CN103589328A - Photostable nylon resin paint - Google Patents
Photostable nylon resin paint Download PDFInfo
- Publication number
- CN103589328A CN103589328A CN201310506764.3A CN201310506764A CN103589328A CN 103589328 A CN103589328 A CN 103589328A CN 201310506764 A CN201310506764 A CN 201310506764A CN 103589328 A CN103589328 A CN 103589328A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- raw material
- nylon resin
- mix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a photostable nylon resin paint which is prepared from the following raw materials in parts by weight: 60-70 parts of nylon 1212 resin, 1-2 parts of chitosan, 2-3 parts of polysiloxane, 3-4 parts of polybenzimidazole fiber, 1-2 parts of tetrabromobisphenol A, 1-2 parts of tetramethoxymethyl glycoluril, 2-3 parts of photostabilizer 622, 13-20 parts of silicon micropowder, 10-14 parts of methyl methacrylate, 1-3 parts of poly-4-methyl-1-amylene, 2-3 parts of citronella oil and 20-25 parts of composite filler. The paint has the advantages of high photostability, favorable leveling property of the coated film, high adhesive strength, favorable protective performance for the substrate, high safety and environment protection.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of light and stablizes nylon resin coating.
Background technology
Object is exposed among atmosphere, is subject to the erosion of oxygen, moisture etc., causes the breakoff phenomenons such as corrosion of metal, foxy, cement weathering.At article surface, be coated with coating; form layer protecting film; can stop or postpone generation and the development of these breakoff phenomenons; extended the work-ing life of various materials; along with social development; requirement for coating quality is also more and more higher, also more and more higher for the pursuit of the performances such as anticorrosion, waterproof, grease proofing, chemicals-resistant, fast light, heatproof.
Summary of the invention
The object of the invention is just to provide a kind of light and stablizes nylon resin coating.
The present invention is achieved by the following technical solutions:
Stablize a nylon resin coating, it is comprised of the raw material of following weight parts:
Nylon 1212 resin 60-70, chitosan 1-2, polysiloxane 2-3, polybenzimidazole fibre 3-4, tetrabromo-bisphenol 1-2, tetramethoxymethylglycoluril 1-2, photostabilizer 622 2-3, silicon powder 13-20, methyl methacrylate 10-14, poly--4-methyl-1-pentene 1-3, pamorusa oil 2-3, compounded mix 20-25;
Described compounded mix is comprised of the raw material of following weight parts:
Black husky 5-7, chrysotile 10-16, jade powder 10-15, ceramics powder 3-5, alkylolamide 2-3, octyl group isothiazolinone 1-2,2,6-ditertbutylparacresol 1-2;
Above-mentioned black sand, jade powder, chrysotile are mixed, at 500-600 ℃, calcine 2-3 hour, after discharging is cooling, add octyl group isothiazolinone, add suitable quantity of water again and fully grind, the hydrochloric acid adjusting PH that adds 10-15% is 4-5, adds ceramics powder, at 80-100 ℃, be incubated 10-20 minute, grind, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying is dry, obtain powder, mix with each raw material of residue, fully grind, cross 80-100 mesh sieve, obtain described compounded mix.
Light is stablized a preparation method for nylon resin coating, comprises the following steps:
Above-mentioned chitosan is mixed with silicon powder, polysiloxane, after stirring, add poly--4-methyl-1-pentene, pamorusa oil, 400-600 rev/min of dispersed with stirring 10-12 minute, mix with each raw material of residue, melt extrude compressing tablet, air-cooled, abrasive dust, sieve, and obtains described light and stablize nylon resin coating.
Advantage of the present invention is:
Coating of the present invention has good light stability, and the good leveling property of filming has very strong bond strength, good to the protectiveness of base material, safety and environmental protection.
Embodiment
Embodiment 1
Stablize a nylon resin coating, it by following weight parts (kilogram) raw material form:
Nylon 1212 resin 70, chitosan 1, polysiloxane 2, polybenzimidazole fibre 4, tetrabromo-bisphenol 1, tetramethoxymethylglycoluril 1, photostabilizer 622 3, silicon powder 20, methyl methacrylate 12, poly--4-methyl-1-pentene 1, pamorusa oil 2, compounded mix 25;
Described compounded mix is comprised of the raw material of following weight parts:
Black husky 7, chrysotile 16, jade powder 15, ceramics powder 5, alkylolamide 3, octyl group isothiazolinone 1,2,6-ditertbutylparacresol 1;
Above-mentioned black sand, jade powder, chrysotile are mixed, at 600 ℃, calcine 2 hours, after discharging is cooling, add octyl group isothiazolinone, add suitable quantity of water again and fully grind, adding 15% hydrochloric acid, to regulate PH be 4, adds ceramics powder, at 100 ℃, be incubated 20 minutes, grind, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying is dry, obtain powder, mix with each raw material of residue, fully grind, cross 100 mesh sieves, obtain described compounded mix.
Light is stablized a preparation method for nylon resin coating, comprises the following steps:
Above-mentioned chitosan is mixed with silicon powder, polysiloxane, after stirring, add poly--4-methyl-1-pentene, pamorusa oil, 600 revs/min of dispersed with stirring 12 minutes, mix with each raw material of residue, melt extrude compressing tablet, air-cooled, abrasive dust, sieve, and obtains described light and stablize nylon resin coating.
Performance test:
Shock resistance: >=50kg/cm;
Hardness: 2H.
Claims (2)
1. light is stablized a nylon resin coating, it is characterized in that what it was comprised of the raw material of following weight parts:
Nylon 1212 resin 60-70, chitosan 1-2, polysiloxane 2-3, polybenzimidazole fibre 3-4, tetrabromo-bisphenol 1-2, tetramethoxymethylglycoluril 1-2, photostabilizer 622 2-3, silicon powder 13-20, methyl methacrylate 10-14, poly--4-methyl-1-pentene 1-3, pamorusa oil 2-3, compounded mix 20-25;
Described compounded mix is comprised of the raw material of following weight parts:
Black husky 5-7, chrysotile 10-16, jade powder 10-15, ceramics powder 3-5, alkylolamide 2-3, octyl group isothiazolinone 1-2,2,6-ditertbutylparacresol 1-2;
Above-mentioned black sand, jade powder, chrysotile are mixed, at 500-600 ℃, calcine 2-3 hour, after discharging is cooling, add octyl group isothiazolinone, add suitable quantity of water again and fully grind, the hydrochloric acid adjusting PH that adds 10-15% is 4-5, adds ceramics powder, at 80-100 ℃, be incubated 10-20 minute, grind, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying is dry, obtain powder, mix with each raw material of residue, fully grind, cross 80-100 mesh sieve, obtain described compounded mix.
2. light as claimed in claim 1 is stablized a preparation method for nylon resin coating, it is characterized in that comprising the following steps:
Above-mentioned chitosan is mixed with silicon powder, polysiloxane, after stirring, add poly--4-methyl-1-pentene, pamorusa oil, 400-600 rev/min of dispersed with stirring 10-12 minute, mix with each raw material of residue, melt extrude compressing tablet, air-cooled, abrasive dust, sieve, and obtains described light and stablize nylon resin coating.