CN105820735A - Water-based polyurethane modified epoxy resin environment-friendly paint and preparation method thereof - Google Patents
Water-based polyurethane modified epoxy resin environment-friendly paint and preparation method thereof Download PDFInfo
- Publication number
- CN105820735A CN105820735A CN201610274936.2A CN201610274936A CN105820735A CN 105820735 A CN105820735 A CN 105820735A CN 201610274936 A CN201610274936 A CN 201610274936A CN 105820735 A CN105820735 A CN 105820735A
- Authority
- CN
- China
- Prior art keywords
- parts
- epoxy resin
- paint
- add
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based polyurethane modified epoxy resin environment-friendly paint and a preparation method thereof. The paint is composed of the following raw materials in parts by weight: 40-50 parts of water-based polyurethane epoxy modified resin emulsion, 20-25 parts of composite ferrotitanium pigment, 8-10 parts of iron red, 10-15 parts of talcum powder, 0.8-1 part of composite bentonite, 1-1.5 parts of dispersing agent, 0.8-1 part of wetting agent, 0.5 part of defoaming agent, 0.5 part of flash etching inhibitor, 3-5 parts of film forming aid and 0.5 part of silane coupling agent. The water-based paint used instead of the traditional toxic solvent-soluble paint has the advantages of high strength, high adhesive force, excellent corrosion resistance, high flexibility, high weather resistance and environment friendliness. The service lives of the paint and painted substance are greatly prolonged; and the paint can not hazard the environment and human health, and thus, has very broad market prospects.
Description
Technical field
The present invention relates to environmental protection coating material of a kind of waterborne polyurethane modified epoxy resin and preparation method thereof, belong to technical field of coatings.
Background technology
At present, the loss summation that the disasters such as China is annual exceeds well over fire because the economic loss that the corrosion of metal based article causes accounts for the 4% of gross national product, earthquake are brought, therefore, carry out anticorrosive paint and have great significance;And water paint technology and non-harmful pigment technology meet the environmental requirement of country because of it, VOC content is low, non-hazardous, danger;Paid attention to by domestic and international paint field and environmental administration always.Paint field is by traditional handicraft development at a quick pace to the direction of greenization.In order to adapt to the new demand in market, my company technique team utilizes the waterborne polyurethane modified epoxy resin emulsion that original base material is made, possesses the feature that volatile organic content is low, the high intensity of existing epoxy resin, high adhesion force, chemical resistance and antiseptic property, there are again the pliability of polyurethane, wearability, richness, ageing resistance and film property, the shortcoming overcoming the simple pliability deficiency adding resin material completely, making the coating that it is made, weather-proof effect of prestressed is the most excellent and safety and environmental protection.
Summary of the invention
It is an object of the invention to provide environmental protection coating material of a kind of waterborne polyurethane modified epoxy resin and preparation method thereof.
The present invention adopts the following technical scheme that
The environmental protection coating material of waterborne polyurethane modified epoxy resin, the weight portion of its constitutive material is: aqueous polyurethane epoxy modified resin emulsion: 40-50, composite iron-titanium pigment: 20-25, iron oxide red: 8-10, Pulvis Talci: 10-15, composite bentonite: 0.8-1, dispersant: 1-1.5, wetting agent: 0.8-1, defoamer: 0.5, sudden strain of a muscle corrosion inhibitor: 0.5, coalescents: 3-5, silane coupler: 0.5.
The constitutive material of described aqueous polyurethane epoxy modified resin emulsion is, isophorone diisocyanate 20-25, polybutylene glyool adipate 2-3, ethylene glycol 4-6, dihydromethyl propionic acid 0.4-0.6, N-Methyl pyrrolidone 1-1.5, epoxy resin 30-40, triethylamine 2-4, ethylenediamine 0.4-0.6, dibutyl tin laurate 0.2-0.4, acetone 0.3-0.5.
The preparation method of the environmental protection coating material of waterborne polyurethane modified epoxy resin, including:
(1) aqueous polyurethane epoxy modified resin emulsion is prepared: under drying nitrogen is protected, to equipped with thermometer, four tank bodies of blender and reflux condenser add the epoxy resin of processed, isophorone diisocyanate and dibutyl tin laurate, control temperature at 80-85 DEG C, react 2 hours, cool to 75-80 DEG C, add glycol reaction about 30 minutes, add the dihydromethyl propionic acid that N-Methyl pyrrolidone dissolves, react 1.5 hours, cool to 65 DEG C again, add E-20, continue insulation reaction 2 hours, then 20-25 DEG C is cooled to, add triethylamine after adding acetone dilution to neutralize, then with the deionized water of room temperature carries out emulsifying, finally carry out aqueous phase chain extension with ethylenediamine;Evacuation slough acetone this emulsion;
(2) waterborne polyurethane modified cold coating synthesis: prepare in aqueous polyurethane epoxy modified resin emulsion, composite iron-titanium powder pigment, iron oxide red, Pulvis Talci, composite bentonite, dispersant, wetting agent, defoamer, sudden strain of a muscle corrosion inhibitor, coalescents, silane coupler amine aforementioned proportion input tank by above-mentioned, use high speed dispersor 1500r/45min, then go to sand mill and fineness is got to 30 mesh, be filled in container and get final product fill after coating froth breaking.
Beneficial effects of the present invention:
The coating of the aqueous of the present invention replaces the agent soluble paint of conventional toxic, has the anti-corrosive properties of high intensity, high adhesion force and excellence, pliability, weatherability, environmental-protecting performance;Can greatly strengthen the service life of coating and spray, and environmental and human health impacts will not be endangered, there is boundless market prospect.
Detailed description of the invention
Embodiment 1: the environmental protection coating material of waterborne polyurethane modified epoxy resin, the weight portion (kg) of its constitutive material is: aqueous polyurethane epoxy modified resin emulsion: 45, composite iron-titanium pigment: 22, iron oxide red: 9, Pulvis Talci: 12, composite bentonite: 0.9, dispersant: 1.2, wetting agent: 0.9, defoamer: 0.5, sudden strain of a muscle corrosion inhibitor: 0.5, coalescents: 4, silane coupler: 0.5.
The constitutive material (kg) of described aqueous polyurethane epoxy modified resin emulsion is, isophorone diisocyanate 22, polybutylene glyool adipate 2.5, ethylene glycol 5, dihydromethyl propionic acid 0.5, N-Methyl pyrrolidone 1.2, epoxy resin 35, triethylamine 3, ethylenediamine 0.5, dibutyl tin laurate 0.3, acetone 0.4.
The preparation method of the environmental protection coating material of waterborne polyurethane modified epoxy resin, including:
(1) aqueous polyurethane epoxy modified resin emulsion is prepared: under drying nitrogen is protected, to equipped with thermometer, four tank bodies of blender and reflux condenser add the epoxy resin of processed, isophorone diisocyanate and dibutyl tin laurate, control temperature at 80-85 DEG C, react 2 hours, cool to 75-80 DEG C, add glycol reaction about 30 minutes, add the dihydromethyl propionic acid that N-Methyl pyrrolidone dissolves, react 1.5 hours, cool to 65 DEG C again, add E-20, continue insulation reaction 2 hours, then 20-25 DEG C is cooled to, add triethylamine after adding acetone dilution to neutralize, then with the deionized water of room temperature carries out emulsifying, finally carry out aqueous phase chain extension with ethylenediamine;Evacuation slough acetone this emulsion;
(2) waterborne polyurethane modified cold coating synthesis: prepare in aqueous polyurethane epoxy modified resin emulsion, composite iron-titanium powder pigment, iron oxide red, Pulvis Talci, composite bentonite, dispersant, wetting agent, defoamer, sudden strain of a muscle corrosion inhibitor, coalescents, silane coupler amine aforementioned proportion input tank by above-mentioned, use high speed dispersor 1500r/45min, then go to sand mill and fineness is got to 30 mesh, be filled in container and get final product fill after coating froth breaking.
Claims (3)
1. the environmental protection coating material of a waterborne polyurethane modified epoxy resin, it is characterised in that the weight portion of its constitutive material is: aqueous polyurethane epoxy modified resin emulsion: 40-50, composite iron-titanium pigment: 20-25, iron oxide red: 8-10, Pulvis Talci: 10-15, composite bentonite: 0.8-1, dispersant: 1-1.5, wetting agent: 0.8-1, defoamer: 0.5, dodge corrosion inhibitor: 0.5, coalescents: 3-5, silane coupler: 0.5.
The environmental protection coating material of waterborne polyurethane modified epoxy resin the most according to claim 1, the constitutive material that it is characterized in that described aqueous polyurethane epoxy modified resin emulsion is, isophorone diisocyanate 20-25, polybutylene glyool adipate 2-3, ethylene glycol 4-6, dihydromethyl propionic acid 0.4-0.6, N-Methyl pyrrolidone 1-1.5, epoxy resin 30-40, triethylamine 2-4, ethylenediamine 0.4-0.6, dibutyl tin laurate 0.2-0.4, acetone 0.3-0.5.
3. the preparation method of the environmental protection coating material of a waterborne polyurethane modified epoxy resin as claimed in claim 1, it is characterised in that including:
(1) aqueous polyurethane epoxy modified resin emulsion is prepared: under drying nitrogen is protected, to equipped with thermometer, four tank bodies of blender and reflux condenser add the epoxy resin of processed, isophorone diisocyanate and dibutyl tin laurate, control temperature at 80-85 DEG C, react 2 hours, cool to 75-80 DEG C, add glycol reaction about 30 minutes, add the dihydromethyl propionic acid that N-Methyl pyrrolidone dissolves, react 1.5 hours, cool to 65 DEG C again, add E-20, continue insulation reaction 2 hours, then 20-25 DEG C is cooled to, add triethylamine after adding acetone dilution to neutralize, then with the deionized water of room temperature carries out emulsifying, finally carry out aqueous phase chain extension with ethylenediamine;Evacuation slough acetone this emulsion;
(2) waterborne polyurethane modified cold coating synthesis: prepare in aqueous polyurethane epoxy modified resin emulsion, composite iron-titanium powder pigment, iron oxide red, Pulvis Talci, composite bentonite, dispersant, wetting agent, defoamer, sudden strain of a muscle corrosion inhibitor, coalescents, silane coupler amine aforementioned proportion input tank by above-mentioned, use high speed dispersor 1500r/30min, then go to sand mill and fineness is got to 30 mesh, be filled in container and get final product fill after coating froth breaking.