CN104975162A - 一种铲斗焊接接头的表面处理工艺 - Google Patents

一种铲斗焊接接头的表面处理工艺 Download PDF

Info

Publication number
CN104975162A
CN104975162A CN201510365189.9A CN201510365189A CN104975162A CN 104975162 A CN104975162 A CN 104975162A CN 201510365189 A CN201510365189 A CN 201510365189A CN 104975162 A CN104975162 A CN 104975162A
Authority
CN
China
Prior art keywords
weld
surface treatment
welding joint
scraper bowl
toe
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510365189.9A
Other languages
English (en)
Inventor
何拥军
何嘉圣
何嘉贤
赖卫华
郭守亮
韦柳祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LIUZHOU JINMAO MACHINERY CO Ltd
Original Assignee
LIUZHOU JINMAO MACHINERY CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LIUZHOU JINMAO MACHINERY CO Ltd filed Critical LIUZHOU JINMAO MACHINERY CO Ltd
Priority to CN201510365189.9A priority Critical patent/CN104975162A/zh
Publication of CN104975162A publication Critical patent/CN104975162A/zh
Pending legal-status Critical Current

Abstract

本发明公开一种铲斗焊接接头的表面处理工艺，包括如下步骤：将铲斗焊接接头预处理后，对焊缝、焊趾及热影响区域超声冲击至它们表面至深度为160μm的区间内晶粒平均尺寸不大于200nm后，热处理。本发明采用该工艺处理铲斗焊接件焊接接头后，焊接接头表面组织形成稳定的细化层，表面粗糙度低，表面硬度增加，焊趾区域过渡平滑，且处理表面存在很高残余压应力，大大提高了焊接接头的塑性、抗疲劳以及抗磨损强度。

Description

一种铲斗焊接接头的表面处理工艺
技术领域
本发明属于焊接技术领域，具体是一种铲斗焊接接头的表面处理工艺。
背景技术
现随着产业结构的变化和科学技术的发展，先进的焊接结构是降低材料消耗、减轻结构质量的有效途径。
铲斗焊接接头，需要更高的温度、较大的熔池尺寸，热影响区金属在高温下的停留时间长，因此，易引起焊接接头的过热倾向，使晶粒变得十分粗大，接头的塑性显著降低，抗疲劳、抗磨损性能下降。
发明内容
本发明的技术方案是这样实现的：一种铲斗焊接接头的表面处理工艺，包括如下步骤：将铲斗焊接接头预处理后，对焊缝、焊趾及热影响区域超声冲击至它们表面至深度为160μm 的区间内晶粒平均尺寸不大于200nm 后，热处理。
优选地，还包括对焊缝、焊趾及热影响区域再次超声冲击至他们的表面压应力不小于180MPa。
优选地，所述预处理中，对焊趾区域进行机械加工时，加工方向与加工区域工况下的主应力线方向一致。
优选地，热处理为在200-300℃条件下保温30-60min 后空冷。
优选地，热处理的升温速率为1-2℃ /s。
本发明的有益效果：采用该工艺处理铲斗焊接件焊接接头后，焊接接头表面组织形成稳定的细化层，表面粗糙度低，表面硬度增加，焊趾区域过渡平滑，且处理表面存在很高残余压应力，大大提高了焊接接头的塑性、抗疲劳以及抗磨损强度。
具体实施方式
对本发明提供的实施方式作进一步详细的说明：
一种铲斗焊接接头的表面处理工艺，包括如下步骤：将铲斗焊接接头预处理后，对焊缝、焊趾及热影响区域超声冲击至它们表面至深度为160μm 的区间内晶粒平均尺寸不大于200nm 后，热处理。
优选地，还包括对焊缝、焊趾及热影响区域再次超声冲击至他们的表面压应力不小于180MPa。
优选地，所述预处理中，对焊趾区域进行机械加工时，加工方向与加工区域工况下的主应力线方向一致。
优选地，热处理为在200-300℃条件下保温30-60min 后空冷。
优选地，热处理的升温速率为1-2℃ /s。
本发明的有益效果：采用该工艺处理铲斗焊接件焊接接头后，焊接接头表面组织形成稳定的细化层，表面粗糙度低，表面硬度增加，焊趾区域过渡平滑，且处理表面存在很高残余压应力，大大提高了焊接接头的塑性、抗疲劳以及抗磨损强度。
 在此说明书中，本发明已参照其特定的实施例作了描述。但是，很显然仍可以做出各种修改和变换而不背离本发明的精神和范围。因此，说明书应被认为是说明性的而非限制性的。

Claims (5)

1.一种铲斗焊接接头的表面处理工艺，其特征在于，包括如下步骤：
将铲斗焊接接头预处理后，对焊缝、焊趾及热影响区域超声冲击至它们表面至深度为160μm 的区间内晶粒平均尺寸不大于200nm 后，热处理。
2. 如权利要求1 所述的铲斗焊接接头的表面处理工艺，其特征在于还包括对焊缝、焊趾及热影响区域再次超声冲击至他们的表面压应力不小于180MPa。
3. 如权利要求1 所述的铲斗焊接接头的表面处理工艺，其特征在于，所述预处理中，对焊趾区域进行机械加工时，加工方向与加工区域工况下的主应力线方向一致。
4. 如权利要求1 所述的铲斗焊接接头的表面处理工艺，其特征在于，热处理为在200-300℃条件下保温30-60min 后空冷。
5. 如权利要求4 所述的铲斗焊接接头的表面处理工艺，其特征在于，热处理的升温速率为1-2℃ /s。
CN201510365189.9A 2015-06-29 2015-06-29 一种铲斗焊接接头的表面处理工艺 Pending CN104975162A (zh)