CN101864236A - Aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish - Google Patents
Aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish Download PDFInfo
- Publication number
- CN101864236A CN101864236A CN 201010215899 CN201010215899A CN101864236A CN 101864236 A CN101864236 A CN 101864236A CN 201010215899 CN201010215899 CN 201010215899 CN 201010215899 A CN201010215899 A CN 201010215899A CN 101864236 A CN101864236 A CN 101864236A
- Authority
- CN
- China
- Prior art keywords
- epoxy ester
- modified epoxy
- acrylic modified
- aqueous acrylic
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish. The baking finish consists of the following components in part by weight: 45 to 65 parts of aqueous acrylic modified epoxy ester resin, 2 to 20 parts of amino resin, 5 to 35 parts of pigment, 0 to 15 parts of filler, 1 to 3 parts of water dispersible dryer, 0.1 to 0.55 part of pH regulator, 5 to 15 parts of softened water, 0.2 to 0.4 part of dispersant, 0.3 to 0.5 part of wetting agent, 0.15 to 0.25 part of flatting agent, 0.3 to 0.5 part of antifoaming agent, and 0.2 to 0.3 part of preservative and mildew preventive. Without organic solvent, the baking finish is safe, energy-saving and free from pollution; the pencil hardness reaches 2H, the coating performance is stable, the film-coating mechanical strength is high, the positive and negative impact resistance can reach 5Kg.cm, and the flexibility can reach 1mm; the baking finish can integrate antirust and anticorrosive functions, can be used as primer or topcoat, reduces the construction process, is simple and quick to operate, can be sprayed or dip-coated, and can be quickly cured; a coated film does not become yellow; and the baking finish meets the development direction of aqueous anticorrosive paint.
Description
Technical field
The invention belongs to technical field of coatings, be particularly useful for the protection and the ornamental aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish of vehicular traffic, engineering machinery, household electrical appliance and steel furniture production etc.
Background technology
Existing domestic water-based anticorrosive paint still is divided into two kinds of priming paint and finish paints mostly, to use respectively during brushing, so just must consider whether priming paint and finish paint can supportingly use, and whether can combine in the film process, therefore bring certain trouble to construction.In order to reduce construction technology, reduce construction cost, the research of water-based anticorrosive paint has in recent years focused on the aqueous corrosion resisting paint without need of cleaning rust of bottom surface unification.In addition, water-based anticorrosive paint is strong to the dependency of construction environment, how to guarantee to obtain fast drying, well behaved coating under high humidity, low temperature and enclosed environment, is still the following problem of research emphatically that needs of water-based anticorrosive paint.Patent CN101591500A adopts the aqueous self-drying acrylic acid modified alkyd antirust paint of self-crosslinking technology preparation, and rate of drying is improved, but its performance of filming such as hardness etc. also need the long duration just can reach specified value.A kind of water-based acrylic acid modified alcoholic acid amino baking vanish that Inst. of Marine Chemical Engineering (CN1405254A) is introduced, drying condition is 120 * 30min, and the mechanical property of filming is strong, and hardness reaches 2H, but only limits to use as priming paint, and its drying time is slightly long.
Summary of the invention
The object of the present invention is to provide a kind of.A kind of aqueous acrylic modified epoxy ester bottom surface unification baking vanish and preparation method thereof is provided.To realize
Aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish of the present invention is that the component by following weight part constitutes:
Aqueous acrylic modified epoxy ester resin 45-65; Aminoresin 2-20; Pigment 5-35; Filler 0-15; Aqueous dispersion type siccative 1-3; PH conditioning agent 0.1-0.55; Softening water 5-15; Dispersion agent 0.2-0.4 part; Wetting agent 0.3-0.5 part, flow agent 0.15-0.25 part, defoamer 0.3-0.5 part, sanitas and mould inhibitor 0.2-0.3 part.
Described aqueous acrylic modified epoxy ester resin is to carry out grafting under the action of evocating by the acrylic monomer of the vinyl monomer of the epoxy ester performed polymer of 20-30 weight part and 5-15 part, 5-15 part, 0.5-1 part, again through the resulting water-soluble products of Water-borne modification; Its acid number is 20-40mgKOH/g, and solid part is 30-50%., apply for patent of invention on the same day in addition, denomination of invention is: " a kind of aqueous acrylic modified epoxy ester resin and synthetic method thereof ", application number are 201010215288.6.
Its solid part of aqueous acrylic modified epoxy ester resin is 30-50%; It is the base-material as protective system, and film after the curing existing Resins, epoxy mechanical properties strength height, the good characteristics of antiseptic property have acrylic resin good weatherability, ornamental high characteristics again.
Described aminoresin comprise following one or more: the pure etherificate melamine resin of first (fourth, isobutyl), the pure etherificate trimeric cyanamide methylal resin of first (fourth, isobutyl), the pure etherificate trimeric cyanamide of first (fourth, isobutyl)-urea methylal resin.Its optimum amount is 3-8 part.
Described aqueous dispersion type siccative comprise following one or more: cobalt iso-octoate, zirconium naphthenate, zinc naphthenate; Its optimum amount is 1-3 part.
Described PH conditioning agent comprises following one or more: ammoniacal liquor, triethylamine, N, N-dimethylethanolamine, optimum amount are 0.2-0.5 part.
Described softening water is deionized water or distilled water.
Described pigment comprise following one or more: titanium dioxide, red iron oxide, iron oxide yellow, phthalocyanine blue, high-carbon black pigment, zinc oxide, strontium chromate, medium chrome yellow medium yellow, zinc phosphate, modified zinc phosphate, aluminium triphosphate, modification aluminium triphosphate etc., its optimum amount is 10-30 part.Pigment and metal base be by physical shielding or chemical passivation, effectively hinders water vapour and oxygen permeates to metal base, thus obstacle corrosion of metal effectively.
Described filler comprise following one or more: process white, talcum powder, sericite, calcined kaolin, silica powder, diatomite, its optimum amount are 0-0 part.The coating cost has not only been lowered in the use of filler, and can play the effect that improves functional coating film.Can prevent the coating sagging and in filming, absorb the function of stretching stress, minimizing crack and hole as talcum powder; Sericite in powder can improve the weathering resistance of filming, anti-water-permeable greatly, strengthen and film and matrix sticking power and coating strength, improves film apparent; Process white can improve coating suspension, improves smoothness etc.
Described dispersion agent is one or more of sodium, ammonium or amine salt of ethene modification unsaturated carboxylic acid (ester) multipolymer, and optimum amount is 0.2-0.4 part;
Described wetting agent is one or more among Tego-245, BYK-341, the SURFYNOLGA, and its optimum amount is 0.3-0.5 part;
Described flow agent is not solvent-laden modified siloxane, and as the EFKA-3580 of Efka company, optimum amount is 0.15-0.25 part;
Described defoamer is the organic silicon modified by polyether defoamer, mainly is among the EFKA-2550 of the SN313 of BYK-020, German Henkel company, Dutch Efka company one or more, and optimum amount is 0.3-0.5 part; Sanitas and mould inhibitor are the heterocyclic type compound, are mainly the KATHONLXE sanitas of Rohm-Hass, one or more in the ActicideTHP sanitas of SKANEM8 mould inhibitor and Britain Thor company, and optimum amount is respectively 0.2-0.3 part.
The preparation method of aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish may further comprise the steps:
(1) presses aqueous acrylic modified epoxy ester resin 45-65, aminoresin 2-20, pigment 5-35, filler 0-15, dispersion agent 0.2-0.4 part; Wetting agent 0.3-0.5 part, flow agent 0.15-0.25 part, defoamer 0.3-0.5 part, sanitas and mould inhibitor 0.2-0.3 part), siccative 1-3, PH conditioning agent 0.1-0.55, deionized water 5-15 get the raw materials ready;
(2) in Scattered Kettle, add the softening water, the dispersion agent in the formula ratio auxiliary agent, wetting agent of formula ratio, 2/3 defoamer, stir with the adjustable high-speed dispersion machine;
(2) add the aqueous acrylic modified epoxy ester resin of formula ratio 1/2 and the aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir;
(3) pigment, the filler of adding formula ratio stir, and keep 1-2 hour, get slurry;
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤45um;
(5) be transferred to proportion container at above-mentioned mill base, add second half aqueous acrylic modified epoxy ester resin again, flow agent, sanitas, mould inhibitor and the remaining defoamer of formula ratio stirs;
(6) detect pH value, add an amount of PH conditioning agent, regulating PH is between 8 to 10;
(7) filter, packing gets finished product.
Advantage of the present invention:
(1) be base-material with homemade aqueous acrylic modified epoxy ester resin, be substantially free of organic solvent, especially benzene kind solvent is safe, energy-conservation and pollution-free; (2) poly-hydroxy and amino resin crosslinked excessively in the acrylic modified epoxy ester water-base resin, two keys on the unsaturated fatty acids also can be cross-linked with each other, formed higher cross-linking density, so pencil hardness is up to 2H, coating property is stable, the physical strength of filming height, impact resistance is positive and negative all can to reach 50Kg.cm, and snappiness can reach 1mm.(3) (4) can be integrated antirust and anti-corrosion function, and antirust, anti-corrosive is once brushed, and has saved and has been coated with ETL estimated time of loading and cost; Both can be used as the priming paint use and also can be used as the finish paint use, need not consider the matching capacity problem of bottom surface lacquer during construction, therefore reduced construction technology, (5) are simple and quick, both can spray, but also dip-coating, storing temperature can be low to moderate 120 ℃ (guaranteeing storing time 20 minutes), and storing time can be soon to 10 minutes (keeping 140 ℃ of storing temperatures), under this baking condition, but completely solidified, the not xanthochromia of filming; (6) reduced energy consumption, energy-conserving and environment-protective; The developing direction that meets the water-repellent preservation lacquer.
Embodiment
Below illustrate the present invention, but the present invention not only be confined in these examples-
Embodiment 1: the synthetic method of aqueous acrylic modified epoxy ester resin
(1) linolic acid 650g, eleostearic acid 300g, E-12 Resins, epoxy 240.5g are added in the reaction flask.Stirring is warming up to 150 ~ 190 ℃, adds tetramethylolmethane 140g, TriMethylolPropane(TMP) 185g, m-phthalic acid 280g, ester catalyst plumbous oxide 1.5g successively.Be warming up to 220 ℃, and make acid number reach 20mgKOH/g.Be cooled to 150 ℃, add phthalic anhydride 110g, be warming up to 210 ℃, keep reacting to acid number 20mgKOH/g, cooling is preserved with dimethylbenzene 450g latting drown, makes the epoxy ester performed polymer.
(2) getting above-mentioned epoxy ester performed polymer 615g adds in the reaction flask 2, vinylbenzene 300g, butyl acrylate 130g, vinylformic acid 70g, benzoyl peroxide (BPO) 20g are mixed, after treating BPO dissolving fully, adopt the dropping mode reinforced, under reflux state, dripped off in 3 hours, insulation was kept 1 hour again, continue to drip initiator solution 2 hours, and insulation was kept 2 hours, extract solvent, add propylene glycol monomethyl ether 250g, obtaining acid number is 50mgKOH/g, and solid part is 74% acrylic modified epoxy ester resin.
Add triethylamine 30g and stir in above-mentioned acrylic modified epoxy ester resin, slowly adding deionized water 1200g to PH then is 9.8.Obtain water-soluble acrylic modified epoxy ester resin a.Its acid number is 39mgKOH/g, and solid part is 45%.
Embodiment 2
(1) the defoamer EFKA-2550 of adding 135g deionized water, 3g dispersant B YK-P105,4g wetting agent BYK-341,2.7g in Scattered Kettle stirs with the adjustable high-speed dispersion machine.
(2) add the aqueous acrylic modified epoxy ester resin of 250g and the 40g methylated melamine aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir.
(3) adding 30g titanium dioxide, 6g phthalocyanine blue, 6g high-carbon black pigment, 88.5g ultra-fine barium sulfate, 22.5g strontium chromate, 132g medium chrome yellow medium yellow stir, and keep 1-2 hour, get slurry.
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤35um.
(5) be transferred to proportion container at above-mentioned mill base, add 250g aqueous acrylic modified epoxy ester resin, 2g flow agent EFKA-3580,20g siccative zinc naphthenate, 2g sanitas ActicideTHP, 2g mould inhibitor SKANEM8 and 1.3g defoamer EFKA-2550 again and stir.
(6) detect pH value, add the PH conditioning agent diethanolamine of 3g, regulate PH between 8 to 10.
(7) filter, packing, the stock gets aqueous acrylic modified epoxy ester bottom surface unification baking vanish a.
Embodiment 3
(1) the defoamer EFKA-2550 of adding 130g deionized water, 3g dispersant B YK-P105,4g wetting agent Tego-245,2.7g in Scattered Kettle stirs with the adjustable high-speed dispersion machine.
(2) add the aqueous acrylic modified epoxy ester resin of 250g and the 40g isopropylcarbinol etherify melamine formal aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir.
(3) adding 15g titanium dioxide, 147g iron oxide red, 78g zinc phosphate, 3g ultra-fine barium sulfate, 2g strontium chromate stir, and keep 1-2 hour, get slurry.
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤35um.
(5) be transferred to proportion container at above-mentioned mill base, add 250g aqueous acrylic modified epoxy ester resin, 2g flow agent EFKA-3580,20g siccative cobalt iso-octoate, 2g sanitas ActicideTHP, 2g mould inhibitor SKANEM8 and 1.3g defoamer EFKA-2550 again and stir.
(6) detect pH value, add 3gPH conditioning agent triethylamine, regulate PH between 8 to 10.
(7) filter, packing, the stock gets aqueous acrylic modified epoxy ester bottom surface unification baking vanish b.
Embodiment 4:
(1) the defoamer BYK-020 of adding 140g deionized water, 3g dispersant B YK-P105,4g wetting agent BYK-341,2.7g in Scattered Kettle stirs with the adjustable high-speed dispersion machine.
(2) add the aqueous acrylic modified epoxy ester resin of 250g and the 40g butanol etherification trimeric cyanamide-urea formal aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir.
(3) add 27g high-carbon black pigment, 20g ultra-fine barium sulfate and 100g aluminium triphosphate and stir, kept 1-2 hour, get slurry.
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤35um.
(5) be transferred to proportion container at above-mentioned mill base, add 250g aqueous acrylic modified epoxy ester resin, 2g flow agent EFKA-3580,20g siccative zinc naphthenate, 2g sanitas ActicideTHP, 2g mould inhibitor SKANEM8 and 1.3g defoamer BYK-020 again and stir.
(6) detect pH value, add the PH conditioning agent diethanolamine of 3g, regulate PH between 8 to 10.
(7) filter, packing, the stock gets aqueous acrylic modified epoxy ester bottom surface unification baking vanish c.
Embodiment 5
(1) the defoamer BYK-020 of adding 90g deionized water, 3g dispersant B YK-P105,4g wetting agent Tego-245,2.7g in Scattered Kettle stirs with the adjustable high-speed dispersion machine.
(2) add the aqueous acrylic modified epoxy ester resin of 300g and the 50g methylated melamine aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir.
(3) add 165g titanium dioxide, 30g phthalocyanine blue, 20g ultra-fine barium sulfate and 5g strontium chromate and stir, kept 1-2 hour, get slurry.
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤35um.
(5) be transferred to proportion container at above-mentioned mill base, add 300g aqueous acrylic modified epoxy ester resin, 2g flow agent EFKA-3580,20g siccative cobalt iso-octoate, 2g sanitas ActicideTHP, 2g mould inhibitor SKANEM8 and 1.3g defoamer BYK-020 again and stir.
(6) detect pH value, add the PH conditioning agent triethylamine of 4g, regulate PH between 8 to 10.
(7) filter, packing, the stock gets aqueous acrylic modified epoxy ester bottom surface unification baking vanish d.
Embodiment 6
(1) the defoamer EFKA-2550 of adding 150g deionized water, 3g dispersion agent EFKA-4560,4g wetting agent BYK-341,2.7g in Scattered Kettle stirs with the adjustable high-speed dispersion machine.
(2) add the aqueous acrylic modified epoxy ester resin of 300g and the 50g isopropylcarbinol etherify melamine formal aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir.
(3) add 40g high-carbon black pigment, 100g ultra-fine barium sulfate and 20g strontium chromate and stir, kept 1-2 hour, get slurry.
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤35um.
(5) be transferred to proportion container at above-mentioned mill base, add 300g aqueous acrylic modified epoxy ester resin, 2g flow agent EFKA-3580,20g siccative zinc naphthenate, 2g sanitas ActicideTHP, 2g mould inhibitor SKANEM8 and 1.3g defoamer EFKA-2550 again and stir.
(6) detect pH value, add the PH conditioning agent diethanolamine of 4g, regulate PH between 8 to 10.
(7) filter, packing, the stock gets aqueous acrylic modified epoxy ester bottom surface unification baking vanish e.
Embodiment 7
(1) the defoamer BYK-020 of adding 140g deionized water, 3g dispersion agent EFKA-4560,4g wetting agent Tego-245,2.7g in Scattered Kettle stirs with the adjustable high-speed dispersion machine.
(2) add the aqueous acrylic modified epoxy ester resin of 300g and the 50g butanol etherification trimeric cyanamide-urea formal aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir.
(3) add 5g high-carbon black pigment, 150g iron oxide red and 10g strontium chromate and stir, kept 1-2 hour, get slurry.
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤35um.
(5) be transferred to proportion container at above-mentioned mill base, add 300g aqueous acrylic modified epoxy ester resin, 2g flow agent EFKA-3580,20g siccative cobalt iso-octoate, 2g sanitas ActicideTHP, 2g mould inhibitor SKANEM8 and 1.3g defoamer BYK-020 again and stir.
(6) detect pH value, add the PH conditioning agent triethylamine of 4g, regulate PH between 8 to 10.
(7) filter, packing, the stock gets aqueous acrylic modified epoxy ester bottom surface unification baking vanish f.
The performance of the water-repellent preservation baking vanish of the foregoing description preparation is listed in table 1
Table 1 water-repellent preservation baking vanish performance
Claims (5)
1. an aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish is characterized in that, is that the component by following weight part constitutes: aqueous acrylic modified epoxy ester resin 45-65; Aminoresin 2-20; Pigment 5-35; Filler 0-15; Aqueous dispersion type siccative 1-3; PH conditioning agent 0.1-0.55; Softening water 5-15; Dispersion agent 0.2-0.4 part; Wetting agent 0.3-0.5 part, flow agent 0.15-0.25 part, defoamer 0.3-0.5 part, sanitas and mould inhibitor 0.2-0.3 part.
2. a kind of aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish according to claim 1, it is characterized in that, described aqueous acrylic modified epoxy ester resin is to carry out grafting under the action of evocating by the acrylic monomer of the vinyl monomer of the epoxy ester performed polymer of 20-30 weight part and 5-15 part, 5-15 part, 0.5-1 part, again through the resulting water-soluble products of Water-borne modification; Its acid number is 20-40mgKOH/g, and solid part is 30-50%.
3. a kind of aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish according to claim 1, it is characterized in that, described aminoresin comprise following one or more: the pure etherificate melamine resin of first (fourth, isobutyl), the pure etherificate trimeric cyanamide methylal resin of first (fourth, isobutyl), the pure etherificate trimeric cyanamide of first (fourth, isobutyl)-urea methylal resin, its consumption is the 3-8 weight part.
4. a kind of aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish according to claim 1 is characterized in that, described PH conditioning agent is following one or more: ammoniacal liquor, triethylamine, N, N-dimethylethanolamine, its optimum amount are 0.2-0.5 part.
5. the preparation method of an aqueous acrylic modified epoxy ester primer-topcoat integrated anticorrosive baking finish is characterized in that, may further comprise the steps:
(1) presses aqueous acrylic modified epoxy ester resin 45-65, aminoresin 2-20, pigment 5-35, filler 0-15, dispersion agent 0.2-0.4 part; Wetting agent 0.3-0.5 part, flow agent 0.15-0.25 part, defoamer 0.3-0.5 part, sanitas and mould inhibitor 0.2-0.3 part, siccative 1-3, PH conditioning agent 0.1-0.55, softening water 5-15 get the raw materials ready;
(2) in Scattered Kettle, add the softening water, the dispersion agent in the formula ratio auxiliary agent, wetting agent of formula ratio, 2/3 defoamer, stir with the adjustable high-speed dispersion machine;
(2) add the aqueous acrylic modified epoxy ester resin of formula ratio 1/2 and the aminoresin of formula ratio, under the rotating speed of 400-500rpm, stir;
(3) pigment, the filler of adding formula ratio stir, and keep 1-2 hour, get slurry;
(4) above-mentioned slurry is ground by shredder,, get mill base until fineness≤45um;
(5) be transferred to proportion container at above-mentioned mill base, add second half aqueous acrylic modified epoxy ester resin again, flow agent, sanitas, mould inhibitor and the remaining defoamer of formula ratio stirs;
(6) detect pH value, add an amount of PH conditioning agent, regulating PH is between 8 to 10;
(7) filter, the packing back is a finished product.