CN105036700A - Preparation process of multicolor hollow ceramic plate - Google Patents
Preparation process of multicolor hollow ceramic plate Download PDFInfo
- Publication number
- CN105036700A CN105036700A CN201510426310.4A CN201510426310A CN105036700A CN 105036700 A CN105036700 A CN 105036700A CN 201510426310 A CN201510426310 A CN 201510426310A CN 105036700 A CN105036700 A CN 105036700A
- Authority
- CN
- China
- Prior art keywords
- batching
- mixture
- preparation technology
- multicolor
- hollow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A multicolor hollow ceramic plate is prepared from an ingredient 1, an ingredient 2 and an ingredient 3 in a weight ratio of 1:2:1. The invention provides a preparation process of a multicolor hollow ceramic plate, which has good performance, safety, fireproof, environmental protection, good self-cleaning performance, rich bright and mild color, no stain, good decorative effect, and thermal shock resistance and frost resistance superior to those of the prior art.
Description
Technical field
The present invention relates to the preparation technology of a kind of Multicolor hollow pottery plate.
Background technology
It is by being dried by original ore soil that current existing wet vacuum squeezes the preparation of mud moulding process Raw, and by moisture controlled at 5%-9%, broken by Raymond machine, material fineness is made to control below 60 orders, then put in storage, finally by formula batching, then finished product hollow ceramic plate can be obtained by mud extruder, drying tower, kiln.
As application number: shaping hollow ceramic plate of a kind of Multi-color wet described in 201210116644.8 and preparation method thereof, although the finished product pottery plate various colors that this technique provides, bright in luster, good decorating effect, its thermal shock resistance and anti-freezing property lower.
Summary of the invention
In order to overcome the problems referred to above, the invention provides the preparation technology of a kind of Multicolor hollow pottery plate.
For achieving the above object, technical scheme provided by the invention is:
A preparation technology for Multicolor hollow pottery plate, its by weight ratio be the batching one of 1:2:1, batching two, batching three be prepared from; Wherein:
Batching one is made up of the raw material of following per-cent: carclazyte 30-35%, pyrite tailing 20-30%, black earth 5-8%, quartz sand 10-15%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.4-0.6% and goth black 2.3%;
Batching two is made up of the raw material of following per-cent: talcum 28-32%, black earth 15-20%, kaolin 11-14%, rutile 20-28%, zirconium white 7-12%, rotten sodium 0.3%, fluidizer 0.4-0.6% and orange 4.3-5.8%;
Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 20-29%, Reactive alumina 11-15%, fused quartz 21-28%, lithium feldspar 8-13%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 4.3-5.8%.
In described batching one, the raw material of auxiliary agent is made up of brown alundum powder 1-1.8, tripoly phosphate sodium STPP 2-4, jade powder 5.5-6.5, tripoly phosphate sodium STPP 1-2, aluminium hydroxide 12-15.
In described batching two, described fluidizer is methylcellulose gum or carboxymethyl cellulose.
The preparation technology of described batching one comprises the following steps:
1) by after brown alundum powder, tripoly phosphate sodium STPP, jade powder, tripoly phosphate sodium STPP, aluminium hydroxide mixing, grinding distribution is even, obtains auxiliary agent;
2) auxiliary agent step 1) obtained and carclazyte, pyrite tailing, black earth, quartz sand, silicon pyroxene, idiosome toughener, rotten sodium, Fe
2o
3and goth black co-grinding, cross 100-200 mesh sieve;
3) by step 2) mixture that the obtains water that adds same weight puts into stirrer together and is uniformly mixed 0.5-1 hour;
4) mixture after step 3) being stirred carries out drying by spray-drying tower, until biodiversity is 5-6%;
5) dried for step 4) mixture is put into ageing tower old 20 hours, namely obtain batching one.
The preparation technology of described batching two comprises the following steps:
1) get talcum, black earth, kaolin, rutile, zirconium white, rotten sodium, fluidizer and orange co-grinding, cross 100-200 mesh sieve;
2) water mixture that step 1) obtains being added same weight is put into stirrer together and is uniformly mixed 0.5-1 hour;
3) by step 2) stir after mixture carry out drying by spray-drying tower, until biodiversity is 9-12%;
4) dried for step 3) mixture is put into ageing tower old 25 hours, namely obtain batching two.
The preparation technology of described batching three comprises the following steps:
1) get bimodal Alpha-alumina micro mist, Reactive alumina, fused quartz, lithium feldspar, silicon pyroxene, talcum, idiosome toughener, rotten sodium, dispergator and iron oxide red co-grinding, cross 100-200 mesh sieve;
2) water mixture that step 1) obtains being added same weight is put into stirrer together and is uniformly mixed 0.5-1 hour;
3) by step 2) stir after mixture carry out drying by spray-drying tower, until biodiversity is 4-5%;
4) dried for step 3) mixture is put into ageing tower old 21 hours, namely obtain batching three.
The preparation technology of described hollow ceramic plate comprises the following steps:
1) be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 9 hours of same weight;
2) mixture after step 1) being ground carries out drying by spray-drying tower, until biodiversity is 25%;
3) by step 2) to squeeze mud by de-airing extruder shaping for dried mixture, obtains pottery board member base substrate;
4) pottery board member base substrate step 3) obtained carries out drying by spray-drying tower, until biodiversity is less than 3%;
5) dried for step 4) pottery board member base substrate being put into temperature is that the kiln of 1429 DEG C is calcined, and after completing, insulation 14 hours, namely obtains finished product hollow ceramic plate.
the usefulness of technique scheme is:
The invention provides the preparation technology of a kind of Multicolor hollow pottery plate, by the hollow ceramic plate obtained by preparation method of the present invention, functional, fire safety, environmental protection, self-cleaning is good, and various colors is bright in luster, color and luster is gentle, without color spot, decorative effect is good, and the hollow ceramic plate that thermal shock resistance and frost resistance provide higher than prior art.
Embodiment
embodiment 1
A preparation technology for Multicolor hollow pottery plate, its by weight ratio be the batching one of 1:2:1, batching two, batching three be prepared from; Wherein:
Batching one is made up of the raw material of following per-cent: carclazyte 34%, pyrite tailing 26%, black earth 6%, quartz sand 12%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.5% and goth black 2.3%;
Batching two is made up of the raw material of following per-cent: talcum 31%, black earth 20%, kaolin 12%, rutile 20%, zirconium white 8%, rotten sodium 0.3%, fluidizer 0.4% and orange 4.9%;
Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 28%, Reactive alumina 14%, fused quartz 28%, lithium feldspar 10%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 5.1%.
In described batching one, the raw material of auxiliary agent is made up of brown alundum powder 1-1.8, tripoly phosphate sodium STPP 2-4, jade powder 5.5-6.5, tripoly phosphate sodium STPP 1-2, aluminium hydroxide 12-15.
In described batching two, described fluidizer is methylcellulose gum or carboxymethyl cellulose.
The preparation technology of described batching one comprises the following steps:
1) by after brown alundum powder, tripoly phosphate sodium STPP, jade powder, tripoly phosphate sodium STPP, aluminium hydroxide mixing, grinding distribution is even, obtains auxiliary agent;
2) auxiliary agent step 1) obtained and carclazyte, pyrite tailing, black earth, quartz sand, silicon pyroxene, idiosome toughener, rotten sodium, Fe
2o
3and goth black co-grinding, cross 100-200 mesh sieve;
3) by step 2) mixture that the obtains water that adds same weight puts into stirrer together and is uniformly mixed 0.5-1 hour;
4) mixture after step 3) being stirred carries out drying by spray-drying tower, until biodiversity is 5-6%;
5) dried for step 4) mixture is put into ageing tower old 20 hours, namely obtain batching one.
The preparation technology of described batching two comprises the following steps:
1) get talcum, black earth, kaolin, rutile, zirconium white, rotten sodium, fluidizer and orange co-grinding, cross 100-200 mesh sieve;
2) water mixture that step 1) obtains being added same weight is put into stirrer together and is uniformly mixed 0.5-1 hour;
3) by step 2) stir after mixture carry out drying by spray-drying tower, until biodiversity is 9-12%;
4) dried for step 3) mixture is put into ageing tower old 25 hours, namely obtain batching two.
The preparation technology of described batching three comprises the following steps:
1) get bimodal Alpha-alumina micro mist, Reactive alumina, fused quartz, lithium feldspar, silicon pyroxene, talcum, idiosome toughener, rotten sodium, dispergator and iron oxide red co-grinding, cross 100-200 mesh sieve;
2) water mixture that step 1) obtains being added same weight is put into stirrer together and is uniformly mixed 0.5-1 hour;
3) by step 2) stir after mixture carry out drying by spray-drying tower, until biodiversity is 4-5%;
4) dried for step 3) mixture is put into ageing tower old 21 hours, namely obtain batching three.
The preparation technology of described hollow ceramic plate comprises the following steps:
1) be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 9 hours of same weight;
2) mixture after step 1) being ground carries out drying by spray-drying tower, until biodiversity is 25%;
3) by step 2) to squeeze mud by de-airing extruder shaping for dried mixture, obtains pottery board member base substrate;
4) pottery board member base substrate step 3) obtained carries out drying by spray-drying tower, until biodiversity is less than 3%;
5) dried for step 4) pottery board member base substrate being put into temperature is that the kiln of 1429 DEG C is calcined, and after completing, insulation 14 hours, namely obtains finished product hollow ceramic plate.
embodiment 2
The preparation technology of a kind of Multicolor hollow pottery plate as described in Example 1, wherein:
Batching one is made up of the raw material of following per-cent: carclazyte 32%, pyrite tailing 28%, black earth 5%, quartz sand 14%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.6% and goth black 2.3%;
Batching two is made up of the raw material of following per-cent: talcum 29%, black earth 18%, kaolin 13%, rutile 22%, zirconium white 10%, rotten sodium 0.3%, fluidizer 0.5% and orange 5.3%;
Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 25%, Reactive alumina 12%, fused quartz 26%, lithium feldspar 9%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 5.6%.
The preparation technology of described hollow ceramic plate comprises the following steps:
1) be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 7 hours of same weight;
2) mixture after step 1) being ground carries out drying by spray-drying tower, until biodiversity is 27%;
3) by step 2) to squeeze mud by de-airing extruder shaping for dried mixture, obtains pottery board member base substrate;
4) pottery board member base substrate step 3) obtained carries out drying by spray-drying tower, until biodiversity is less than 3%;
5) dried for step 4) pottery board member base substrate being put into temperature is that the kiln of 1430 DEG C is calcined, and after completing, insulation 13 hours, namely obtains finished product hollow ceramic plate.
embodiment 3
The preparation technology of a kind of Multicolor hollow pottery plate as described in Example 1, wherein:
Batching one is made up of the raw material of following per-cent: carclazyte 30%, pyrite tailing 30%, black earth 5%, quartz sand 15%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.4% and goth black 2.3%;
Batching two is made up of the raw material of following per-cent: talcum 32%, black earth 15%, kaolin 14%, rutile 20%, zirconium white 12%, rotten sodium 0.3%, fluidizer 0.4% and orange 5.8%;
Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 20%, Reactive alumina 15%, fused quartz 21%, lithium feldspar 13%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 4.3%.
The preparation technology of described hollow ceramic plate comprises the following steps:
1) be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 10 hours of same weight;
2) mixture after step 1) being ground carries out drying by spray-drying tower, until biodiversity is 30%;
3) by step 2) to squeeze mud by de-airing extruder shaping for dried mixture, obtains pottery board member base substrate;
4) pottery board member base substrate step 3) obtained carries out drying by spray-drying tower, until biodiversity is less than 3%;
5) dried for step 4) pottery board member base substrate being put into temperature is that the kiln of 1435 DEG C is calcined, and after completing, insulation 13 hours, namely obtains finished product hollow ceramic plate.
embodiment 4
The preparation technology of a kind of Multicolor hollow pottery plate as described in Example 1, wherein:
Batching one is made up of the raw material of following per-cent: carclazyte 35%, pyrite tailing 20%, black earth 8%, quartz sand 10%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.6% and goth black 2.3%;
Batching two is made up of the raw material of following per-cent: talcum 28%, black earth 20%, kaolin 11%, rutile 28%, zirconium white 7%, rotten sodium 0.3%, fluidizer 0.6% and orange 4.3%;
Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 29%, Reactive alumina 11%, fused quartz 28%, lithium feldspar 8%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 5.8%.
The preparation technology of described hollow ceramic plate comprises the following steps:
1) be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 7 hours of same weight;
2) mixture after step 1) being ground carries out drying by spray-drying tower, until biodiversity is 20%;
3) by step 2) to squeeze mud by de-airing extruder shaping for dried mixture, obtains pottery board member base substrate;
4) pottery board member base substrate step 3) obtained carries out drying by spray-drying tower, until biodiversity is less than 3%;
5) dried for step 4) pottery board member base substrate being put into temperature is that the kiln of 1425 DEG C is calcined, and after completing, insulation 15 hours, namely obtains finished product hollow ceramic plate.
test method:
Operative norm of the present invention: standard GB/T/T27972-2011, test the finished product hollow ceramic plate obtained by above-mentioned four embodiments of the present invention respectively, result is as shown in table 1, and performance meets relevant regulations.
Table 1
Can be found out by table 1, through the finished product hollow ceramic plate obtained by above-mentioned four embodiments of the present invention, be about to by weight ratio be the batching one of 1:2:1, batching two, batching three be prepared from, batching one is made up of the raw material of following per-cent: carclazyte 30-35%, pyrite tailing 20-30%, black earth 5-8%, quartz sand 10-15%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.4-0.6% and goth black 2.3%; Batching two is made up of the raw material of following per-cent: talcum 28-32%, black earth 15-20%, kaolin 11-14%, rutile 20-28%, zirconium white 7-12%, rotten sodium 0.3%, fluidizer 0.4-0.6% and orange 4.3-5.8%; Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 20-29%, Reactive alumina 11-15%, fused quartz 21-28%, lithium feldspar 8-13%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 4.3-5.8%; Be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 7-10 hour of same weight; Mixture after grinding is carried out drying by spray-drying tower, until biodiversity is 20-30%; Dried mixture is squeezed mud by de-airing extruder shaping, obtain pottery board member base substrate; The pottery board member base substrate obtained is carried out drying by spray-drying tower, until biodiversity is less than 3%; It is that the kiln of 1425-1435 DEG C is calcined that dried pottery board member base substrate puts into temperature, is incubated the finished product hollow ceramic plate obtained for 13-15 hour after completing, and its performance meets concerned countries standard regulation.
test one:pottery plate thermal shock resistance is measured.
test materials:multicolor hollow pottery plate obtained by the present invention's four embodiments, application number are the hollow ceramic plate of 201210116644.8 and common pottery plate.
test method:according to standard GB/T/T27972-2011, undertaken by GB/T3810.9 regulation.
national standard:there is not crackle through 10 knock tests or burst.
test-results:
1, the Multicolor hollow pottery plate obtained by the embodiment of the present invention one:
In test, there is slight crackle the 22nd time, burst for the 25th time in flawless or burst phenomenon in product of the present invention 17 times above test.
2, the Multicolor hollow pottery plate obtained by the embodiment of the present invention two:
In test, there is slight crackle the 19th time, burst for the 22nd time in flawless or burst phenomenon in product of the present invention 17 times above test.
3, the Multicolor hollow pottery plate obtained by the embodiment of the present invention three:
In test, there is slight crackle the 17th time, burst for the 20th time in flawless or burst phenomenon in product of the present invention 15 times above test.
4, the Multicolor hollow pottery plate obtained by the embodiment of the present invention four:
In test, there is slight crackle the 18th time, burst for the 20th time in flawless or burst phenomenon in product of the present invention 17 times above test.
5, application number is the hollow ceramic plate of 201210116644.8:
In test, there is slight crackle the 14th time, burst for the 15th time in flawless or burst phenomenon in this product 12 times above test.
6, common pottery plate:
In test, flawless or burst phenomenon in this product 11 times above test, bursts for the 13rd time.
conclusion (of pressure testing):
Can find out by testing a test-results, through the finished product Multicolor hollow pottery plate obtained by above-mentioned four embodiments of the present invention, be about to by weight ratio be the batching one of 1:2:1, batching two, batching three be prepared from, batching one is made up of the raw material of following per-cent: carclazyte 30-35%, pyrite tailing 20-30%, black earth 5-8%, quartz sand 10-15%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.4-0.6% and goth black 2.3%; Batching two is made up of the raw material of following per-cent: talcum 28-32%, black earth 15-20%, kaolin 11-14%, rutile 20-28%, zirconium white 7-12%, rotten sodium 0.3%, fluidizer 0.4-0.6% and orange 4.3-5.8%; Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 20-29%, Reactive alumina 11-15%, fused quartz 21-28%, lithium feldspar 8-13%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 4.3-5.8%; Be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 7-10 hour of same weight; Mixture after grinding is carried out drying by spray-drying tower, until biodiversity is 20-30%; Dried mixture is squeezed mud by de-airing extruder shaping, obtain pottery board member base substrate; The pottery board member base substrate obtained is carried out drying by spray-drying tower, until biodiversity is less than 3%; It is that the kiln of 1425-1435 DEG C is calcined that dried pottery board member base substrate puts into temperature, the finished product hollow ceramic plate obtained for 13-15 hour is incubated after completing, thermal shock resistance exceedes the pottery plate that prior art provides, farther higher than common pottery plate, wherein best through the finished product pottery plate performance that the technical scheme described in embodiment one is obtained.
test two:finished product pottery plate anti-freezing property is measured.
test materials:multicolor hollow pottery plate obtained by the embodiment of the present invention one, application number are the hollow ceramic plate of 201210116644.8 and common pottery plate.
test method:according to standard GB/T/T27972-2011, undertaken by GB/T3810.12 regulation.
test-results:
1, the Multicolor hollow pottery plate obtained by the embodiment of the present invention one:
In test, there is slight crackle the 180th time, burst for the 190th time in flawless or burst phenomenon in product of the present invention 150 times above test.
2, application number is the hollow ceramic plate of 201210116644.8:
In test, there is slight crackle the 150th time, burst for the 160th time in flawless or burst phenomenon in this product 130 times above test.
3, common pottery plate:
In test, there is slight crackle the 130th time, burst for the 140th time in flawless or burst phenomenon in this product 110 times above test.
conclusion (of pressure testing):
Can find out by testing two test-results, through the finished product Multicolor hollow pottery plate obtained by above-mentioned four embodiments of the present invention, be about to by weight ratio be the batching one of 1:2:1, batching two, batching three be prepared from, batching one is made up of the raw material of following per-cent: carclazyte 34%, pyrite tailing 26%, black earth 6%, quartz sand 12%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.5% and goth black 2.3%; Batching two is made up of the raw material of following per-cent: talcum 31%, black earth 20%, kaolin 12%, rutile 20%, zirconium white 8%, rotten sodium 0.3%, fluidizer 0.4% and orange 4.9%; Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 28%, Reactive alumina 14%, fused quartz 28%, lithium feldspar 10%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 5.1%; Be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 9 hours of same weight; Mixture after grinding is carried out drying by spray-drying tower, until biodiversity is 25%; Dried mixture is squeezed mud by de-airing extruder shaping, obtain pottery board member base substrate; The pottery board member base substrate obtained is carried out drying by spray-drying tower, until biodiversity is less than 3%; It is that the kiln of 1429 DEG C is calcined that dried pottery board member base substrate puts into temperature, and after completing, insulation obtained finished product hollow ceramic plate after 14 hours, and anti-freezing property exceedes the pottery plate that prior art provides, farther higher than common pottery plate.
Claims (6)
1. a preparation technology for Multicolor hollow pottery plate, is characterized in that: its by weight ratio be the batching one of 1:2:1, batching two, batching three be prepared from; Wherein: batching one is made up of the raw material of following per-cent: carclazyte 30-35%, pyrite tailing 20-30%, black earth 5-8%, quartz sand 10-15%, auxiliary agent 7%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.4-0.6% and goth black 2.3%; Batching two is made up of the raw material of following per-cent: talcum 28-32%, black earth 15-20%, kaolin 11-14%, rutile 20-28%, zirconium white 7-12%, rotten sodium 0.3%, fluidizer 0.4-0.6% and orange 4.3-5.8%; Batching three is made up of the raw material of following per-cent: bimodal Alpha-alumina micro mist 20-29%, Reactive alumina 11-15%, fused quartz 21-28%, lithium feldspar 8-13%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 4.3-5.8%; The preparation technology of described hollow ceramic plate comprises the following steps:
1) be the batching one of 1:2:1 by weight ratio, batching two, batching three add mix and blend in stirrer, and add the water mixed grinding 7-10 hour of same weight;
2) mixture after step 1) being ground carries out drying by spray-drying tower, until biodiversity is 20-30%;
3) by step 2) to squeeze mud by de-airing extruder shaping for dried mixture, obtains pottery board member base substrate;
4) pottery board member base substrate step 3) obtained carries out drying by spray-drying tower, until biodiversity is less than 3%;
5) dried for step 4) pottery board member base substrate being put into temperature is that the kiln of 1425-1435 DEG C is calcined, and is incubated 13-15 hour, namely obtains finished product hollow ceramic plate after completing.
2. the preparation technology of a kind of Multicolor hollow pottery plate as claimed in claim 1, it is characterized in that: in described batching one, the raw material of auxiliary agent is made up of brown alundum powder 1-1.8, tripoly phosphate sodium STPP 2-4, jade powder 5.5-6.5, tripoly phosphate sodium STPP 1-2, aluminium hydroxide 12-15.
3. the preparation technology of a kind of Multicolor hollow pottery plate as claimed in claim 1, is characterized in that: the preparation technology of described batching one comprises the following steps:
1) by after brown alundum powder 1-1.8, tripoly phosphate sodium STPP 2-4, jade powder 5.5-6.5, tripoly phosphate sodium STPP 1-2, aluminium hydroxide 12-15 mixing, grinding distribution is even, obtains auxiliary agent;
2) auxiliary agent step 1) obtained by 7% per-cent and carclazyte 34%, pyrite tailing 26%, black earth 6%, quartz sand 12%, silicon pyroxene 3%, idiosome toughener 3%, rotten sodium 0.3%, Fe
2o
30.5% and goth black 2.3% co-grinding, cross 100-200 mesh sieve;
3) by step 2) mixture that the obtains water that adds same weight puts into stirrer together and is uniformly mixed 0.5-1 hour;
4) mixture after step 3) being stirred carries out drying by spray-drying tower, until biodiversity is 5-6%;
5) dried for step 4) mixture is put into ageing tower old 20 hours, namely obtain batching one.
4. the preparation technology of a kind of Multicolor hollow pottery plate as claimed in claim 1, is characterized in that: the preparation technology of described batching two comprises the following steps:
1) get talcum 31%, black earth 20%, kaolin 12%, rutile 20%, zirconium white 8%, rotten sodium 0.3%, fluidizer 0.4% and orange 4.9% co-grinding, cross 100-200 mesh sieve;
2) water mixture that step 1) obtains being added same weight is put into stirrer together and is uniformly mixed 0.5-1 hour;
3) by step 2) stir after mixture carry out drying by spray-drying tower, until biodiversity is 9-12%;
4) dried for step 3) mixture is put into ageing tower old 25 hours, namely obtain batching two.
5. the preparation technology of a kind of Multicolor hollow pottery plate as claimed in claim 1, is characterized in that: the preparation technology of described batching three comprises the following steps:
1) get bimodal Alpha-alumina micro mist 28%, Reactive alumina 14%, fused quartz 28%, lithium feldspar 10%, silicon pyroxene 3%, talcum 3%, idiosome toughener 3%, rotten sodium 0.3%, dispergator 0.4% and iron oxide red 5.1% co-grinding, cross 100-200 mesh sieve;
2) water mixture that step 1) obtains being added same weight is put into stirrer together and is uniformly mixed 0.5-1 hour;
3) by step 2) stir after mixture carry out drying by spray-drying tower, until biodiversity is 4-5%;
4) dried for step 3) mixture is put into ageing tower old 21 hours, namely obtain batching three.
6. the preparation technology of a kind of Multicolor hollow pottery plate as claimed in claim 1, it is characterized in that: in described batching two, described fluidizer is methylcellulose gum or carboxymethyl cellulose.