The preparation method of switching cabinet antifouling paste, it is characterized in that: by epoxy phenolics, polyester acrylate, 2-methyl diacrylate methyl esters, Mono-n-butyltin, montmorillonite powder, wilkinite adds in ethyl acetate, be warming up to 55-60 ℃, stir 30-40 minute, be warming up to again 80-85 ℃, within interval 5-8 minute, add successively vinyl acetate, sodium bicarbonate, two Lauryl Alcohol esters, auxiliary agent, while feeding in raw material, stir, continue to stir 40-45 minute, add again other remaining component, after 1600-1800 rev/min of high speed dispersion 15-20 minute, proceed to grinding, obtain 20-50 μ m slurry, obtain.
When the present invention sprays object plane, the air pressure Etech of spray gun is at 0.25-0.35Mpa, and spray gun is apart from the about 20-30cm of object plane distance, and after spraying, room temperature is standing, seasoning.
Performance index of the present invention:
1, snappiness mm≤2
2, hardness >=3H
3, high temperature resistant (130 ℃) >=480h
4, shock-resistance 65
5, salt spray resistance (120h level) >=3
6, water tolerance (29 ± 1 ℃ of 240h): non-foaming, do not come off
7, oil resistant (90# gasoline, 56h): non-foaming, do not come off
8, alkali resistance (GB/T9755-2001): by 48 hours
9, artificial weathering ageing resistance (GB/T9755-2001): by 1300 hours.
Claims (2)
1. a switching cabinet antifouling paste, is characterized in that being made by the raw material of following weight part: E-12 epoxy resin 45-50, aminoresin 30-40, epoxy phenolics 40-50, polyester acrylate 20-24,2-methyl diacrylate methyl esters 6-8, Mono-n-butyltin 1-2, montmorillonite powder 2-3, wilkinite 12-14, anti-aging agent OD 1-2, bamboo charcoal powder 4-5, ethyl acetate 10-12, vinyl acetate 2-3, sodium bicarbonate 2-3, two Lauryl Alcohol ester 4-5, auxiliary agent 4-5; Auxiliary agent is made by the raw material of following weight part: attapulgite 100-110, jade powder 12-13, sepiolite 20-23, manganous sulfate 6-8, zinc oxide 3-4, zinc sulfate 2-3, Zinc Stearate 2-3, xitix 1-2, Radix Angelicae Sinensis oil 0.1-0.2, linking agent TAC1-2; Preparation method is pulverized and mixed attapulgite, jade powder, sepiolite, manganous sulfate, grinds and obtains 200-300 order powder, will in mixed powder, add Zinc Stearate, stir, briquetting material under 30-40Mpa, sends in 950-980 ℃ of calcining furnace, calcining 3-4 hour, after cooling, take out pulverizing and obtain 300-400 order powder, add zinc sulfate, xitix to continue grinding distribution 1-2 hour in the powder of gained, finally add other remaining component, grind 2-3 hour, obtain.
2. the preparation method of switching cabinet antifouling paste according to claim 1, it is characterized in that: by epoxy phenolics, polyester acrylate, 2-methyl diacrylate methyl esters, Mono-n-butyltin, montmorillonite powder, wilkinite adds in ethyl acetate, be warming up to 55-60 ℃, stir 30-40 minute, be warming up to again 80-85 ℃, within interval 5-8 minute, add successively vinyl acetate, sodium bicarbonate, two Lauryl Alcohol esters, auxiliary agent, while feeding in raw material, stir, continue to stir 40-45 minute, add again other remaining component, after 1600-1800 rev/min of high speed dispersion 15-20 minute, proceed to grinding, obtain 20-50 μ m slurry, obtain.