CN104263202A - Harbor instrument powdery paint - Google Patents
Harbor instrument powdery paint Download PDFInfo
- Publication number
- CN104263202A CN104263202A CN201410430885.9A CN201410430885A CN104263202A CN 104263202 A CN104263202 A CN 104263202A CN 201410430885 A CN201410430885 A CN 201410430885A CN 104263202 A CN104263202 A CN 104263202A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- instrument
- harbour
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a harbor instrument powdery paint, which is composed of the following raw materials in parts by weight: 40 to 60 parts of E12 epoxy resin, 5 to 10 parts of triethylene tetramine, 0.5 to 1 part of triallyl cyanurate, 1 to 2 parts of isopropyl tri(dioctylpyrophosphate) titanate, 2 to 3 parts of bamboo carbon powder, 7 to 10 parts of celestite powder, 1.3 to 2 parts of 2,6-bitert-butyl-paracresol, 0.2 to 1 part of zirconium fluoride, 0.1 to 0.4 part of 2,4,6-tri(dimethylaminomethyl)phenol, and 10 to 13 parts of composite filling material. The binding force between the powdery paint coating and the substrate is strong. The paint coating has the advantages of high mechanical strength, strong penetration resistant performance, good chemical stability, strong resistance to sea water corrosion, and low surface roughness. Moreover, the friction between the paint coating and the fluid is very small, and thus the damage to the coating can be reduced.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of harbour instrument powder coating.
Background technology
Along with the development of society; the Working environment of various instrument becomes more complicated; vault, harbour, shaft bottom, deep water, tunnel, chemical industry factory site etc.; high/low temperature change, high pressure, HI high impact, high corrosion etc. have impact on the normal use of this instrument greatly; and applied by efficient powder coating; good protected effect can be played, reduce the spoilage of instrument.
Summary of the invention
The object of the invention is exactly to provide a kind of harbour instrument powder coating.
The present invention is achieved by the following technical solutions:
A kind of harbour instrument powder coating, is characterized in that what it was made up of the raw material of following weight parts:
E12 epoxy resin 40-60, triethylene tetramine 5-10, triallyl cyanurate 0.5-1, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 1-2, bamboo charcoal powder 2-3, celestite powder 7-10,2,6-ditertbutylparacresol 1.3-2, Zirconium tetrafluoride 0.2-1,2,4,6-tri-(dimethylamino methyl) phenol 0.1-0.4, compounded mix 10-13;
Described compounded mix is made up of the raw material of following weight parts:
Laterite 30-40, wollastonite powder 10-14, attapulgite 8-10, process white 6-8, chitosan 2-3, cocounut oil 1-2, cyanacrylate 0.1-0.3;
By above-mentioned laterite, wollastonite powder, attapulgite mixing, 2-4 hour is calcined at 600-800 DEG C, discharging cools rear and process white mixed grinding, add after cyanacrylate being heated to 25-30 DEG C, 300-400 rev/min of dispersed with stirring 4-6 minute, adds chitosan, cocounut oil, abundant ball milling, cross 100-120 mesh sieve, obtain described compounded mix.
A preparation method for harbour instrument powder coating, comprises the following steps:
By above-mentioned bamboo charcoal powder, celestite powder mixing, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is added after stirring, stirring heating 4-6 minute at 60-70 DEG C, be cooled to normal temperature, add each raw material of residue, by melt extruding in forcing machine, then after compressing tablet fragmentation, pulverize through pulverising mill, sieve again, obtain described harbour instrument powder coating.
Advantage of the present invention is:
The physical strength of powder coating coating of the present invention and the strong coating of base material bonding force self is high, and impermeabilisation ability is strong, and chemical stability is good, has very high resistance to the corrosion of seawater, and coatingsurface roughness is low, little with fluid friction, can reduce the infringement to coating.
Embodiment
Embodiment 1,
A kind of harbour instrument powder coating, it is made up of the raw material of following weight parts (kilogram):
E12 epoxy resin 60, triethylene tetramine 10, triallyl cyanurate 0.5, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 1, bamboo charcoal powder 2, celestite powder 10,2,6-ditertbutylparacresol 1.3, Zirconium tetrafluoride 0.2,2,4,6-tri-(dimethylamino methyl) phenol 0.4, compounded mix 10;
Described compounded mix is made up of the raw material of following weight parts:
Laterite 40, wollastonite powder 14, attapulgite 10, process white 8, chitosan 3, cocounut oil 1, cyanacrylate 0.3;
By above-mentioned laterite, wollastonite powder, attapulgite mixing, calcine 4 hours at 800 DEG C, discharging cools rear and process white mixed grinding, add after cyanacrylate being heated to 30 DEG C, 400 revs/min of dispersed with stirring 6 minutes, add chitosan, cocounut oil, abundant ball milling, cross 120 mesh sieves, obtain described compounded mix.
A preparation method for harbour instrument powder coating, comprises the following steps:
By above-mentioned bamboo charcoal powder, celestite powder mixing, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is added after stirring, stirring heating 6 minutes at 70 DEG C, be cooled to normal temperature, add each raw material of residue, by melt extruding in forcing machine, then after compressing tablet fragmentation, pulverize through pulverising mill, sieve again, obtain described harbour instrument powder coating.
Performance test:
Shock resistance: >=50kg/cm;
Hardness >=2H.
Claims (2)
1. a harbour instrument powder coating, is characterized in that what it was made up of the raw material of following weight parts:
E12 epoxy resin 40-60, triethylene tetramine 5-10, triallyl cyanurate 0.5-1, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 1-2, bamboo charcoal powder 2-3, celestite powder 7-10,2,6-ditertbutylparacresol 1.3-2, Zirconium tetrafluoride 0.2-1,2,4,6-tri-(dimethylamino methyl) phenol 0.1-0.4, compounded mix 10-13;
Described compounded mix is made up of the raw material of following weight parts:
Laterite 30-40, wollastonite powder 10-14, attapulgite 8-10, process white 6-8, chitosan 2-3, cocounut oil 1-2, cyanacrylate 0.1-0.3;
By above-mentioned laterite, wollastonite powder, attapulgite mixing, 2-4 hour is calcined at 600-800 DEG C, discharging cools rear and process white mixed grinding, add after cyanacrylate being heated to 25-30 DEG C, 300-400 rev/min of dispersed with stirring 4-6 minute, adds chitosan, cocounut oil, abundant ball milling, cross 100-120 mesh sieve, obtain described compounded mix.
2. a preparation method for harbour as claimed in claim 1 instrument powder coating, is characterized in that comprising the following steps:
By above-mentioned bamboo charcoal powder, celestite powder mixing, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester is added after stirring, stirring heating 4-6 minute at 60-70 DEG C, be cooled to normal temperature, add each raw material of residue, by melt extruding in forcing machine, then after compressing tablet fragmentation, pulverize through pulverising mill, sieve again, obtain described harbour instrument powder coating.