CN104946069A - Production technique of special anticorrosive paint for bus ducts - Google Patents
Production technique of special anticorrosive paint for bus ducts Download PDFInfo
- Publication number
- CN104946069A CN104946069A CN201510231679.XA CN201510231679A CN104946069A CN 104946069 A CN104946069 A CN 104946069A CN 201510231679 A CN201510231679 A CN 201510231679A CN 104946069 A CN104946069 A CN 104946069A
- Authority
- CN
- China
- Prior art keywords
- mixing
- bus duct
- production technique
- anticorrosive paint
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technique of a special anticorrosive paint for bus ducts, which comprises the following steps: mixing an epoxy resin and an acrylic resin in a reaction kettle at 45-55 DEG C at the rate of 150-190 r/minute for 1-2 hours; and after finishing mixing, adding a silane coupling agent and chlorinated paraffin, continuing stirring for 30-60 minutes, adding aluminum powder, titanium white and three curing agents, uniformly mixing at 40-55 DEG C at the rate of 120-150 r/minute, and naturally cooling to normal temperature. The anticorrosive paint can effectively protect the bus duct, avoid the problem of electrical short-circuit and the like in the bus duct due to oxidation corrosion, and enhances the durability and safety.
Description
Technical field
The present invention relates to a kind of protective system, particularly a kind of production technique of bus duct anticorrosion paint special.
Technical background
Along with emerging in large numbers of modernization project facility and equipment, the fast increasing of power consumption of all trades and professions, the appearance in especially numerous Highrise buildingss and large-sized workshop workshop, traditional cable as transmission pressure can not meet the demands in big current delivery system, and the parallel connection of multiway cable uses and brings inconvenience to in-site installation construction connection.Bus duct arises at the historic moment as a kind of new distribution wire, and bus duct, compared with traditional cable, fully demonstrates its superiority when big current is carried.
Bus duct is divided into outer steel shell, aluminum alloy casing and aluminum-steel hybrid outer shell bus slot by its sheating material, and as a kind of power distribution unit of efficient conveying electric current, because of the easy oxidized corrosion of its material characteristic, need be coated with one deck protective system increases wearing quality and security.
Summary of the invention
The object of this invention is to provide a kind of production technique of bus duct anticorrosion paint special; adopt the protective system that the present invention obtains; can available protecting bus duct; prevent bus duct from causing the problems such as electric short circuit because of oxidation corrosion; avoid causing the problems such as electric short circuit because of the oxidation corrosion of bus duct shell, improve wearing quality and security.
For solving the problem, technical scheme of the present invention is:
A kind of production technique of bus duct anticorrosion paint special, wherein, its preparation method is as follows: epoxy resin and acrylic resin are put into reactor and mixes, mixing time is 1-2h, mixing temperature is 45-55 degree, mixing rate is 150-190r/min, silane coupling agent and clorafin is added after mixing terminates, continue to stir 30-60min, then add aluminium powder, titanium dioxide, three solidifying agent, mixing temperature is 40-55 degree, and mixing rate is 120-150r/min, until after mixing, naturally cool to normal temperature.
The production technique of above-mentioned a kind of bus duct anticorrosion paint special, wherein, described solidifying agent is the one of trimethylammonium in diamines or m-xylene diamine.
Beneficial effect of the present invention is:
The present invention adopts new formulation; unique formula is adopted to accomplish effectively anticorrosion; and there is the advantages such as resistance to salt water is strong, asepsis environment-protecting; adopt the protective system that the present invention obtains; can available protecting bus duct; prevent bus duct from causing the problems such as electric short circuit because of oxidation corrosion, improve wearing quality and security.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
32 parts of epoxy resin are put into reactor with 18 parts of acrylic resins mix, mixing time is 1.5h, mixing temperature is 45 degree, and mixing rate is 180r/min, adds 7 parts of silane coupling agents and 12 parts of clorafins after mixing terminates, continue to stir 30min, then add 7 parts of aluminium powders, 5 parts of titanium dioxides, 12 parts of trimethylammoniums diamines, mixing temperature is 50 degree, and mixing rate is 140r/min, until after mixing, naturally cool to normal temperature.
Embodiment 2
30 parts of epoxy resin are put into reactor with 15 parts of acrylic resins mix, mixing time is 1h, mixing temperature is 50 degree, and mixing rate is 150r/min, adds 6 parts of silane coupling agents and 10 parts of clorafins after mixing terminates, continue to stir 30min, then add 6 parts of aluminium powders, 6 parts of titanium dioxides, 10 parts of trimethylammoniums diamines, mixing temperature is 55 degree, and mixing rate is 130r/min, until after mixing, naturally cool to normal temperature.
Embodiment 3
28 parts of epoxy resin are put into reactor with 12 parts of acrylic resins mix, mixing time is 1h, mixing temperature is 55 degree, and mixing rate is 160r/min, adds 6 parts of silane coupling agents and 13 parts of clorafins after mixing terminates, continue to stir 30min, then add 8 parts of aluminium powders, 5 parts of titanium dioxides, 11 parts of m-xylene diamines, mixing temperature is 50 degree, and mixing rate is 150r/min, until after mixing, naturally cool to normal temperature.
Adopt the protective system that obtains of the present invention, can available protecting bus duct, prevent bus duct from causing the problems such as electric short circuit because of oxidation corrosion, improve wearing quality and security.
The above; be only the present invention's preferably embodiment, but protection scope of the present invention is not limited thereto, is anyly familiar with those skilled in the art in the technical scope that the present invention discloses; the change that can expect easily or replacement, all should be encompassed in protection scope of the present invention.Therefore, protection scope of the present invention should be as the criterion with the protection domain of claims.
Claims (2)
1. the production technique of a bus duct anticorrosion paint special, it is characterized by, its preparation method is as follows: epoxy resin and acrylic resin are put into reactor and mixes, mixing time is 1-2h, mixing temperature is 45-55 degree, mixing rate is 150-190r/min, silane coupling agent and clorafin is added after mixing terminates, continue to stir 30-60min, then add aluminium powder, titanium dioxide, three solidifying agent, mixing temperature is 40-55 degree, and mixing rate is 120-150r/min, until after mixing, naturally cool to normal temperature.
2. the production technique of a kind of bus duct anticorrosion paint special as claimed in claim 1, is characterized by, and described solidifying agent is the one of trimethylammonium in diamines or m-xylene diamine.