CN103497552A - Anticorrosion wear-resistant powdery paint - Google Patents
Anticorrosion wear-resistant powdery paint Download PDFInfo
- Publication number
- CN103497552A CN103497552A CN201310393160.2A CN201310393160A CN103497552A CN 103497552 A CN103497552 A CN 103497552A CN 201310393160 A CN201310393160 A CN 201310393160A CN 103497552 A CN103497552 A CN 103497552A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- wear resisting
- ball milling
- powder paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anticorrosion wear-resistant powdery paint which is composed of the raw materials of, by weight: 1-2 parts of triethanolamine, 50-60 parts of tetraphenol ethane tetraglycidyl ether epoxy resin, 2-5 parts of polybenzimidazole, 2-3 parts of diacetyl aniline, 3-5 parts of polyvinyl butyral, 0.2-0.4 parts of cyanuric triallyl, 2-3 parts of poly-4-methyl-1-pentene, 3-5 parts of aluminum nitride powder, and 10-20 parts of a composite filling material. The powder provided by the invention has anticorrosion, wear-resistant, and strengthening functions, and can be widely applied in corrosion resistance of various metal pipes and machinery in acidic/alkaline environments. The powdery paint can also be used for strengthening cast pipes, and can be used as a binder for rigid materials.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of anti-corrosion wear resisting powder paint.
Background technology
Its characteristic of powder coating has: 1, this product is containing toxicity, containing solvent with containing the virose material that volatilizees, therefore without poisoning, without the problem of the public hazards such as discharge of fire, nothing " three wastes ", meet the requirement of national environmental protection method fully.2, utilization rate of raw materials is high, the powder that the powder supplies business of some famous brand names produces, and it crosses the powder recoverable of spray, and the highest utilization ratio even can reach more than 99%.3, after the coated article pre-treatment, one-off construction, without primary coat, can obtain filming of adequate thickness, easily realizes automated operation, and production efficiency is high, can reduce costs.4, coating densification, sticking power, resistance to impact shock and toughness are all good, and corner coverage is high, have good resistance to corrosive chemicals energy and electrical insulation properties.5, powder coating storage, transportation safety and convenient.
Summary of the invention
The object of the invention is exactly for a kind of anti-corrosion wear resisting powder paint is provided.
The present invention is achieved by the following technical solutions:
A kind of anti-corrosion wear resisting powder paint is characterized in that what it was comprised of the raw material of following weight parts:
Trolamine 1-2, tetraphenolic ethane tetraglycidel ether epoxy resin 50-60, polybenzimidazole 2-5, di-acetyl aniline 2-3, polyvinyl butyral acetal 3-5, triallyl cyanurate 0.2-0.4, poly--4-methyl-1-pentene 2-3, aluminum nitride powder 3-5, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Gibbsite 30-40, attapulgite 20-30, silicon carbide 6-10, magnesium hydroxide 3-5, carboxymethyl cellulose 1-2, Jojoba oil 2-3;
Above-mentioned gibbsite, attapulgite, silicon carbide are mixed, insulation calcining 2-4 hour under 600-800 ℃, send into after discharging is cooling in ball mill and carry out the ball milling mixing, add again magnesium hydroxide and carboxymethyl cellulose, continue ball milling 1-2 hour, add ball milling after Jojoba oil is heated to 25-30 ℃, cross the 80-100 mesh sieve, obtain described compounded mix.
A kind of preparation method of anti-corrosion wear resisting powder paint comprises the following steps:
Above-mentioned each raw material is mixed, melt extrude through forcing machine, air-cooled, coarse reduction, abrasive dust, sieve, and obtains described anti-corrosion wear resisting powder paint.
Advantage of the present invention is:
That powder of the present invention has is anticorrosion, wear-resisting, the effect of strengthening, can be widely used in various metallic conduits, and in acid or alkali environment, the protection against corrosion of machinery, also can be used to strengthen cast tube, can also make the binding agent of rigid material.
Embodiment
Embodiment 1,
A kind of anti-corrosion wear resisting powder paint, it is comprised of the raw material of following weight parts (kilogram):
Trolamine 2, tetraphenolic ethane tetraglycidel ether epoxy resin 60, polybenzimidazole 5, di-acetyl aniline 2, polyvinyl butyral acetal 3, triallyl cyanurate 0.4, poly--4-methyl-1-pentene 2, aluminum nitride powder 3, compounded mix 20;
Described compounded mix is comprised of the raw material of following weight parts:
Gibbsite 40, attapulgite 30, silicon carbide 10, magnesium hydroxide 5, carboxymethyl cellulose 1, Jojoba oil 2;
Above-mentioned gibbsite, attapulgite, silicon carbide are mixed, under 800 ℃, the insulation calcining is 4 hours, send into after discharging is cooling in ball mill and carry out the ball milling mixing, add again magnesium hydroxide and carboxymethyl cellulose, continue ball milling 1 hour, add ball milling after Jojoba oil is heated to 30 ℃, cross 100 mesh sieves, obtain described compounded mix.
A kind of preparation method of anti-corrosion wear resisting powder paint comprises the following steps:
Above-mentioned each raw material is mixed, melt extrude through forcing machine, air-cooled, coarse reduction, abrasive dust, sieve, and obtains described anti-corrosion wear resisting powder paint.
Performance test:
Anti-solvent: 240 hours, unchanged;
Salt-fog test (1000h): unchanged.
Claims (2)
1. an anti-corrosion wear resisting powder paint is characterized in that what it was comprised of the raw material of following weight parts:
Trolamine 1-2, tetraphenolic ethane tetraglycidel ether epoxy resin 50-60, polybenzimidazole 2-5, di-acetyl aniline 2-3, polyvinyl butyral acetal 3-5, triallyl cyanurate 0.2-0.4, poly--4-methyl-1-pentene 2-3, aluminum nitride powder 3-5, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Gibbsite 30-40, attapulgite 20-30, silicon carbide 6-10, magnesium hydroxide 3-5, carboxymethyl cellulose 1-2, Jojoba oil 2-3;
Above-mentioned gibbsite, attapulgite, silicon carbide are mixed, insulation calcining 2-4 hour under 600-800 ℃, send into after discharging is cooling in ball mill and carry out the ball milling mixing, add again magnesium hydroxide and carboxymethyl cellulose, continue ball milling 1-2 hour, add ball milling after Jojoba oil is heated to 25-30 ℃, cross the 80-100 mesh sieve, obtain described compounded mix.
2. the preparation method of an anti-corrosion wear resisting powder paint as claimed in claim 1 is characterized in that comprising the following steps:
Above-mentioned each raw material is mixed, melt extrude through forcing machine, air-cooled, coarse reduction, abrasive dust, sieve, and obtains described anti-corrosion wear resisting powder paint.