CN105037798A - Multifunctional environment-friendly modified calcium carbonate and preparation method thereof - Google Patents
Multifunctional environment-friendly modified calcium carbonate and preparation method thereof Download PDFInfo
- Publication number
- CN105037798A CN105037798A CN201510378877.9A CN201510378877A CN105037798A CN 105037798 A CN105037798 A CN 105037798A CN 201510378877 A CN201510378877 A CN 201510378877A CN 105037798 A CN105037798 A CN 105037798A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- parts
- modified calcium
- deionized water
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses multifunctional environment-friendly modified calcium carbonate and a preparation method thereof. The modified calcium carbonate is characterized by being prepared from the following raw materials in parts by weight: 100 to 150 parts of calcium carbonate, 30 to 50 parts of sodium oleate, 0.3 to 0.7 part of sodium dodecyl benzene sulfonate, 1 to 3 parts of sodium bicarbonate, 4 to 8 parts of styrene, 0.02 to 0.05 part of potassium persulfate, 3 to 5 parts of gas-phase silicon dioxide, 2 to 3 parts of organic bentonite, 3 to 4 parts of epoxy triglyceride, 1 to 3 parts of ammonium molybdate, 2 to 4 parts of polyethylene powder, and a proper amount of deionized water. The added epoxy triglyceride, ammonium molybdate, and polyethylene powder interact with each other to strengthen the oleophylic effect of calcium carbonate surface, thus the compatibility between the modified calcium carbonate and organic substances is good, the modified calcium carbonate can be more easily dispersed in high-molecular polymer; the modified calcium carbonate can be used to fill PVC materials, the reinforcing effect is better than that of common calcium carbonate, the modified calcium carbonate is environment-friendly and safe, and has a good application effect in various fields, and thus the modified calcium carbonate is worthy to promote.
Description
Technical field
The present invention relates to industrial filler field, particularly a kind of multi-functional environment-protection modified calcium carbonate and preparation method thereof.
Background technology
Calcium carbonate is as rubber, the filler of plastics, the thermotolerance of goods can be improved, wear resistance, dimensional stability, rigidity and workability, and reduce the cost of goods, but the hydroxyl that its surface has wetting ability stronger, present stronger alkalescence, the affinity of the calcium carbonate that this hydrophilic thin oil properties makes and organic polymer is poor, easy formation aggregate, part in superpolymer is caused to disperse uneven, thus cause boundary defect between bi-material, direct effect is bad, and calcium carbonate is as filler, its acid resistance, slickness, the performances such as whiteness need further raising, therefore, in order to improve the physicals of the strengthening action of calcium carbonate and dispersing property in the composite and modified calcium carbonate filled composite materials, be necessary to adopt different surface-modifying agents and treatment process to carry out surface modification to calcium carbonate powders, and then widen the Application Areas of calcium carbonate.
Polymer/inorganic particle matrix material is a kind of type material, which overcome simple inorganic particulate not easily to process, organic polymer intensity is lower, the shortcomings such as less stable, under synergistic effect, can obtain upgrading than inorganic particulate and organic polymer, more excellent performance, improve the stability of composite prod and the dispersiveness in organic phase, the performances such as physical strength, the present invention adopts polymer overmold modified calcium carbonate, solve the hydrophilic oleophobic of carbonic acid carbon, dispersed bad, free settling, physical strength is not high, the problems such as enhancement cannot be reached with polymer compatibility difference, improve the range of application of calcium carbonate.
Summary of the invention
The object of this invention is to provide a kind of multi-functional environment-protection modified calcium carbonate and preparation method thereof.In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of multi-functional environment-protection modified calcium carbonate and preparation method thereof, is made up of the raw material of following weight part: calcium carbonate 100-150, sodium oleate 30-50, Sodium dodecylbenzene sulfonate 0.3-0.7, sodium bicarbonate 1-3, vinylbenzene 4-8, Potassium Persulphate 0.02-0.05, aerosil 3-5, organobentonite 2-3, epoxidation tri-glyceride 3-4, ammonium molybdate 1-3, polyethylene powder 2-4, deionized water are appropriate;
A kind of multi-functional environment-protection modified calcium carbonate of the present invention and preparation method thereof, be made up of following concrete steps:
(1) sodium oleate is added the aqueous solution sodium oleate that deionized water dissolving makes 1%, electric stirring 10min raised temperature to 60 ° C, add calcium carbonate and stir 1.5h, stirred suction filtration after rear standing 4-6h, with deionized water wash, dry for standby under 80 ° of C in an oven;
(2) modified calcium carbonate obtained for step (1) is added in the four-necked bottle with driven stirring rod and reflux condensing tube, adding appropriate water stirring makes modified calcium carbonate become slurries, stirring is stopped to add Sodium dodecylbenzene sulfonate and sodium bicarbonate, vinylbenzene is added after stirring 0.5h in a nitrogen atmosphere, persulfate aqueous solution is dripped after mixture being warming up to 80 ° of C, constant temperature is centrifugal after keeping 80 ° of C8h, with dry under 80 ° of C in an oven after deionized water rinsing, after to be ground into 300-400 order for subsequent use;
(3) the methanol solution activation 0.5h of 3-5 times amount is added after organobentonite and aerosil being mixed, 5 μm are less than to particle diameter again at grinding machine for grinding 2-3h, add deionized water ultrasonic disperse more even, transfer in flask the product adding step (2) gained again, raised temperature is to 80-100 ° of C, the ultrasonic methyl alcohol that is back to volatilizees, and dries product;
(4) by remaining mixing of materials, stir when being heated to 40-60 ° of C, then the product adding step (3) gained is under the rotating speed of 1300-1500 rev/min, stirs 8-10min, naturally cool to room temperature after insulation 10-15min, grind to form nanometer powdery.
Advantage of the present invention is: the present invention's sodium oleate makes calcium carbonate surface organise as properties-correcting agent, calcium carbonate particles surface is made to have certain hydrophobicity, and double bond is introduced calcium carbonate surface, using modified calcium carbonate particle as seed, the method of letex polymerization has prepared polystyrene coated caco3 composite particles, enhance the consistency of calcium carbonate and polymkeric substance, and easily disperse, not easily reunite, physical strength is high, the present invention is also by aerosil and organobentonite activation aftertreatment modified calcium carbonate, silicon-dioxide is made to stick to the surface of calcium carbonate, not free settling, be uniformly dispersed, suspension stability is good, and further enhancing the oilness of calcium carbonate, water tolerance and high thermal resistance, calcium carbonate is had a wide range of applications in the industry, the epoxidation tri-glyceride added, ammonium molybdate and polyethylene powder interact, strengthen the oleophilic function of calcium carbonate surface, good with organism consistency, easilier to disperse in high molecular polymer, this modified calcium carbonate powder is when filling pvc material, reinforcing effect more before modified calcium carbonate is excellent, Environmental Safety of the present invention, good effect is all had in each field, be worthy to be popularized.
Specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of multi-functional environment-protection modified calcium carbonate and preparation method thereof, is made up of the raw material of following weight part (kilogram): calcium carbonate 150, sodium oleate 46, Sodium dodecylbenzene sulfonate 0.6, sodium bicarbonate 2, vinylbenzene 6, Potassium Persulphate 0.04, aerosil 4, organobentonite 3, epoxidation tri-glyceride 3, ammonium molybdate 2, polyethylene powder 3, deionized water are appropriate;
A kind of multi-functional environment-protection modified calcium carbonate of the present invention and preparation method thereof, be made up of following concrete steps:
(1) sodium oleate is added the aqueous solution sodium oleate that deionized water dissolving makes 1%, electric stirring 10min raised temperature to 60 ° C, add calcium carbonate and stir 1.5h, stirred suction filtration after rear standing 6h, with deionized water wash, dry for standby under 80 ° of C in an oven;
(2) modified calcium carbonate obtained for step (1) is added in the four-necked bottle with driven stirring rod and reflux condensing tube, adding appropriate water stirring makes modified calcium carbonate become slurries, stirring is stopped to add Sodium dodecylbenzene sulfonate and sodium bicarbonate, vinylbenzene is added after stirring 0.5h in a nitrogen atmosphere, persulfate aqueous solution is dripped after mixture being warming up to 80 ° of C, constant temperature is centrifugal after keeping 80 ° of C8h, with dry under 80 ° of C in an oven after deionized water rinsing, after to be ground into 400 orders for subsequent use;
(3) the methanol solution activation 0.5h of 5 times amount is added after organobentonite and aerosil being mixed, 5 μm are less than to particle diameter again at grinding machine for grinding 2h, add deionized water ultrasonic disperse more even, transfer in flask the product adding step (2) gained again, raised temperature to 100 ° C, the ultrasonic methyl alcohol that is back to volatilizees, and dries product;
(4) by remaining mixing of materials, stir when being heated to 40 ° of C, then the product adding step (3) gained is under the rotating speed of 1500 revs/min, stirs 8min, naturally cool to room temperature after insulation 10min, grind to form nanometer powdery.
The modified calcium carbonate produce the present invention and unmodified calcium carbonate performance compare, obtain modified calcium carbonate and reduce 53.5% than unmodified calcium carbonate oil-absorption(number), settling volume reduces 61.2%, viscosity reduces 60.5%, and tap density reduces 16.8%, and modified calcium carbonate oleophilic drainage is described, good with polymer compatibility, and tap density diminishes, illustrate that calcium carbonate dispersing property is good, not easily reunite.
Claims (2)
1. multi-functional environment-protection modified calcium carbonate and preparation method thereof, it is characterized in that, be made up of the raw material of following weight part: calcium carbonate 100-150, sodium oleate 30-50, Sodium dodecylbenzene sulfonate 0.3-0.7, sodium bicarbonate 1-3, vinylbenzene 4-8, Potassium Persulphate 0.02-0.05, aerosil 3-5, organobentonite 2-3, epoxidation tri-glyceride 3-4, ammonium molybdate 1-3, polyethylene powder 2-4, deionized water are appropriate.
2. a kind of multi-functional environment-protection modified calcium carbonate and preparation method thereof according to claim 1, is characterized in that, be made up of following concrete steps:
(1) sodium oleate is added the aqueous solution sodium oleate that deionized water dissolving makes 1%, electric stirring 10min raised temperature to 60 ° C, add calcium carbonate and stir 1.5h, stirred suction filtration after rear standing 4-6h, with deionized water wash, dry for standby under 80 ° of C in an oven;
(2) modified calcium carbonate obtained for step (1) is added in the four-necked bottle with driven stirring rod and reflux condensing tube, adding appropriate water stirring makes modified calcium carbonate become slurries, stirring is stopped to add Sodium dodecylbenzene sulfonate and sodium bicarbonate, vinylbenzene is added after stirring 0.5h in a nitrogen atmosphere, persulfate aqueous solution is dripped after mixture being warming up to 80 ° of C, constant temperature is centrifugal after keeping 80 ° of C8h, with dry under 80 ° of C in an oven after deionized water rinsing, after to be ground into 300-400 order for subsequent use;
(3) the methanol solution activation 0.5h of 3-5 times amount is added after organobentonite and aerosil being mixed, 5 μm are less than to particle diameter again at grinding machine for grinding 2-3h, add deionized water ultrasonic disperse more even, transfer in flask the product adding step (2) gained again, raised temperature is to 80-100 ° of C, the ultrasonic methyl alcohol that is back to volatilizees, and dries product;
(4) by remaining mixing of materials, stir when being heated to 40-60 ° of C, then the product adding step (3) gained is under the rotating speed of 1300-1500 rev/min, stirs 8-10min, naturally cool to room temperature after insulation 10-15min, grind to form nanometer powdery.