CN104975290A - Processing process for gilding plate - Google Patents
Processing process for gilding plate Download PDFInfo
- Publication number
- CN104975290A CN104975290A CN201410832284.0A CN201410832284A CN104975290A CN 104975290 A CN104975290 A CN 104975290A CN 201410832284 A CN201410832284 A CN 201410832284A CN 104975290 A CN104975290 A CN 104975290A
- Authority
- CN
- China
- Prior art keywords
- plate
- gold
- decorated
- sheet material
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing process for a gilding plate. The processing process comprises the following specific steps: selecting a plate raw material and carrying out tape rolling on the plate raw material by a reeling and unreeling machine; carrying out checkered plate rolling on the whole coil of the tape-coiled plate; carrying out leaching and oil removal on the tape-coiled plate; carrying out roller coating on the surface of the plate by gilding paint, and roasting the plate for 3-5 minutes in a high-temperature cabinet of 800-900 DEG C, wherein the thickness of the gilding paint layer is 10-20 microns; carrying out film laminating on the surface of the gilding plate paint layer of the plate by an automatic film laminating machine; and carrying out leveling and straightening on the film-laminated plate, wherein the plate raw material is an iron plate, a stainless steel plate, a galvanized plate or other metal plates. The processing process disclosed by the invention is simple in process, good in effect, wide in range of application and capable of carrying out gliding processing on plates of different materials to achieve effects of dazzling and durability, so that the technical problems of a gliding process in industries such as decoration, arts and crafts, sign-board couplets and the like are solved, and therefore, the processing process has an extensive practical value and market competitive capacity.
Description
Technical field
The present invention relates to a kind of gilding technology, specifically a kind of complete processing of gold-decorated plate.
Background technology
Gold-decorated is the conventional metals decoration technology namely produced from Pre-Qin Times, is a kind of traditional way, so far still among the people popular, gold-plated or mercury is gold-plated also known as fire.All rather popular after the Eastern Zhou Dynasty and Han dynasty, be one of the most commendable at that time bronze, brass or copper ware surface decoration tech, be successively called that gold painting, golden yellow painting, gold paintings, oil gidling, gold-plated, the Song dynasty title that begins is gold-decorated.
Make a general survey of tourist attraction through the ages, those gold-decorated flying dragons in palace temple, public house, teahouse walk phoenix, gold-decorated Bodhisattva arhat, the gold-decorated board couplet written on scrolls and hung on the pillars of a hall etc., although broad air, splendid, but complex process, expensive after all, ordinary people all can not consumed, and has modern age people to carry out gold-decorated at bronze, brass or copper ware or ceramic watch body, but its material requires high, and the scope of application is little.
Summary of the invention
The object of the present invention is to provide a kind of applied widely, complete processing that material requires low gold-decorated plate, to solve the problem proposed in above-mentioned background technology.
For achieving the above object, the invention provides following technical scheme:
A complete processing for gold-decorated plate, concrete steps are as follows:
(1) choose sheet material raw material, and with unwinding and rewinding machine, sheet material raw material is carried out winding process and obtain winding sheet material;
(2) winding sheet material entire volume is carried out the process of cotton ginning card;
(3) carry out pouring to winding sheet material to deoil, remove the formation protection that plate surface is coated with;
(4) carry out roller coating with gold-decorated coating on the surface of sheet material, then make sheet material be the high-temperature cabinet baking 3-5min of 800-900 DEG C through excess temperature, make gold-decorated coating solidification at plate surface, the thickness of gold-decorated dope layer is 10-20um;
(5) carry out pad pasting process with the surface of automatic film applicator to the gold-decorated dope layer of sheet material thus gold-decorated dope layer is protected;
(6) leveling alignment is carried out to the sheet material after pad pasting, place with the rolling of unwinding and rewinding machine or be split into dull and stereotyped placement;
(7) quality examination is carried out, qualified rear check and accepting storing.
As the further scheme of the present invention: described sheet material raw material is iron plate, stainless steel plate, galvanized sheet or other sheet metals.
As the further scheme of the present invention: described gold-decorated coating comprises according to the raw material of weight part: coating 93.5-99 part, copper powder 6-15 part, bronze 0.5-10 part.
As the present invention's further scheme: described coating is aqueous paint, resin paint or transparent gloss oil.
Compared with prior art, the invention has the beneficial effects as follows:
Present invention process is simple, effective, applied widely, gold-decorated process can be carried out on the sheet material of unlike material, reach bright and glittering and long-lived effect, solve the technical barriers of industry on gilding technology such as decoration, industrial art and the making of the signboard couplet written on scrolls and hung on the pillars of a hall, there is practical value and the market competitiveness widely.
Embodiment
Be described in more detail below in conjunction with the technical scheme of embodiment to this patent.
Embodiment 1
In the embodiment of the present invention, a kind of complete processing of gold-decorated plate, concrete steps are as follows:
(1) choose iron plate, stainless steel plate, galvanized sheet be sheet material raw material, and with unwinding and rewinding machine, sheet material raw material is carried out winding process and obtain winding sheet material;
(2) winding sheet material entire volume is carried out the process of cotton ginning card;
(3) carry out pouring to winding sheet material to deoil, remove the formation protection that plate surface is coated with;
(4) carry out roller coating with gold-decorated coating on the surface of sheet material, then make sheet material be the high-temperature cabinet baking 3min of 800 DEG C through excess temperature, make gold-decorated coating solidification at plate surface, the thickness of gold-decorated dope layer is 10um; Described gold-decorated coating comprises according to the raw material of weight percent: aqueous paint 93.5 parts, copper powder 6 parts, bronze 0.5 part;
(5) carry out pad pasting process with the surface of automatic film applicator to the gold-decorated dope layer of sheet material thus gold-decorated dope layer is protected;
(6) leveling alignment is carried out to the sheet material after pad pasting, place with the rolling of unwinding and rewinding machine or be split into dull and stereotyped placement;
(7) quality examination is carried out, qualified rear check and accepting storing.
Embodiment 2
In the embodiment of the present invention, a kind of complete processing of gold-decorated plate, concrete steps are as follows:
(1) choose iron plate, stainless steel plate, galvanized sheet be sheet material raw material, and with unwinding and rewinding machine, sheet material raw material is carried out winding process and obtain winding sheet material;
(2) winding sheet material entire volume is carried out the process of cotton ginning card;
(3) carry out pouring to winding sheet material to deoil, remove the formation protection that plate surface is coated with;
(4) carry out roller coating with gold-decorated coating on the surface of sheet material, then make sheet material be the high-temperature cabinet baking 3.5min of 820 DEG C through excess temperature, make gold-decorated coating solidification at plate surface, the thickness of gold-decorated dope layer is 12um; Described gold-decorated coating comprises according to the raw material of weight percent: aqueous paint 95 parts, copper powder 8 parts, bronze 3 parts;
(5) carry out pad pasting process with the surface of automatic film applicator to the gold-decorated dope layer of sheet material thus gold-decorated dope layer is protected;
(6) leveling alignment is carried out to the sheet material after pad pasting, place with the rolling of unwinding and rewinding machine or be split into dull and stereotyped placement;
(7) quality examination is carried out, qualified rear check and accepting storing.
Embodiment 3
In the embodiment of the present invention, a kind of complete processing of gold-decorated plate, concrete steps are as follows:
(1) choose iron plate, stainless steel plate, galvanized sheet be sheet material raw material, and with unwinding and rewinding machine, sheet material raw material is carried out winding process and obtain winding sheet material;
(2) winding sheet material entire volume is carried out the process of cotton ginning card;
(3) carry out pouring to winding sheet material to deoil, remove the formation protection that plate surface is coated with;
(4) carry out roller coating with gold-decorated coating on the surface of sheet material, then make sheet material be the high-temperature cabinet baking 4min of 850 DEG C through excess temperature, make gold-decorated coating solidification at plate surface, the thickness of gold-decorated dope layer is 15um; Described gold-decorated coating comprises according to the raw material of weight percent: resin paint 96 parts, copper powder 10 parts, bronze 5 parts;
(5) carry out pad pasting process with the surface of automatic film applicator to the gold-decorated dope layer of sheet material thus gold-decorated dope layer is protected;
(6) leveling alignment is carried out to the sheet material after pad pasting, place with the rolling of unwinding and rewinding machine or be split into dull and stereotyped placement;
(7) quality examination is carried out, qualified rear check and accepting storing.
Embodiment 4
In the embodiment of the present invention, a kind of complete processing of gold-decorated plate, concrete steps are as follows:
(1) choose iron plate, stainless steel plate, galvanized sheet be sheet material raw material, and with unwinding and rewinding machine, sheet material raw material is carried out winding process and obtain winding sheet material;
(2) winding sheet material entire volume is carried out the process of cotton ginning card;
(3) carry out pouring to winding sheet material to deoil, remove the formation protection that plate surface is coated with;
(4) carry out roller coating with gold-decorated coating on the surface of sheet material, then make sheet material be the high-temperature cabinet baking 4.5min of 880 DEG C through excess temperature, make gold-decorated coating solidification at plate surface, the thickness of gold-decorated dope layer is 18um; Described gold-decorated coating comprises according to the raw material of weight percent: resin paint 98 parts, copper powder 12 parts, bronze 8 parts;
(5) carry out pad pasting process with the surface of automatic film applicator to the gold-decorated dope layer of sheet material thus gold-decorated dope layer is protected;
(6) leveling alignment is carried out to the sheet material after pad pasting, place with the rolling of unwinding and rewinding machine or be split into dull and stereotyped placement;
(7) quality examination is carried out, qualified rear check and accepting storing.
Embodiment 5
In the embodiment of the present invention, a kind of complete processing of gold-decorated plate, concrete steps are as follows:
(1) choose iron plate, stainless steel plate, galvanized sheet be sheet material raw material, and with unwinding and rewinding machine, sheet material raw material is carried out winding process and obtain winding sheet material;
(2) winding sheet material entire volume is carried out the process of cotton ginning card;
(3) carry out pouring to winding sheet material to deoil, remove the formation protection that plate surface is coated with;
(4) carry out roller coating with gold-decorated coating on the surface of sheet material, then make sheet material be the high-temperature cabinet baking 5min of 900 DEG C through excess temperature, make gold-decorated coating solidification at plate surface, the thickness of gold-decorated dope layer is 20um; Described gold-decorated coating comprises according to the raw material of weight percent: transparent gloss oil 99 parts, copper powder 15 parts, bronze 10 parts;
(5) carry out pad pasting process with the surface of automatic film applicator to the gold-decorated dope layer of sheet material thus gold-decorated dope layer is protected;
(6) leveling alignment is carried out to the sheet material after pad pasting, place with the rolling of unwinding and rewinding machine or be split into dull and stereotyped placement;
(7) quality examination is carried out, qualified rear check and accepting storing.
Present invention process is simple, effective, applied widely, gold-decorated process can be carried out on the sheet material of unlike material, reach bright and glittering and long-lived effect, solve the technical barriers of industry on gilding technology such as decoration, industrial art and the making of the signboard couplet written on scrolls and hung on the pillars of a hall, there is practical value and the market competitiveness widely.
Above the better embodiment of this patent is explained in detail, but this patent is not limited to above-mentioned embodiment, in the ken that one skilled in the relevant art possesses, various change can also be made under the prerequisite not departing from this patent aim.
Claims (4)
1. a complete processing for gold-decorated plate, is characterized in that, concrete steps are as follows:
(1) choose sheet material raw material, and with unwinding and rewinding machine, sheet material raw material is carried out winding process and obtain winding sheet material;
(2) winding sheet material entire volume is carried out the process of cotton ginning card;
(3) carry out pouring to winding sheet material to deoil, remove the formation protection that plate surface is coated with;
(4) after roller coating is carried out on the surface of sheet material, make sheet material toast 3-5min through the high-temperature cabinet that excess temperature is 800-900 DEG C with gold-decorated coating, make gold-decorated coating solidification at plate surface, the thickness of gold-decorated dope layer is 10-20um;
(5) carry out pad pasting process with the surface of automatic film applicator to the gold-decorated dope layer of sheet material thus gold-decorated dope layer is protected;
(6) leveling alignment is carried out to the sheet material after pad pasting, place with the rolling of unwinding and rewinding machine or be split into dull and stereotyped placement;
(7) quality examination is carried out, qualified rear check and accepting storing.
2. the complete processing of gold-decorated plate according to claim 1, is characterized in that, described sheet material raw material is iron plate, stainless steel plate, galvanized sheet or other sheet metals.
3. the complete processing of gold-decorated plate according to claim 1, is characterized in that, described gold-decorated coating comprises according to the raw material of weight part: coating 93.5-99 part, copper powder 6-15 part, bronze 0.5-10 part.
4. the complete processing of gold-decorated plate according to claim 3, is characterized in that, described coating is aqueous paint, resin paint or transparent gloss oil.