CN104946085A - 一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料 - Google Patents
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料 Download PDFInfo
- Publication number
- CN104946085A CN104946085A CN201510399959.1A CN201510399959A CN104946085A CN 104946085 A CN104946085 A CN 104946085A CN 201510399959 A CN201510399959 A CN 201510399959A CN 104946085 A CN104946085 A CN 104946085A
- Authority
- CN
- China
- Prior art keywords
- nanometer
- resistant
- metal shell
- parts
- silicon carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料,该涂料由以下重量份的组分组成:环氧树脂42-50份、环氧树脂固化剂20-26份、陶瓷骨料碳化硅28-34份、陶瓷骨料氧化铝10-12份、纳米碳化硅3-4份、纳米二氧化硅1-2份、研磨剂2-3份、消泡剂0.3-0.6份、润湿剂0.1-0.2份和流平剂0.8-1.2份。本发明利用纳米碳化硅和纳米二氧化硅等纳米材料来进一步提高环氧树脂涂料的耐磨性能和防腐性能,制备得到的智能烟灰缸金属外壳专用纳米防腐耐磨涂料增加了使用寿命,从而也增加了能烟灰缸金属外壳的使用寿命,且本发明制备方法简单,制备工艺简便。
Description
技术领域
本发明涉及一种涂料,具体地说是一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料。
背景技术
环氧树脂涂料在金属表面具有很高的粘结力和机械强度,其耐化学药品性和耐油性较好。因此,在金属基材表面涂覆环氧树脂基防腐蚀涂料可大大提高金属基材的防腐蚀能力,延长其使用寿命,节约资源,具有非常重要的应用价值。
随着纳米科技的快速发展,纳米材料的优异性能逐渐被应用于涂料工业中,通过添加纳米填料可以提高环氧涂料的防腐能力和耐磨性能。目前,纳米材料的应用主要包括两个方面:一、是将纳米材料添加到某种传统材料中去,来进一步提高传统材料的性能;二、是将纳米材料通过成型工艺制成纳米固体材料。
智能烟灰缸被已经开始慢慢普及市场,智能烟灰缸金属外壳涂覆主要以环氧树脂涂料为主,以此来达到表面防腐的目的,但是智能烟灰缸随着使用时间的不断增加,其金属外壳表面仍然会出现一些腐蚀锈斑和磨损痕迹,防腐性能有待进一步提高,严重影响了智能烟灰缸金属外壳的外观,从而也降低了使用寿命。
发明内容
针对上述技术问题,本发明提供一种防腐性能好的、耐磨性能好的、制备方法简单的、制备工艺简便的智能烟灰缸金属外壳专用纳米防腐耐磨涂料,延长了的使用寿命。
本发明所要解决的技术问题采用以下技术方案来实现:
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料,该涂料由以下重量份的组分组成:环氧树脂42-50份、环氧树脂固化剂20-26份、陶瓷骨料碳化硅28-34份、陶瓷骨料氧化铝10-12份、纳米碳化硅3-4份、纳米二氧化硅1-2份、研磨剂2-3份、消泡剂0.3-0.6份、润湿剂0.1-0.2份和流平剂0.8-1.2份。
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料的制备方法,包以下步骤:
(1)、先将固定颗粒状的陶瓷骨料碳化硅、陶瓷骨料氧化铝、纳米碳化硅、纳米二氧化硅、研磨剂依次加入研磨机中,研磨机研磨10-15分钟;
(2)、再加入环氧树脂和环氧树脂固化剂,得到混合物;
(3)、将步骤(2)中得到的混合物依次加入消泡剂、润湿剂、流平剂,在室温条件下利用搅拌机均匀搅拌10-30分钟,得到所需涂料。
本发明的有益效果是:本发明利用纳米碳化硅和纳米二氧化硅等纳米材料来进一步提高环氧树脂涂料的耐磨性能和防腐性能,制备得到的智能烟灰缸金属外壳专用纳米防腐耐磨涂料增加了使用寿命,从而也增加了能烟灰缸金属外壳的使用寿命,且本发明制备方法简单,制备工艺简便。
具体实施方式
为了使本发明实现的技术手段和创作特征易于明白了解,下面对本发明进一步阐述。
实施例一:
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料,该涂料由以下重量份的组分组成:环氧树脂42份、环氧树脂固化剂20份、陶瓷骨料碳化硅28份、陶瓷骨料氧化铝10份、纳米碳化硅3份、纳米二氧化硅1份、研磨剂2份、消泡剂0.3份、润湿剂0.1份和流平剂0.8份。
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料的制备方法,包以下步骤:
(1)、先将固定颗粒状的陶瓷骨料碳化硅、陶瓷骨料氧化铝、纳米碳化硅、纳米二氧化硅、研磨剂依次加入研磨机中,研磨机研磨10分钟;
(2)、再加入环氧树脂和环氧树脂固化剂,得到混合物;
(3)、将步骤(2)中得到的混合物依次加入消泡剂、润湿剂、流平剂,在室温条件下利用搅拌机均匀搅拌10分钟,得到所需涂料。
实施例二:
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料,该涂料由以下重量份的组分组成:环氧树脂46份、环氧树脂固化剂23份、陶瓷骨料碳化硅31份、陶瓷骨料氧化铝11份、纳米碳化硅3.5份、纳米二氧化硅1.5份、研磨剂2.5份、消泡剂0.45份、润湿剂0.15份和流平剂1.0份。
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料的制备方法,包以下步骤:
(1)、先将固定颗粒状的陶瓷骨料碳化硅、陶瓷骨料氧化铝、纳米碳化硅、纳米二氧化硅、研磨剂依次加入研磨机中,研磨机研磨12分钟;
(2)、再加入环氧树脂和环氧树脂固化剂,得到混合物;
(3)、将步骤(2)中得到的混合物依次加入消泡剂、润湿剂、流平剂,在室温条件下利用搅拌机均匀搅拌20分钟,得到所需涂料。
实施例三:
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料,该涂料由以下重量份的组分组成:环氧树脂50份、环氧树脂固化剂26份、陶瓷骨料碳化硅34份、陶瓷骨料氧化铝12、纳米碳化硅4份、纳米二氧化硅2份、研磨剂3份、消泡剂0.6份、润湿剂0.2份和流平剂1.2份。
一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料的制备方法,包以下步骤:
(1)、先将固定颗粒状的陶瓷骨料碳化硅、陶瓷骨料氧化铝、纳米碳化硅、纳米二氧化硅、研磨剂依次加入研磨机中,研磨机研磨15分钟;
(2)、再加入环氧树脂和环氧树脂固化剂,得到混合物;
(3)、将步骤(2)中得到的混合物依次加入消泡剂、润湿剂、流平剂,在室温条件下利用搅拌机均匀搅拌30分钟,得到所需涂料。
上述实施例一、实施例二和实施例三按照各重量份的材料制备出来的智能烟灰缸金属外壳专用纳米防腐耐磨涂料,其中纳米碳化硅的用量和纳米二氧化硅的用量等纳米材料对智能烟灰缸金属外壳专用纳米防腐耐磨涂料的防腐性能性能和耐磨性能的影响如表1所示。
表1
实施例 | 纳米碳化硅的用量/份 | 纳米二氧化硅的用量/份 | 耐磨性/h | 防腐性/h |
实施例一 | 3 | 1 | 141 | 180 |
实施例二 | 3.5 | 1.5 | 148 | 243 |
实施例三 | 4 | 2 | 152 | 247 |
从表1可知,所述纳米碳化硅的用量和纳米二氧化硅的用量不断增加,实施例一、实施例二、实施例三的耐磨性能和防腐性能都在增加,但是从实施例二和实施例三可以看出智能烟灰缸金属外壳专用纳米防腐耐磨涂料的防腐性和耐磨性随着纳米碳化硅的用量和纳米二氧化硅的用量继续增加已经趋于稳定,其中实施例二中纳米碳化硅用量占总用量的2.9%,纳米二氧化硅用量占总用量的1.2%,而实施例三中碳化硅用量占总用量的3.0%,纳米二氧化硅用量占总用量的1.5%,因此碳化硅用量占总用量的3%左右、纳米二氧化硅用量占总用量在1.2%-1.5%之间时制备出来的智能烟灰缸金属外壳专用纳米防腐耐磨涂料在防腐性能和耐磨性能上较好,提高了智能烟灰缸金属外壳专用纳米防腐耐磨涂料的使用寿命,从而提高了智能烟灰缸金属外壳的使用寿命,达到了目的。
本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (2)
1.一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料,其特征在于:该涂料由以下重量份的组分组成:环氧树脂42-50份、环氧树脂固化剂20-26份、陶瓷骨料碳化硅28-34份、陶瓷骨料氧化铝10-12份、纳米碳化硅3-4份、纳米二氧化硅1-2份、研磨剂2-3份、消泡剂0.3-0.6份、润湿剂0.1-0.2份和流平剂0.8-1.2份。
2.根据权利要求1所述的一种智能烟灰缸金属外壳专用纳米防腐耐磨涂料的制备方法,其特征在于:包以下步骤:
(1)、先将固定颗粒状的陶瓷骨料碳化硅、陶瓷骨料氧化铝、纳米碳化硅、纳米二氧化硅、研磨剂依次加入研磨机中,研磨机研磨10-15分钟;
(2)、再加入环氧树脂和环氧树脂固化剂,得到混合物;
(3)、将步骤(2)中得到的混合物依次加入消泡剂、润湿剂、流平剂,在室温条件下利用搅拌机均匀搅拌10-30分钟,得到所需涂料。