CN104989061A - Ultraviolet curing color flat decoration plate and manufacturing method thereof - Google Patents
Ultraviolet curing color flat decoration plate and manufacturing method thereof Download PDFInfo
- Publication number
- CN104989061A CN104989061A CN201410848683.6A CN201410848683A CN104989061A CN 104989061 A CN104989061 A CN 104989061A CN 201410848683 A CN201410848683 A CN 201410848683A CN 104989061 A CN104989061 A CN 104989061A
- Authority
- CN
- China
- Prior art keywords
- decorating board
- carry out
- decorative panel
- ultraviolet light
- ultraviolet curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a manufacturing method of an ultraviolet curing color flat decoration plate. The method includes: (1) forming a primer surface on the front surface of a decoration substrate; (2) performing roller painting of colored paints on the front surface of the decoration substrate and performing ultraviolet curing; (3) performing roller painting of finishing paints on the front surface of the decoration substrate and performing ultraviolet curing; and (4) performing roller painting of flat finishing paints on the cured finishing paints and performing ultraviolet curing. The decoration plate manufactured by the method is advantaged by high-definition emulation, bright and saturated color, smooth and wear-resistant surface, light weight, and low cost.
Description
Technical field
The present invention relates to a kind of decorative panel and manufacture method thereof, particularly relate to a kind of ultraviolet curing chromatic zero diopter decorative panel and manufacture method thereof.
Background technology
Ultraviolet light (UV) solidification be utilize the photonasty of light trigger (sensitising agent), light-initiated formation excited ecological molecule under ultraviolet light irradiation, chemical reactions such as resolving into free radical or ion, make unsaturated compounds carry out being polymerized, connect skill, be crosslinked reaches the object of solidification.UV-curing technology has been applied in the manufacture of decorative panel.The base material of UV-curing technology is adopted to comprise cement pressure plate, multilayer solid wood board, density board, glass magnesium PLASTIC LAMINATED.But the ultraviolet light polymerization decorative panel being base material manufacture with the sheet material of mentioned kind can not meet at present to inexpensive, lightweight, the requirement that thickness is thin of decorative panel.
Summary of the invention
The present invention is intended to solve above-described problem.The object of this invention is to provide a kind of ultraviolet curing chromatic zero diopter decorative panel and manufacture method thereof.
According to an aspect of the present invention, provide a kind of manufacture method of ultraviolet curing chromatic zero diopter decorative panel, said method comprising the steps of:
(1) priming paint face is formed in the front of decorating board;
(2) be coated with colored paint in the face-side roll of described decorating board, and carry out ultraviolet light polymerization;
(3) at the front roller coat finish paint of described decorating board, and ultraviolet light polymerization is carried out;
(4) roller coat zero diopter finish paint on the described finish paint through overcuring, and carry out ultraviolet light polymerization.
Wherein, before described step (1), also step is comprised:
Carry out dust removal process at the back side of described decorating board, then at the back side roller coat seal coat of described decorating board, and carry out ultraviolet light polymerization;
Also step is comprised after described step (4):
Diaphragm is covered in the front of described decorating board.
Wherein, described step (1) comprising:
(11) dust removal process is carried out in the front of described decorating board;
(12) be coated with adhesion primer in the face-side roll of described decorating board, and carry out ultraviolet light polymerization;
(13) washed ore light and dust removal process are carried out to the front of described decorating board;
(14) at the face-side roll coating white priming paint of described decorating board, and ultraviolet light polymerization is carried out;
(15) close sanding priming paint at the front roller coat of described decorating board, and carry out ultraviolet light polymerization;
(16) sanding, infrared levelling and dust removal process are carried out to the front of described decorating board;
(17) be coated with attachment primer in the face-side roll of described decorating board, and carry out ultraviolet light polymerization, form priming paint face.
Wherein, described step (2) also comprises:
Carry out at least three times roller coat colored paints in the front of described decorating board, wherein, often all carry out ultraviolet light polymerization all over after roller coat colored paint.
Wherein, the roller coat in described step (12) and described step (15) adopts just against the mode of roller roller coat.
Wherein, in described step (13), adopt 240 order sand paper to carry out the process of washed ore light to the front of described decorating board, in described step (16), adopt 400 order sand paper to sand flat seal coat on the front of described decorating board.
Wherein, the time of carrying out ultraviolet light polymerization in each step is 3-10s, and ultraviolet light polymerization is 5 DEG C of-40 DEG C of normal temperature cures.
Wherein, in each step, the thickness of roll coat enamel is 0.05-0.12mm.
Wherein, described decorating board is gypsum plank.
According to another aspect of the present invention, a kind of ultraviolet curing chromatic zero diopter decorative panel manufactured by above-mentioned manufacture method is provided.
Ultraviolet curing chromatic zero diopter decorative panel of the present invention and manufacture method thereof can bring the lot of advantages relative to other kind substrates, and such as, cost is low, applied range etc.In addition, the material feature of said method and gypsum plank self combines, and is different from existing UV-curing technology.Adopt the decorative panel of said method manufacture to have better hardness and wiping properties, be more applicable for the dalle in building.Hardness of film >=the 2H of this decorative panel, and there is acid resistance, alkali resistance, the performance that solvent resistant wiping is >100 time.
The decorative panel that ultraviolet curing chromatic zero diopter decorative board production method according to the present invention can manufacture has high definition emulation, saturated, smooth surface is wear-resisting, light weight is inexpensive feature bright in luster.Above-mentioned manufacture method curing rate is fast, production efficiency is high, Environmental Safety.
Read the following description for exemplary embodiment with reference to accompanying drawing, other property features of the present invention and advantage will become clear.
Accompanying drawing explanation
To be incorporated in manual and the accompanying drawing forming a part for manual shows embodiments of the invention, and together with the description for explaining principle of the present invention.In the drawings, similar Reference numeral is used for key element like representation class.Accompanying drawing in the following describes is some embodiments of the present invention, instead of whole embodiment.For those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can be obtained according to these accompanying drawings.
Fig. 1 schematically illustrates the flow chart according to ultraviolet curing chromatic zero diopter decorative board production method of the present invention.
Detailed description of the invention
For making the object of the embodiment of the present invention, technical scheme and advantage clearly, below in conjunction with the accompanying drawing in the embodiment of the present invention, technical scheme in the embodiment of the present invention is clearly and completely described, obviously, described embodiment is the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.It should be noted that, when not conflicting, the embodiment in the application and the feature in embodiment can be combined mutually.
In existing UV-curing technology, according to the difference of base material, the technique of the ultraviolet light polymerization of employing is also different.Such as, when being applied to wood surface, need the characteristics such as the moisture content of consideration timber; When being applied to cement matrix, need the alkaline matrix considering cement.
At present, also UV-curing technology is not applied to gypsum plank.Due to gypsum plank self inexpensive, lightweight, thickness is thin, be that substrate applications UV-curing technology can bring huge economic benefit with gypsum plank, therefore, inventors performed a large amount of experiments, UV-curing technology is applied to gypsum plank.Inventor draws by experiment, when UV-curing technology is applied to gypsum plank, take into full account the particularity of gypsum plank material, adopt special production technology.Introduce the manufacture method according to ultraviolet curing chromatic zero diopter decorative panel of the present invention below in detail.
Manufacture method according to ultraviolet curing chromatic zero diopter decorative panel of the present invention comprises the following steps:
(1) priming paint face is formed in the front of decorating board;
(2) be coated with colored paint in the face-side roll of decorating board, and carry out ultraviolet light polymerization;
(3) at the front roller coat finish paint of decorating board, and ultraviolet light polymerization is carried out;
(4) roller coat zero diopter finish paint on the finish paint through overcuring, and carry out ultraviolet light polymerization.
Also step was comprised: carry out dust removal process at the back side of decorating board, then at the back side roller coat seal coat of decorating board, and carry out ultraviolet light polymerization before step (1).Ultraviolet light polymerization in this step adopts two mercury lamp curing to be cured.The above-mentioned step processed the back side of decorating board is to shield to substrate; due to the cure shrinkage that sheet material is very large can be caused after front surface coated multiple layers of cured coating; therefore apply the tension force that seal coat can offset sheet material two sides overleaf, prevent substrate deformation.
Above-mentioned steps (1) forms priming paint mask body and comprises in the front of decorating board:
(11) dust removal process is carried out in the front of decorating board.
(12) be coated with adhesion primer in the face-side roll of decorating board, and carry out ultraviolet light polymerization.
(13) washed ore light and dust removal process are carried out to the front of decorating board.
(14) at the face-side roll coating white priming paint of decorating board, and ultraviolet light polymerization is carried out.Wherein the object of roller coat white primer be to improve after adhesive power, the fullness of coating in step, enable coating by uniform pickup.
(15) close sanding priming paint at the front roller coat of decorating board, and carry out ultraviolet light polymerization.Wherein roller coat closes the object of sanding priming paint is make the absorption of decorating board to upper coating become even, and effectively can prevent moisture, plays the effect of alkali resistant isolation.
(16) sanding, infrared levelling and dust removal process are carried out to the front of decorating board.
(17) be coated with attachment primer in the face-side roll of decorating board, and carry out ultraviolet light polymerization, form priming paint face.Wherein roller coat adheres to the adhesive power of coating in step after the object of primer is raising.
In addition, also comprise in above-mentioned steps (2): carry out at least three times roller coat colored paints in the front of described decorating board, wherein, often all carrying out ultraviolet light polymerization all over after roller coat colored paint.It should be noted that, carrying out at least three times roller coat colored paints is to make final color fuller, through overtesting, just at least can reach colour and the decorative effect of expection after roller coat three times colored paints.
Also step is comprised: cover diaphragm in the front of described decorating board after step (4).Thus form ultraviolet light polymerization zero diopter decorative panel.
Wherein, two gallium lamp curing is adopted to be cured in above-mentioned steps (2), (3), (12) and (14), adopt gallium gallium iron iron four lamp curing to be cured in step (4) and step (15), in step (17), adopt single mercury lamp curing to be cured.
In addition, the roller coat in step (12) and described step (15) adopts just against the mode of roller roller coat, to make paint even.Roller coat in other steps can adopt the mode of single roller roller coat.
In step (13), 240 order sand paper are adopted to carry out the process of washed ore light to the front of described decorating board.In step (16), adopt 400 order sand paper to sand flat seal coat on the front of described decorating board, and all need to carry out dust removal process after sanding and infrared levelling process.And in step (16), the object of infrared levelling is to raise system temperature, is convenient to the enforcement of later step.
The time of carrying out ultraviolet light polymerization in each step above-mentioned is 3-10s.The temperature of carrying out ultraviolet light polymerization in each step is normal temperature 5 DEG C-40 DEG C.Further, in each step, the thickness of roll coat enamel is 0.05-0.12mm.
Below provide specific embodiment.In following embodiment, be all applied to gypsum plank for this ultraviolet curing chromatic zero diopter method.
embodiment one
Manufacture method according to ultraviolet curing chromatic zero diopter decorative panel of the present invention comprises the following steps:
1) dust removal process is carried out to the back side of Thistle board;
2) adopt the mode of single roller roller coat at the thick seal coat of the backside coating 0.05mm of Thistle board, and adopt two mercury lamp curing to carry out the UV solidification of 3s;
3) turnover panel, and dust removal process is carried out to the front of Thistle board;
4) adopt just against the mode of roller roller coat at the thick adhesion primer of the front surface coated 0.05mm of Thistle board, object makes paint even, and adopt gallium gallium lamp curing to carry out the UV solidification of 3s;
5), after having solidified, washed ore light and dust removal process are carried out to Thistle board surface;
6) white primer that single roller roller coat 0.05mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 3s;
7) adopt just against the seal coat that roller roller coat 0.05mm is thick, and adopt gallium gallium iron iron lamp curing to carry out the UV solidification of 3s;
8) adopt 400 order sand paper to carry out sanding to the decorative panel completing primer coating, sand flat the seal coat on the front of described decorating board and carry out dust removal process, then carry out infrared levelling and dust removal process again;
9) the attachment primer that single roller roller coat 0.05mm is thick, and adopt single mercury lamp curing to carry out the UV solidification of 3s, form priming paint face;
10) colored paint that single roller roller coat 0.05mm is thick on priming paint face, and adopt two gallium lamp curing to carry out the UV solidification of 3s;
11) colored paint that single roller roller coat 0.05mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 3s;
12) colored paint that single roller roller coat 0.05mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 3s;
13) finish paint that single roller roller coat 0.05mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 3s;
14) just against the zero diopter finish paint that roller roller coat 0.05mm is thick, and gallium gallium iron iron lamp curing is adopted to carry out the UV solidification of 3s;
15) after having solidified, cover diaphragm at plaque surface, form UV and solidify zero diopter decorative panel.
Above-described UV solidification is all carried out under 5 DEG C of-40 DEG C of normal temperature conditions.
Hardness of film >=the 2H of the ultraviolet curing chromatic zero diopter decorative panel manufactured by said method, and there is acid resistance, alkali resistance, the performance that solvent resistant wiping is >100 time.
embodiment two
Manufacture method according to ultraviolet curing chromatic zero diopter decorative panel of the present invention comprises the following steps:
1) dust removal process is carried out to the back side of Thistle board;
2) adopt the mode of single roller roller coat at the thick seal coat of the backside coating 0.08mm of Thistle board, and adopt two mercury lamp curing to carry out the UV solidification of 6s;
3) turnover panel, and dust removal process is carried out to the front of Thistle board;
4) adopt just against the mode of roller roller coat at the thick adhesion primer of the front surface coated 0.08mm of Thistle board, object makes paint even, and adopt gallium gallium lamp curing to carry out the UV solidification of 6s;
5), after having solidified, washed ore light and dust removal process are carried out to Thistle board surface;
6) white primer that single roller roller coat 0.08mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 6s;
7) adopt just against the seal coat that roller roller coat 0.08mm is thick, and adopt gallium gallium iron iron lamp curing to carry out the UV solidification of 6s;
8) adopt 400 order sand paper to carry out sanding to the decorative panel completing primer coating, sand flat the seal coat on the front of described decorating board and carry out dust removal process, then carry out infrared levelling and dust removal process again;
9) the attachment primer that single roller roller coat 0.08mm is thick, and adopt single mercury lamp curing to carry out the UV solidification of 6s, form priming paint face;
10) colored paint that single roller roller coat 0.08mm is thick on priming paint face, and adopt two gallium lamp curing to carry out the UV solidification of 6s;
11) colored paint that single roller roller coat 0.08mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 6s;
12) colored paint that single roller roller coat 0.08mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 6s;
13) finish paint that single roller roller coat 0.08mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 6s;
14) just against the zero diopter finish paint that roller roller coat 0.08mm is thick, and gallium gallium iron iron lamp curing is adopted to carry out the UV solidification of 6s;
15) after having solidified, cover diaphragm at plaque surface, form UV and solidify zero diopter decorative panel.
Above-described UV solidification is all carried out under 5 DEG C of-40 DEG C of normal temperature conditions.
Hardness of film >=the 2H of the ultraviolet curing chromatic zero diopter decorative panel manufactured by said method, and there is acid resistance, alkali resistance, the performance that solvent resistant wiping is >100 time.
embodiment three
Manufacture method according to ultraviolet curing chromatic zero diopter decorative panel of the present invention comprises the following steps:
1) dust removal process is carried out to the back side of Thistle board;
2) adopt the mode of single roller roller coat at the thick seal coat of the backside coating 0.12mm of Thistle board, and adopt two mercury lamp curing to carry out the UV solidification of 10s;
3) turnover panel, and dust removal process is carried out to the front of Thistle board;
4) adopt just against the mode of roller roller coat at the thick adhesion primer of the front surface coated 0.12mm of Thistle board, object makes paint even, and adopt gallium gallium lamp curing to carry out the UV solidification of 10s;
5), after having solidified, washed ore light and dust removal process are carried out to Thistle board surface;
6) white primer that single roller roller coat 0.12mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 10s;
7) adopt just against the seal coat that roller roller coat 0.12mm is thick, and adopt gallium gallium iron iron lamp curing to carry out the UV solidification of 10s;
8) adopt 400 order sand paper to carry out sanding to the decorative panel completing primer coating, sand flat the seal coat on the front of described decorating board and carry out dust removal process, then carry out infrared levelling and dust removal process again;
9) the attachment primer that single roller roller coat 0.12mm is thick, and adopt single mercury lamp curing to carry out the UV solidification of 10s, form priming paint face;
10) colored paint that single roller roller coat 0.12mm is thick on priming paint face, and adopt two gallium lamp curing to carry out the UV solidification of 10s;
11) colored paint that single roller roller coat 0.12mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 10s;
12) colored paint that single roller roller coat 0.12mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 10s;
13) finish paint that single roller roller coat 0.12mm is thick, and adopt two gallium lamp curing to carry out the UV solidification of 10s;
14) just against the zero diopter finish paint that roller roller coat 0.12mm is thick, and gallium gallium iron iron lamp curing is adopted to carry out the UV solidification of 10s;
15) after having solidified, cover diaphragm at plaque surface, form UV and solidify zero diopter decorative panel.
Above-described UV solidification is all carried out under 5 DEG C of-40 DEG C of normal temperature conditions.
Hardness of film >=the 2H of the ultraviolet curing chromatic zero diopter decorative panel manufactured by said method, and there is acid resistance, alkali resistance, the performance that solvent resistant wiping is >100 time.
It should be noted that, current UV-curing technology is not all applied to gypsum plank, but due to gypsum plank self inexpensive, lightweight, thickness is thin, is that substrate applications UV-curing technology can bring huge economic benefit with gypsum plank.Therefore, take gypsum plank as the lot of advantages that decorating board can bring relative to other kind substrates, such as, cost be low, applied range etc.In addition, the material feature of said method and gypsum plank self combines, and is different from existing UV-curing technology.Adopt the decorative panel of said method manufacture to have better hardness and wiping properties, be more applicable for the dalle in building.
According to the decorative panel of ultraviolet curing chromatic zero diopter decorative board production method of the present invention manufacture, there is high definition emulation, saturated, smooth surface is wear-resisting, light weight is inexpensive feature bright in luster.Above-mentioned manufacture method curing rate is fast, production efficiency is high, Environmental Safety.
Last it is noted that above embodiment is only in order to illustrate technical scheme of the present invention, be not intended to limit.Although with reference to previous embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (10)
1. a manufacture method for ultraviolet curing chromatic zero diopter decorative panel, is characterized in that, said method comprising the steps of:
(1) priming paint face is formed in the front of decorating board;
(2) be coated with colored paint in the face-side roll of described decorating board, and carry out ultraviolet light polymerization;
(3) at the front roller coat finish paint of described decorating board, and ultraviolet light polymerization is carried out;
(4) roller coat zero diopter finish paint on the described finish paint through overcuring, and carry out ultraviolet light polymerization.
2. the manufacture method of ultraviolet curing chromatic zero diopter decorative panel as claimed in claim 1, is characterized in that, before described step (1), also comprise step:
Carry out dust removal process at the back side of described decorating board, then at the back side roller coat seal coat of described decorating board, and carry out ultraviolet light polymerization;
Also step is comprised after described step (4):
Diaphragm is covered in the front of described decorating board.
3. the manufacture method of ultraviolet curing chromatic zero diopter decorative panel as claimed in claim 1, it is characterized in that, described step (1) comprising:
(11) dust removal process is carried out in the front of described decorating board;
(12) be coated with adhesion primer in the face-side roll of described decorating board, and carry out ultraviolet light polymerization;
(13) washed ore light and dust removal process are carried out to the front of described decorating board;
(14) at the face-side roll coating white priming paint of described decorating board, and ultraviolet light polymerization is carried out;
(15) close sanding priming paint at the front roller coat of described decorating board, and carry out ultraviolet light polymerization;
(16) sanding, infrared levelling and dust removal process are carried out to the front of described decorating board;
(17) be coated with attachment primer in the face-side roll of described decorating board, and carry out ultraviolet light polymerization, form priming paint face.
4. the manufacture method of ultraviolet curing chromatic zero diopter decorative panel as claimed in claim 1, it is characterized in that, described step (2) also comprises:
Carry out at least three times roller coat colored paints in the front of described decorating board, wherein, often all carry out ultraviolet light polymerization all over after roller coat colored paint.
5. the manufacture method of ultraviolet curing chromatic zero diopter decorative panel as claimed in claim 3, is characterized in that, the roller coat employing in described step (12) and described step (15) is just against the mode of roller roller coat.
6. the manufacture method of ultraviolet curing chromatic zero diopter decorative panel as claimed in claim 3, it is characterized in that, in described step (13), 240 order sand paper are adopted to carry out the process of washed ore light to the front of described decorating board, in described step (16), 400 order sand paper are adopted to sand flat seal coat on the front of described decorating board.
7. the manufacture method of the ultraviolet curing chromatic zero diopter decorative panel according to any one of claim 1-6, it is characterized in that, the time of carrying out ultraviolet light polymerization in each step is 3-10s, and ultraviolet light polymerization is 5 DEG C of-40 DEG C of normal temperature cures.
8. the manufacture method of the ultraviolet curing chromatic zero diopter decorative panel according to any one of claim 1-6, it is characterized in that, in each step, the thickness of roll coat enamel is 0.05-0.12mm.
9. the manufacture method of the ultraviolet curing chromatic zero diopter decorative panel according to any one of claim 1-6, it is characterized in that, described decorating board is gypsum plank.
10. according to the ultraviolet curing chromatic zero diopter decorative panel that the manufacture method according to any one of claim 1-9 manufactures.