CN105017645A - 一种高强度包装用塑料薄膜 - Google Patents
一种高强度包装用塑料薄膜 Download PDFInfo
- Publication number
- CN105017645A CN105017645A CN201510473241.2A CN201510473241A CN105017645A CN 105017645 A CN105017645 A CN 105017645A CN 201510473241 A CN201510473241 A CN 201510473241A CN 105017645 A CN105017645 A CN 105017645A
- Authority
- CN
- China
- Prior art keywords
- parts
- packaging
- plastic film
- film used
- packaging bag
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种高强度包装用塑料薄膜,涉及包装材料技术领域,所述高强度抗菌包装袋由以下重量份的原料制成:玉米淀粉40-60份,聚丙烯树脂100-120份,聚乙烯蜡6-10份,尼龙25-40份,抗氧剂0.1-0.5份,碳酸钙10-15份,亚麻纤维2-4份,硅烷偶联剂0.2-0.8份,本发明通过在原料中添加尼龙和亚麻纤维来增加包装袋的强度;且在原料中加入了玉米淀粉,提高了该种包装袋的可降解性,降解产物对环境无污染,不仅降低包装袋的成本,还减少了对环境的污染,绿色环保。
Description
技术领域
本发明涉及包装材料技术领域,具体涉及一种高强度包装用塑料薄膜。
背景技术
包装袋是指用于包装各种用品的袋子,使货物在生产流通过程中方便运输,容易存储。广泛用于日常生活和工业生产中。随着我国经济的快速发展,国内居民的购买力水平和消费意愿也逐步增强,消费观念将趋向进一步提高生活质量。长期来看,我国饮料、酒类、食用油及调味品等液态食品行业仍有较大增长空间,尤其是农村地区消费能力的提升将大大拉动其对饮料等液态食品的消费。总之,下游行业的快速发展以及人们对生活品质的追求,必然要求企业投入相应的包装设备以满足生产的需要,同时也将对包装机械的高精度、智能化、高速化水平提出更高的要求,因此我国液态食品包装机械将呈现出较为广阔的市场前景。但现有技术的包装袋存在一些缺陷,如包装袋强度不够,容易造成包装袋的撕裂,便起不到包装的作用;抗菌性存在不足,食物容易腐败变质。
发明内容
本发明所要解决的问题是提供一种强度高,抗菌性好,可降解的包装用塑料薄膜。
为了实现上述目的,本发明采取的技术方案为:所提供的一种高强度包装用塑料薄膜,它由以下重量份的原料制成:玉米淀粉40-60份,聚丙烯树脂100-120份,聚乙烯蜡6-10份,尼龙25-40份,抗氧剂0.1-0.5份,碳酸钙10-15份,亚麻纤维2-4份,硅烷偶联剂0.2-0.8份。
优选的,所述高强度包装用塑料薄膜,它由以下重量份的原料制成:玉米淀粉45份,聚丙烯树脂100份,聚乙烯蜡7份,尼龙28份,抗氧剂0.2份,碳酸钙12份,亚麻纤维2份,硅烷偶联剂0.2份。
优选的,所述聚乙烯蜡具体为PE520。
本发明的有益效果:本发明通过在原料中添加尼龙和亚麻纤维来增加包装袋的强度;且在原料中加入了玉米淀粉,提高了该种包装袋的可降解性,降解产物对环境无污染,不仅降低包装袋的成本,还减少了对环境的污染,绿色环保。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施方式,进一步阐述本发明。
实施例1:
一种高强度包装用塑料薄膜,它由以下重量份的原料制成:玉米淀粉45份,聚丙烯树脂100份,聚乙烯蜡PE520 7份,尼龙28份,抗氧剂0.2份,碳酸钙12份,亚麻纤维2份,硅烷偶联剂0.2份。
基于上述,本发明通过在原料中添加尼龙和亚麻纤维来增加包装袋的强度;且在原料中加入了玉米淀粉,提高了该种包装袋的可降解性,降解产物对环境无污染,不仅降低包装袋的成本,还减少了对环境的污染,绿色环保。
显然本发明具体实现并不受上述方式的限制,只要采用了本发明的方法构思和技术方案进行的各种非实质性的改进,或未经改进将本发明的构思和技术方案直接应用于其它场合的,均在本发明的保护范围之内。
Claims (3)
1.一种高强度包装用塑料薄膜,其特征在于,它由以下重量份的原料制成:玉米淀粉40-60份,聚丙烯树脂100-120份,聚乙烯蜡6-10份,尼龙25-40份,抗氧剂0.1-0.5份,碳酸钙10-15份,亚麻纤维2-4份,硅烷偶联剂0.2-0.8份。
2. 根据权利要求1所述的一种高强度包装用塑料薄膜,其特征在于,它由以下重量份的原料制成:玉米淀粉45份,聚丙烯树脂100份,聚乙烯蜡7份,尼龙28份,抗氧剂0.2份,碳酸钙12份,亚麻纤维2份,硅烷偶联剂0.2份。
3. 根据权利要求1或2所述的一种高强度包装用塑料薄膜,其特征在于,所述聚乙烯蜡具体为PE520。