CN105086167A - 一种环保型高阻燃易撕边三元乙丙垫片胶料及制备方法 - Google Patents
一种环保型高阻燃易撕边三元乙丙垫片胶料及制备方法 Download PDFInfo
- Publication number
- CN105086167A CN105086167A CN201410205228.4A CN201410205228A CN105086167A CN 105086167 A CN105086167 A CN 105086167A CN 201410205228 A CN201410205228 A CN 201410205228A CN 105086167 A CN105086167 A CN 105086167A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- sulphur
- rubber compound
- torn
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型高阻燃易撕边三元乙丙垫片胶料,所述的三元乙丙垫片胶料包括以下成份和重量份:三元乙丙橡胶100份,氧化锌5~15份,硬脂酸1~2份,高耐磨炭黑5~15份,纳米高岭土15~40份,内润滑剂1~3份,氢氧化铝80~120份,阻燃剂EPZ30~60份,硼酸锌10~20份,三氧化二锑7~20份,Si690.5~2份,石蜡油10~20份,硫磺0.8~2份,促进剂EP33-752.5~4份;所述的三元乙丙橡胶门尼粘度为60~70,乙烯含量45%~55%,第三单体ENB含量不小于5.5%;其制备方法为:上述成份中除硫磺和促进剂EP33-75外的成份在密炼机中混炼100℃排料;接着,在开炼机上加入硫磺及促进剂EP33-75,最后,返炼后用精密预成型机制作成一定形状和重量的胶坯;本发明的环保型高阻燃易撕边三元乙丙垫片胶料具有高阻燃、环保、绝缘性好和易撕边的优点。
Description
技术领域
本发明属于三元乙丙垫片胶料制备技术领域,特别涉及一种环保型高阻燃易撕边三元乙丙垫片胶料及制备方法。
背景技术
三元乙丙橡胶是乙烯、丙烯以及非共轭二烯烃的三元共聚物,每年全世界的消费量是80万吨;三元乙丙橡胶最主要的特性就是其优越的耐氧化、抗臭氧和抗侵蚀的能力;由于三元乙丙橡胶属于聚烯烃家族,它具有极好的硫化特性;在所有橡胶当中,EPDM具有最低的比重;它能吸收大量的填料和油而影响特性不大;因此可以制作成本低廉的橡胶化合物,但三元乙丙橡胶是一种易燃物质,如何制备环保型、低卤高效三元乙丙胶料是近几年研究的热点,单用无机阻燃剂Al(OH)3或Mg(OH)2存在着阻燃效果不理想及大量填充后产品物性差的缺点;单用有机卤化合物存在着发烟量大的缺点;另外现有的三元乙丙橡胶撕边比较麻烦。
发明内容
针对上述问题,本发明的目的是提供环保型高阻燃易撕边三元乙丙垫片胶料及制备方法,制备环保型低卤高效三元乙丙胶料,并且要有较好的绝缘性能,所制得产品易撕去废边。
本发明的技术解决方案:一种环保型高阻燃易撕边三元乙丙垫片胶料,所述的三元乙丙垫片胶料包括以下成份和重量份:三元乙丙橡胶100份,氧化锌5~15份,硬脂酸1~2份,高耐磨炭黑5~15份,纳米高岭土15~40份,内润滑剂1~3份,氢氧化铝80~120份,阻燃剂EPZ30~60份,硼酸锌10~20份,三氧化二锑7~20份,Si690.5~2份,石蜡油10~20份,硫磺0.8~2份,促进剂EP33-752.5~4份;所述的三元乙丙橡胶门尼粘度为60~70,乙烯含量45%~55%,第三单体ENB含量不小于5.5%。
其制备方法如下:
首先将上述的成份安装重量份进行选料;
其次,将上述成份中除硫磺和促进剂EP33-75外的成份在密炼机中混炼100℃排料;
接着,待上述胶料冷却后在开炼机上加入硫磺及促进剂EP33-75,停放12h以上;
最后,返炼后用精密预成型机制作成一定形状和重量的胶坯,然后放入模具中,在平板硫化机上硫化。
有益效果:
与现有技术相比,本发明的环保型高阻燃易撕边三元乙丙垫片胶料及制备方法,具有以下优点:
1.高阻燃:按GB/T5169.5针焰试验,试验结果为tb=0,即离火即熄灭;
2.环保:没有重金属,多溴联苯及多溴联苯醚,符合ROHS要求;
3.绝缘性好:其击穿电压强度为13.3KV/mm;
4.易撕边:提高工效一倍以上,且撕边后产品边缘光滑,很少有毛刺。
具体实施方式
本发明的环保型高阻燃易撕边三元乙丙垫片胶料,所述的三元乙丙垫片胶料包括以下成份和重量份:三元乙丙橡胶100份,氧化锌5~15份,硬脂酸1~2份,高耐磨炭黑5~15份,纳米高岭土15~40份,内润滑剂1~3份,氢氧化铝80~120份,阻燃剂EPZ30~60份,硼酸锌10~20份,三氧化二锑7~20份,Si690.5~2份,石蜡油10~20份,硫磺0.8~2份,促进剂EP33-752.5~4份;所述的三元乙丙橡胶门尼粘度为60~70,乙烯含量45%~55%,第三单体ENB含量不小于5.5%。
其制备方法如下:
首先将上述的成份安装重量份进行选料;
其次,将上述成份中除硫磺和促进剂EP33-75外的成份在密炼机中混炼100℃排料;
接着,待上述胶料冷却后在开炼机上加入硫磺及促进剂EP33-75,停放12h以上;
最后,返炼后用精密预成型机制作成一定形状和重量的胶坯,然后放入模具中,在平板硫化机上硫化。
上面所述的实施例仅仅是对本发明的优选实施方式进行描述,并非对本发明的构思和范围进行限定。在不脱离本发明设计构思的前提下,本领域普通人员对本发明的技术方案做出的各种变型和改进,均应落入到本发明的保护范围,本发明请求保护的技术内容,已经全部记在权利要求书中。
Claims (2)
1.一种环保型高阻燃易撕边三元乙丙垫片胶料,其特征在于:所述的三元乙丙垫片胶料包括以下成份和重量份:三元乙丙橡胶100份,氧化锌5~15份,硬脂酸1~2份,高耐磨炭黑5~15份,纳米高岭土15~40份,内润滑剂1~3份,氢氧化铝80~120份,阻燃剂EPZ30~60份,硼酸锌10~20份,三氧化二锑7~20份,Si690.5~2份,石蜡油10~20份,硫磺0.8~2份,促进剂EP33-752.5~4份;所述的三元乙丙橡胶门尼粘度为60~70,乙烯含量45%~55%,第三单体ENB含量不小于5.5%。
2.一种环保型高阻燃易撕边三元乙丙垫片胶料的制备方法:其特征在于:
首先,将上述的成份安装重量份进行选料;
其次,将上述成份中除硫磺和促进剂EP33-75外的成份在密炼机中混炼100℃排料;
接着,待上述胶料冷却后在开炼机上加入硫磺及促进剂EP33-75,停放12h以上;
最后,返炼后用精密预成型机制作成一定形状和重量的胶坯,然后放入模具中,在平板硫化机上硫化。