CN105038524B - 一种油桶桶体用改性丙烯酸树脂节能环保涂料 - Google Patents
一种油桶桶体用改性丙烯酸树脂节能环保涂料 Download PDFInfo
- Publication number
- CN105038524B CN105038524B CN201510552499.1A CN201510552499A CN105038524B CN 105038524 B CN105038524 B CN 105038524B CN 201510552499 A CN201510552499 A CN 201510552499A CN 105038524 B CN105038524 B CN 105038524B
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic resin
- oil drum
- coating
- saving
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种油桶桶体用改性丙烯酸树脂节能环保涂料，所述涂料采用双酚A环氧树脂改性丙烯酸树脂，使得所述涂料具有优异的阻燃和耐磨性能，而且固化速度快，还具有较好的力学性能、耐老化性能及耐化学腐蚀性能，附着力强、延展性好、耐高温、使用寿命长，改变加工工艺，在油桶桶体板坯上集中完成辊涂处理，简化加工手续，无需单独设置喷涂车间。
Description
技术领域
本发明涉及一种油桶桶体用改性丙烯酸树脂节能环保涂料。
背景技术
丙烯酸树脂是由丙烯酸酯和甲基丙烯酸酯以及其他烯属单体共聚制成的树脂，与其他合成高分子树脂相比，丙烯酸树脂具有许多突出的优点，如优异的耐光、耐候性，户外暴晒耐久性强，耐紫外光照射不易分解和变黄，能长期保持原有的光泽和色泽，耐热性好，有较好的耐酸、碱、盐、油脂和洗涤剂等化学品沾污及腐蚀性能，极好的柔韧性和最低颜料反应性。因此，在汽车、家电、金属家具、卷材工业、仪器仪表、建筑、纺织品、木制品、造纸和塑料制品等工业上有着广泛的应用。
然而，丙烯酸树脂的线形结构导致的热黏冷脆、抗回黏性和耐热性不佳等缺点对其应用范围有一定限制。丙烯酸树脂的均相结构使得它的耐寒性能和耐热性能难以兼顾，如要增加耐低温性能，则会损失耐高温性能，反之亦然，因而普通的丙烯酸类涂饰材料就不可避免地存在上述缺点。
通过与其他单体、树脂共聚和改性，可以变化涂料的各方面性能，制成多种不同性能及应用领域的涂料。环氧改性丙烯酸树脂是在环氧树脂分子链的两端引入丙烯基不饱和双键，然后与其他单体共聚，这样，就使得环氧树脂的各种优良性能(丰满度、光泽、硬度、附着力等)在丙烯酸树脂中得到充分发挥，综合性能各取所长，其干性、丰满度、光泽、硬度等综合性能优于一般的丙烯酸树脂，适用于装饰性要求特别高的场合，如塑料表面涂装，以满足塑料制品的使用、加工过程如表面处理、电镀、烫金、镀膜等的需要。
目前，国内存在如下环氧改性丙烯酸树脂涂料：
中国专利CN201210564995.5，公开了一种以丙烯酸树脂为原料的涂料，由以下重量份的成分组成：环氧树脂30～60；热塑性丙烯酸树脂20～30；阻燃剂10～15；氧化锌10～20；颜料10～15；甲醇1～3；去离子水10～15。然而，该专利虽然列出了环氧树脂及热塑性丙烯酸树脂，但并未形成环氧改性丙烯酸树脂的有机结合，无法使得涂料具备环氧改性丙烯酸树脂的优良性能。
此外，现有丙烯酸树脂涂料的涂装方式大多采用喷涂涂装，例如中国专利CN201310607469.7，公开了一种粉末涂料用热固性丙烯酸树脂，该树脂酯配以其他物料制成的热固性粉末涂料，喷涂后所形成的涂膜，具有优异的耐候性、良好的流平性能、优异的表面硬度和高光泽性、耐久性和装饰性能；可用于室内或室外金属型材或建筑材料。能够在一定程度上替代TGIC，避免了毒性物的使用。
然而，喷涂是通过喷枪或碟式雾化器，借助于压力或离心力，分散成均匀而微细的雾滴，施涂于被涂物表面的涂装方法。喷涂中的主要问题是高度分散的漆雾和挥发出来的溶剂(即挥发性有机污染物，VOCs)，既污染环境，不利于人体健康，又浪费涂料，造成经济损失。挥发、扩散到空气中的涂料，则形成挥发性有机污染物，危害人体健康。在喷涂车间，涂料作为挥发性有机污染物的主要来源，喷涂车间内空气中挥发性有机化合物浓度过高时很容易引起急性中毒，轻者会出现头痛、头晕、咳嗽、恶心、呕吐、或呈酩醉状；重者会出现肝中毒甚至很快昏迷，有的还可能有生命危险。长期待在挥发性有机化合物污染的喷涂车间内，可引起慢性中毒，损害肝脏和神经系统、引起全身无力、瞌睡、皮肤瘙痒等。有的还可能引起内分泌失调、影响性功能；苯和二甲苯还能损害系统，以至引发白血病。
发明内容
本发明的目的在于提供一种油桶桶体用改性丙烯酸树脂节能环保涂料，所述涂料采用双酚A环氧树脂改性丙烯酸树脂，使得所述涂料具有优异的阻燃和耐磨性能，而且固化速度快，还具有较好的力学性能、耐老化性能及耐化学腐蚀性能，附着力强、延展性好、耐高温、使用寿命长，改变加工工艺，在油桶桶体板坯上集中完成辊涂处理，简化加工手续，无需单独设置喷涂车间。
为达到上述目的，本发明采用的技术方案是：
一种油桶桶体用改性丙烯酸树脂节能环保涂料，所述涂料中各成分质量分数如下：环氧改性丙烯酸树脂：60～70份，羟丙基甲基纤维素：3～5份，氨基树脂：5～10份，氨乙基哌嗪：10～15份，2-巯醇基苯并噻唑：3～8份，十二烷基苯磺酸钠：5～15份，月桂醇硫酸钠：1～5份，硅酸铝：10～20份，亚甲基双环己烷胺：2～6份，聚二甲基硅氧烷：2～5份，磷酸锌：5～8份，钠基膨润土：4～8份，聚酰胺蜡浆：5～10份，环氧丙烷丁基醚：30～40份，水：90～100份。
进一步，所述涂料中各成分质量分数如下：环氧改性丙烯酸树脂：60～65份，羟丙基甲基纤维素：3～5份，氨基树脂：5～7份，氨乙基哌嗪：10～14份，2-巯醇基苯并噻唑：3～4份，十二烷基苯磺酸钠：5～8份，月桂醇硫酸钠：1～3份，硅酸铝：10～15份，亚甲基双环己烷胺：2～4份，聚二甲基硅氧烷：2～5份，磷酸锌：5～8份，钠基膨润土：4～6份，聚酰胺蜡浆：5～8份，环氧丙烷丁基醚：30～35份，水：95～100份。
优选地，所述涂料中各成分质量分数如下：环氧改性丙烯酸树脂：65份，羟丙基甲基纤维素：4份，氨基树脂：6份，氨乙基哌嗪：13份，2-巯醇基苯并噻唑：3份，十二烷基苯磺酸钠：6份，月桂醇硫酸钠：3份，硅酸铝：13份，亚甲基双环己烷胺：3份，聚二甲基硅氧烷：4份，磷酸锌：6份，钠基膨润土：5份，聚酰胺蜡浆：5份，环氧丙烷丁基醚：30份，水：95份。
另，所述环氧改性丙烯酸树脂中各成分质量分数如下：丙烯酸20～30份，甲基丙烯酸甲酯20～25份，甲基丙烯酰胺10～15份，丙烯酸-2-乙基己酯10～15份，十二硫醇1～5份，甲基异丁基酮2～7份，双酚A环氧树脂20～30份，三羟甲基丙烷三丙烯酸酯2～5份，过氧化二苯甲酰5～10份，水80～100份。
另有，所述环氧改性丙烯酸树脂中各成分质量分数如下：丙烯酸20～30份，甲基丙烯酸甲酯20～23份，甲基丙烯酰胺10～13份，丙烯酸-2-乙基己酯10～12份，十二硫醇1～4份，甲基异丁基酮2～5份，双酚A环氧树脂20～25份，三羟甲基丙烷三丙烯酸酯2～5份，过氧化二苯甲酰5～8份，水80～90份。
优选地，所述环氧改性丙烯酸树脂中各成分质量分数如下：丙烯酸22份，甲基丙烯酸甲酯20份，甲基丙烯酰胺11份，丙烯酸-2-乙基己酯12份，十二硫醇2份，甲基异丁基酮4份，双酚A环氧树脂23份，三羟甲基丙烷三丙烯酸酯5份，过氧化二苯甲酰6份，水80份。
再，所述环氧改性丙烯酸树脂的制备，包括如下步骤：在装有回流冷凝器、搅拌器、温度计的四口烧瓶中，加入所述双酚A环氧树脂，活性溶剂和水，搅拌并加热至70～80℃，滴加丙烯酸，1～2h内滴加完毕，反应1.5～2h，然后将甲基丙烯酸甲酯，甲基丙烯酰胺，丙烯酸-2-乙基己酯，十二硫醇及过氧化二苯甲酰在搅拌器内混合均匀，溶解后得混合液，将所述混合液滴加至四口烧瓶内，反应2～4h，降温至50℃以下，反应完毕，得所述环氧改性丙烯酸树脂。
再有，所述涂料通过辊涂方式涂覆到油桶桶体板坯表面，辊涂温度230～240℃，辊涂次数为1～2次。
本发明的有益效果在于：
所述涂料采用双酚A环氧树脂改性丙烯酸树脂，具有优异的阻燃和耐磨性能，而且固化速度快，还具有较好的力学性能、耐老化性能及耐化学腐蚀性能，附着力强、延展性好、耐高温、使用寿命长，改变加工工艺，在油桶桶体板坯上集中完成辊涂处理，简化加工手续，无需单独设置喷涂车间。
在油桶桶体板坯阶段即可通过辊涂将本发明所提供的涂料涂装在油桶桶体板坯表面，形成涂层，可直接进行后续加工，得成型油桶桶体，即使结构复杂的油桶桶体结构，也在板坯阶段完成了涂料涂装，无需后续涂装，代替了现有工艺中“先加工成所需形状，然后再喷涂得到成型产品”的工艺，涂料与油桶桶体板坯附着力强，不会因加工工艺而产生裂纹或脱落。由于是辊涂成型快干的辊涂工艺代替喷涂工艺，涂装时涂料的利用度能达到90％以上，减少了空气中的挥发和浪费，有效降低因喷涂导致涂料挥发形成的VOCs，辊涂车间内VOCs排放量≤420ppm，涂料环保效果好。对辊涂涂装完成的油桶桶体制品进行加工，油桶桶体T弯性能可达0T(辊涂后的成品厚板180°弯折后，完全无缝隙并拢，涂料不爆裂脱落)或者1T(厚板两次180°折弯后，最外层的涂料面不脱落，不爆裂)，保证油桶桶体质量。
具体实施方式
下面通过具体实施例对本发明做进一步的说明，但实施例并不限制本发明的保护范围。
表1为本发明实施例所述一种油桶桶体用改性丙烯酸树脂节能环保涂料成分质量分数列表。表2为本发明实施例所述环氧改性丙烯酸树脂成分质量分数列表。表3为本发明实施例所述一种油桶桶体用改性丙烯酸树脂节能环保涂料性能参数列表。表4为本发明实施例所述一种油桶桶体用改性丙烯酸树脂节能环保涂料辊涂在油桶桶体板坯表面后的涂层性能参数列表。
所述油桶桶体用改性丙烯酸树脂节能环保涂料配制方法如下：
将各组分加入高速分散机内，搅拌均匀后，高速分散30～60min，搅拌、出料、过滤、包装、入库。
所述环氧改性丙烯酸树脂的制备，包括如下步骤：在装有回流冷凝器、搅拌器、温度计的四口烧瓶中，加入所述双酚A环氧树脂，活性溶剂和水，搅拌并加热至70～80℃，滴加丙烯酸，1～2h内滴加完毕，反应1.5～2h，然后将甲基丙烯酸甲酯，甲基丙烯酰胺，丙烯酸-2-乙基己酯，十二硫醇及过氧化二苯甲酰在搅拌器内混合均匀，溶解后得混合液，将所述混合液滴加至四口烧瓶内，反应2～4h，降温至50℃以下，反应完毕，得所述环氧改性丙烯酸树脂。
表1(单位：份)
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
| 环氧改性丙烯酸树脂 | 65 | 68 | 70 | 60 | 63 |
| 羟丙基甲基纤维素 | 4 | 5 | 3 | 5 | 4 |
| 氨基树脂 | 6 | 5 | 10 | 9 | 8 |
| 氨乙基哌嗪 | 13 | 10 | 12 | 15 | 11 |
| 2-巯醇基苯并噻唑 | 3 | 8 | 5 | 7 | 6 |
| 十二烷基苯磺酸钠 | 6 | 11 | 5 | 15 | 10 |
| 月桂醇硫酸钠 | 3 | 1 | 2 | 5 | 4 |
| 硅酸铝 | 13 | 10 | 15 | 20 | 18 |
| 亚甲基双环己烷胺 | 3 | 5 | 4 | 6 | 2 |
| 聚二甲基硅氧烷 | 4 | 2 | 5 | 4 | 3 |
| 磷酸锌 | 6 | 6 | 8 | 5 | 7 |
| 钠基膨润土 | 5 | 8 | 7 | 4 | 6 |
| 聚酰胺蜡浆 | 5 | 8 | 9 | 10 | 7 |
| 环氧丙烷丁基醚 | 30 | 35 | 40 | 36 | 38 |
| 水 | 95 | 90 | 92 | 100 | 98 |
表2(单位：份)
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
| 丙烯酸 | 22 | 20 | 25 | 30 | 28 |
| 甲基丙烯酸甲酯 | 20 | 23 | 22 | 25 | 24 |
| 甲基丙烯酰胺 | 11 | 13 | 10 | 15 | 12 |
| 丙烯酸-2-乙基己酯 | 12 | 10 | 13 | 15 | 14 |
| 十二硫醇 | 2 | 3 | 5 | 4 | 1 |
| 甲基异丁基酮 | 4 | 3 | 5 | 7 | 2 |
| 双酚A环氧树脂 | 23 | 25 | 20 | 28 | 30 |
| 三羟甲基丙烷三丙烯酸酯 | 5 | 3 | 4 | 2 | 3 |
| 过氧化二苯甲酰 | 6 | 5 | 8 | 10 | 7 |
| 水 | 80 | 90 | 95 | 100 | 85 |
表3
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
| 拉伸强度(MPa) | 40 | 35 | 36 | 37 | 38 |
| 断裂伸长率(％) | 9.5 | 8.5 | 8.8 | 9.3 | 9.2 |
| 邵氏硬度 | 70 | 65 | 60 | 68 | 62 |
将本发明实施例所述一种油桶桶体用改性丙烯酸树脂节能环保涂料通过辊涂方式涂覆在油桶桶体板坯表面，在200℃下固化后，冷却至室温，放置48小时，测定板坯表面涂层性能如表4所示。其中，耐冲击性能测试方法参照国家标准GB/T1732-93规定的测定漆膜耐冲击性能的方法，以固定质量(1kg)的重锤落于试板上而不引起漆膜破坏的最大高度(cm)表示漆膜耐冲击性能。
表4
| 实施例1 | 实施例2 | 实施例3 | 实施例4 | 实施例5 | |
| 耐冲击性能(cm) | 120 | 110 | 118 | 116 | 114 |
| 耐盐雾时长(h) | 3150 | 3100 | 2900 | 2950 | 3130 |
| 人工加速老化时长(h) | 3200 | 3250 | 3280 | 3100 | 3190 |
| 耐热性能 | 780 | 740 | 750 | 700 | 760 |
采用本发明所提供的一种油桶桶体用改性丙烯酸树脂节能环保涂料涂装油桶桶体板坯后制得的产品包装金属盒，T弯性能可达0T或者1T。涂料利用率高，每30公斤涂料可涂装1吨板坯。在230℃高温下不开裂、不变色，抗老化能力强，放置在户外连续日照10～15年不泛黄、不变色。耐酸耐腐蚀能力强，将辊涂好的产品放入85℃水内煮2H生再逐渐加热到100℃，产品无变色、掉漆、起泡。在常温下用5％的Nad溶液浸泡24H后，产品表面无锈蚀、变色及镀层脱落。把纯棉布蘸满95％酒精包在500g砝码上，以每分钟40-60次的速度(20mm)左右的行程在产品表面擦试50个循环，无掉色脱油。依照美国ASTM中的划X法检测涂覆有本发明所提供涂料的成型油桶桶体制品，可达到ISO等级的0＝ASTM等级，切口边缘完全光滑，边缘没有一点的剥落。
需要说明的是，以上实施例仅用以说明本发明的技术方案而非限制。尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的范围，其均应涵盖在本发明的权利要求范围中。
Claims (7)
1.一种油桶桶体用改性丙烯酸树脂节能环保涂料，其特征在于，所述涂料中各成分质量分数如下：
环氧改性丙烯酸树脂：60~70份，羟丙基甲基纤维素：3~5份，氨基树脂：5~10份，氨乙基哌嗪：10~15份，2-巯醇基苯并噻唑：3~8份，十二烷基苯磺酸钠：5~15份，月桂醇硫酸钠：1~5份，硅酸铝：10~20份，亚甲基双环己烷胺：2~6份，聚二甲基硅氧烷：2~5份，磷酸锌：5~8份，钠基膨润土：4~8份，聚酰胺蜡浆：5~10份，环氧丙烷丁基醚：30~40份，水：90~100份；
所述环氧改性丙烯酸树脂中各成分质量分数如下：丙烯酸20~30份，甲基丙烯酸甲酯20~25份，甲基丙烯酰胺10~15份，丙烯酸-2-乙基己酯10~15份，十二硫醇1~5份，甲基异丁基酮2~7份，双酚A环氧树脂20~30份，三羟甲基丙烷三丙烯酸酯2~5份，过氧化二苯甲酰5~10份，水80~100份。
2.根据权利要求1所述的一种油桶桶体用改性丙烯酸树脂节能环保涂料，其特征在于，所述涂料中各成分质量分数如下：环氧改性丙烯酸树脂：60~65份，羟丙基甲基纤维素：3~5份，氨基树脂：5~7份，氨乙基哌嗪：10~14份，2-巯醇基苯并噻唑：3~4份，十二烷基苯磺酸钠：5~8份，月桂醇硫酸钠：1~3份，硅酸铝：10~15份，亚甲基双环己烷胺：2~4份，聚二甲基硅氧烷：2~5份，磷酸锌：5~8份，钠基膨润土：4~6份，聚酰胺蜡浆：5~8份，环氧丙烷丁基醚：30~35份，水：95~100份。
3.根据权利要求1所述的一种油桶桶体用改性丙烯酸树脂节能环保涂料，其特征在于，所述涂料中各成分质量分数如下：环氧改性丙烯酸树脂：65份，羟丙基甲基纤维素：4份，氨基树脂：6份，氨乙基哌嗪：13份，2-巯醇基苯并噻唑：3份，十二烷基苯磺酸钠：6份，月桂醇硫酸钠：3份，硅酸铝：13份，亚甲基双环己烷胺：3份，聚二甲基硅氧烷：4份，磷酸锌：6份，钠基膨润土：5份，聚酰胺蜡浆：5份，环氧丙烷丁基醚：30份，水：95份。
4.根据权利要求1所述的一种油桶桶体用改性丙烯酸树脂节能环保涂料，其特征在于，所述环氧改性丙烯酸树脂中各成分质量分数如下：丙烯酸20~30份，甲基丙烯酸甲酯20~23份，甲基丙烯酰胺10~13份，丙烯酸-2-乙基己酯10~12份，十二硫醇1~4份，甲基异丁基酮2~5份，双酚A环氧树脂20~25份，三羟甲基丙烷三丙烯酸酯2~5份，过氧化二苯甲酰5~8份，水80~90份。
5.根据权利要求1所述的一种油桶桶体用改性丙烯酸树脂节能环保涂料，其特征在于，所述环氧改性丙烯酸树脂中各成分质量分数如下：丙烯酸22份，甲基丙烯酸甲酯20份，甲基丙烯酰胺11份，丙烯酸-2-乙基己酯12份，十二硫醇2份，甲基异丁基酮4份，双酚A环氧树脂23份，三羟甲基丙烷三丙烯酸酯5份，过氧化二苯甲酰6份，水80份。
6.根据权利要求1所述的一种油桶桶体用改性丙烯酸树脂节能环保涂料，其特征在于，所述环氧改性丙烯酸树脂的制备，包括如下步骤：
在装有回流冷凝器、搅拌器、温度计的四口烧瓶中，加入所述双酚A环氧树脂，活性溶剂和水，搅拌并加热至70~80℃，滴加丙烯酸，1~2h内滴加完毕，反应1.5~2h，然后将甲基丙烯酸甲酯，甲基丙烯酰胺，丙烯酸-2-乙基己酯，十二硫醇及过氧化二苯甲酰在搅拌器内混合均匀，溶解后得混合液，将所述混合液滴加至四口烧瓶内，反应2~4h，降温至50℃以下，反应完毕，得所述环氧改性丙烯酸树脂。
7.根据权利要求1~6中任一项所述的一种油桶桶体用改性丙烯酸树脂节能环保涂料，其特征在于，所述涂料通过辊涂方式涂覆到油桶桶体板坯表面，辊涂温度230~240℃，辊涂次数为1~2次。