CN1049677A - 一种改性葡萄糖衍生物粘合剂 - Google Patents
一种改性葡萄糖衍生物粘合剂 Download PDFInfo
- Publication number
- CN1049677A CN1049677A CN 89106535 CN89106535A CN1049677A CN 1049677 A CN1049677 A CN 1049677A CN 89106535 CN89106535 CN 89106535 CN 89106535 A CN89106535 A CN 89106535A CN 1049677 A CN1049677 A CN 1049677A
- Authority
- CN
- China
- Prior art keywords
- parts
- starch
- add
- derivatives
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及无毒无污染水基粘合剂,以改性葡萄
糖衍生物为原料,磺酸盐和硫酸盐表面活性剂为分散
润湿剂,干酪素、明胶、聚丙烯酸酯、聚醋酸乙烯酯和
聚苯乙烯-丁二烯乳液为溶液助剂,在低于淀粉糊化
温度下加热制得,工艺、设备简单,制得的粘合剂粘结
强度高,可采用涂敷、浸渍、喷涂方法施胶。
Description
本发明涉及粘合剂,特别是一种无毒、无污染的改性葡萄糖粘合剂及其制备方法。
粘合技术在日常生活、科技、生产各个领域都具有重要地位,人们需要的粘合剂种类繁多,其中淀粉类粘合剂由于无毒、价格低廉,常为室内装饰、纸制品和无纺织物的生产过程所采用。但由于此类粘合剂通常由淀粉加热至糊化温度而制得。在使用过程中常因粘度不易控制而达不到理想的效果,粘度过高则难以用于浸渍工艺,粘度过低,则影响粘合牢度。
本发明的目的在于,要提供一种在使用过程中粘度影响小、渗透性较好的葡萄糖衍生物粘合剂。
本发明粘合剂由改性葡萄糖衍生物作原料,磺酸盐表面活性剂,或硫酸盐表面活性剂作分散润湿剂,干酪素、明胶、聚丙烯酸酯、聚醋酸乙烯酯、聚苯乙烯-丁二烯乳液作稳定剂制成。其制备工艺为:在磺酸盐或硫酸盐表面活性剂的水溶液中加入淀粉搅拌成悬浮液,边搅拌边加热至淀粉糊化温度下,再加水稀释至需要的浓度,再加入干酪素、明胶、聚丙烯酸酯乳液、聚醋酸乙烯酯乳液、聚苯乙烯-丁二烯乳液等助剂。
本粘合剂也可以加入交联剂以增加粘合强度和耐水性,加入防腐剂以便长期保存。
本粘合剂可以单独使用,当粘合剂施加到被粘合物上后,再加温到改性淀粉的糊化温度以上,即在80-150℃烘干,即完成粘合过程。
本发明粘合剂,由于在配制时淀粉尚未达到糊化温度,所以粘度较低,易于渗透到纤维制品等被粘合物深层中去,而当粘合剂施加到被粘合物中和被粘物相迂时,淀粉才在高温下产生糊化,使粘结强度增高,从而大大方便了使用。
本发明的内容通过以下实施例进一步说明:
实施例1.取羟丙基淀粉25份,加入2%的十六烷基苯磺酸钠水溶液65份,搅拌,加水15份,继续搅拌,并升温至55-70℃,加入10%的明胶10份,制成粘合剂。
使用这种溶液制造非织造布时,为增加柔软性,可再加入5%浓度的氯化钙25份作增塑剂,用260份水稀释,然后浸渍纤维网,轧液 在80-130℃烘干,即得非织造布。
实施例2.羟丙基淀粉30份,加入0.5%的十二烷基硫酸钠水溶液60份,搅拌,再加入60份水,边升温边搅拌,升温至50-65℃,边搅拌边加水144份稀释,然后加入10%的干酪素水溶液6份,即成所需粘合剂。
为了延长粘合剂的存放期,还可以加入10%的硼酸水溶液6份。
实施例3.羟丙基淀粉25份,加入1%的十六烷基苯磺酸钠水溶液75份搅拌成悬浮液,加水150份,搅拌,升温至65-70℃,边搅拌边加水247份稀释,然后再加入10%的聚丙烯酸乳液3份,即成所需的粘合剂。
实施例4.磷酸酯淀粉25份,加入1.6%的十二烷基硫酸钠75份,搅拌,升温至85-94℃,然后加水170份稀释,再加入10%的干酪素5份,即得所需的粘合剂。
为增加防水性能及粘合强度,使用本粘合剂时可加入1%的硼砂水溶液75份作交联剂,用这种粘合剂浸渍纤维网,轧液,然后经100-150℃烘干即得非职造布。
实施例5.磷酸酯淀粉30份,搅拌下加入0.3%的十二烷基硫酸钠100份,然后加水120份,搅拌,升温至80-90℃,然后加240份水稀释,再加入10%聚苯乙烯乳液10份,即得粘合剂溶液。
实施例6.磷酸酯淀粉30份,加入1.5%十六烷基苯磺酸钠100份,然后加水120份,搅拌升温至80-90℃,然后加水235份稀释,再加入10%的聚醋酸乙烯酯乳液15份,即得粘合剂溶液。
实施例7.磷酸酯淀粉40份,搅拌下加入2%的十六烷基苯磺酸钠100份,然后加水110份,升温至80-90℃,然后加水230份稀释,再加入10%的聚丙烯酸酯乳液20份,即得粘合剂溶液。
Claims (2)
1、本发明粘合剂由改性葡萄糖衍生物,分散润湿剂、助剂和水所组成,其特征在于,改性葡萄糖衍生物为羟丙基淀粉和磷酸酯淀粉,分散润湿剂为磺酸盐及硫酸盐表面活性剂,助剂为干酪素、明胶、聚丙烯酸酯、聚醋酸乙烯酯、聚苯乙烯丁二烯乳液。
2、本发明粘合剂的制造方法,其特征在于将淀粉加入含0.2-1.6%磺酸盐、硫酸盐表面活性剂的水溶液中搅拌,使成悬浮液,在淀粉的糊化温度以下,再加入适量的水和相当于淀粉量1-2%的干酪素,或1-5%的明胶、聚丙烯酸酯乳液、聚醋酸乙烯酯乳液、聚苯乙烯-丁二烯乳液。