CN105086516A - Modified calcium carbonate with high whiteness and wide application range and preparation method thereof - Google Patents
Modified calcium carbonate with high whiteness and wide application range and preparation method thereof Download PDFInfo
- Publication number
- CN105086516A CN105086516A CN201510515112.5A CN201510515112A CN105086516A CN 105086516 A CN105086516 A CN 105086516A CN 201510515112 A CN201510515112 A CN 201510515112A CN 105086516 A CN105086516 A CN 105086516A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- parts
- modified calcium
- deionized water
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses modified calcium carbonate with high whiteness and a wide application range and a preparation method thereof. Modified calcium carbonate is characterized by being prepared from the following raw materials in parts by weight: 100-150 parts of calcium carbonate, 30-50 parts of sodium oleate, 0.3-0.7 part of sodium dodecyl benzene sulfonate, 1-3 parts of sodium bicarbonate, 4-8 parts of styrene, 0.02-0.05 part of potassium persulfate, 3-5 parts of fumed silica, 2-3 parts of organic bentonite, 1-2 parts of shea butter, 2-3 parts of nano barium sulfate, 2-3 parts of activated zinc oxide and proper amount of deionized water. The whiteness of calcium carbonate powder is improved and the light, weather and chemical corrosion resistance, impact strength, and the like of the product can be improved through synergistic effects of the shea butter, nano barium sulfate and activated zinc oxide, so that the quality of the product is greatly improved and the product is worthy to be popularized.
Description
Technical field
The present invention relates to industrial filler field, modified calcium carbonate that particularly a kind of whiteness high use range is wide and preparation method thereof.
Background technology
Calcium carbonate is as rubber, the filler of plastics, the thermotolerance of goods can be improved, wear resistance, dimensional stability, rigidity and workability, and reduce the cost of goods, but the hydroxyl that its surface has wetting ability stronger, present stronger alkalescence, the affinity of the calcium carbonate that this hydrophilic thin oil properties makes and organic polymer is poor, easy formation aggregate, part in superpolymer is caused to disperse uneven, thus cause boundary defect between bi-material, direct effect is bad, and calcium carbonate is as filler, its acid resistance, slickness, the performances such as whiteness need further raising, therefore, in order to improve the physicals of the strengthening action of calcium carbonate and dispersing property in the composite and modified calcium carbonate filled composite materials, be necessary to adopt different surface-modifying agents and treatment process to carry out surface modification to calcium carbonate powders, and then widen the Application Areas of calcium carbonate.
Polymer/inorganic particle matrix material is a kind of type material, which overcome simple inorganic particulate not easily to process, organic polymer intensity is lower, the shortcomings such as less stable, under synergistic effect, can obtain upgrading than inorganic particulate and organic polymer, more excellent performance, improve the stability of composite prod and the dispersiveness in organic phase, the performances such as physical strength, the present invention adopts polymer overmold modified calcium carbonate, solve the hydrophilic oleophobic of carbonic acid carbon, dispersed bad, free settling, physical strength is not high, the problems such as enhancement cannot be reached with polymer compatibility difference, improve the range of application of calcium carbonate.
Summary of the invention
The object of this invention is to provide wide modified calcium carbonate of a kind of whiteness high use range and preparation method thereof.In order to realize object of the present invention, the present invention is by following scheme implementation:
Modified calcium carbonate that a kind of whiteness high use range is wide and preparation method thereof, is made up of the raw material of following weight part: calcium carbonate 100-150, sodium oleate 30-50, Sodium dodecylbenzene sulfonate 0.3-0.7, sodium bicarbonate 1-3, vinylbenzene 4-8, Potassium Persulphate 0.02-0.05, gas phase aerosil 3-5, organobentonite 2-3, shea butter 1-2, nano barium sulfate 2-3, active zinc flower 2-3, deionized water are appropriate;
Modified calcium carbonate that a kind of whiteness high use range of the present invention is wide and preparation method thereof, be made up of following concrete steps:
(1) sodium oleate is added the aqueous solution sodium oleate that deionized water dissolving makes 1%, electric stirring 10min raised temperature to 60 ° C, add calcium carbonate and stir 1.5h, stirred suction filtration after rear standing 4-6h, with deionized water wash, dry for standby under 80 ° of C in an oven;
(2) modified calcium carbonate obtained for step (1) is added in the four-necked bottle with driven stirring rod and reflux condensing tube, adding appropriate water stirring makes modified calcium carbonate become slurries, stirring is stopped to add Sodium dodecylbenzene sulfonate and sodium bicarbonate, vinylbenzene is added after stirring 0.5h in a nitrogen atmosphere, persulfate aqueous solution is dripped after mixture being warming up to 80 ° of C, constant temperature is centrifugal after keeping 80 ° of C8h, with dry under 80 ° of C in an oven after deionized water rinsing, after to be ground into 300-400 order for subsequent use;
(3) the methanol solution activation 0.5h of 3-5 times amount is added after organobentonite and aerosil being mixed, 5 μm are less than to particle diameter again at grinding machine for grinding 2-3h, add deionized water ultrasonic disperse more even, transfer in flask the product adding step (2) gained again, raised temperature is to 80-100 ° of C, the ultrasonic methyl alcohol that is back to volatilizees, and dries product;
(4) by remaining mixing of materials, stir when being heated to 40-60 ° of C, then the product adding step (3) gained is under the rotating speed of 1300-1500 rev/min, stirs 8-10min, naturally cool to room temperature after insulation 10-15min, grind to form nanometer powdery.
Advantage of the present invention is: the present invention's sodium oleate makes calcium carbonate surface organise as properties-correcting agent, calcium carbonate particles surface is made to have certain hydrophobicity, and double bond is introduced calcium carbonate surface, using modified calcium carbonate particle as seed, the method of letex polymerization has prepared polystyrene coated caco3 composite particles, enhance the consistency of calcium carbonate and polymkeric substance, and easily disperse, not easily reunite, physical strength is high, the present invention is also by aerosil and organobentonite activation aftertreatment modified calcium carbonate, silicon-dioxide is made to stick to the surface of calcium carbonate, not free settling, be uniformly dispersed, suspension stability is good, and further enhancing the oilness of calcium carbonate, water tolerance and high thermal resistance, calcium carbonate is had a wide range of applications in the industry, the shea butter added, nano barium sulfate and active zinc flower three synergy, improve the whiteness of calcium carbonate powders, and the fast light of product can be improved, weather-proof, the effect of the aspect such as resistance to chemical attack and resistance to impact shock, greatly improve the quality of product, be worthy to be popularized.
Specific embodiments
Below by specific examples, the present invention is described in detail.
Modified calcium carbonate that a kind of whiteness high use range is wide and preparation method thereof, is made up of the raw material of following weight part (kilogram): calcium carbonate 150, sodium oleate 46, Sodium dodecylbenzene sulfonate 0.6, sodium bicarbonate 2, vinylbenzene 7, Potassium Persulphate 0.05, gas phase aerosil 5, organobentonite 3, shea butter 2, nano barium sulfate 3, active zinc flower 3, deionized water are appropriate;
Modified calcium carbonate that a kind of whiteness high use range of the present invention is wide and preparation method thereof, be made up of following concrete steps:
(1) sodium oleate is added the aqueous solution sodium oleate that deionized water dissolving makes 1%, electric stirring 10min raised temperature to 60 ° C, add calcium carbonate and stir 1.5h, stirred suction filtration after rear standing 6h, with deionized water wash, dry for standby under 80 ° of C in an oven;
(2) modified calcium carbonate obtained for step (1) is added in the four-necked bottle with driven stirring rod and reflux condensing tube, adding appropriate water stirring makes modified calcium carbonate become slurries, stirring is stopped to add Sodium dodecylbenzene sulfonate and sodium bicarbonate, vinylbenzene is added after stirring 0.5h in a nitrogen atmosphere, persulfate aqueous solution is dripped after mixture being warming up to 80 ° of C, constant temperature is centrifugal after keeping 80 ° of C8h, with dry under 80 ° of C in an oven after deionized water rinsing, after to be ground into 400 orders for subsequent use;
(3) the methanol solution activation 0.5h of 5 times amount is added after organobentonite and aerosil being mixed, 5 μm are less than to particle diameter again at grinding machine for grinding 2h, add deionized water ultrasonic disperse more even, transfer in flask the product adding step (2) gained again, raised temperature to 100 ° C, the ultrasonic methyl alcohol that is back to volatilizees, and dries product;
(4) by remaining mixing of materials, stir when being heated to 50 ° of C, then the product adding step (3) gained is under the rotating speed of 1500 revs/min, stirs 8min, naturally cool to room temperature after insulation 10min, grind to form nanometer powdery.
The modified calcium carbonate produce the present invention and unmodified calcium carbonate performance compare, obtain modified calcium carbonate and reduce 53.8% than unmodified calcium carbonate oil-absorption(number), settling volume reduces 63.8%, viscosity reduces 60.2%, and tap density reduces 15.9%, and modified calcium carbonate oleophilic drainage is described, good with polymer compatibility, and tap density diminishes, illustrate that calcium carbonate dispersing property is good, not easily reunite.
Claims (2)
1. modified calcium carbonate that a whiteness high use range is wide and preparation method thereof, it is characterized in that, be made up of the raw material of following weight part: calcium carbonate 100-150, sodium oleate 30-50, Sodium dodecylbenzene sulfonate 0.3-0.7, sodium bicarbonate 1-3, vinylbenzene 4-8, Potassium Persulphate 0.02-0.05, gas phase aerosil 3-5, organobentonite 2-3, shea butter 1-2, nano barium sulfate 2-3, active zinc flower 2-3, deionized water are appropriate.
2. modified calcium carbonate that a kind of whiteness high use range is wide according to claim 1 and preparation method thereof, is characterized in that, be made up of following concrete steps:
(1) sodium oleate is added the aqueous solution sodium oleate that deionized water dissolving makes 1%, electric stirring 10min raised temperature to 60 ° C, add calcium carbonate and stir 1.5h, stirred suction filtration after rear standing 4-6h, with deionized water wash, dry for standby under 80 ° of C in an oven;
(2) modified calcium carbonate obtained for step (1) is added in the four-necked bottle with driven stirring rod and reflux condensing tube, adding appropriate water stirring makes modified calcium carbonate become slurries, stirring is stopped to add Sodium dodecylbenzene sulfonate and sodium bicarbonate, vinylbenzene is added after stirring 0.5h in a nitrogen atmosphere, persulfate aqueous solution is dripped after mixture being warming up to 80 ° of C, constant temperature is centrifugal after keeping 80 ° of C8h, with dry under 80 ° of C in an oven after deionized water rinsing, after to be ground into 300-400 order for subsequent use;
(3) the methanol solution activation 0.5h of 3-5 times amount is added after organobentonite and aerosil being mixed, 5 μm are less than to particle diameter again at grinding machine for grinding 2-3h, add deionized water ultrasonic disperse more even, transfer in flask the product adding step (2) gained again, raised temperature is to 80-100 ° of C, the ultrasonic methyl alcohol that is back to volatilizees, and dries product;
(4) by remaining mixing of materials, stir when being heated to 40-60 ° of C, then the product adding step (3) gained is under the rotating speed of 1300-1500 rev/min, stirs 8-10min, naturally cool to room temperature after insulation 10-15min, grind to form nanometer powdery.