CN105039789A - 一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件及其铸造工艺 - Google Patents
一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件及其铸造工艺 Download PDFInfo
- Publication number
- CN105039789A CN105039789A CN201510378550.1A CN201510378550A CN105039789A CN 105039789 A CN105039789 A CN 105039789A CN 201510378550 A CN201510378550 A CN 201510378550A CN 105039789 A CN105039789 A CN 105039789A
- Authority
- CN
- China
- Prior art keywords
- nano active
- alloy
- aluminum oxide
- active aluminum
- active alumina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及铝合金汽车零部件技术领域，具体涉及一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件及其铸造工艺，该零部件用复合材料在常规铝合金材料中添加了表面包覆硅溶胶的纳米活性氧化铝，经过这样处理后的纳米活性氧化铝不仅保持了其独特的原始形态，还提高了与金属熔液的相容性，这样就使得纳米材料在熔液中能迅速扩散，达到稳定高效的改善了合金材料组织性能和力学性能的功效，其能有效的提高材料的致密性和尺寸稳定性，韧性佳，不易变形，这种铝合金材料铸造得到的零部件具有轻质、耐用、抗蠕变等优点，极具应用价值。
Description
技术领域
本发明涉及铝合金汽车零部件技术领域，具体涉及一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件及其铸造工艺。
背景技术
汽车由十几万个零部件组成，其中大部分为金属材料，汽车零部件的轻量化、安全化和节约化是实现汽车现代化的根本条件，也是提高汽车竞争能力的必由之路。铝合金具有比强度高、耐腐蚀性能优良、易于成形、较易再生利用，具有传统的铸铁、钢等材料不可比拟的优点，因此，近年来由铝合金制造的零部件在汽车工业中逐渐被广泛的应用。
我国已经成为世界上第五大汽车工业国，然而我国汽车的平均用铝量与其他发达国家相比仍然存在较大的差异，进一步开发、深化铝合金的性能和生产工艺就显得尤为重要。
发明内容
本发明的目的在于，提供一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件及其铸造工艺，为了实现上述目的，本发明采用的技术方案如下：
一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件，其特征在于，该铝合金零部件材料由以下重量份的原料制成：铝80-100、硼0.8-1、铁1-1.5、镍0.2-0.3、纳米铜2-3、稀土硅铁合金0.1-0.2、纳米活性氧化铝2-4、固含量为10-15%的硅溶胶8-10、杂质≤0.01。
所述的一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件的铸造工艺为：
（1）先将纳米活性氧化铝投入硅溶胶中，超声搅拌使得纳米活性氧化铝在溶胶中均匀分散，随后将混合浆料经热风干燥，完全除去水分自然冷却至室温，随后再将所得粉体加热至750-800℃，恒温备用；
（2）将其它剩余物料混合，投入电阻炉中，加热至750-800℃熔炼处理，再将步骤（1）所得物料投入合金液中，机械搅拌30-40min后加入精炼剂，精炼处理结束后将熔体浇注成型，即得。
有益效果：本发明在常规铝合金材料中添加了表面包覆硅溶胶的纳米活性氧化铝，经过这样处理后的纳米活性氧化铝不仅保持了其独特的原始形态，还提高了与金属熔液的相容性，这样就使得纳米材料在熔液中能迅速扩散，达到稳定高效的改善了合金材料组织性能和力学性能的功效，其能有效的提高材料的致密性和尺寸稳定性，韧性佳，不易变形，这种铝合金材料铸造得到的零部件具有轻质、耐用、抗蠕变等优点，极具应用价值。
具体实施方式
实施例
本实施例的铝合金零部件由以下重量份的原料制成：铝95、硼0.9、铁1.2、镍0.2、纳米铜2.5、稀土硅铁合金0.2、纳米活性氧化铝3.5、固含量为15%的硅溶胶8、杂质≤0.01。
其铸造工艺为：
（1）先将纳米活性氧化铝投入硅溶胶中，超声搅拌使得纳米活性氧化铝在溶胶中均匀分散，随后将混合浆料经热风干燥，完全除去水分自然冷却至室温，随后再将所得粉体加热至800℃，恒温备用；
（2）将其它剩余物料混合，投入电阻炉中，加热至800℃熔炼处理，再将步骤（1）所得物料投入合金液中，机械搅拌40min后加入精炼剂，精炼处理结束后将熔体浇注成型，即得。
本实施例制得的合金取试样进行性能测试结果为：抗拉强度：365MPa，延伸率：17.2%，硬度：135HB。该批次零部件使用寿命较传统铝合金零部件平均提升28%以上。
Claims (2)
1.一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件，其特征在于，该零部件材料由以下重量份的原料制成：铝80-100、硼0.8-1、铁1-1.5、镍0.2-0.3、纳米铜2-3、稀土硅铁合金0.1-0.2、纳米活性氧化铝2-4、固含量为10-15％的硅溶胶8-10、杂质≤0.01。
2.如权利要求1所述的一种掺混纳米活性氧化铝的高韧性复合铝合金汽车零部件的铸造工艺，其特征在于，所述的铸造工艺为：
(1)先将纳米活性氧化铝投入硅溶胶中，超声搅拌使得纳米活性氧化铝在溶胶中均匀分散，随后将混合浆料经热风干燥，完全除去水分自然冷却至室温，随后再将所得粉体加热至750-800℃，恒温备用；
(2)将其它剩余物料混合，投入电阻炉中，加热至750-800℃熔炼处理，再将步骤(1)所得物料投入合金液中，机械搅拌30-40min后加入精炼剂，精炼处理结束后将熔体浇注成型，即得。