CN107868520A - A kind of barrier coat used on the stool leg of wooden stool - Google Patents

A kind of barrier coat used on the stool leg of wooden stool Download PDF

Info

Publication number
CN107868520A
CN107868520A CN201711249002.4A CN201711249002A CN107868520A CN 107868520 A CN107868520 A CN 107868520A CN 201711249002 A CN201711249002 A CN 201711249002A CN 107868520 A CN107868520 A CN 107868520A
Authority
CN
China
Prior art keywords
parts
stool
silane
barrier coat
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711249002.4A
Other languages
Chinese (zh)
Inventor
金继善
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201711249002.4A priority Critical patent/CN107868520A/en
Publication of CN107868520A publication Critical patent/CN107868520A/en
Withdrawn legal-status Critical Current

Abstract

The barrier coat used on a kind of stool leg of wooden stool, it is related to household implements processing technical field, it is characterised in that：It is made up of the material of following parts by weight, 17 23 parts of resin, 602 7 13 parts of silane coupler KH, 29 parts of adipic acid propanediol polyester, double 28 parts of ten four carbon alcohols esters, modified 7 12 parts of bauxite, 26 parts of butyl acrylate, 15 parts of zinc stearate, 37 parts of 1,6 hexamethylene diisocyanate, 27 parts of phenyl glycidyl ether, 14 parts of polyvinyl alcohol, 25 parts of vinyl three (β methoxy ethoxies) silane, 10 17 parts of auxiliary additive, 5 10 parts of age resistor, 21 27 parts of deionized water.The inventive method is reasonable, easy to implement, anti-corrosion, protection against the tide, mould proof.

Description

A kind of barrier coat used on the stool leg of wooden stool
Technical field
The present invention relates to household implements to process technical field, and in particular to is used on a kind of stool leg of wooden stool Barrier coat.
Background technology
Stool is a kind of furniture, and general is mostly wood plate surface, mostly unbacked thing to sit on, thin-and-long.
Part：
Stool leg, similar to the pillar in building, supporting member；
Stool face, similar to the roof in building, power is distributed on stool leg, it is small with the big pressure of people's contact area, sit And do not ache (otherwise directly sit people on leg and can't stand), indispensable role is act as in the life of the common people；
The bar of lateral connection, similar to a tree, used in making timber for boats in ancient building, it is connected to stool leg and is not easy to fall apart by it.
The small stool of Chinese tradition, it is elegant in appearance, durable in use.Making stool has certain technology content.Stool Angle is that one-inch puts two points (length of actual upper horizontal beam is also that one-inch puts two points.Here it is Chinese tradition craftsman to sum up what is come Experience, we not forget that ancestors leave many valuable wealth to us).All use metric system instead now and do not have to Chinese system of weights. So after by actual measure, the angle for drawing stool is 12 degree.I thinks that not all stool is all 12 degree！Such as bar The bar stool stool different with other length, in order to attractive in appearance and practical, thus it is possible to vary some angles are also normal thing.It is practical Angle be 10,12 and 15 3 kind.
And because the use of present stool is very extensive, it is particularly wooden, due to many stool it is often long when Between use out of doors, so can easily make moist, be mouldy etc., and easily ftracture, be broken, so for the security that uses just Do not ensure.
The content of the invention
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, embodiment party Just, anti-corrosion, protection against the tide, a kind of mould proof wooden stool stool leg on the barrier coat that uses.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of barrier coat used on the stool leg of wooden stool, it is characterised in that：By the material system of following parts by weight Into,
Resin 17-23 parts, silane coupler KH-6027-13 parts, adipic acid propanediol polyester 2-9 parts, double ten four carbon alcohols esters 2-8 parts, modified bauxite 7-12 parts, butyl acrylate 2-6 parts, zinc stearate 1-5 parts, hexamethylene diisocyanate 3-7 parts, benzene Base glycidol ether 2-7 parts, polyvinyl alcohol 1-4 parts, ('beta '-methoxy ethyoxyl) the silane 2-5 of vinyl three parts, auxiliary additive 10-17 parts, age resistor 5-10 parts, deionized water 21-27 parts；
The resin is one kind in polyvinyl resin, phenolic resin, epoxy resin, Lauxite, polyamide；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, antioxidant D, age resistor CPPD；
The preparation method of the modified bauxite is to grind bauxite and cross 400-500 mesh sieves, be then placed on 40 DEG C At a temperature of toast 40 minutes, then add the pure water of 0.62 times of its quality, stirred 30 minutes under 50 DEG C of temperature constant state, Then dimethyl terephthalate (DMT) is added, and is warming up to 55 DEG C, 1.8 hours is then stirred, re-dry, re-grinds, Bauxite must be modified；
The mass ratio of the dimethyl terephthalate (DMT) and bauxite is 1：3.3；
The auxiliary additive is made up of the material of following parts by weight,
1 part of kuh-seng, 2 parts of the bark of ash, 3 parts of the root bark of shaggy-fruited dittany, 4 parts of radix scutellariae, 5 parts of saltcake, 6 parts of felwort, 7 parts of the capsule of weeping forsythia, 1 part of adder-wort You, 2 parts of rhizome of cyrtomium, 3 parts of cow-bezoar, 4 parts of radix cynanchi atrati, 5 parts of rheum officinale, 6 parts of blackberry lily, 4 parts of kaladana, 7 parts of mung bean；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, it is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of the barrier coat used on a kind of stool leg of wooden stool is,
I by resin, silane coupler KH-602, adipic acid propanediol polyester, double ten four carbon alcohols esters, modified bauxite, third Olefin(e) acid butyl ester, zinc stearate, 1, hexamethylene-diisocyanate, deionized water are put into reactor, mixed at a temperature of 40-50 DEG C 1 hour；
II is added to phenyl glycidyl ether, polyvinyl alcohol, vinyl three ('beta '-methoxy ethyoxyl) silane, age resistor In I, and 55-65 DEG C is warming up to, continues to mix 1.5 hours；
70-80 DEG C is warming up to after the completion of III mixing and adds auxiliary additive, mixing cools to 45-55 DEG C after 30 minutes, Continue to mix 1.5 hours.
Beneficial effects of the present invention are：Described material is combined stirring, mix, by way of heating, cooling, The performance of product has obtained more powerful optimization and release, and almost non-toxic pollution-free, does not all have for environment, human body Injure and destroy, and with the addition of the material of biomass, be also a very good selection with biological coating now, it is nontoxic Pollution-free and cost is cheap, also the effect with effective crack resistence, also the effect with anti-corrosion and waterproof, by increasing capacitance it is possible to increase uses Life-span.The inventive method is reasonable, easy to implement, anti-corrosion, protection against the tide, mould proof.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, enter below One step illustrates the present invention.
Embodiment 1
A kind of barrier coat used on the stool leg of wooden stool, it is characterised in that：By the material system of following parts by weight Into,
17 parts of resin, silane coupler KH-6027 parts, 2 parts of adipic acid propanediol polyester, double 2 parts of ten four carbon alcohols esters, modification It is 7 parts of bauxite, 2 parts of butyl acrylate, 1 part of zinc stearate, 3 parts of hexamethylene diisocyanate, 2 parts of phenyl glycidyl ether, poly- 1 part of vinyl alcohol, 2 parts of vinyl three ('beta '-methoxy ethyoxyl) silane, 10 parts of auxiliary additive, 5 parts of age resistor, deionized water 21 Part；
The resin is one kind in polyvinyl resin, phenolic resin, epoxy resin, Lauxite, polyamide；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, antioxidant D, age resistor CPPD；
The preparation method of the modified bauxite is to grind bauxite and cross 400-500 mesh sieves, be then placed on 40 DEG C At a temperature of toast 40 minutes, then add the pure water of 0.62 times of its quality, stirred 30 minutes under 50 DEG C of temperature constant state, Then dimethyl terephthalate (DMT) is added, and is warming up to 55 DEG C, 1.8 hours is then stirred, re-dry, re-grinds, Bauxite must be modified；
The mass ratio of the dimethyl terephthalate (DMT) and bauxite is 1：3.3；
The auxiliary additive is made up of the material of following parts by weight,
1 part of kuh-seng, 2 parts of the bark of ash, 3 parts of the root bark of shaggy-fruited dittany, 4 parts of radix scutellariae, 5 parts of saltcake, 6 parts of felwort, 7 parts of the capsule of weeping forsythia, 1 part of adder-wort You, 2 parts of rhizome of cyrtomium, 3 parts of cow-bezoar, 4 parts of radix cynanchi atrati, 5 parts of rheum officinale, 6 parts of blackberry lily, 4 parts of kaladana, 7 parts of mung bean；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, it is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of the barrier coat used on a kind of stool leg of wooden stool is,
I by resin, silane coupler KH-602, adipic acid propanediol polyester, double ten four carbon alcohols esters, modified bauxite, third Olefin(e) acid butyl ester, zinc stearate, 1, hexamethylene-diisocyanate, deionized water are put into reactor, mixed at a temperature of 40-50 DEG C 1 hour；
II is added to phenyl glycidyl ether, polyvinyl alcohol, vinyl three ('beta '-methoxy ethyoxyl) silane, age resistor In I, and 55-65 DEG C is warming up to, continues to mix 1.5 hours；
70-80 DEG C is warming up to after the completion of III mixing and adds auxiliary additive, mixing cools to 45-55 DEG C after 30 minutes, Continue to mix 1.5 hours.
Embodiment 2
A kind of barrier coat used on the stool leg of wooden stool, it is characterised in that：By the material system of following parts by weight Into,
23 parts of resin, silane coupler KH-60213 parts, 9 parts of adipic acid propanediol polyester, double 8 parts of ten four carbon alcohols esters, change 12 parts of bauxite of property, 6 parts of butyl acrylate, 5 parts of zinc stearate, 7 parts of hexamethylene diisocyanate, 7 parts of phenyl glycidyl ether, 4 parts of polyvinyl alcohol, 5 parts of vinyl three ('beta '-methoxy ethyoxyl) silane, 17 parts of auxiliary additive, 10 parts of age resistor, deionization 27 parts of water；
The resin is one kind in polyvinyl resin, phenolic resin, epoxy resin, Lauxite, polyamide；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, antioxidant D, age resistor CPPD；
The preparation method of the modified bauxite is to grind bauxite and cross 400-500 mesh sieves, be then placed on 40 DEG C At a temperature of toast 40 minutes, then add the pure water of 0.62 times of its quality, stirred 30 minutes under 50 DEG C of temperature constant state, Then dimethyl terephthalate (DMT) is added, and is warming up to 55 DEG C, 1.8 hours is then stirred, re-dry, re-grinds, Bauxite must be modified；
The mass ratio of the dimethyl terephthalate (DMT) and bauxite is 1：3.3；
The auxiliary additive is made up of the material of following parts by weight,
1 part of kuh-seng, 2 parts of the bark of ash, 3 parts of the root bark of shaggy-fruited dittany, 4 parts of radix scutellariae, 5 parts of saltcake, 6 parts of felwort, 7 parts of the capsule of weeping forsythia, 1 part of adder-wort You, 2 parts of rhizome of cyrtomium, 3 parts of cow-bezoar, 4 parts of radix cynanchi atrati, 5 parts of rheum officinale, 6 parts of blackberry lily, 4 parts of kaladana, 7 parts of mung bean；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, it is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of the barrier coat used on a kind of stool leg of wooden stool is,
I by resin, silane coupler KH-602, adipic acid propanediol polyester, double ten four carbon alcohols esters, modified bauxite, third Olefin(e) acid butyl ester, zinc stearate, 1, hexamethylene-diisocyanate, deionized water are put into reactor, mixed at a temperature of 40-50 DEG C 1 hour；
II is added to phenyl glycidyl ether, polyvinyl alcohol, vinyl three ('beta '-methoxy ethyoxyl) silane, age resistor In I, and 55-65 DEG C is warming up to, continues to mix 1.5 hours；
70-80 DEG C is warming up to after the completion of III mixing and adds auxiliary additive, mixing cools to 45-55 DEG C after 30 minutes, Continue to mix 1.5 hours.
Embodiment 3
A kind of barrier coat used on the stool leg of wooden stool, it is characterised in that：By the material system of following parts by weight Into,
20 parts of resin, silane coupler KH-60220 parts, 7 parts of adipic acid propanediol polyester, double 6 parts of ten four carbon alcohols esters, change 11 parts of bauxite of property, 4 parts of butyl acrylate, 3 parts of zinc stearate, 5 parts of hexamethylene diisocyanate, 6 parts of phenyl glycidyl ether, 2 parts of polyvinyl alcohol, 3 parts of vinyl three ('beta '-methoxy ethyoxyl) silane, 14 parts of auxiliary additive, 8 parts of age resistor, deionized water 25 parts；
The resin is one kind in polyvinyl resin, phenolic resin, epoxy resin, Lauxite, polyamide；
The age resistor is one kind in antioxidant A W, anti-aging agent RD, antioxidant A, antioxidant D, age resistor CPPD；
The preparation method of the modified bauxite is to grind bauxite and cross 400-500 mesh sieves, be then placed on 40 DEG C At a temperature of toast 40 minutes, then add the pure water of 0.62 times of its quality, stirred 30 minutes under 50 DEG C of temperature constant state, Then dimethyl terephthalate (DMT) is added, and is warming up to 55 DEG C, 1.8 hours is then stirred, re-dry, re-grinds, Bauxite must be modified；
The mass ratio of the dimethyl terephthalate (DMT) and bauxite is 1：3.3；
The auxiliary additive is made up of the material of following parts by weight,
1 part of kuh-seng, 2 parts of the bark of ash, 3 parts of the root bark of shaggy-fruited dittany, 4 parts of radix scutellariae, 5 parts of saltcake, 6 parts of felwort, 7 parts of the capsule of weeping forsythia, 1 part of adder-wort You, 2 parts of rhizome of cyrtomium, 3 parts of cow-bezoar, 4 parts of radix cynanchi atrati, 5 parts of rheum officinale, 6 parts of blackberry lily, 4 parts of kaladana, 7 parts of mung bean；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant 4-5 hour of middle baking, it is then placed in equipment and grinds and cross 400-500 mesh sieves, the clear water for adding 0.7 times of quality of materials stirs 1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
The preparation method of the barrier coat used on a kind of stool leg of wooden stool is,
I by resin, silane coupler KH-602, adipic acid propanediol polyester, double ten four carbon alcohols esters, modified bauxite, third Olefin(e) acid butyl ester, zinc stearate, 1, hexamethylene-diisocyanate, deionized water are put into reactor, mixed at a temperature of 40-50 DEG C 1 hour；
II is added to phenyl glycidyl ether, polyvinyl alcohol, vinyl three ('beta '-methoxy ethyoxyl) silane, age resistor In I, and 55-65 DEG C is warming up to, continues to mix 1.5 hours；
70-80 DEG C is warming up to after the completion of III mixing and adds auxiliary additive, mixing cools to 45-55 DEG C after 30 minutes, Continue to mix 1.5 hours.
The coating used on a kind of plank, it is made up of the material of following parts by weight,
15 parts of phenolic resin, 10 parts of silane resin acceptor kh-550, double 6 parts of ten four carbon alcohols esters, modified 11 parts of bauxite, propylene It is 4 parts of acid butyl ester, 6 parts of phenyl glycidyl ether, 2 parts of polyvinyl alcohol, 3 parts of vinyl three ('beta '-methoxy ethyoxyl) silane, anti-old 25 parts of agent A8 parts, water；
Preparation method：Above-mentioned material is put into reactor 2 hours of reaction, Ran Housheng at a temperature of 50-60 DEG C 10 DEG C of temperature, continue to react 1.5 hours.
By experiment, measure 1-3 of the embodiment of the present invention and comparative example performance and effect, such as following table：
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its Equivalent thereof.

Claims (2)

  1. A kind of 1. barrier coat used on stool leg of wooden stool, it is characterised in that：It is made up of the material of following parts by weight,
    Resin 17-23 parts, silane coupler KH-6027-13 parts, adipic acid propanediol polyester 2-9 parts, double ten four carbon alcohols ester 2-8 Part, modified bauxite 7-12 parts, butyl acrylate 2-6 parts, zinc stearate 1-5 parts, hexamethylene diisocyanate 3-7 parts, phenyl Glycidol ether 2-7 parts, polyvinyl alcohol 1-4 parts, ('beta '-methoxy ethyoxyl) the silane 2-5 of vinyl three parts, auxiliary additive 10- 17 parts, age resistor 5-10 parts, deionized water 21-27 parts.
  2. 2. the barrier coat used on a kind of stool leg of wooden stool according to claim 1, it is characterised in that：It is described A kind of preparation method of the barrier coat used on stool leg of wooden stool is,
    I by resin, silane coupler KH-602, adipic acid propanediol polyester, double ten four carbon alcohols esters, modified bauxite, acrylic acid Butyl ester, zinc stearate, 1, hexamethylene-diisocyanate, deionized water are put into reactor, and 1 is mixed at a temperature of 40-50 DEG C Hour；
    During phenyl glycidyl ether, polyvinyl alcohol, vinyl three ('beta '-methoxy ethyoxyl) silane, age resistor are added to I by II, And 55-65 DEG C is warming up to, continue to mix 1.5 hours；
    70-80 DEG C is warming up to after the completion of III mixing and adds auxiliary additive, mixing cools to 45-55 DEG C after 30 minutes, continue Mix 1.5 hours.
CN201711249002.4A 2017-12-01 2017-12-01 A kind of barrier coat used on the stool leg of wooden stool Withdrawn CN107868520A (en)