CN105086493A - 一种塑料垃圾桶的配方 - Google Patents
一种塑料垃圾桶的配方 Download PDFInfo
- Publication number
- CN105086493A CN105086493A CN201510529237.3A CN201510529237A CN105086493A CN 105086493 A CN105086493 A CN 105086493A CN 201510529237 A CN201510529237 A CN 201510529237A CN 105086493 A CN105086493 A CN 105086493A
- Authority
- CN
- China
- Prior art keywords
- parts
- formula
- plastic dustbin
- present
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种塑料垃圾桶的配方，包括：将各组分按配比放入搅拌机内充分搅拌均匀后，将混合料加入双螺杆挤出机挤出造粒，挤出温度为130℃。本发明所述塑料垃圾桶的配方，可以克服现有技术中耐热性差、用户体验差和使用寿命短等缺陷，以实现耐热性好、用户体验好和使用寿命长的优点。
Description
技术领域
本发明涉及塑料制品技术领域，具体地，涉及一种塑料垃圾桶的配方。
背景技术
以合成树脂或天然树脂为基础原料，加入（或不加）各种塑料助剂、增强材料和填料，在一定温度、压力下，加工塑制成型或交联固化成型，得的固体材料或制品。塑料是指以树脂（或在加工过程中用单体直接聚合）为主要成分，以增塑剂、填充剂、润滑剂、着色剂等添加剂为辅助成分，在加工过程中能流动成型的材料，是合成的高分子化合物，可以自由改变形体样式。利用单体原料以合成或缩合反应聚合而成的材料，由合成树脂及填料、增塑剂、稳定剂、润滑剂、色料等添加剂组成的，它的主要成分是合成树脂。
目前，塑料的应用遍及工农业、生活的各个领域，塑料制品在人们的日常生活中也已经不可缺少。现在的手机壳体大部分都是采用塑料制成，而目前的塑料制品一般都不能耐150度以上的高温，并且色彩比较单调，无法通过转印机将色彩图案转印到制品上。
在实现本发明的过程中，发明人发现现有技术中至少存在耐热性差、用户体验差和使用寿命短等缺陷。
发明内容
本发明的目的在于，针对上述问题，提出一种塑料垃圾桶的配方，以实现耐热性好、用户体验好和使用寿命长的优点。
为实现上述目的，本发明采用的技术方案是：一种塑料垃圾桶的配方，包括：
⑴按以下重量份数配比各组分：
增韧剂：1份；
成核剂：0.5份；
抗氧剂：0.3份；
钛白粉：0.18份；
扩散油：1.2份；
扩散粉：1.05份；
聚对苯二甲酸乙二醇酯：份6；
聚对苯二甲酸丁二醇酯：3份；
防腐剂：0.2份；
着色剂：1.3份；
稳定剂：2.15份；
硫酸钡：4.6份；
合成树脂：8份；
⑵将各组分按配比放入搅拌机内充分搅拌均匀后，将混合料加入双螺杆挤出机挤出造粒，挤出温度为130℃。
本发明各实施例的塑料垃圾桶的配方，由于包括：将各组分按配比放入搅拌机内充分搅拌均匀后，将混合料加入双螺杆挤出机挤出造粒，挤出温度为130℃；从而可以克服现有技术中耐热性差、用户体验差和使用寿命短的缺陷，以实现耐热性好、用户体验好和使用寿命长的优点。
本发明的其它特征和优点将在随后的说明书中阐述，并且，部分地从说明书中变得显而易见，或者通过实施本发明而了解。
下面通过实施例，对本发明的技术方案做进一步的详细描述。
具体实施方式
以下对本发明的优选实施例进行说明，应当理解，此处所描述的优选实施例仅用于说明和解释本发明，并不用于限定本发明。
根据本发明实施例，提供了一种塑料垃圾桶的配方，包括：
⑴按以下重量份数配比各组分：
增韧剂：1份；
成核剂：0.5份；
抗氧剂：0.3份；
钛白粉：0.18份；
扩散油：1.2份；
扩散粉：1.05份；
聚对苯二甲酸乙二醇酯：份6；
聚对苯二甲酸丁二醇酯：3份；
防腐剂：0.2份；
着色剂：1.3份；
稳定剂：2.15份；
硫酸钡：4.6份；
合成树脂：8份；
⑵将各组分按配比放入搅拌机内充分搅拌均匀后，将混合料加入双螺杆挤出机挤出造粒，挤出温度为130℃。
本发明的技术方案所得产品，经验证，耐热性高；表面能够有效吸收热升华墨水油墨，将热升华油墨打印出来的影像透过加温的方式，将用户喜欢的影像附着在产品表面上，提升使用的个性化效果；具有阻燃和耐高温的性能。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (1)
1.一种塑料垃圾桶的配方，其特征在于，包括：
⑴按以下重量份数配比各组分：
增韧剂：1份；
成核剂：0.5份；
抗氧剂：0.3份；
钛白粉：0.18份；
扩散油：1.2份；
扩散粉：1.05份；
聚对苯二甲酸乙二醇酯：份6；
聚对苯二甲酸丁二醇酯：3份；
防腐剂：0.2份；
着色剂：1.3份；
稳定剂：2.15份；
硫酸钡：4.6份；
合成树脂：8份；
⑵将各组分按配比放入搅拌机内充分搅拌均匀后，将混合料加入双螺杆挤出机挤出造粒，挤出温度为130℃。