CN104946070A - Special anticorrosive coating for bus duct - Google Patents

Special anticorrosive coating for bus duct Download PDF

Info

Publication number
CN104946070A
CN104946070A CN201510231680.2A CN201510231680A CN104946070A CN 104946070 A CN104946070 A CN 104946070A CN 201510231680 A CN201510231680 A CN 201510231680A CN 104946070 A CN104946070 A CN 104946070A
Authority
CN
China
Prior art keywords
parts
bus duct
anticorrosive coating
special anticorrosive
mixing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510231680.2A
Other languages
Chinese (zh)
Inventor
陈道华
马道平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Shilin Electrical Equipment Co Ltd
Original Assignee
Jiangsu Shilin Electrical Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Shilin Electrical Equipment Co Ltd filed Critical Jiangsu Shilin Electrical Equipment Co Ltd
Priority to CN201510231680.2A priority Critical patent/CN104946070A/en
Publication of CN104946070A publication Critical patent/CN104946070A/en
Pending legal-status Critical Current

Abstract

The invention discloses a special anticorrosive coating for a bus duct. The special anticorrosive coating is prepared from the following components in parts by mass: 26-35 parts of epoxy resin, 10-20 parts of acrylic resin, 5-8 parts of silane coupling agent, 10-15 parts of chlorinated paraffin, 5-10 parts of aluminum powder, 3-8 parts of titanium white and 8-15 parts of curing agent. The special anticorrosive coating for the bus duct has the advantages of high non-corrosibility, high salt water resistance, non-toxicity, environmental-friendly and the like; the anticorrosive coating is capable of effectively protecting the bus duct, preventing the problems of electrical short circuit and the like of the bus duct due to oxidation corrosion, and improving the durability and safety.

Description

A kind of bus duct anticorrosion paint special
Technical field
The present invention relates to a kind of protective system, particularly a kind of bus duct anticorrosion paint special.
Technical background
Along with emerging in large numbers of modernization project facility and equipment, the fast increasing of power consumption of all trades and professions, the appearance in especially numerous Highrise buildingss and large-sized workshop workshop, traditional cable as transmission pressure can not meet the demands in big current delivery system, and the parallel connection of multiway cable uses and brings inconvenience to in-site installation construction connection.Bus duct arises at the historic moment as a kind of new distribution wire, and bus duct, compared with traditional cable, fully demonstrates its superiority when big current is carried.
Bus duct is divided into outer steel shell, aluminum alloy casing and aluminum-steel hybrid outer shell bus slot by its sheating material, and as a kind of power distribution unit of efficient conveying electric current, because of the easy oxidized corrosion of its material characteristic, need be coated with one deck protective system increases wearing quality and security.
Summary of the invention
The object of this invention is to provide a kind of bus duct anticorrosion paint special, increase the antiseptic power of bus duct, improve wearing quality, avoid causing the problems such as electric short circuit because of the oxidation corrosion of bus duct shell, improve security.
For solving the problem, technical scheme of the present invention is:
A kind of bus duct anticorrosion paint special, wherein, its moiety is as follows according to the mass fraction:
Epoxy resin 26-35 part
Acrylic resin 10-20 part
Silane coupling agent 5-8 part
Clorafin 10-15 part
Aluminium powder 5-10 part
Titanium dioxide 3-8 part
Solidifying agent 8-15 part
Above-mentioned a kind of bus duct anticorrosion paint special, wherein, preferably, its moiety is as follows according to the mass fraction:
Epoxy resin 32 parts
Acrylic resin 18 parts
Silane coupling agent 7 parts
Clorafin 12 parts
Aluminium powder 6 parts
Titanium dioxide 5 parts
12 parts, solidifying agent.
Above-mentioned a kind of bus duct anticorrosion paint special, wherein, described solidifying agent is the one of trimethylammonium in diamines or m-xylene diamine.
Beneficial effect of the present invention is:
The present invention adopts new formulation; unique formula is adopted to accomplish effectively anticorrosion; and there is the advantages such as resistance to salt water is strong, asepsis environment-protecting; adopt the protective system that the present invention obtains; can available protecting bus duct; prevent bus duct from causing the problems such as electric short circuit because of oxidation corrosion, improve wearing quality and security.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
32 parts of epoxy resin are put into reactor with 18 parts of acrylic resins mix, mixing time is 1.5h, mixing temperature is 45 degree, and mixing rate is 180r/min, adds 7 parts of silane coupling agents and 12 parts of clorafins after mixing terminates, continue to stir 30min, then add 7 parts of aluminium powders, 5 parts of titanium dioxides, 12 parts of trimethylammoniums diamines, mixing temperature is 50 degree, and mixing rate is 140r/min, until after mixing, naturally cool to normal temperature.
Embodiment 2
30 parts of epoxy resin are put into reactor with 15 parts of acrylic resins mix, mixing time is 1h, mixing temperature is 50 degree, and mixing rate is 150r/min, adds 6 parts of silane coupling agents and 10 parts of clorafins after mixing terminates, continue to stir 30min, then add 6 parts of aluminium powders, 6 parts of titanium dioxides, 10 parts of trimethylammoniums diamines, mixing temperature is 55 degree, and mixing rate is 130r/min, until after mixing, naturally cool to normal temperature.
Embodiment 3
28 parts of epoxy resin are put into reactor with 12 parts of acrylic resins mix, mixing time is 1h, mixing temperature is 55 degree, and mixing rate is 160r/min, adds 6 parts of silane coupling agents and 13 parts of clorafins after mixing terminates, continue to stir 30min, then add 8 parts of aluminium powders, 5 parts of titanium dioxides, 11 parts of m-xylene diamines, mixing temperature is 50 degree, and mixing rate is 150r/min, until after mixing, naturally cool to normal temperature.
Unique formula of the present invention is adopted to accomplish effectively anticorrosion; and there is the advantages such as resistance to salt water is strong, asepsis environment-protecting, and adopt the protective system that the present invention obtains, can available protecting bus duct; prevent bus duct from causing the problems such as electric short circuit because of oxidation corrosion, improve wearing quality and security.
The above; be only the present invention's preferably embodiment, but protection scope of the present invention is not limited thereto, is anyly familiar with those skilled in the art in the technical scope that the present invention discloses; the change that can expect easily or replacement, all should be encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claims.

Claims (2)

1. a bus duct anticorrosion paint special, is characterized in that, its moiety is as follows according to the mass fraction:
Epoxy resin 26-35 part
Acrylic resin 10-20 part
Silane coupling agent 5-8 part
Clorafin 10-15 part
Aluminium powder 5-10 part
Titanium dioxide 3-8 part
Solidifying agent 8-15 part.
2. a kind of bus duct anticorrosion paint special as claimed in claim 1, is characterized in that, described solidifying agent is the one of trimethylammonium in diamines or m-xylene diamine.
CN201510231680.2A 2015-05-08 2015-05-08 Special anticorrosive coating for bus duct Pending CN104946070A (en)