CN105040273A - 一种防蛀羽绒复合保暖材料及其制备方法 - Google Patents
一种防蛀羽绒复合保暖材料及其制备方法 Download PDFInfo
- Publication number
- CN105040273A CN105040273A CN201510349591.8A CN201510349591A CN105040273A CN 105040273 A CN105040273 A CN 105040273A CN 201510349591 A CN201510349591 A CN 201510349591A CN 105040273 A CN105040273 A CN 105040273A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber
- moth
- heat insulation
- pla
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防蛀羽绒复合保暖材料,其特征是由下述重量份的原料制得:鸭绒30-40,黄麻纤维10-15,聚乳酸复合纤维10-20,聚乙烯醇纤维5-10,羧甲基纤维素钠0.3-0.5,月桂酸钠0.1-0.2,茶皂素0.1-0.2,棕榈油1-2,纳米二氧化硅0.1-0.2,水10-15。本发明的羽绒复合保暖材料不仅具有优良的保暖性能,透气吸湿性、回弹性好,强度高,且具有良好的防虫、防蛀性能,有利于制品的贮存,使用性能良好。
Description
技术领域
本发明涉及保暖材料领域,具体涉及一种防蛀羽绒复合保暖材料及其制备方法。
背景技术
羽绒是一种天然蛋白质纤维材料,由于其优良的弹性、吸湿透气性能而被作为纺织材料大量使用,在棉花、羊毛、蚕丝和羽绒四大天然保暖材料中,羽绒的保暖性能最佳。羽绒最为传统的用途是作为填充料用于各种保暖制品,主要是服装和床上用品,其制品具有柔软、蓬松、具有弹性、保暖性好等优点,受到广泛的欢迎。然而羽绒强度较差,长期使用后易折断,耐久性低;吸湿后保暖效果下降,而且来源紧张、价格昂贵、易虫蛀、易滋生细菌,无法得到大量普及应用。因此,随着纺织工业的不断发展,复合型保暖材料日益受到重视。通过对原材料和工艺的调整和改进,复合型保暖材料能克服单一类型材料的不足,降低成本、保持优良的保暖性能和使用性能,具有广阔的市场前景和较高的研究价值。
发明内容
本发明的目的是提供一种防蛀羽绒复合保暖材料,兼具良好的力学性能和保暖性能。
本发明是通过以下技术方案实现的:
一种防蛀羽绒复合保暖材料,其是由下述重量份的原料制得:
鸭绒30-40,黄麻纤维10-15,聚乳酸复合纤维10-20,聚乙烯醇纤维5-10,羧甲基纤维素钠0.3-0.5,月桂酸钠0.1-0.2,茶皂素0.1-0.2,棕榈油1-2,纳米二氧化硅0.1-0.2,水10-15;
所述的聚乳酸复合纤维由下述重量份的原料制得:聚乳酸40-50,贝壳粉4-6,甘油4-8,硅烷偶联剂KH-5500.3-0.5;所述聚乳酸复合纤维的制备方法是将贝壳粉与硅烷偶联剂KH-550混合后100-120℃处理1-2h,冷却后与其余原料混合均匀,常温放置3-5h后用双螺杆挤出机于160-180℃条件下造料,再以常规熔融纺丝法纺丝,即得。
一种防蛀羽绒复合保暖材料的制备方法,包括以下步骤:
(1)将黄麻纤维、聚乳酸复合纤维、聚乙烯醇纤维用纺织开松机分别开松,充分混合后,再与鸭绒混合、除杂,得混合纤维;
(2)将纳米二氧化硅和羧甲基纤维素钠加入水中搅拌均匀后超声分散5-10min,再加入茶皂素和月桂酸钠70-80℃、600-800r/min搅拌10-15min,最后加入其余原料同样条件下搅拌20-30min,得复合乳剂;
(3)将(2)中的复合乳剂均匀喷洒到(1)中的混合纤维上并于60-80℃搅拌混合2-4h,再次进行开松混合,然后进行梳理、气流成网机成网,最后于120℃-140℃热熔粘合,即得羽绒复合保暖材料。
本发明的优点是:
将聚乳酸与贝壳粉共混后熔融纺丝制得聚乳酸复合纤维,利用贝壳粉本身的多孔结构和增韧等性能,提高聚乳酸复合纤维的力学性能和吸湿透气性能;将得到的聚乳酸复合纤维与羽绒及其余纤维材料共混,结合纳米二氧化硅对混合纤维材料进行表面处理,有利于提高其强度、稳定性和抗老化性能,同时通过其余原料的复配,使制得的羽绒复合保暖材料不仅具有优良的保暖性能,透气吸湿性、回弹性好,强度高,且具有良好的防虫、防蛀性能,有利于制品的贮存,使用性能良好。
具体实施方式
本发明非限定实施例如下:
一种防蛀羽绒复合保暖材料,由下列重量(kg)的组分原料制备而成:
鸭绒35,黄麻纤维12,聚乳酸复合纤维15,聚乙烯醇纤维8,羧甲基纤维素钠0.4,月桂酸钠0.15,茶皂素0.15,棕榈油1.5,纳米二氧化硅0.15,水12;
所述的聚乳酸复合纤维由下述重量份的原料制得:聚乳酸45,贝壳粉5,甘油6,硅烷偶联剂KH-5500.4;所述聚乳酸复合纤维的制备方法是将贝壳粉与硅烷偶联剂KH-550混合后100℃处理1h,冷却后与其余原料混合均匀,常温放置3h后用双螺杆挤出机于160-180℃条件下造料,再以常规熔融纺丝法纺丝,即得。
防蛀羽绒复合保暖材料的制备方法包括以下步骤:
(1)将亚麻纤维、聚乳酸复合纤维、聚乙烯醇纤维用纺织开松机分别开松,充分混合后,再与鸭绒混合、除杂,得混合纤维;
(2)将纳米二氧化硅和羧甲基纤维素钠加入水中搅拌均匀后超声分散5min,再加入茶皂素和月桂酸钠80℃、800r/min搅拌10min,最后加入其余原料同样条件下搅拌20min,得复合乳剂;
(3)将(2)中的复合乳剂均匀喷洒到(1)中的混合纤维上并于80℃搅拌混合4h,再次进行开松混合,然后进行梳理、气流成网机成网,最后于140℃热熔粘合,即得羽绒复合保暖材料。
对上述制得的羽绒复合保暖材料进行性能测试,结果如下:
保暖率:90.1%;
压缩弹性率:86.5%;
断裂强力:纵向7.2N,横向18.4N。
Claims (2)
1.一种防蛀羽绒复合保暖材料,其特征在于,其是由下述重量份的原料制得:
鸭绒30-40,黄麻纤维10-15,聚乳酸复合纤维10-20,聚乙烯醇纤维5-10,羧甲基纤维素钠0.3-0.5,月桂酸钠0.1-0.2,茶皂素0.1-0.2,棕榈油1-2,纳米二氧化硅0.1-0.2,水10-15;
所述的聚乳酸复合纤维由下述重量份的原料制得:聚乳酸40-50,贝壳粉4-6,甘油4-8,硅烷偶联剂KH-5500.3-0.5;所述聚乳酸复合纤维的制备方法是将贝壳粉与硅烷偶联剂KH-550混合后100-120℃处理1-2h,冷却后与其余原料混合均匀,常温放置3-5h后用双螺杆挤出机于160-180℃条件下造料,再以常规熔融纺丝法纺丝,即得。
2.根据权利要求1所述的一种防蛀羽绒复合保暖材料的制备方法,其特征在于,包括以下步骤:
(1)将黄麻纤维、聚乳酸复合纤维、聚乙烯醇纤维用纺织开松机分别开松,充分混合后,再与鸭绒混合、除杂,得混合纤维;
(2)将纳米二氧化硅和羧甲基纤维素钠加入水中搅拌均匀后超声分散5-10min,再加入茶皂素和月桂酸钠70-80℃、600-800r/min搅拌10-15min,最后加入其余原料同样条件下搅拌20-30min,得复合乳剂;
(3)将(2)中的复合乳剂均匀喷洒到(1)中的混合纤维上并于60-80℃搅拌混合2-4h,再次进行开松混合,然后进行梳理、气流成网机成网,最后于120℃-140℃热熔粘合,即得羽绒复合保暖材料。