CN103589280B - A kind of breathing epoxy coating - Google Patents
A kind of breathing epoxy coating Download PDFInfo
- Publication number
- CN103589280B CN103589280B CN201310506800.6A CN201310506800A CN103589280B CN 103589280 B CN103589280 B CN 103589280B CN 201310506800 A CN201310506800 A CN 201310506800A CN 103589280 B CN103589280 B CN 103589280B
- Authority
- CN
- China
- Prior art keywords
- powder
- raw material
- epoxy coating
- breathing
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of breathing epoxy coating, it is made up of the raw material of following weight parts: E-12 epoxy resin 70-76, beta-diketon 0.7-1, fatty alcohol-polyoxyethylene ether 1-2, cuprichexafluorosilicate 2-3, diethylenetriamine 10-13, diatomite 1-2, boric acid 2-3, butyl polyacrylate 3-5, alkyl phosphate diethanolamine salt 1-2, Radix Angelicae Sinensis oil 2-4, sepiolite powder 10-15, compounded mix 10-13; Coating good permeability of the present invention, aobvious bubble, shrinkage cavity or particle, coating stable, weather resisteant is strong, and the protectiveness for base material is good.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of breathing epoxy coating.
Background technology
Object is exposed among air, is subject to the erosion of oxygen, moisture etc., causes the breakoff phenomenons such as corrosion of metal, foxy, cement weathering.Coating is coated with at article surface; form layer protecting film; can stop or postpone generation and the development of these breakoff phenomenons; the work-ing life of various material is extended; along with the development of society; requirement for coating quality is also more and more higher, and the pursuit for the performance such as anticorrosion, waterproof, grease proofing, chemicals-resistant, fast light, heatproof is also more and more higher.
Summary of the invention
The object of the invention is just to provide a kind of breathing epoxy coating.
The present invention is achieved by the following technical solutions:
A kind of breathing epoxy coating, it is made up of the raw material of following weight parts:
E-12 epoxy resin 70-76, beta-diketon 0.7-1, fatty alcohol-polyoxyethylene ether 1-2, cuprichexafluorosilicate 2-3, diethylenetriamine 10-13, diatomite 1-2, boric acid 2-3, butyl polyacrylate 3-5, alkyl phosphate diethanolamine salt 1-2, Radix Angelicae Sinensis oil 2-4, sepiolite powder 10-15, compounded mix 10-13;
Described compounded mix is made up of the raw material of following weight parts:
Black husky 5-7, chrysotile 10-16, jade powder 10-15, ceramics powder 3-5, alkylolamide 2-3, octylisothiazolinone 1-2,2,6 ditertiary butyl p cresol 1-2;
By above-mentioned black sand, jade powder, chrysotile mixing, at 500-600 DEG C, calcine 2-3 hour, after discharging cooling, add octylisothiazolinone, add suitable quantity of water more fully to grind, the hydrochloric acid adding 10-15% regulates PH to be 4-5, adds ceramics powder, at 80-100 DEG C, be incubated 10-20 minute, grinding, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, obtain powder, mix with each raw material of residue, fully grind, cross 80-100 mesh sieve, obtain described compounded mix.
A preparation method for breathing epoxy coating, comprises the following steps:
Mixed with diatomite by above-mentioned sepiolite powder, add Radix Angelicae Sinensis oil, insulated and stirred 40-50 minute at 60-80 DEG C, mix with each raw material of residue, melt extrude, compressing tablet, air-cooled, abrasive dust, sieves, and obtains described breathing epoxy coating.
Advantage of the present invention is:
Coating good permeability of the present invention, aobvious bubble, shrinkage cavity or particle, coating stable, weather resisteant is strong, and the protectiveness for base material is good.
Embodiment
Embodiment 1
A kind of breathing epoxy coating, it is made up of the raw material of following weight parts (kilogram):
E-12 epoxy resin 76, beta-diketon 0.7, fatty alcohol-polyoxyethylene ether 1, cuprichexafluorosilicate 2, diethylenetriamine 13, diatomite 1, boric acid 2, butyl polyacrylate 5, alkyl phosphate diethanolamine salt 1, Radix Angelicae Sinensis oil 4, sepiolite powder 15, compounded mix 13;
Described compounded mix is made up of the raw material of following weight parts:
Black husky 5, chrysotile 16, jade powder 15, ceramics powder 5, alkylolamide 3, octylisothiazolinone 2,2,6 ditertiary butyl p cresol 2;
By above-mentioned black sand, jade powder, chrysotile mixing, calcine 2 hours at 500 DEG C, after discharging cooling, add octylisothiazolinone, add suitable quantity of water more fully to grind, the hydrochloric acid adding 15% regulates PH to be 5, adds ceramics powder, at 100 DEG C, be incubated 10 minutes, grinding, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, obtain powder, mix with each raw material of residue, fully grind, cross 100 mesh sieves, obtain described compounded mix.
A preparation method for breathing epoxy coating, comprises the following steps:
Mixed with diatomite by above-mentioned sepiolite powder, add Radix Angelicae Sinensis oil, insulated and stirred 40 minutes at 80 DEG C, mix with each raw material of residue, melt extrude, compressing tablet, air-cooled, abrasive dust, sieves, and obtains described breathing epoxy coating.
Performance test:
Shock resistance: >=50kg/cm;
Hardness: 2H.
Claims (2)
1. a breathing epoxy coating, is characterized in that what it was made up of the raw material of following weight parts: E-12 epoxy resin 70-76, beta-diketon 0.7-1, fatty alcohol-polyoxyethylene ether 1-2, cuprichexafluorosilicate 2-3, diethylenetriamine 10-13, diatomite 1-2, boric acid 2-3, butyl polyacrylate 3-5, alkyl phosphate diethanolamine salt 1-2, Radix Angelicae Sinensis oil 2-4, sepiolite powder 10-15, compounded mix 10-13; Described compounded mix is made up of the raw material of following weight parts: black husky 5-7, chrysotile 10-16, jade powder 10-15, ceramics powder 3-5, alkylolamide 2-3, octylisothiazolinone 1-2,2,6 ditertiary butyl p cresol 1-2; By above-mentioned black sand, jade powder, chrysotile mixing, at 500-600 DEG C, calcine 2-3 hour, after discharging cooling, add octylisothiazolinone, add suitable quantity of water more fully to grind, the salt acid for adjusting pH adding 10-15% is 4-5, adds ceramics powder, at 80-100 DEG C, be incubated 10-20 minute, grinding, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, obtain powder, mix with each raw material of residue, fully grind, cross 80-100 mesh sieve, obtain described compounded mix.
2. the preparation method of a breathing epoxy coating as claimed in claim 1, it is characterized in that comprising the following steps: above-mentioned sepiolite powder is mixed with diatomite, add Radix Angelicae Sinensis oil, insulated and stirred 40-50 minute at 60-80 DEG C, mixes with each raw material of residue, melt extrudes, compressing tablet, air-cooled, abrasive dust, sieves, and obtains described breathing epoxy coating.