CN205989538U - A kind of chromatic pattern metal floor for decoration - Google Patents
A kind of chromatic pattern metal floor for decoration Download PDFInfo
- Publication number
- CN205989538U CN205989538U CN201620774120.1U CN201620774120U CN205989538U CN 205989538 U CN205989538 U CN 205989538U CN 201620774120 U CN201620774120 U CN 201620774120U CN 205989538 U CN205989538 U CN 205989538U
- Authority
- CN
- China
- Prior art keywords
- layer
- decoration
- floor
- pattern
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
This utility model discloses a kind of chromatic pattern metal floor for decoration; described color metal decorative pattern floor is color metal decorative pattern " floor plaster " product for decoration, and metal floor is followed successively by protecting film, wearing layer, printed decoration layer, metal substrate layer, Performance of Pressure Sensitive Adhesive layer and organosilicon protection sheet from top to bottom.Protecting film is PVC protection glued membrane, and the lower surface of metal substrate layer is bonded with Performance of Pressure Sensitive Adhesive layer, and the lower surface of Performance of Pressure Sensitive Adhesive layer is organosilicon protection sheet.Described wearing layer is application Al on printed decoration layer for the heat cure2O3（Or SiO2）Wear-resistant protection coating, or Al on printed decoration layer for the high-temperature bearing fusion2O3Dipping abrasion-proof paper protective layer.After described floor plaster is installed, gross thickness gross thickness is only 100～2000 μm.Have wear-and corrosion-resistant, damp-proof and moth-proof, be not afraid of humidity, be not afraid of into water, will not deform, will not go mouldy, anti-microbial property good, simple and fast of constructing, fire prevention is nontoxic, and the advantages of low price.
Description
Technical field
This utility model is related to a kind of chromatic pattern metal floor for decoration, belongs to decorating and renovating material technical field.
Background technology
20 end of the centurys so far, with the fast development of real estate industry of China, various floor China with fast development it
Gesture obtains spread, and indoor floor is conducive to sound-insulating and heat-insulating, improves finishing class and office comfort level of living.City at present
On face, mainly there are wood floors and a plastic floor in popular floor, wherein wood floors possess class height, environmental protection, wear-resisting, anti-corrosion,
The advantages of mothproof, easy maintenance is arranged, weak point is：Use for a long time that moisture effect is poor, yielding after immersion go bad, flameproof effect
Difference, price is relatively expensive；Plastic floor advantage is wear-resisting, easy to clean, water proofing property are good, maintenance is easy, construction is easy and quick, valency
Lattice are cheap, and it is convenient to change after abrasion, and its weak point is：Resistance to elevated temperatures is poor, and fire protecting performance is poor, has severe toxicity volatilization after catching fire
Thing, is chronically in wet environment change of also impaired concurrently mildewing, and anti-microbial property is poor.
Utility model patent《A kind of Sound insulation flooringses》(CN201520540310) it is including floor base material layer and compound its
Its multilayer material, for the purpose of sound insulation, above floor base material layer, the metal film layer Main Function of setting is isolation sound, and gold
Belong to and be additionally provided with sound absorbing layer and architectural surface on face, described sound absorbing layer is the extremely soft foaming layer of poly- ammonia ", therefore this floor belongs to shelves
Secondary higher plastic floor species；Utility model patent《Environment-friendly type abrasive floor》(CN201520711570) include being attached at ground
The metal pad pasting layer being provided with rollet of plate surface, is provided with fluorescent material and silica gel filler, pad pasting layer in described rollet
Bottom surface be provided with gluing oxidant layer.From its structure, the metallic diaphragm positioned at top layer is directly contacted with the external world, though groove is anti-skidding,
But because metal film layer surface is not provided with any wear-resistant material layer, therefore this metallic diaphragm is easy to wear, another aspect metallic diaphragm
Though surface is machined with rollet, when there is accumulated water on surface, or air pressure and indoor and outdoor temperature difference change cause cross-ventilation
When, water membrane can be adhered in these rollet surfaces, therefore prevents that wet and slippery effect is very limited, or even can mislead user loosening
Vigilant；Utility model patent《Multifunctional floor film》(CN201520295928) floor film disclosed in, functional layer includes：Receive
Rice AgCuZn alloy layer, magnetic plastic layer, PVC foam material substrate.Weak point is：Nano silver copper zinc alloy layer for its
The antibacterial of directly contact has certain killing effect, but to covering the antibacterial on the antibacterial corpse that the first layer surface is died, does not just have
Have any effect, ground surface is often rubbish and a lot of place of antibacterial, the setting of this film layer can with the use on this floor,
Substantially do not have any effect, simply a conception of species；On the other hand, described basic unit is PVC foam material, therefore floor
Design is thicker.
In view of the problems referred to above of existing floor material have good wear-resisting, anti-wet and slippery, anti-quarter it is necessary to design is a kind of
Draw, anti-soil and fire protecting performance, good decorating effect and extremely cheap, current wood ground can be substituted in some beta sites
Plate or a kind of top grade floor decorative material of plastic floor.
Content of the invention
The purpose of this utility model is the problem proposing for background technology, overcomes existing timber floor or plastic floor etc. to lack
Point, a kind of chromatic pattern metal floor for decoration of design.
In order to achieve the above object, this utility model adopts below scheme：
A kind of chromatic pattern metal floor for decoration, is for decoration " floor plaster " with color metal decorative pattern system
Product, described metal floor is followed successively by five-layer structure from top to bottom, including：Protecting film 1, the wearing layer 2 setting thickness, setting thickness
Printed decoration layer 3, metal substrate layer 4, Performance of Pressure Sensitive Adhesive layer 5, organosilicon protection sheet 6；Wherein：Protecting film 1 and organosilicon are protected
Shield paper 6 is temporary protective layer, and wearing layer 2, printed decoration layer 3, metal substrate layer 4 and Performance of Pressure Sensitive Adhesive layer 5 are basic functions
Layer；Described protecting film 1 is PVC protection glued membrane；The lower surface of described metal substrate layer 4 and Performance of Pressure Sensitive Adhesive layer 5 bond；Described pressure
The lower surface of quick glue adhesive linkage 5 is organosilicon protection sheet 6；It is characterized in that：
Described wearing layer 2 is application Al on printed decoration layer 3 for the heat cure2O3, or SiO2Wear-resistant protection applies
Layer, or Al on printed decoration layer 3 for the high-temperature bearing fusion2O3Dipping abrasion-proof paper protective layer；
Preferably：When wearing layer 2 adopts Al2O3During dipping abrasion-proof paper protective layer, described PVC protection glued membrane is nonessential setting
Put.
As mentioned above a kind of for decoration chromatic pattern metal floor it is characterised in that：The thickness of described wearing layer 2 is
10～1000 μm.
As mentioned above a kind of for decoration chromatic pattern metal floor it is characterised in that：Described printed decoration layer 3
Thickness is 10～1000 μm, and the pattern of printed decoration layer 3 includes：Wood-grain-imitating pattern, marble grain pattern, carpet stricture of vagina pattern,
Granite pattern；Or printed out with anaglyph pattern in metal substrate layer 4 upper surface with foam ink.
As mentioned above a kind of for decoration chromatic pattern metal floor it is characterised in that：The material of described metal substrate layer 4
Matter includes：Rustless steel or aluminium alloy, tin alloy, copper alloy；The thickness of described metal substrate layer 4 is set as 0.01～1.5mm；Gold
Belong to substrate layer 4 upper surface be：Minute surface or dull surface, sand face, mill stricture of vagina or patterned surface；Described metal substrate layer 4 includes：Metal
Paper tinsel, metallic plate or winding.
As mentioned above a kind of for decoration chromatic pattern metal floor it is characterised in that：Described Performance of Pressure Sensitive Adhesive layer 5
Thickness is 100～1000 μm.
As mentioned above a kind of for decoration chromatic pattern metal floor it is characterised in that：Described basic training ergosphere total
Thickness is 100～2000 μm.
A kind of manufacture method of the chromatic pattern metal floor for decoration is carried out as follows as mentioned above：
Step one：The hydroxylating of metal base upper surface and microporous
By thickness be 0.01～1.5mm rustless steel or aluminium alloy or tin alloy or copper alloy foil (plate) or winding class
Metal base, goes to degrease, cleans up, and is then placed on and is respectively containing chemical composition and concentration：
CrO3(5～250g/l) and H2SO4In the chemical oxidation solution of (5～490g/l), or
HNO3(5～250g/l) and H2O2In the chemical oxidation solution of (5～250g/l), or
In the chemical solution of NaOH (1～100g/l), or (NH4)2Mo2O7And H2SO4The chemical oxygen of (5～250g/l)
Change in solution, carry out chemical treatment, form oh group and (or) oxide-film and a large amount of corrosion in described metallic substrate surface
Micropore；
Step 2：Printed decoration layer
By way of the continuous offset printing of drum-type, or trans-printing mode, the metal base handled well in step one
Upper surface print one layer of decorative coating, or print one layer of decorations coating with anaglyph with foam ink；Institute
The pattern stating decoration figure layer arbitrarily sets on demand；
Step 3：Coating surface wearing layer
The abrasion-resistant clear coat of one layer strong with basal body binding force of coating, thick coating on the printed decoration layer that step 2 completes
Degree is set as 10～1200 μm, and the component of described clear coat includes：Macromolecular material and inserts, described macromolecular material is
Piano lacquer or polyurethane or tripolycyanamide or melamine resin；Described inserts are nanometer Al2O3Or Nano-meter SiO_22；
Again coating is heating and curing, forms robust surface wear-resistant layer；
Described wear resistant transparent paint or antiwear epoxy resin paint；
Step 4：Protection is processed
Complete to print after wearing layer by step 3, roll the PVC glued membrane pasting last layer protectiveness in wearing layer upper surface；
Its advantage is：PVC glued membrane is conducive to protecting wearing layer upper surface in transport or sales process.
Step 5：The metal base back side arranges adhesivess
In metal base lower surface application (or stickup) last layer pressure sensitive adhesive；Its advantage is：Convenient construction,
This utility model product is installed：During color metal decorative pattern floor, can after the wipe clean of ground directly lay this color metal
Decorative pattern floor, then rolls with cylinder, and construction is simple and quick.In addition, this pressure sensitive adhesive in use with
Personnel walk about, and adhesive effect can be become better and better, and so can avoid the slip on floor.
Step 6：Back-protective is processed
In the lower surface of step 5 bonding pressure sensitive adhesive, by way of rolling, press one layer of organosilicon protection sheet.Its beneficial effect
It is really：Convenient construction：As long as this layer of paper is torn and floor described in the utility model can be bonded in ground surface；In addition there is this layer
Protection sheet is also convenient for sale, transport and the keeping of described flooring product, prevents pressure sensitive adhesive from arbitrarily bonding to elsewhere.
When wear-resistant protective layer adopts Al2O3When dipping abrasion-proof paper high-temperature bearing merges on printed decoration layer 3, described making
Method is carried out as follows：
Step one：The hydroxylating of metal base upper surface and microporous
By thickness be 0.01～1.5mm rustless steel or aluminium alloy or tin alloy or copper alloy foil (plate) or winding class
Metal base, goes to degrease, cleans up, and is then placed on and is respectively containing chemical composition and concentration：
CrO3(5～250g/l) and H2SO4In the chemical oxidation solution of (5～490g/l), or
HNO3(5～250g/l) and H2O2In the chemical oxidation solution of (5～250g/l), or
In the chemical solution of NaOH (1～100g/l), or (NH4)2Mo2O7And H2SO4The chemical oxygen of (5～250g/l)
Change in solution, carry out chemical treatment, form oh group and (or) oxide-film and a large amount of corrosion in described metallic substrate surface
Micropore；
Step 2：Printed decoration layer
By way of the continuous offset printing of drum-type, or trans-printing mode, the metal base handled well in step one
Upper surface print one layer of decorative coating, or print one layer of decorations coating with anaglyph with foam ink；Institute
The pattern stating decoration figure layer arbitrarily sets on demand；
Step 3：In printed decoration layer surface, Al is set2O3Dipping abrasion-proof paper protective layer
On the printed decoration layer that step 2 completes, by high-temperature bearing amalgamation mode, merge one layer of Al2O3Dipping is wear-resisting
Paper；Its advantage is：Strengthen ostentatious wear-resisting, the anti-delineation of colored printing, antifouling property.
Step 4：The metal base back side arranges adhesivess
In metal base lower surface application (or stickup) last layer pressure sensitive adhesive；Its advantage is：Convenient construction,
This utility model product is installed：During color metal decorative pattern floor, can after the wipe clean of ground directly lay this color metal
Decorative pattern floor, then rolls with cylinder, and construction is simple and quick.In addition, this pressure sensitive adhesive in use with
Personnel walk about, and adhesive effect can be become better and better, and so can avoid the slip on floor.
Step 5：Back-protective is processed
In the lower surface of step 5 bonding pressure sensitive adhesive, by way of rolling, press one layer of organosilicon protection sheet.Its beneficial effect
It is really：Convenient construction：As long as this layer of paper is torn and floor described in the utility model can be bonded in ground surface；In addition there is this layer
Protection sheet is also convenient for sale, transport and the keeping of described flooring product, prevents pressure sensitive adhesive from arbitrarily bonding to elsewhere.
The beneficial effects of the utility model are：
(1) a kind of chromatic pattern metal floor for decoration of this utility model has：Wear-resisting, anti-corrosion, moistureproof, mothproof, no
Be afraid of moist, be not afraid of into water, will not deform, will not go mouldy, the features such as anti-microbial property is good.
(2) construction simple and fast, using more, better with ground adhesive effect.
(3) fire prevention, nontoxic, even if running into fire, will not burn, will not endanger people's life security, have timber floor and moulding
The incomparable advantage of adhesive floor.
(4) ratio timber floor environmental protection, can greatly save the forest reserves, have the social meaning being highly profitable.
(5) low price, this metal chromatic pattern floor (such as can use 0.03mm thick with very thin metal base
304 rustless steel winding) make, its cost price can low to several yuans of every square meter, this price advantage can make this reality
The color metal decorative pattern flooring products being provided with novel method are in megastore, public place of entertainment, beta site, emergency dwelling etc.
The decorative applications of ground surface are promoted rapidly.
Brief description
Fig. 1 is a kind of chromatic pattern metal floor schematic diagram for decoration of this utility model embodiment.
Description of symbols in accompanying drawing：1 protecting film, 2 wearing layers, 3 printed decoration layers, 4 metal substrate layer, 5 pressures
Quick glue adhesive linkage, 6 organosilicon protection sheets.
Specific embodiment
Below in conjunction with accompanying drawing, this utility model embodiment is described further, for making the purpose of this utility model, technology
Scheme and advantage are clearer, below technical scheme in this utility model be clearly and completely described it is clear that described
Embodiment be a part of embodiment of this utility model, rather than whole embodiment.Based on the embodiment in this utility model,
The every other embodiment that those of ordinary skill in the art are obtained under the premise of not making creative work, broadly falls into this reality
With novel protected scope.
Refer to the attached drawing 1, a kind of chromatic pattern metal floor for decoration of this utility model includes dividing successively from top to bottom
Cloth：Protecting film 1, the wearing layer 2 setting thickness, the printed decoration layer 3 setting thickness, metal substrate layer 4, Performance of Pressure Sensitive Adhesive layer
5th, organosilicon protection sheet 6；Wherein：Protecting film 1 and organosilicon protection sheet 6 are temporary protective layers, wearing layer 2, printed decoration layer
3rd, metal substrate layer 4 and Performance of Pressure Sensitive Adhesive layer 5 are basic training ergospheres；Described protecting film 1 is PVC protection glued membrane；Described Metal Substrate
The lower surface of material layer 4 is bonded with Performance of Pressure Sensitive Adhesive layer 5；The lower surface of described Performance of Pressure Sensitive Adhesive layer 5 is organosilicon protection sheet 6；Institute
Stating wearing layer 2 is application Al on printed decoration layer 3 for the heat cure2O3(or SiO2) wear-resistant protection coating, or high temperature holds
Pressure merges the Al on printed decoration layer 32O3Dipping abrasion-proof paper protective layer.When wearing layer 2 adopts Al2O3Dipping abrasion-proof paper protection
During layer, described PVC protection glued membrane can be arranged.
The thickness of described wearing layer 2 is 10～1000 μm, and the thickness of described printed decoration layer 3 is 10～1000 μm, institute
The thickness stating metal substrate layer 4 is 0.01～1.5mm, and the thickness of described Performance of Pressure Sensitive Adhesive layer 5 is 100～1000 μm, described base
The gross thickness of this functional layer is 100～2000 μm.
The pattern of printed decoration layer 3 includes：Wood-grain-imitating pattern, marble grain pattern, carpet stricture of vagina pattern, granite figure
Case；Or other patterns true to nature imitating natural material, or any pattern that user likes, can also be and existed with foam ink
Metal substrate layer 4 upper surface prints out with anaglyph pattern.
The material of described metal substrate layer 4 sets and includes：Rustless steel or aluminium alloy, tin alloy, copper alloy；Metal substrate layer
4 upper surface is：Minute surface or dull surface, sand face, mill stricture of vagina or patterned surface；The apparent shape of metal substrate layer 4 is metal forming (plate)
Or coiled strip.
The manufacture method of the above-mentioned chromatic pattern metal floor for decoration, by different embodiments, is respectively described below：
Embodiment one：
Choose 304 thick rustless steel winding of 0.1mm as base material, early stage pretreatment oil removing cleaning, drying.
Step one：Substrate surface hydroxylating and microporous
The stainless steel substrate after above-mentioned process is clean, it is placed on and is respectively containing chemical composition and concentration：CrO3
(50g/l) and H2SO4(100g/l) in chemical oxidation solution, chemical oxidation 10min in 85 DEG C of environment of temperature, above-mentioned not
Rust steel material surface forms oh group and porous oxide film, bonding with printing layer thereon and its in order to greatly enhance base material
The adhesion of layer material.
Step 2：Printed decoration layer
In the unilateral upper table of have passed through the stainless steel substrate that step one is handled well one by way of the continuous offset printing of drum-type
One layer of Wood-grain-imitating patterned layer is printed in face (front), is dried by the requirement of ink used.
Step 3：Coating surface wear-resistant protection coating
In order to strengthen ostentatious wear-resisting, the anti-delineation of above-mentioned colored printing, antifouling property, first in above-mentioned combination with decorative surfaces
One layer of abrasion-resistant clear coat very strong with basal body binding force of upper coating, the thickness of this coating is about 500 μm, the one-tenth of this clear dope
Divide and include：Macromolecular material melamine resin and inserts nano-scale alumina.Then, require according to coating, carry out thermosetting
Change, form robust surface abrasion resistance protective layer.Above-mentioned wear resistant transparent paint make method manufacture method and coating, solidification
Method is as follows：
(1) the preparation of melamine-formaldehyde resin adhesive, raw material and formula (mol ratio) set：
Tripolycyanamide: formaldehyde: polyvinyl alcohol: methanol=1: 3: 0.05: 6
First methanol and polyvinyl alcohol are added in reactor by setting mol amount, be warming up to 75 DEG C, be incubated complete to polyvinyl alcohol
CL, is subsequently adding the formaldehyde measuring, the sodium hydroxide solution tune pH value being 30% with concentration to 9.5, and addition measures
Tripolycyanamide, react that (measurement of the general amine-formaldehyde resins reaction end of trimerization refers to than number to water under 89～91 DEG C of environment
Mark, GB/T14732-93) it is 1:When 2.5 be terminal, be cooled to 35 DEG C standby.
(2) divide by above-mentioned solid：Tripolycyanamide: Al2O3=1: 2 ratio, by way of ultrasonic disperse, by Al2O3All
In the even melamine-formaldehyde resin adhesive solution being dispersed in step (1), as wear resistant transparent paint used by this utility model, this painting
Material is a kind of suspension, Extemporaneous only in application.
(3), by above-mentioned (2) ready wear resistant transparent paint, it is placed in a circulation stirring groove, by continuous roll coating model,
Printed decoration layer surface coatings to step 2.This step contain coating container be a circulation stirring groove it is therefore an objective to
In order to prevent Al2O3Precipitation.
(4) the rustless steel winding of coated wear resistant transparent paint is put in oven, temperature is carried out at being 138～142 DEG C
Dry solidification.
In order to both ensure the Al in above-mentioned wear-resistant paint2O3Granule does not deposit, and uniformly divides again in suspension system
Dissipate, do not condense, the clear dope used by this utility model can be developed using commercially available Tai Er (Dynea) chemical company
Appropriate, the special melmac of viscosity.
Step 4：Protection is processed
Semi-finished product front surface roll-in after processing through above-mentioned steps one, step 2 and step 3 for the metal base is pasted
Last layer PVC adhesive tape protects glued membrane.
Step 5：Substrate backside arranges adhesivess
Metal base be have passed through the semi-finished product after above-mentioned steps one～step 4 is processed and climb over face, on other side surface
One layer of commercially available pressure sensitive adhesive of (back side) application.
Step 6：Back-protective is processed
Above-mentioned metal base have passed through above-mentioned steps one to step 5 process, being provided with the one side of pressure sensitive adhesive, then leads to
Cross the mode of rolling, press one layer of organosilicon protection sheet.
After above-mentioned six steps, color metal decorative pattern floor described in the utility model completes.
Embodiment two：
Choose the thick aluminium alloy winding of 0.2mm as base material, front its gives process oil removing, cleans and dry.
Step one：Substrate surface hydroxylating and microporous
The aluminum alloy base material after above-mentioned process is clean, it is placed on and is respectively containing chemical composition and concentration：NaOH
(30g/l) in chemical solution, chemical attack 1min under temperature 60 C environment, form hydroxyl in above-mentioned aluminum alloy material surface
Group and porous membrane layer, in order to greatly enhance the adhesion of base material and printing layer thereon and its lower bonding layer material.
Step 2：Printed decoration layer
Unilateral in have passed through the above-mentioned aluminum alloy base material after step one is processed one by way of the continuous offset printing of drum-type
One layer of Wood-grain-imitating patterned layer is printed on surface (front), then is dried by the requirement of ink used.
Step 3：Coating surface wear-resistant protection coating
In order to strengthen ostentatious wear-resisting, the anti-delineation of above-mentioned colored printing, antifouling property, first in above-mentioned combination with decorative surfaces
One layer of abrasion-resistant clear coat very strong with basal body binding force of upper coating, the thickness of this coating is about 500 μm, this wear resistant transparent paint
For commercial polyurethane wear-resistant paint, the coating of described wear resistant transparent paint, curing are as follows：
(1) upper above-mentioned coating is placed in a circulation stirring groove, by continuous roll coating model, coatings to step
Two printed decoration layer surface.
(2) the aluminium alloy winding of coated wear resistant transparent paint is in oven, according to consolidating of commercial polyurethane wear-resistant paint
Change time and temperature requirement are dried solidification.
Step 4：Protection is processed
Metal base be have passed through the semi-finished product front surface roll-in after above-mentioned steps one～step 3 is processed and paste last layer
PVC adhesive tape glued membrane.
Step 5：Substrate backside arranges adhesivess
Metal base be have passed through the semi-finished product after above-mentioned steps one～step 4 is processed to turn over, in other side upper table
One layer of commercially available pressure sensitive adhesive of face (back side) application.
Step 6：Back-protective is processed
Above-mentioned metal base be have passed through after the process of above-mentioned steps one～step 5, be finally provided with the one of pressure sensitive adhesive
Face, by way of rolling, presses one layer of organosilicon protection sheet.
After above-mentioned six steps, color metal decorative pattern floor described in the utility model completes.
Embodiment three：
Choose 304 thick rustless steel winding of 0.1mm as base material, early stage processes oil removing, cleans and dry.
Step one：Substrate surface hydroxylating and microporous
The aluminum alloy base material after above-mentioned process is clean, it is placed on and is respectively containing chemical composition and concentration：CrO3
(50g/l) and H2SO4(100g/l), in chemical oxidation solution, chemical oxidation 10min at 85 DEG C of temperature, in above-mentioned rustless steel
Material surface forms oh group and porous oxide film, in order to greatly enhance base material and printing layer thereon and its lower adhesive linkage material
The adhesion of material.
Step 2：Printed decoration layer
Unilateral in have passed through the above-mentioned stainless steel substrate that step (1) is handled well one by way of the continuous offset printing of drum-type
One layer of Wood-grain-imitating patterned layer is printed on surface (front), is dried by the requirement of ink used.
Step 3：In printed decoration layer surface, Al is set2O3Wear-resistant protective layer
In order to strengthen ostentatious wear-resisting, the anti-delineation of above-mentioned colored printing, antifouling property, above-mentioned metal base is passing through
After above-mentioned steps one and step 2, then commercially available reinforced composite floorboard Al2O3Dipping abrasion-proof paper is merged by high-temperature bearing
Mode, on above-mentioned printed decoration layer merge one layer of wear-resisting, anti-delineation protective layer.
Al2O3Abrasion-proof paper wearing coat and the hot pressing plasticizing forming method of printed decoration layer:In accordance with Al2O3Dipping abrasion-proof paper
The requirement to hot press pressure and temperature for the manufacturer carries out plastifying bonding forming.
Step 4：Substrate backside arranges adhesivess
Metal base be have passed through the semi-finished product after above-mentioned steps one～step 3 is processed to turn over, on other side surface
One layer of commercially available pressure sensitive adhesive of (back side) application.
Step 5：Back-protective is processed
Above-mentioned metal base be have passed through after the process of above-mentioned steps one～step 4, be finally provided with the one of pressure sensitive adhesive
Face, then by way of rolling, press one layer of organosilicon protection sheet.
After above-mentioned five steps, color metal decorative pattern floor described in the utility model completes.
Example IV：
Choose the thick aluminium alloy winding of 0.2mm as base material, pre-treatment oil removing, cleaning.
Step one：Substrate surface hydroxylating and microporous
The aluminum alloy base material after above-mentioned process is clean, it is placed on and is respectively containing chemical composition and concentration：NaOH
(30g/l) in chemical solution, chemical oxidation 1min under temperature 50 C, form oh group in above-mentioned aluminum alloy material surface
And porous membrane layer, in order to greatly enhance the adhesion of base material and printing layer thereon and its lower bonding layer material.
Step 2：Printed decoration layer
Unilateral in have passed through the above-mentioned aluminum alloy base material after step one is processed one by way of the continuous offset printing of drum-type
Upper surface (front) prints one layer of Wood-grain-imitating patterned layer, is dried by the requirement of ink used.
Step 3：In printing layer surface setting Al2O3Wear-resistant protective layer
In order to strengthen ostentatious wear-resisting, the anti-delineation of above-mentioned colored printing, antifouling property, above-mentioned metal base is passing through
After above-mentioned steps one and step 2, then commercially available reinforced composite floorboard Al2O3Dipping abrasion-proof paper is merged by high-temperature bearing
Mode, on above-mentioned printed decoration layer merge one layer of wear-resisting, anti-delineation protective layer.
Al2O3Abrasion-proof paper wearing coat and the hot pressing plasticizing forming method of printed decoration layer:In accordance with Al2O3Dipping abrasion-proof paper
The requirement to hot press pressure and temperature for the manufacturer carries out plastifying bonding forming.
Step 4：Protection is processed
Metal base be have passed through the semi-finished product front surface roll-in after above-mentioned steps one～step 3 is processed and paste last layer
PVC adhesive tape glued membrane.
Step 5：Substrate backside arranges adhesivess
Metal base be have passed through the semi-finished product after above-mentioned steps 1～step 4 is processed to turn over, on other side surface
One layer of commercially available pressure sensitive adhesive of (back side) application.
Step 6：Back-protective is processed
Above-mentioned metal base be have passed through after the process of above-mentioned steps 1～step 5, be finally provided with the one of pressure sensitive adhesive
Face, then by way of rolling, press one layer of organosilicon protection sheet.
After above-mentioned six steps, color metal decorative pattern floor described in the utility model completes.
Claims (6)
1. a kind of chromatic pattern metal floor for decoration, is for decoration " floor plaster " with color metal decorative pattern system
Product, described metal floor is followed successively by five-layer structure from top to bottom, including：Protecting film（1）, set thickness wearing layer（2）, set
The printed decoration layer of thickness（3）, metal substrate layer（4）, Performance of Pressure Sensitive Adhesive layer（5）, organosilicon protection sheet（6）；Wherein：Protecting film
（1）With organosilicon protection sheet（6）It is temporary protective layer, wearing layer（2）, printed decoration layer（3）, metal substrate layer（4）And pressure
Quick glue adhesive linkage（5）It is basic training ergosphere；Described protecting film（1）It is PVC protection glued membrane；Described metal substrate layer（4）Following table
Face and Performance of Pressure Sensitive Adhesive layer（5）Bonding；Described Performance of Pressure Sensitive Adhesive layer（5）Lower surface be organosilicon protection sheet（6）；Its feature exists
In：
Described wearing layer（2）It is application heat cure in printed decoration layer（3）On Al2O3, or SiO2Wear-resistant protection applies
Layer, or high-temperature bearing fusion is in printed decoration layer（3）On Al2O3Dipping abrasion-proof paper protective layer；
Work as wearing layer（2）Using Al2O3During dipping abrasion-proof paper protective layer, described PVC protection glued membrane is nonessential setting.
2. as claimed in claim 1 a kind of for decoration chromatic pattern metal floor it is characterised in that：Described wearing layer（2）
Thickness be 10～1000 μm.
3. as claimed in claim 1 a kind of for decoration chromatic pattern metal floor it is characterised in that：Described printed decoration
Layer（3）Thickness be 10～1000 μm, printed decoration layer（3）Pattern include：Wood-grain-imitating pattern, marble grain pattern,
Carpet stricture of vagina pattern, granite pattern；Or with foam ink in metal substrate layer（4）Upper surface prints out with anaglyph
Pattern.
4. as claimed in claim 1 a kind of for decoration chromatic pattern metal floor it is characterised in that：Described metal substrate layer
（4）Material include：Rustless steel or aluminium alloy, tin alloy, copper alloy；The thickness of described metal substrate layer 4 is set as 0.01～
1.5mm；Metal substrate layer（4）Upper surface be：Minute surface or dull surface, sand face, mill stricture of vagina or patterned surface；Described metal substrate layer
（4）Including：Metal forming, metallic plate or winding.
5. as claimed in claim 1 a kind of for decoration chromatic pattern metal floor it is characterised in that：Described Performance of Pressure Sensitive Adhesive
Layer（5）Thickness be 100～1000 μm.
6. as claimed in claim 1 a kind of for decoration chromatic pattern metal floor it is characterised in that：Described basic training ergosphere
Gross thickness be 100～2000 μm.