CN105062717A - Glass window scale remover and preparation method thereof - Google Patents
Glass window scale remover and preparation method thereof Download PDFInfo
- Publication number
- CN105062717A CN105062717A CN201510478780.5A CN201510478780A CN105062717A CN 105062717 A CN105062717 A CN 105062717A CN 201510478780 A CN201510478780 A CN 201510478780A CN 105062717 A CN105062717 A CN 105062717A
- Authority
- CN
- China
- Prior art keywords
- parts
- scale remover
- glass
- preparation
- glass window
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a glass window scale remover and a preparation method thereof. The scale remover comprises, by weight, 20-30 parts of ethylene glycol, 8-15 parts of trisodium phosphate, 5-10 parts of polyethylene glycol, 6-12 parts of isopropyl alcohol, 0.5-2 parts of calcium chloride, 10-15 parts of ethanol, 0.5-2 parts of polyglycerol fatty acid ester, 0.5-2 parts of talcum powder, and 70 - 80 parts of water. The preparation method includes: adding all the components into hot water, stirring and mixing the components uniformly, and performing cooling to room temperature, thus obtaining the glass window scale remover. The glass window scale remover provided by the invention has no corrosion to glass and does not ice, and can be widely applied to various glass windows and all seasons. Also, use of scale remover consumes little time, and only spray is needed. And the glass window scale remover provided by the invention has good lubrication effect, can prevent small granules from damaging glass during wiping, and has no peculiar smell.
Description
Technical field
The invention belongs to glass cleaner preparing technical field, particularly a kind of glass port scale remover and preparation method thereof.
Background technology
Glass is a kind of comparatively transparent solid matter, and form contiguous network structure when melting, process of cooling medium viscosity increases gradually and hardens and non crystallized silicates non-metallic material.The composition major ingredient of simple glass chemical oxide is silicon-dioxide.Be widely used in buildings, be used for, every wind printing opacity, belonging to mixture.Glass is easy to there will be the problem such as dust, spot, how the problem for people more and more pay close attention to is washed to glass.Ammonia solution or gasoline or other glass scale remover can be used at present to clean, by cleaning glass window after water and ammonia solution or gasoline or the mixing of other glass scale remover during cleaning, wiping is carried out with dry cloth again after glass is slightly dry, use inconvenience, simultaneously because the kind of glass is varied, treat the scale remover that different glass needs different, therefore need a kind of easy to use and scale remover that use range is wide.
Summary of the invention
The object of the invention is to provide a kind of glass port scale remover and preparation method thereof to overcome above the deficiencies in the prior art.
The present invention is realized by following technique means:
A kind of glass port scale remover, comprises in components by weight percent: ethylene glycol 20-30 part, tertiary sodium phosphate 8-15 part, polyoxyethylene glycol 5-10 part, Virahol 6-12 part, calcium chloride 0.5-2 part, ethanol 10-15 part, polyglycerol fatty acid ester 0.5-2 part, talcum powder 0.5-2 part, water 70-80 part.
Described glass port scale remover, can preferably comprise in components by weight percent: ethylene glycol 25-28 part, tertiary sodium phosphate 10-13 part, polyoxyethylene glycol 7-10 part, Virahol 8-11 part, calcium chloride 0.8-1.3 part, ethanol 12-14 part, polyglycerol fatty acid ester 0.8-1.2 part, talcum powder 1-1.5 part, water 75-78 part.
The preparation method of the glass port scale remover described in more than one, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) heat water to 50-60 DEG C, add each component and be uniformly mixed, be down to room temperature.
The preparation method of described glass port scale remover, in step (2), stirring velocity can be 30-40 rev/min, and the time can be 20-30 minute.
Glass port scale remover of the present invention is to glass non-corrosiveness, do not freeze, various types of glass port and various season can be widely used in, and use this scale remover short time consumption few, only need to spray, and glass port scale remover of the present invention has good lubrication, prevent small-particle during wiping from causing damage to glass, free from extraneous odour.
Embodiment
Embodiment 1
A kind of glass port scale remover, comprises in components by weight percent: ethylene glycol 20 parts, tertiary sodium phosphate 8 parts, polyoxyethylene glycol 5 parts, Virahol 6 parts, 0.5 part, calcium chloride, ethanol 10 parts, polyglycerol fatty acid ester 0.5 part, talcum powder 0.5 part, 70 parts, water.
The preparation method of above-described glass port scale remover, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) heat water to 50 DEG C, add each component and be uniformly mixed, wherein stirring velocity is 30 revs/min, and the time is 20 minutes, is then down to room temperature.
Embodiment 2
A kind of glass port scale remover, comprises in components by weight percent: ethylene glycol 25 parts, tertiary sodium phosphate 10 parts, polyoxyethylene glycol 7 parts, Virahol 8 parts, 0.8 part, calcium chloride, ethanol 12 parts, polyglycerol fatty acid ester 0.8 part, talcum powder 1 part, 75 parts, water.
The preparation method of above-described glass port scale remover, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) heat water to 55 DEG C, add each component and be uniformly mixed, wherein stirring velocity is 35 revs/min, and the time is 22 minutes, is then down to room temperature.
Embodiment 3
A kind of glass port scale remover, comprises in components by weight percent: ethylene glycol 26 parts, tertiary sodium phosphate 12 parts, polyoxyethylene glycol 8 parts, Virahol 10 parts, 1 part, calcium chloride, ethanol 13 parts, polyglycerol fatty acid ester 1 part, talcum powder 1.2 parts, 76 parts, water.
The preparation method of above-described glass port scale remover, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) heat water to 58 DEG C, add each component and be uniformly mixed, wherein stirring velocity is 40 revs/min, and the time is 25 minutes, is then down to room temperature.
Embodiment 4
A kind of glass port scale remover, comprises in components by weight percent: ethylene glycol 28 parts, tertiary sodium phosphate 13 parts, polyoxyethylene glycol 10 parts, Virahol 11 parts, 1.3 parts, calcium chloride, ethanol 14 parts, polyglycerol fatty acid ester 1.2 parts, talcum powder 1.5 parts, 78 parts, water.
The preparation method of above-described glass port scale remover, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) heat water to 55 DEG C, add each component and be uniformly mixed, wherein stirring velocity is 36 revs/min, and the time is 25 minutes, is then down to room temperature.
Embodiment 5
A kind of glass port scale remover, comprises in components by weight percent: ethylene glycol 30 parts, tertiary sodium phosphate 15 parts, polyoxyethylene glycol 10 parts, Virahol 12 parts, 2 parts, calcium chloride, ethanol 15 parts, polyglycerol fatty acid ester 2 parts, talcum powder 2 parts, 80 parts, water.
The preparation method of above-described glass port scale remover, is prepared according to following steps:
(1) each component is taken according to weight part;
(2) heat water to 60 DEG C, add each component and be uniformly mixed, wherein stirring velocity is 40 revs/min, and the time is 30 minutes, is then down to room temperature.
Glass port scale remover of the present invention is to glass non-corrosiveness, do not freeze, various types of glass port and various season can be widely used in, and use this scale remover short time consumption few, only need to spray, and glass port scale remover of the present invention has good lubrication, prevent small-particle during wiping from causing damage to glass, free from extraneous odour.
Claims (4)
1. a glass port scale remover, is characterized in that, comprises in components by weight percent: ethylene glycol 20-30 part, tertiary sodium phosphate 8-15 part, polyoxyethylene glycol 5-10 part, Virahol 6-12 part, calcium chloride 0.5-2 part, ethanol 10-15 part, polyglycerol fatty acid ester 0.5-2 part, talcum powder 0.5-2 part, water 70-80 part.
2. glass port scale remover according to claim 1, it is characterized in that, comprise in components by weight percent: ethylene glycol 25-28 part, tertiary sodium phosphate 10-13 part, polyoxyethylene glycol 7-10 part, Virahol 8-11 part, calcium chloride 0.8-1.3 part, ethanol 12-14 part, polyglycerol fatty acid ester 0.8-1.2 part, talcum powder 1-1.5 part, water 75-78 part.
3. a preparation method for the glass port scale remover described in claim 1 or 2, is characterized in that, be prepared according to following steps:
(1) each component is taken according to weight part;
(2) heat water to 50-60 DEG C, add each component and be uniformly mixed, be down to room temperature.
4. the preparation method of glass port scale remover according to claim 3, is characterized in that, in step (2), stirring velocity is 30-40 rev/min, and the time is 20-30 minute.