CN103540231A - Anti-rust paint for switch cabinet body and preparation method thereof - Google Patents
Anti-rust paint for switch cabinet body and preparation method thereof Download PDFInfo
- Publication number
- CN103540231A CN103540231A CN201310515248.7A CN201310515248A CN103540231A CN 103540231 A CN103540231 A CN 103540231A CN 201310515248 A CN201310515248 A CN 201310515248A CN 103540231 A CN103540231 A CN 103540231A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- powder
- switch cabinet
- rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an anti-rust paint for a switch cabinet body. The anti-rust paint is characterized in that the anti-rust paint is prepared from the following raw materials in parts by weight: 72-77 parts of E-12 epoxy resin, 12-14 parts of fumed silica, 1-2 parts of zinc oxide, 1-2 parts of butyl tin mercaptide, 4-5 parts of bentonite, 12-14 parts of xylene, 2-3 parts of kaolin powder, 2-3 parts of zinc stearate, 14-17 parts of magnesium hydroxide, 8-10 parts of chlorinated paraffin, 4-5 parts of acrylonitrile and 4-5 parts of auxiliaries. The auxiliaries can improve the optical performance of the anti-rust paint, enable the dispersion of the paint to be uniform, further maintain the stability of the paint and improve the film-forming effect. The anti-rust paint provided by the invention has the advantages of effectively solving the thixotropic problem of the paint, greatly improving the adhesion to a steel plate material of the switch cabinet body, reducing the number of construction channels, ensuring the thickness of a paint film, and realizing stable physical properties, low toxicity, chemical medium resistance and strong weather resistance of the paint film.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly a kind of switch cabinet rust-inhibiting paint and preparation method thereof.
Background technology
Electric, switch, instrument cabinet (switch cabinet) are a kind of electric equipment, and outside line is introduced into master switch in cabinet, then enters sub-control switch, and each needs to arrange by it along separate routes.As instrument, automatic control, electric motor magnetic switch, various alternating current contactors etc., what have also establishes pressurizing chamber and low-pressure chamber switching cabinet, is provided with high voltage bus, and as power station etc., what have is also provided with as protecting the low-frequency load reduction of major equipment.Switching cabinet Working environment diversity, some environment are severe, need be coated with enamelled coating on cabinet surface, and with high temperature resistant, cold-resistant, UV resistant, corrosion-resistant etc., but that existing paint cannot meet is electric, the different requirements of switch, instrument cabinet.
Summary of the invention
The object of this invention is to provide a kind of switch cabinet rust-inhibiting paint and preparation method thereof.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
A rust-inhibiting paint, is characterized in that being made by the raw material of following weight part: E-12 epoxy resin 72-77, aerosil 12-14, zinc oxide 1-2, thiol-butyl tin 1-2, wilkinite 4-5, dimethylbenzene 12-14, kaolin powder 2-3, Zinc Stearate 2-3, magnesium hydroxide 14-17, clorafin 8-10, vinyl cyanide 4-5, auxiliary agent 4-5; Auxiliary agent is made by the raw material of following weight part: attapulgite 100-110, jade powder 12-13, sepiolite 20-23, manganous sulfate 6-8, zinc oxide 3-4, zinc sulfate 2-3, Zinc Stearate 2-3, xitix 1-2, Radix Angelicae Sinensis oil 0.1-0.2, linking agent TAC1-2; Preparation method is pulverized and mixed attapulgite, jade powder, sepiolite, manganous sulfate, grinds and obtains 200-300 order powder, will in mixed powder, add Zinc Stearate, stir, briquetting material under 30-40Mpa, sends in 950-980 ℃ of calcining furnace, calcining 3-4 hour, after cooling, take out pulverizing and obtain 300-400 order powder, add zinc sulfate, xitix to continue grinding distribution 1-2 hour in the powder of gained, finally add other remaining component, grind 2-3 hour, obtain.
The preparation method of described switch cabinet rust-inhibiting paint, it is characterized in that: Zinc Stearate, magnesium hydroxide, clorafin, vinyl cyanide are added in dimethylbenzene, be warming up to 65-70 ℃, stir 30-40 minute, be warming up to again 82-87 ℃, within interval 5-10 minute, add successively E-12 epoxy resin, zinc oxide, thiol-butyl tin, auxiliary agent, after stirring while feeding in raw material, continue to stir 40-45 minute, add again other remaining component, after 1600-1800 rev/min of high speed dispersion 20-30 minute, proceed to grinding, obtain 20-50 μ m slurry, obtain.
Auxiliary agent of the present invention has improved optical property, and paint is uniformly dispersed, and has maintained stability, the raising film-formation result of paint; The present invention can not only effectively solve the thixotroping problem of paint, and can greatly improve its sticking power to switch cabinet steel plate materials, reduces construction road number, guarantees film thickness, the stable physical property of paint film, and toxicity is low, resistant to chemical media, weathering resistance is strong.
Embodiment
A rust-inhibiting paint, by following weight part (kilogram) raw material make: E-12 epoxy resin 72, aerosil 12, zinc oxide 1, thiol-butyl tin 2, wilkinite 5, dimethylbenzene 12, kaolin powder 3, Zinc Stearate 3, magnesium hydroxide 14, clorafin 8, vinyl cyanide 5, auxiliary agent 4;
Described auxiliary agent by following weight part (kilogram) raw material make: attapulgite 100, jade powder 12, sepiolite 20, manganous sulfate 6, zinc oxide 3, zinc sulfate 2, Zinc Stearate 3, xitix 1, Radix Angelicae Sinensis oil 0.1, linking agent TAC1; Preparation method is pulverized and mixed attapulgite, jade powder, sepiolite, manganous sulfate, grinds and obtains 200-300 order powder, will in mixed powder, add Zinc Stearate, stir, briquetting material under 30-40Mpa, sends in 950-980 ℃ of calcining furnace, calcining 3-4 hour, after cooling, take out pulverizing and obtain 300-400 order powder, add zinc sulfate, xitix to continue grinding distribution 1-2 hour in the powder of gained, finally add other remaining component, grind 2-3 hour, obtain.
The preparation method of described switch cabinet rust-inhibiting paint, it is characterized in that: Zinc Stearate, magnesium hydroxide, clorafin, vinyl cyanide are added in dimethylbenzene, be warming up to 65-70 ℃, stir 30-40 minute, be warming up to again 82-87 ℃, within interval 5-10 minute, add successively E-12 epoxy resin, zinc oxide, thiol-butyl tin, auxiliary agent, after stirring while feeding in raw material, continue to stir 40-45 minute, add again other remaining component, after 1600-1800 rev/min of high speed dispersion 20-30 minute, proceed to grinding, obtain 20-50 μ m slurry, obtain.
When the present invention sprays object plane, the air pressure Etech of spray gun is at 0.25-0.35Mpa, and spray gun is apart from the about 20-30cm of object plane distance, and after spraying, room temperature is standing, seasoning.
Performance index of the present invention:
1, snappiness mm≤2
2, hardness >=3H
3, high temperature resistant (130 ℃) >=480h
4, shock-resistance 65
5, salt spray resistance (120h level) >=3
6, water tolerance (29 ± 1 ℃ of 240h): non-foaming, do not come off
7, oil resistant (90# gasoline, 56h): non-foaming, do not come off
8, alkali resistance (GB/T9755-2001): by 48 hours
9, artificial weathering ageing resistance (GB/T9755-2001): by 1300 hours.
Claims (2)
1. a switch cabinet rust-inhibiting paint, is characterized in that being made by the raw material of following weight part: E-12 epoxy resin 72-77, aerosil 12-14, zinc oxide 1-2, thiol-butyl tin 1-2, wilkinite 4-5, dimethylbenzene 12-14, kaolin powder 2-3, Zinc Stearate 2-3, magnesium hydroxide 14-17, clorafin 8-10, vinyl cyanide 4-5, auxiliary agent 4-5; Auxiliary agent is made by the raw material of following weight part: attapulgite 100-110, jade powder 12-13, sepiolite 20-23, manganous sulfate 6-8, zinc oxide 3-4, zinc sulfate 2-3, Zinc Stearate 2-3, xitix 1-2, Radix Angelicae Sinensis oil 0.1-0.2, linking agent TAC1-2; Preparation method is pulverized and mixed attapulgite, jade powder, sepiolite, manganous sulfate, grinds and obtains 200-300 order powder, will in mixed powder, add Zinc Stearate, stir, briquetting material under 30-40Mpa, sends in 950-980 ℃ of calcining furnace, calcining 3-4 hour, after cooling, take out pulverizing and obtain 300-400 order powder, add zinc sulfate, xitix to continue grinding distribution 1-2 hour in the powder of gained, finally add other remaining component, grind 2-3 hour, obtain.
2. the preparation method of switch cabinet rust-inhibiting paint according to claim 1, it is characterized in that: Zinc Stearate, magnesium hydroxide, clorafin, vinyl cyanide are added in dimethylbenzene, be warming up to 65-70 ℃, stir 30-40 minute, be warming up to again 82-87 ℃, within interval 5-10 minute, add successively E-12 epoxy resin, zinc oxide, thiol-butyl tin, auxiliary agent, after stirring while feeding in raw material, continue to stir 40-45 minute, add again other remaining component, after 1600-1800 rev/min of high speed dispersion 20-30 minute, proceed to grinding, obtain 20-50 μ m slurry, obtain.