CN104946092B - Jing Yin composite floor board of cork wood ultraviolet light solidifies painting design - Google Patents
Jing Yin composite floor board of cork wood ultraviolet light solidifies painting design Download PDFInfo
- Publication number
- CN104946092B CN104946092B CN201510287216.5A CN201510287216A CN104946092B CN 104946092 B CN104946092 B CN 104946092B CN 201510287216 A CN201510287216 A CN 201510287216A CN 104946092 B CN104946092 B CN 104946092B
- Authority
- CN
- China
- Prior art keywords
- elasticity
- modified epoxy
- solidification
- acrylic ester
- epoxy acrylic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention belongs to ultraviolet light to solidify field of new materials.More particularly, to the Jing Yin de-noising painting design applied to composite floor board of cork wood.The present invention provides a kind of high degree of comfort, Jing Yin composite board ultraviolet light solidification painting design, is made up of UV bouncing putties, UV elasticity sandings priming paint, UV elastic primers, UV elasticity finish paints.By the composite floor board of cork wood of application elasticity UV systems, whole coating elastic reinforcement, walked in people when on floor, cushioning effect can be played, so as to reach de-noising muting function.
Description
Technical field
The invention belongs to ultraviolet light to solidify field of new materials.More particularly, to the Jing Yin de-noising applied to composite floor board of cork wood
Painting design.The present invention provides a kind of Jing Yin, high degree of comfort composite board ultraviolet light solidification painting design.
Technical background
At present, solid wooden floor board plays an important role in the home decoration, but some problems caused by it also annoying
User, noise are exactly the more important.According to statistics, solid wooden floor board occurs noise problem due to a variety of causes after mating formation
Probability is up to more than 80%.For this problem, we provide a kind of ultraviolet light solidification application applied on composite floor board of cork wood
System.By the cork flooring of application elasticity UV systems, whole coating elastic reinforcement, walk when on floor, can play slow in people
Punching acts on, so as to reach de-noising muting function.Ultraviolet-curing paint is a kind of efficient, environmental protection, energy-conservation, high-quality photocuring material
Material, China floor, furniture industry more and more carry out protection and the decoration of sheet material using UV curing process.
Many floors enterprise developments related mute floor board, comprehensive current applicable cases, these mute floor boards are mainly deposited
In following deficiency：
1. product practical application effect does not reach the effect that products propaganda data is declared.
2. timber floor of the bottom with plastic cushion, VOC emission amount is larger, influences indoor environment.
3. the floor of application elasticity UV coating, not enough, de-noising muting function is poor for elasticity.
The content of the invention
It is for the technical problem to be solved in the present invention：In order to solve in above-mentioned technical background to apply existing for existing floor and
A kind of a kind of performance deficiency, there is provided Jing Yin composite floor board of cork wood ultraviolet light solidification painting design, there is provided Jing Yin cork of UV applications
Floor.
The wherein formula of UV painting designs, according to the difference of the functions such as the elasticity of coating, pliability, comfortableness, planarization
Demand is prepared.
The technical solution adopted for the present invention to solve the technical problems is：A kind of Jing Yin composite floor board of cork wood UV coated-bodies
System, including the multiple tracks application such as UV bouncing putties, UV elasticity sandings priming paint, UV elastic primers, UV elasticity finish paints.First, at UV bottoms
In the application of paint, alternately multiple tracks application is carried out by layer function difference is applied, then carries out UV elasticity finish paint applications again.After each application
Ultraviolet light solidification is carried out, next process is then entered back into and carries out application.
It is a feature of the present invention that：
UV bouncing putty prescription quality percentages are as follows：
Modified epoxy acrylic ester： 30-50%
Two official's aliphatic elastic polyurethane acrylate： 20-40%
Tripropylene glycol class diacrylate TP: 5-15%
Iso-bornyl acrylate IBOA: 5-15%
Aerosil： 5-10%
Other auxiliary agents： 1-5%
Light trigger： 2-8%
Auxiliary agent includes dispersant, levelling agent, defoamer etc., and this professional person is generally known that auxiliary dosage, therefore herein not
It is described in detail again.
UV bouncing putties are mainly using modified epoxy acrylic ester, two official's aliphatic elastic polyurethane acrylate, 3 third
Glycols diacrylate TP, iso-bornyl acrylate IBOA are film forming binder.Modified epoxy acrylic ester is Zhong Shan sections field
4220。
The present invention is mainly by adjusting film forming binder modified epoxy acrylic ester, two official's aliphatic elastic polyurethane acrylic acid
Ester, tripropylene glycol class diacrylate TP, iso-bornyl acrylate IBOA content adjust the elasticity of film layer, pliability,
And form different elastic and flexible UV bouncing putties needed for different processes in primer painting process.
The prescription quality percentage of UV elasticity sanding priming paint is as follows：
Modified epoxy acrylic ester： 30-50%
Polyester acrylate： 20-30%
Tripropylene glycol class diacrylate TP: 5-20%
Other auxiliary agents： 1-5%
Talcum powder： 5-15%
Light trigger： 2-8%
Auxiliary agent includes dispersant, levelling agent, defoamer etc., and this professional person is generally known that auxiliary dosage, therefore herein not
It is described in detail again.
UV elasticity sandings priming paint is mainly by modified epoxy acrylic ester, polyester acrylate, tripropylene glycol class diacrylate
Ester TP forms film forming binder.Modified epoxy acrylic ester is Zhong Shan sections field 4220.
The present invention is mainly by adjusting film forming binder modified epoxy acrylic ester, polyester acrylate, tripropylene glycol class two
Acrylate TP composition adjusts the sanding of film layer and elasticity, and provides for cork sheet after sanding smooth, smooth
Surface effect.
The prescription quality percentage of UV elastic primers is as follows:
Modified epoxy acrylic ester： 10-30%
Two official's aliphatic elastic polyurethane acrylate： 20-50%
Polyester acrylate： 5-15%
Tripropylene glycol class diacrylate TP: 5-15%
Hydroxyethyl methacrylate HEMA: 2-10%
Other auxiliary agents： 1-5%
Light trigger： 2-8%
UV elastic primers are mainly by modified epoxy acrylic ester, two official's aliphatic elastic polyurethane acrylate, polyester third
Olefin(e) acid ester, tripropylene glycol class diacrylate TP, hydroxyethyl methacrylate HEMA composition film forming binders.Modified epoxy acrylic acid
Ester is Zhong Shan sections field 4220.
The present invention is mainly by adjusting film forming binder modified epoxy acrylic ester, two official's aliphatic elastic polyurethane acrylic acid
Ester, polyester acrylate, tripropylene glycol class diacrylate TP, hydroxyethyl methacrylate HEMA content adjust film layer
Elasticity and pliability.
UV elasticity finish paint mass percents are as follows：
Modified epoxy acrylic ester:0-40%
Polyester acrylate：0-30%
Tripropylene glycol class diacrylate TP:10-30%
Hydroxyethyl methacrylate HEMA:0-10%
Other auxiliary agents：1-5%
Flatting silica：5-10%
Light trigger：2-8%
UV elasticity finish paint mainly have modified epoxy acrylic ester, polyester acrylate, tripropylene glycol class diacrylate TP,
Hydroxyethyl methacrylate HEMA forms film forming binder, and modified epoxy acrylic ester is that our company has sold 4220.And pass through tune
The content for saving each component adjusts the elasticity of film layer and pliability, and comfortableness.
A kind of Jing Yin composite floor board of cork wood ultraviolet light solidification painting design, it is characterised in that its UV bouncing putty, UV elasticity
Sanding priming paint, UV elastic primers, the preparation method of UV elasticity finish paints are as follows：
The preparation method of UV bouncing putties is：By modified epoxy acrylic ester, two official's aliphatic urethane acrylates, three
Propandiols diacrylate TP, iso-bornyl acrylate IBOA, aerosil, other auxiliary agents, light trigger press matter
Amount percentage puts into reactor successively, is heated to 60 DEG C~80 DEG C, at a high speed scattered stirring 3 hours.
UV elasticity sanding priming paint preparation methods are：By modified epoxy acrylic ester, polyester acrylate, tripropylene glycol class two
Acrylate TP, other auxiliary agents, talcum powder, light trigger put into reactor successively by mass percentage, are heated to 60 DEG C~80
DEG C, it is scattered at a high speed to stir 3 hours.
UV elastic primer preparation methods are：By modified epoxy acrylic ester, two official's aliphatic urethane acrylates, polyester
Acrylate, tripropylene glycol class diacrylate TP, hydroxyethyl methacrylate HEMA, other auxiliary agents, light trigger press quality
Percentage puts into reactor successively, is heated to 60 DEG C~80 DEG C, at a high speed scattered stirring 3 hours.
UV elasticity finish paint preparation methods are：By modified epoxy acrylic ester, polyester acrylate, the propylene of tripropylene glycol class two
The input reaction successively by mass percentage of acid esters TP, hydroxyethyl methacrylate HEMA, other auxiliary agents, flatting silica, light trigger
Kettle, 60 DEG C~80 DEG C are heated to, at a high speed scattered stirring 3 hours.
A kind of coating process of Jing Yin composite floor board of cork wood ultraviolet light solidification painting design is characterised by：Roller coat UV elasticity is greasy
Son（Solidification）→ UV bouncing putties（Solidification）→ UV elasticity sanding priming paint（Solidification）→ UV elastic primers（Solidification）→ UV elastic bottoms
Paint（Solidification）→ UV elasticity sanding priming paint（Solidification）→ UV elasticity finish paints（Solidification）→ finished product.
Embodiment：
The preparation of 1.UV bouncing putties：By modified epoxy acrylic ester, two official's aliphatic urethane acrylates, 3 the third two
Alcohols diacrylate TP, iso-bornyl acrylate IBOA, aerosil, other auxiliary agents, light trigger press quality hundred
Divide ratio to put into reactor successively, be heated to 60 DEG C~80 DEG C, at a high speed scattered stirring 3 hours.
The preparation at 2.UV elasticity sandings bottom：By modified epoxy acrylic ester, polyester acrylate, the propylene of tripropylene glycol class two
Acid esters TP, other auxiliary agents, talcum powder, light trigger put into reactor successively by mass percentage, are heated to 60 DEG C~80 DEG C, height
The scattered stirring of speed 3 hours.
The preparation of 3.UV elastic primers：By modified epoxy acrylic ester, two official's aliphatic urethane acrylates, polyester third
Olefin(e) acid ester, tripropylene glycol class diacrylate TP, hydroxyethyl methacrylate HEMA, other auxiliary agents, light trigger press quality hundred
Divide ratio to put into reactor successively, be heated to 60 DEG C~80 DEG C, at a high speed scattered stirring 3 hours.
The preparation of 4.UV elasticity finish paints：By modified epoxy acrylic ester, polyester acrylate, tripropylene glycol class diacrylate
Ester TP, hydroxyethyl methacrylate HEMA, other auxiliary agents, flatting silica, light trigger put into reactor successively by mass percentage,
60 DEG C~80 DEG C are heated to, at a high speed scattered stirring 3 hours.
Further illustrate in conjunction with the embodiments：
Embodiment one：
Jing Yin composite floor board of cork wood ultraviolet light solidifies painting design, its UV bouncing putty, UV elasticity sandings bottom, UV elastic bottoms
Paint, the prescription quality percentage of UV elasticity finish paints are as follows：
The prescription quality percentage of UV bouncing putties is：
Modified epoxy acrylic ester： 45%
Two official's aliphatic elastic polyurethane acrylate： 25%
Tripropylene glycol class diacrylate TP: 8%
Iso-bornyl acrylate IBOA: 8%
Aerosil： 8%
Other auxiliary agents： 2%
Light trigger： 4%
The prescription quality percentage of UV elasticity sanding priming paint is：
Modified epoxy acrylic ester： 40%
Polyester acrylate： 25%
Tripropylene glycol class diacrylate TP: 15%
Other auxiliary agents： 2%
Talcum powder： 14%
Light trigger： 4%
The prescription quality percentage of UV elastic primers is：
Modified epoxy acrylic ester： 25%
Two official's aliphatic elastic polyurethane acrylate： 45%
Polyester acrylate： 10%
Tripropylene glycol class diacrylate TP: 10%
Hydroxyethyl methacrylate HEMA: 5%
Other auxiliary agents： 1%
Light trigger： 4%
The prescription quality percentage of UV elasticity finish paints is：
Modified epoxy acrylic ester: 35%
Polyester acrylate： 25%
Tripropylene glycol class diacrylate TP: 20%
Hydroxyethyl methacrylate HEMA: 6%
Other auxiliary agents： 2%
Flatting silica： 8%
Light trigger： 4%
Embodiment two：
Jing Yin composite floor board of cork wood ultraviolet light solidifies painting design, its UV bouncing putty, UV elasticity sandings bottom, UV elastic bottoms
Paint, the prescription quality percentage of UV elasticity finish paints are as follows：
The prescription quality percentage of UV bouncing putties is：
Modified epoxy acrylic ester： 40%
Two official's aliphatic elastic polyurethane acrylate： 20%
Tripropylene glycol class diacrylate TP: 12%
Iso-bornyl acrylate IBOA: 12%
Aerosil： 10%
Other auxiliary agents： 1.5%
Light trigger： 4.5%
The prescription quality percentage of UV elasticity sanding priming paint is：
Modified epoxy acrylic ester： 45%
Polyester acrylate： 20%
Tripropylene glycol class diacrylate TP: 13%
Other auxiliary agents： 2.5%
Talcum powder： 15%
Light trigger： 4.5%
The prescription quality percentage of UV elastic primers is：
Modified epoxy acrylic ester： 20%
Two official's aliphatic elastic polyurethane acrylate： 44%
Polyester acrylate： 12%
Tripropylene glycol class diacrylate TP: 12%
Hydroxyethyl methacrylate HEMA: 6%
Other auxiliary agents： 1.5%
Light trigger： 4.5%
The prescription quality percentage of UV elasticity finish paints is：
Modified epoxy acrylic ester: 40%
Polyester acrylate： 15%
Tripropylene glycol class diacrylate TP: 25%
Hydroxyethyl methacrylate HEMA: 5%
Other auxiliary agents： 1.5%
Flatting silica： 9%
Light trigger： 4.5%
Embodiment three：
Jing Yin composite floor board of cork wood ultraviolet light solidifies painting design, its UV bouncing putty, UV elasticity sandings bottom, UV elastic bottoms
Paint, the prescription quality percentage of UV elasticity finish paints are as follows：
The prescription quality percentage of UV bouncing putties is：
Modified epoxy acrylic ester： 35%
Two official's aliphatic elastic polyurethane acrylate： 35%
Tripropylene glycol class diacrylate TP: 10%
Iso-bornyl acrylate IBOA: 10%
Aerosil： 6%
Other auxiliary agents： 1%
Light trigger： 3%
The prescription quality percentage of UV elasticity sanding priming paint is：
Modified epoxy acrylic ester： 50%
Polyester acrylate： 15%
Tripropylene glycol class diacrylate TP: 20%
Other auxiliary agents： 1.5%
Talcum powder： 10%
Light trigger： 3.5%
The prescription quality percentage of UV elastic primers is：
Modified epoxy acrylic ester： 30%
Two official's aliphatic elastic polyurethane acrylate： 30%
Polyester acrylate： 14%
Tripropylene glycol class diacrylate TP: 14%
Hydroxyethyl methacrylate HEMA: 7%
Other auxiliary agents： 2%
Light trigger： 3%
The prescription quality percentage of UV elasticity finish paints is：
Modified epoxy acrylic ester: 30%
Polyester acrylate： 30%
Tripropylene glycol class diacrylate TP: 15%
Hydroxyethyl methacrylate HEMA: 10%
Other auxiliary agents： 2.5%
Flatting silica： 10%
Light trigger： 3.5%
Coating process involved by above example is：
Roller coat UV putty（Solidification）→ UV putty（Solidification）→ UV elasticity sanding priming paint（Solidification）→ UV elastic primers（Gu
Change）→ UV elastic primers（Solidification）→ UV elasticity sanding priming paint（Solidification）→ UV elasticity finish paints（Solidification）→ finished product.
UV coating obtained by use carries out application according to UV painting designs of the present invention requirement to painting object, after paint film is fully cured
The elastic wood skin paint film property of 72 hours is as follows：
| Detection project | National standard | As a result |
| Adhesive force | GB/T15036.2-2001 | 0-1 levels（100%） |
| Jing Yin test | Adult wears high heels test | 60 decibels of ＜ |
| Flexibility test | Adult wears high heels test | Coating is without impression |
| Cold cycling | GB10592-89 | 4 circulations are without exception |
By the cork flooring of application elasticity UV systems, whole coating elastic reinforcement, walk when on floor, can play in people
Cushioning effect, so as to reach de-noising muting function.
Embodiment of the present invention is only the description carried out to the preferred embodiment of the present invention, not to the present invention
Spirit and scope are defined, and on the premise of design philosophy of the present invention is not departed from, engineers and technicians are to this hair in this area
The all variations and modifications that bright technical scheme is made, protection scope of the present invention, the claimed skill of the present invention all should be fallen into
Art content, all record in detail in the claims.
Claims (4)
1. Jing Yin composite floor board of cork wood ultraviolet light solidifies painting design, by UV bouncing putties, UV elasticity sandings priming paint, UV elastic bottoms
Paint, UV elasticity finish paint composition, it is characterised in that：
(1), the formula material constituent mass percentage of UV bouncing putties is：
Modified epoxy acrylic ester： 30-50%
Two official's aliphatic urethane acrylates： 20-40%
Tripropylene glycol class diacrylate TP: 5-15%
Iso-bornyl acrylate IBOA: 5-15%
Aerosil： 5-10%
Other auxiliary agents： 1-5%
Light trigger： 2-8%
Above each component mass percent sum is 100%；
(2), the formula material constituent mass percentage of UV elasticity sanding priming paint is：
Modified epoxy acrylic ester： 30-50%
Polyester acrylate： 20-30%
Tripropylene glycol class diacrylate TP: 5-20%
Other auxiliary agents： 1-5%
Talcum powder： 5-15%
Light trigger： 2-8%
Above each component mass percent sum is 100%；
(3), the formula material constituent mass percentage of UV elastic primers is：
Modified epoxy acrylic ester： 10-30%
Two official's aliphatic urethane acrylates： 20-50%
Polyester acrylate： 5-15%
Tripropylene glycol class diacrylate TP: 5-15%
Hydroxyethyl methacrylate HEMA: 2-10%
Other auxiliary agents： 1-5%
Light trigger： 2-8%
Above each component mass percent sum is 100%；
(4), the formula material constituent mass percentage of UV elasticity finish paint is：
Modified epoxy acrylic ester: 20-40%
Polyester acrylate： 10-30%
Tripropylene glycol class diacrylate TP: 10-30%
Hydroxyethyl methacrylate HEMA: 2-10%
Other auxiliary agents： 1-5%
Flatting silica： 5-10%
Light trigger： 2-8%
Above each component mass percent sum is 100%.
2. Jing Yin composite floor board of cork wood ultraviolet light solidification painting design according to claim 1, its UV bouncing putty, UV bullets
Property sanding priming paint, UV elastic primers, the preparation method of UV elasticity finish paints, it is characterised in that：
(1), the preparation method of UV bouncing putties is:By modified epoxy acrylic ester, two official's aliphatic urethane acrylates, three
Propandiols diacrylate TP, iso-bornyl acrylate IBOA, aerosil, other auxiliary agents, light trigger press matter
Amount percentage puts into reactor successively, is heated to 60 DEG C~80 DEG C, at a high speed scattered stirring 3 hours；
(2), the preparation method of UV elasticity sanding priming paint is:By modified epoxy acrylic ester, polyester acrylate, tripropylene glycol class
Diacrylate TP, other auxiliary agents, talcum powder, light trigger put into reactor successively by mass percentage, be heated to 60 DEG C~
It is 80 DEG C, scattered at a high speed to stir 3 hours；
(3), the preparation method of UV elastic primers is:By modified epoxy acrylic ester, two official's aliphatic urethane acrylates, gather
Ester acrylate, tripropylene glycol class diacrylate TP, hydroxyethyl methacrylate HEMA, other auxiliary agents, light trigger press matter
Amount percentage puts into reactor successively, is heated to 60 DEG C~80 DEG C, at a high speed scattered stirring 3 hours；
(4), the preparation method of UV elasticity finish paint is:By modified epoxy acrylic ester, polyester acrylate, tripropylene glycol class dipropyl
Input is anti-successively by mass percentage for olefin(e) acid ester TP, hydroxyethyl methacrylate HEMA, other auxiliary agents, flatting silica, light trigger
Kettle is answered, is heated to 60 DEG C~80 DEG C, at a high speed scattered stirring 3 hours.
3. Jing Yin composite floor board of cork wood ultraviolet light solidification painting design according to claim 1, it is characterised in that：Auxiliary agent master
To include dispersant, defoamer, levelling agent.
4. painting design is solidified according to the Jing Yin composite floor board of cork wood ultraviolet light described in claim 1, it is characterised in that application
Technique is：Roller coat UV bouncing putties, solidification → UV bouncing putties, solidification → UV elasticity sanding priming paint, solidification → UV elastic primers,
Solidification → UV elastic primers, solidification → UV elasticity sanding priming paint, solidification → UV elasticity finish paints, solidification → finished product.