CN105086567B - One kind paints special radioresistance solvent and preparation method thereof - Google Patents
One kind paints special radioresistance solvent and preparation method thereof Download PDFInfo
- Publication number
- CN105086567B CN105086567B CN201510487413.1A CN201510487413A CN105086567B CN 105086567 B CN105086567 B CN 105086567B CN 201510487413 A CN201510487413 A CN 201510487413A CN 105086567 B CN105086567 B CN 105086567B
- Authority
- CN
- China
- Prior art keywords
- parts
- radioresistance
- slurry
- solvent
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
One kind paints special radioresistance solvent, is related to chemistry painting industry preparing technical field, is made up of following raw material：8 10 parts of ethyl acetate, 8 10 parts of butyl acetate, 68 parts of methanol, 68 parts of butanol, 35 parts of dimethylbenzene, 35 parts of turpentine oil, 6 10 parts of suspension gelatin, 8 10 parts of radioresistance slurry, 35 parts of anti-settling agent.Beneficial effects of the present invention are：The present invention ensure that the stability of radioresistance medium by the way that radioresistance medium is implanted directly into paint solvent, and radiation resistance is strong, it ensure that the radioresistance paint radiation proof prepared is stable simultaneously, using effect is obvious, environment-protecting and non-poisonous, efficient, market value is high, is easy to promote and uses.
Description
Technical field
The present invention relates to chemistry painting industry preparing technical field, and in particular to one kind paints special radioresistance solvent and its preparation
Method.
Background technology
Paint is that one kind can firmly be covered in body surface, and the chemistry for playing protection, decoration, mark and other specific uses mixes
Compound coating.Chinese coating circle is more authoritative《Coating process》What one book was defined as：" coating is a kind of material, this
Material can be coated in object surface with different construction technologies, and it is firm, thin with some strength, continuous solid-state to form adhesion
Film.The film common name film so formed, also known as paint film or coating.”
Paint is usually to be made up of four parts such as film forming matter, filler (color stuffing), solvent, auxiliary agents, and the solvent of paint is
A kind of volatile organic compound or water, binder resin is dissolved with it, forms the solution for being easy to construction, after the film was formed,
All it evaporate into again in air, it requires that solvent has stronger solvability and very low toxicity, at this stage, with people
The rising of demand, the life that various functions paint is already present in people collect, and radiation proof paint is more salable at present
Paint, but the radiation proof of in the market paint is typically all to be carried out while preparing and painting, such radiation proof paint is direct
Prepare, largely the medium of internal radiation proof can be caused to come off, cause poor performance.
The content of the invention：
The technical problems to be solved by the invention are that providing one kind is formulated reasonable, simple production process, shielding property
Good special radioresistance solvent of paint and preparation method thereof.
The technical problems to be solved by the invention are realized using following technical scheme：
One kind paints special radioresistance solvent, it is characterised in that：It is made up of following raw material：
Ethyl acetate 8-10 parts, butyl acetate 8-10 parts, methanol 6-8 parts, butanol 6-8 parts, dimethylbenzene 3-5 parts, turpentine oil
3-5 parts, suspension gelatin 6-10 parts, radioresistance slurry 8-10 parts, anti-settling agent 3-5 parts.
The preferred component of each raw material is：
9 parts of ethyl acetate, 9 parts of butyl acetate, 7 parts of methanol, 7 parts of butanol, 4 parts of dimethylbenzene, 4 parts of turpentine oil, suspension gelatin 8
Part, 9 parts of radioresistance slurry, 4 parts of anti-settling agent.
Suspension gelatin includes：5 parts of natural resin, 15 parts of water, 8 parts of vinylacetate, 6 parts of polyvinyl alcohol, 3 parts of amylase,
Preparation method：Natural resin is subjected to attrition grinding into powder, then adds water, vinylacetate and polyvinyl alcohol
In slurry after premixing, stir, then add amylase, stir i.e. available.
Described radioresistance slurry is that cactus Aqueous extracts 20-30 parts, copper powder 3-5 parts, ceramic powder 1-3 parts carry out mixing and stirred
Mix obtained slurry.
Described anti-settling agent is polyamide wax.
It is a further object to provide a kind of method for preparing the present invention and painting special radioresistance solvent, its feature
It is：
Ethyl acetate, butyl acetate, methanol, butanol and dimethylbenzene in raw material are mixed first, then input reaction
In kettle, 100-120 DEG C is warming up to, then the suspension gelatin in raw material is added, continues to stir, by turpentine oil and radioresistance slurry
It is pre-mixed, is then added in reactor, is added anti-settling agent in raw material, stir, cooling discharging.
Beneficial effects of the present invention are：The present invention ensure that anti-by the way that radioresistance medium is implanted directly into paint solvent
The stability of radiation medium, radiation resistance is strong, while ensure that the radioresistance paint radiation proof prepared is stable, using effect
Substantially, it is environment-protecting and non-poisonous, efficient, market value is high, be easy to promote and use.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
Weigh ethyl acetate 8kg, butyl acetate 8kg, methanol 6kg, butanol 6kg, dimethylbenzene 3kg, turpentine oil 3kg, suspension
Glue 6kg, radioresistance slurry 8kg, polyamide wax 3kg；
Suspension gelatin includes：5 parts of natural resin, 15 parts of water, 8 parts of vinylacetate, 6 parts of polyvinyl alcohol, 3 parts of amylase,
Preparation method：Natural resin is subjected to attrition grinding into powder, then adds water, vinylacetate and polyvinyl alcohol
In slurry after premixing, stir, then add amylase, stir i.e. available.
Described radioresistance slurry is that cactus Aqueous extracts 20-30 parts, copper powder 3-5 parts, ceramic powder 1-3 parts carry out mixing and stirred
Mix obtained slurry.
The present invention preparation method be：
Ethyl acetate, butyl acetate, methanol, butanol and dimethylbenzene in raw material are mixed first, then input reaction
In kettle, 100-120 DEG C is warming up to, then the suspension gelatin in raw material is added, continues to stir, by turpentine oil and radioresistance slurry
It is pre-mixed, is then added in reactor, is added polyamide wax in raw material, stir, cooling discharging.
Embodiment 2
Weigh ethyl acetate 9kg, butyl acetate 9kg, methanol 7kg, butanol 7kg, dimethylbenzene 4kg, turpentine oil 4kg, suspension
Glue 8kg, radioresistance slurry 9kg, anti-settling agent 4kg；
Suspension gelatin includes：5 parts of natural resin, 15 parts of water, 8 parts of vinylacetate, 6 parts of polyvinyl alcohol, 3 parts of amylase,
Preparation method：Natural resin is subjected to attrition grinding into powder, then adds water, vinylacetate and polyvinyl alcohol
In slurry after premixing, stir, then add amylase, stir i.e. available.
Described radioresistance slurry is that cactus Aqueous extracts 20-30 parts, copper powder 3-5 parts, ceramic powder 1-3 parts carry out mixing and stirred
Mix obtained slurry.
The present invention preparation method be：
Ethyl acetate, butyl acetate, methanol, butanol and dimethylbenzene in raw material are mixed first, then input reaction
In kettle, 100-120 DEG C is warming up to, then the suspension gelatin in raw material is added, continues to stir, by turpentine oil and radioresistance slurry
It is pre-mixed, is then added in reactor, is added polyamide wax in raw material, stir, cooling discharging.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the simply explanation described in above-described embodiment and specification is originally
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. one kind paints special radioresistance solvent, it is characterised in that：It is made up of following raw material：
Ethyl acetate 8-10 parts, butyl acetate 8-10 parts, methanol 6-8 parts, butanol 6-8 parts, dimethylbenzene 3-5 parts, turpentine oil 3-5
Part, suspension gelatin 6-10 parts, radioresistance slurry 8-10 parts, anti-settling agent 3-5 parts；
Described suspension gelatin includes：5 parts of natural resin, 15 parts of water, 8 parts of vinylacetate, 6 parts of polyvinyl alcohol, amylase 3
Part,
Preparation method：Natural resin is subjected to attrition grinding into powder, then adds water, vinylacetate and polyvinyl alcohol premix
In slurry after conjunction, stir, then add amylase, stir i.e. available；
Described radioresistance slurry is that cactus Aqueous extracts 20-30 parts, copper powder 3-5 parts, ceramic powder 1-3 parts mix
The slurry arrived；
The method for preparing the special radioresistance solvent of above-mentioned paint：First by ethyl acetate, butyl acetate, methanol, butanol in raw material
Mixed with dimethylbenzene, then put into reactor, be warming up to 100-120 DEG C, then added the suspension gelatin in raw material,
Continue to stir, turpentine oil and radioresistance slurry are pre-mixed, then add in reactor, add anti-settling agent in raw material, stir
Mix uniformly, cooling discharging.
A kind of 2. special radioresistance solvent of paint according to claim 1, it is characterised in that the preferred component of each raw material
For：It is 9 parts of ethyl acetate, 9 parts of butyl acetate, 7 parts of methanol, 7 parts of butanol, 4 parts of dimethylbenzene, 4 parts of turpentine oil, 8 parts of suspension gelatin, anti-
Radiate 9 parts of slurry, 4 parts of anti-settling agent.
A kind of 3. special radioresistance solvent of paint according to claim 1, it is characterised in that：Described anti-settling agent is polyamides
Amine wax.