CN104988310A - 一种应用磁场净化硫酸锌溶液中锗的方法 - Google Patents

一种应用磁场净化硫酸锌溶液中锗的方法 Download PDF

Info

Publication number
CN104988310A
CN104988310A CN201510456525.0A CN201510456525A CN104988310A CN 104988310 A CN104988310 A CN 104988310A CN 201510456525 A CN201510456525 A CN 201510456525A CN 104988310 A CN104988310 A CN 104988310A
Authority
CN
China
Prior art keywords
magnetic field
zinc sulfate
germanium
sulfate solution
solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510456525.0A
Other languages
English (en)
Other versions
CN104988310B (zh
Inventor
罗永光
张利波
彭金辉
孙成余
孙斯景
曲洪涛
谢庭芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yunnan Chihong International Germanium Industry Co ltd
Yunnan Chihong Zinc and Germanium Co Ltd
Original Assignee
Yunnan Chihong Zinc and Germanium Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Yunnan Chihong Zinc and Germanium Co Ltd filed Critical Yunnan Chihong Zinc and Germanium Co Ltd
Priority to CN201510456525.0A priority Critical patent/CN104988310B/zh
Publication of CN104988310A publication Critical patent/CN104988310A/zh
Application granted granted Critical
Publication of CN104988310B publication Critical patent/CN104988310B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种应用磁场净化硫酸锌溶液中锗的方法，属于冶金和化工领域。本方法采用下述步骤实现：1）将湿法锌冶金过程的中性浸出含锗0.08-2.0mg/L，温度为60-90℃，pH为4.5-5.4的硫酸锌溶液，通过磁场发生器；2）将含锗的硫酸锌溶液在磁砀发生器内停留30-60分钟；3)将磁场处理后的硫酸锌溶液进行液固分离，本发明中锗在硫酸锌溶液中是荷电胶体，在磁场作用下，带荷电的锗胶体定向移动并且凝聚成大颗粒物质，从而实现硫酸锌溶液中锗的净化，本发明中磁场发生器所用磁场为永磁磁场或电磁磁场，硫酸锌溶液中的锗在磁场作用下能够凝聚成大颗粒物质，对锗的除去效果好，作业时间短，无需要投入原料，生产成本低，人工劳动强度小。

Description

一种应用磁场净化硫酸锌溶液中锗的方法
技术领域
本发明涉及一种应用磁场净化硫酸锌溶液中锗的方法，属于冶金和化工领域。
背景技术
    在湿法锌冶金过程中，需要对溶液中的锗进行净化脱除，现有的公知方法是采用氢氧化铁吸附法和锌粉净化法，作业时间长、锌粉消耗高，整体生产成本高。
    因此，有必要对现有净化硫酸锌溶液中锗的方法进行改进，使得在净化过程中不引入新的杂质、净化方法简单且锗的净化率高。
发明内容
 为了克服上述现有技术的不足，本发明提供了一种应用磁场净化硫酸锌溶液中锗的方法，本发明中锗在硫酸锌溶液中是荷电胶体，在磁场作用下，带荷电的锗胶体定向移动并且凝聚成大颗粒物质，从而实现硫酸锌溶液中锗的净化。
为了达到上述目的，本发明提出如下技术方案：
    一种应用磁场净化硫酸锌溶液中锗的方法，该方法采用下述步骤实现：
    1）将湿法锌冶金过程的中性浸出含锗0.08-2.0mg/L，温度为60-90℃，pH为4.5-5.4的硫酸锌溶液，通过磁场发生器；
    2）将含锗的硫酸锌溶液在磁砀发生器内停留30-60分钟；
    3) 将磁场处理后的硫酸锌溶液进行液固分离。
    进一步，所述硫酸锌溶液的PH值为4.5-5.4，锗浓度为0.08-1.5mg/L。
    进一步，在步骤1）中，所述硫酸锌溶液进入磁场方式为间断或连续进入；所述硫酸锌溶液在磁场发生器内完成净化的方式为静置或流动停留净化。
    进一步，步骤2）中，所述的硫酸锌溶液在磁场发生器内进行净化。
    进一步，步骤2）中，磁场发生器内磁场强度5-1000T。
    进一步，步骤2）中，磁场发生器所用磁场为永磁磁场或电磁磁场。
本发明的有益效果：本发明中锗在硫酸锌溶液中是荷电胶体，在磁场作用下，带荷电的锗胶体定向移动并且凝聚成大颗粒物质，从而实现硫酸锌溶液中锗的净化，本发明中磁场发生器所用磁场为永磁磁场或电磁磁场，硫酸锌溶液中的锗在磁场作用下能够凝聚成大颗粒物质，对锗的除去效果好，作业时间短，无需要投入原料，生产成本低，人工劳动强度小。
附图说明
图1为硫酸锌溶液中有机物脱除的工艺示意图；
图2为永磁磁场净化示意图；
图3为电磁场净化示意图。
具体实施方式
如图1-3所示，下面将结合本发明的实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例，基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
    一种应用磁场净化硫酸锌溶液中锗的方法，该方法采用下述步骤实现：
    1）将湿法锌冶金过程的中性浸出含锗0.08-2.0mg/L，温度为60-90℃，pH为4.5-5.4的硫酸锌溶液，通过磁场发生器，磁场发生器内磁场强度5-1000T，磁场发生器所用磁场为永磁磁场或电磁磁场，硫酸锌溶液进入磁场方式为间断或连续进入；所述硫酸锌溶液在磁场发生器内完成净化的方式为静置或流动停留净化；
    2）将含锗的硫酸锌溶液在磁砀发生器内停留30-60分钟，硫酸锌溶液在磁场发生器内进行净化；
    3) 将磁场处理后的硫酸锌溶液进行液固分离。
实施例1
    将焙烧矿中性浸出pH为4.5，锗含量为0.08mg/L的500ml硫酸锌溶液静于永磁磁场强度为15T的磁场中，保持时间30分钟，测量得上清液Ge0.062mg/L。
实施例2
将焙烧矿中性浸出pH为5.0，锗含量为0.46mg/L的500ml硫酸锌溶液静于永磁磁场强度为300T的磁场中，保持时间50分钟，测量得上清液Ge0.07mg/L。
实施例3
    将焙烧矿中性浸出pH为5.4，锗含量为1.65mg/L的500ml硫酸锌溶液静于永磁磁场强度为800T的磁场中，保持时间60分钟，测量得上清液Ge0.064mg/L。
 本发明中锗在硫酸锌溶液中是荷电胶体，在磁场作用下，带荷电的锗胶体定向移动并且凝聚成大颗粒物质，从而实现硫酸锌溶液中锗的净化，本发明中磁场发生器所用磁场为永磁磁场或电磁磁场，硫酸锌溶液中的锗在磁场作用下能够凝聚成大颗粒物质，对锗的除去效果好，作业时间短，无需要投入原料，生产成本低，人工劳动强度小。
以上对本发明实施例所提供的一种应用磁场净化硫酸锌溶液中锗的方法进行了详细介绍，本文中应用了具体个例对本发明的原理及实施方式进行了阐述，以上实施例的说明只是用于帮助理解本发明的方法及其核心思想；同时，对于本领域的一般技术人员，依据本发明的思想，在具体实施方式及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (6)

1.一种应用磁场净化硫酸锌溶液中锗的方法，其特征在于：该方法采用下述步骤实现：
   1）将湿法锌冶金过程的中性浸出含锗0.08-2.0mg/L，温度为60-90℃，pH为4.5-5.4的硫酸锌溶液，通过磁场发生器；
   2）将含锗的硫酸锌溶液在磁砀发生器内停留30-60分钟；
   3) 将磁场处理后的硫酸锌溶液进行液固分离。
2.根据权利要求1所述的一种应用磁场净化硫酸锌溶液中锗的方法，其特征在于：所述硫酸锌溶液的pH值为4.5-5.4，锗浓度为0.08-1.5mg/L。
3.根据权利要求1所述的一种应用磁场净化硫酸锌溶液中锗的方法，其特征在于：步骤1）中，所述硫酸锌溶液进入磁场方式为间断或连续进入；所述硫酸锌溶液在磁场发生器内完成净化的方式为静置或流动停留净化。
4.根据权利要求1所述的一种应用磁场净化硫酸锌溶液中锗的方法，其特征在于：步骤2）中，所述的硫酸锌溶液在磁场发生器内进行净化。
5.根据权利要求1所述的一种应用磁场净化硫酸锌溶液中锗的方法，其特征在于：步骤2）中，磁场发生器内磁场强度5-1000T。
6.根据权利要求1所述的一种应用磁场净化硫酸锌溶液中锗的方法，其特征在于：步骤2）中，磁场发生器所用磁场为永磁磁场或电磁磁场。
CN201510456525.0A 2015-07-30 2015-07-30 一种应用磁场净化硫酸锌溶液中锗的方法 Active CN104988310B (zh)