CN103497552B - A kind of anti-corrosion wear resisting powder paint - Google Patents
A kind of anti-corrosion wear resisting powder paint Download PDFInfo
- Publication number
- CN103497552B CN103497552B CN201310393160.2A CN201310393160A CN103497552B CN 103497552 B CN103497552 B CN 103497552B CN 201310393160 A CN201310393160 A CN 201310393160A CN 103497552 B CN103497552 B CN 103497552B
- Authority
- CN
- China
- Prior art keywords
- powder paint
- wear resisting
- corrosion wear
- raw material
- compounded mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of anti-corrosion wear resisting powder paint, it is made up of the raw material of following weight parts: triethanolamine 1-2, tetraphenolic ethane tetraglycidel ether epoxy resin 50-60, polybenzimidazoles 2-5, biacetyl aniline 2-3, polyvinyl butyral resin 3-5, triallyl cyanurate 0.2-0.4, poly-4-methyl-1-pentene 2-3, aluminum nitride powder 3-5, compounded mix 10-20；Powder of the present invention have anticorrosion, wear-resisting, strengthening effect, can be widely used for various metallic conduit, in acid or alkali environment machinery anticorrosion, also can be used to strengthen cast tube, it is also possible to make the binding agent of rigid material.
Description
Technical field
The invention mainly relates to a kind of coating, particularly relate to a kind of anti-corrosion wear resisting powder paint.
Background technology
Its characteristic of powdery paints has: 1, this product is without toxicity, without solvent with without the virose material that volatilizees, therefore without poisoning, without the problem of fire, the public hazards such as discharge of nothing " three wastes ", comply fully with the requirement of national environmental protection method.2, utilization rate of raw materials is high, and the powder that the powder supplies business of some famous brand names produces, the powder recoverable of its overspray, the highest utilization rate even can reach more than 99%.3, after coated article pre-treatment, one-off construction, it is not necessary to primary coat, the film of adequate thickness can be obtained, easily realize automation mechanized operation, production efficiency is high, it is possible to decrease cost.4, coating densification, adhesive force, impact strength and toughness are all good, and corner coverage is high, has excellent resistance to corrosive chemicals energy and electrical insulation properties.5, powdery paints storage, transportation safety and convenience.
Summary of the invention
The object of the invention is contemplated to provide a kind of anti-corrosion wear resisting powder paint.
The present invention is achieved by the following technical solutions:
A kind of anti-corrosion wear resisting powder paint, it is characterised in that it is made up of the raw material of following weight parts:
Triethanolamine 1-2, tetraphenolic ethane tetraglycidel ether epoxy resin 50-60, polybenzimidazoles 2-5, biacetyl aniline 2-3, polyvinyl butyral resin 3-5, triallyl cyanurate 0.2-0.4, poly-4-methyl-1-pentene 2-3, aluminum nitride powder 3-5, compounded mix 10-20；
Described compounded mix is made up of the raw material of following weight parts:
Gibbsite 30-40, attapulgite 20-30, carborundum 6-10, magnesium hydroxide 3-5, carboxymethyl cellulose 1-2, Jojoba oil 2-3；
By above-mentioned gibbsite, attapulgite, carborundum mixing, insulation calcining 2-4 hour at 600-800 DEG C, send in ball mill after discharging cooling and carry out ball milling mixing, add magnesium hydroxide and carboxymethyl cellulose, continue ball milling 1-2 hour, add after Jojoba oil is heated to 25-30 DEG C, ball milling, cross 80-100 mesh sieve, obtain described compounded mix.
The preparation method of a kind of anti-corrosion wear resisting powder paint, comprises the following steps:
Above-mentioned each raw material is mixed, melt extrudes through extruder, air-cooled, coarse pulverization, pulverizing, sieve, obtain described anti-corrosion wear resisting powder paint.
The invention have the advantage that
Powder of the present invention have anticorrosion, wear-resisting, strengthening effect, can be widely used for various metallic conduit, in acid or alkali environment machinery anticorrosion, also can be used to strengthen cast tube, it is also possible to make the binding agent of rigid material.
Detailed description of the invention
Embodiment 1,
A kind of anti-corrosion wear resisting powder paint, it is made up of the raw material of following weight parts (kilogram):
Triethanolamine 2, tetraphenolic ethane tetraglycidel ether epoxy resin 60, polybenzimidazoles 5, biacetyl aniline 2, polyvinyl butyral resin 3, triallyl cyanurate 0.4, poly-4-methyl-1-pentene 2, aluminum nitride powder 3, compounded mix 20；
Described compounded mix is made up of the raw material of following weight parts:
Gibbsite 40, attapulgite 30, carborundum 10, magnesium hydroxide 5, carboxymethyl cellulose 1, Jojoba oil 2；
By above-mentioned gibbsite, attapulgite, carborundum mixing, insulation calcining 4 hours at 800 DEG C, send in ball mill after discharging cooling and carry out ball milling mixing, add magnesium hydroxide and carboxymethyl cellulose, continue ball milling 1 hour, add after Jojoba oil is heated to 30 DEG C, ball milling, cross 100 mesh sieves, obtain described compounded mix.
The preparation method of a kind of anti-corrosion wear resisting powder paint, comprises the following steps:
Above-mentioned each raw material is mixed, melt extrudes through extruder, air-cooled, coarse pulverization, pulverizing, sieve, obtain described anti-corrosion wear resisting powder paint.
Performance test:
Solvent resistant: 240 hours, unchanged；
Salt spray test (1000h): unchanged.
Claims (2)
1. an anti-corrosion wear resisting powder paint, it is characterised in that it is made up of the raw material of following weight parts:
Triethanolamine 1-2, tetraphenolic ethane tetraglycidel ether epoxy resin 50-60, polybenzimidazoles 2-5, biacetyl aniline 2-3, polyvinyl butyral resin 3-5, triallyl cyanurate 0.2-0.4, poly-4-methyl-1-pentene 2-3, aluminum nitride powder 3-5, compounded mix 10-20；
Described compounded mix is made up of the raw material of following weight parts:
Gibbsite 30-40, attapulgite 20-30, carborundum 6-10, magnesium hydroxide 3-5, carboxymethyl cellulose 1-2, Jojoba oil 2-3；
By above-mentioned gibbsite, attapulgite, carborundum mixing, insulation calcining 2-4 hour at 600-800 DEG C, send in ball mill after discharging cooling and carry out ball milling mixing, add magnesium hydroxide and carboxymethyl cellulose, continue ball milling 1-2 hour, add after Jojoba oil is heated to 25-30 DEG C, ball milling, cross 80-100 mesh sieve, obtain described compounded mix.
2. the preparation method of an anti-corrosion wear resisting powder paint as claimed in claim 1, it is characterised in that comprise the following steps:
Above-mentioned each raw material is mixed, melt extrudes through extruder, air-cooled, coarse pulverization, pulverizing, sieve, obtain described anti-corrosion wear resisting powder paint.