CN105062384A - 一种包装用密封胶及其制备方法 - Google Patents
一种包装用密封胶及其制备方法 Download PDFInfo
- Publication number
- CN105062384A CN105062384A CN201510620953.2A CN201510620953A CN105062384A CN 105062384 A CN105062384 A CN 105062384A CN 201510620953 A CN201510620953 A CN 201510620953A CN 105062384 A CN105062384 A CN 105062384A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- seal gum
- packaging seal
- polyvinyl chloride
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种包装用密封胶,包括聚氯乙烯:50-60份;沥青树脂:20-30份;填充剂:5-10份;增塑剂:3-5份;补强剂:5-8份;交联剂:3-5份。本发明同时公开了其制备方法。本发明通过优化产品配方,合理选配主料和助剂,且整个制备方法简单易操作,产品可直接使用,具有良好的耐热性、机械强度和柔韧性,且吸水率低、密封时间长,密封效果好,使用方便,易于储存。
Description
技术领域
本发明涉及一种密封胶及其制备方法,尤其是涉及一种包装用密封胶及其制备方法,属于造纸助剂技术领域。
背景技术
对于包装用纸箱而言,对于一些需要密封的产品而言,需要密封胶对包装纸箱的连接处进行密封粘合,而目前比较常用的密封胶一方面保质期短,容易失效,密封时间短,对于需要长期储存的物品而言,无法保证包装质量,进而造成物品的损坏;另一方面,在耐热性、机械强度、吸水率、柔韧性方面均无法达到需求,因而大大限制了密封胶的应用范围。
发明内容
为解决现有技术的不足,本发明的目的在于提供一种密封时间长、各项性能优异的包装用密封胶及其制备方法。
为了实现上述目标,本发明采用如下的技术方案:
一种包装用密封胶,其特征在于,包括以下组分,且各组分的重量份数分别为:
聚氯乙烯:50-60份;
沥青树脂:20-30份;
填充剂:5-10份;
增塑剂:3-5份;
补强剂:5-8份;
交联剂:3-5份。
进一步优选,一种包装用密封胶,包括以下组分,且各组分的重量份数分别为:
聚氯乙烯:50份;
沥青树脂:30份;
填充剂:10份;
增塑剂:5份;
补强剂:5份;
交联剂:5份。
且,所述的填充剂为碳酸钙和硅藻土的混合物,且碳酸钙和硅藻土的质量比为3:2。
所述的增塑剂为丁基橡胶、丁腈橡胶、丁苯橡胶中的任一种。
所述的补强剂为二氧化硅。
而所述的交联剂为甲基三乙氧基硅烷。
此外,一种上述的包装用密封胶的制备方法,其特征在于,包括以下步骤:
(1)将聚氯乙烯、沥青树脂、增塑剂、交联剂依次加入到混合机中,在80-100℃的温度条件下搅拌50-60min,使得聚氯乙烯、沥青树脂交联改性;
(2)然后将填充剂和补强剂增加到上述的混合物中,并降温至20-40℃,再利用研磨机进行研磨分散,得到包装用密封胶。
更进一步,所述的包装用密封胶的粒度为过200目筛
本发明的有益之处在于:本发明通过优化产品配方,合理选配主料和助剂,且整个制备方法简单易操作,产品可直接使用,具有良好的耐热性、机械强度和柔韧性,且吸水率低、密封时间长,密封效果好,使用方便,易于储存。
具体实施方式
以下结合具体实施例对本发明作具体的介绍。
以下实施例中,用到的填充剂均为碳酸钙和硅藻土的混合物,且碳酸钙和硅藻土的质量比为均3:2。
实施例1:
按照重量份数计,将50份聚氯乙烯、30份沥青树脂、5份丁基橡胶、5份甲基三乙氧基硅烷依次加入到混合机中,在80℃的温度条件下搅拌50min,使得聚氯乙烯、沥青树脂交联改性;然后将10份填充剂和5份二氧化硅增加到上述的混合物中,并降温至20℃,再利用研磨机进行研磨分散,得到包装用密封胶。
实施例2:
按照重量份数计,将60份聚氯乙烯、20份沥青树脂、3份丁腈橡胶、3份甲基三乙氧基硅烷依次加入到混合机中,在100℃的温度条件下搅拌60min,使得聚氯乙烯、沥青树脂交联改性;然后将5份填充剂和8份二氧化硅增加到上述的混合物中,并降温至40℃,再利用研磨机进行研磨分散,得到包装用密封胶。
实施例3:
按照重量份数计,将55份聚氯乙烯、25份沥青树脂、4份丁苯橡胶、4份甲基三乙氧基硅烷依次加入到混合机中,在90℃的温度条件下搅拌55min,使得聚氯乙烯、沥青树脂交联改性;然后将6份填充剂和6份二氧化硅增加到上述的混合物中,并降温至30℃,再利用研磨机进行研磨分散,得到包装用密封胶。
上述实施例1-3制备得到的包装用密封胶的性能测试结果如表1所示:
表1:
由表1可知:本发明通过优化产品配方,合理选配主料和助剂,且整个制备方法简单易操作,产品可直接使用,具有良好的耐热性、机械强度和柔韧性,且吸水率低、密封时间长,密封效果好,使用方便,易于储存。
以上显示和描述了本发明的基本原理、主要特征和优点。本行业的技术人员应该了解,上述实施例不以任何形式限制本发明,凡采用等同替换或等效变换的方式所获得的技术方案,均落在本发明的保护范围内。
Claims (8)
1.一种包装用密封胶,其特征在于,包括以下组分,且各组分的重量份数分别为:
聚氯乙烯:50-60份;
沥青树脂:20-30份;
填充剂:5-10份;
增塑剂:3-5份;
补强剂:5-8份;
交联剂:3-5份。
2.根据权利要求1所述的一种包装用密封胶,其特征在于,包括以下组分,且各组分的重量份数分别为:
聚氯乙烯:50份;
沥青树脂:30份;
填充剂:10份;
增塑剂:5份;
补强剂:5份;
交联剂:5份。
3.根据权利要求1或2所述的一种包装用密封胶,其特征在于,所述的填充剂为碳酸钙和硅藻土的混合物,且碳酸钙和硅藻土的质量比为3:2。
4.根据权利要求1或2所述的一种包装用密封胶,其特征在于,所述的增塑剂为丁基橡胶、丁腈橡胶、丁苯橡胶中的任一种。
5.根据权利要求1或2所述的一种包装用密封胶,其特征在于,所述的补强剂为二氧化硅。
6.权利要求1或2所述的一种包装用密封胶,其特征在于,所述的交联剂为甲基三乙氧基硅烷。
7.一种权利要求1所述的包装用密封胶的制备方法,其特征在于,包括以下步骤:
(1)将聚氯乙烯、沥青树脂、增塑剂、交联剂依次加入到混合机中,在80-100℃的温度条件下搅拌50-60min,使得聚氯乙烯、沥青树脂交联改性;
(2)然后将填充剂和补强剂增加到上述的混合物中,并降温至20-40℃,再利用研磨机进行研磨分散,得到包装用密封胶。
8.根据权利要求7所述的一种包装用密封胶的制备方法,其特征在于,所述的包装用密封胶的粒度为过200目筛。