CN104945017A - 一种陶瓷可控窑变釉料 - Google Patents

一种陶瓷可控窑变釉料 Download PDF

Info

Publication number
CN104945017A
CN104945017A CN201410113008.9A CN201410113008A CN104945017A CN 104945017 A CN104945017 A CN 104945017A CN 201410113008 A CN201410113008 A CN 201410113008A CN 104945017 A CN104945017 A CN 104945017A
Authority
CN
China
Prior art keywords
parts
glaze
bed material
quartz
following raw
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410113008.9A
Other languages
English (en)
Other versions
CN104945017B (zh
Inventor
陈章椿
侯景泉
敖成祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujian Dehua Chengyi Ceramics Co.,Ltd.
Original Assignee
陈章椿
侯景泉
敖成祥
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 陈章椿, 侯景泉, 敖成祥 filed Critical 陈章椿
Priority to CN201410113008.9A priority Critical patent/CN104945017B/zh
Publication of CN104945017A publication Critical patent/CN104945017A/zh
Application granted granted Critical
Publication of CN104945017B publication Critical patent/CN104945017B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种陶瓷可控窑变釉料，包括冰裂底料所用釉料、结晶底料所用釉料及流纹底料所用釉料，冰裂底料所用釉料的原料配比为：钠长石70份；锂辉石20份；硼酸35份；石英40份；双飞30份；结晶底料所用釉料的原料配比为：石英砂150份；冰晶石30份；无水纯碱50份；白垩10份；硝石5份；流纹底料所用釉料的原料配比为：长石70份；石英50份；石灰石40份；高岭100份；白云石12份；将本发明的釉料经过印花贴到待烧的陶瓷上，就可把冰裂、结晶或流纹的陶瓷和不同的画面有机结合在一起一次烧成，不需要执行特殊烧成制度就能够达到在原来几个陶瓷上并需要几种不同的烧成制度所拥有的装饰效果在同一陶瓷上体现出来。

Description

一种陶瓷可控窑变釉料
技术领域
本发明涉及一种釉料，具体涉及一种陶瓷可控窑变釉料。
背景技术
现有的技术，若是想在一个陶瓷上呈现冰裂、结晶或流纹相结合的效果，就需要分别执行几种烧成制度，且烧成过程不能够一次完成，其过程繁杂，费时费力，生产效率低，生产成本较高。
发明内容
本发明旨在于克服现有技术的不足，提供了一种陶瓷可控窑变釉料。
该陶瓷可控窑变釉料，包括冰裂底料所用釉料、结晶底料所用釉料及流纹底料所用釉料，
所述冰裂底料所用釉料由以下原料按份数配制而成：
钠长石30-70份
锂辉石5-20份
硼酸14-35份
石英8-40份
双飞5-30份；
所述结晶底料所用釉料由以下原料按份数配制而成配方：
石英砂50-150份
冰晶石6-30份
无水纯碱10-50份
白垩 1-10份
硝石2-15份；
所述流纹底料所用釉料由以下原料按份数配制而成配方：
长石 20-70份
石英 5-50份
石灰石 5-40份
高岭 40-100份
白云石1-12份。
优选地，
所述冰裂底料所用釉料由以下原料按份数配制而成：
钠长石50份
锂辉石10份
硼酸28份
石英20份
双飞18份
所述结晶底料所用釉料由以下原料按份数配制而成配方：
石英砂100份
冰晶石18.7份
无水纯碱30份
白垩 4份
硝石 10份；
所述流纹底料所用釉料由以下原料按份数配制而成配方：
长石 43.3份
石英 25.7份
石灰石 17.6份
高岭 70.4份
白云石 6份。
本发明的优点在于：将本发明的釉料经过印花贴到待烧的陶瓷上，就可把冰裂、结晶或流纹的陶瓷和不同的自然画面有机结合在一起，一次烧成，而且不需要执行特殊烧成制度，就能够达到在原来的几个陶瓷上并需要几种不同的烧成制度所拥有的装饰效果在同一陶瓷上体现出来，给人一种赏心悦目的感觉，美不胜收，给陶瓷又披上了一件崭新的外衣，大大简化了此类陶瓷的烧制过程、省时省力，提高了生产效率，降低了生产成本。
具体实施方式：
实施例一
所述冰裂底料所用釉料由以下原料按份数配制而成：
钠长石50份
锂辉石10份
硼酸28份
石英20份
双飞18份
制作时，先将长石、石英、硼酸通过1300°~1400°高温熔成熔块后，将锂辉石、双飞一起球磨10小时左右烘干后即成制品待用。
印花操作时，将所设计花纸局部需要冰裂部位，用上述原料根据需要用网板（80~200目）连印一次即可。如冰裂部位需要某种颜色，可将颜料（视颜色深浅要求从0.5~10%）加入上述底料内，再按上述操作印刷即可。如所需颜色为红色，经过上述操作后，就可提高颜色对比度。
所述结晶底料所用釉料由以下原料按份数配制而成配方：
石英砂100份
冰晶石18.7份
无水纯碱30份
白垩 4份
硝石 10份；
制作时，将上述全部称量通过1400°-1500°变温熔融后全部球磨10-20小时后烘干即成制品待用。
其印花操作与冰裂底料的印花操作相同。
所述流纹底料所用釉料由以下原料按份数配制而成配方：
长石 43.3份
石英 25.7份
石灰石 17.6份
高岭 70.4份
白云石 6份
制作时，将上述各原料称量球磨7-8小时烘干即成制品待用。
其印花操作与冰裂底料的印花操作相同。
实施例二
本实施例中，所述冰裂底料所用釉料由以下原料按份数配制而成：
钠长石30份
锂辉石5份
硼酸14份
石英8份
双飞5份
其制作方法与印花操作与实施例一相同。
所述结晶底料所用釉料由以下原料按份数配制而成配方：
石英砂50份
冰晶石6份
无水纯碱10份
白垩 1份
硝石2份；
其制作方法与印花操作与实施例一相同。
所述流纹底料所用釉料由以下原料按份数配制而成配方：
长石 20份
石英 5份
石灰石 5份
高岭 40份
白云石1份；
其制作方法与印花操作与实施例一相同。
实施例三
本实施例中，所述冰裂底料所用釉料由以下原料按份数配制而成：
钠长石70份
锂辉石20份
硼酸35份
石英40份
双飞5份
其制作方法与印花操作与实施例一相同。
所述结晶底料所用釉料由以下原料按份数配制而成配方：
石英砂150份
冰晶石30份
无水纯碱50份
白垩 10份
硝石15份；
其制作方法与印花操作与实施例一相同。
所述流纹底料所用釉料由以下原料按份数配制而成配方：
长石 70份
石英 50份
石灰石 40份
高岭 100份
白云石12份；
其制作方法与印花操作与实施例一相同。
以上各实施例中的结晶底料与流纹底料可任意重叠印刷本釉料，可烧出意想不到的效果。以上各实施例中的三种釉料按花面设计印刷完好后，和普通花纸一样盖上封面胶晾干后即可贴花烧成。

Claims (2)

1.一种陶瓷可控窑变釉料，其特征在于包括冰裂底料所用釉料、结晶底料所用釉料及流纹底料所用釉料，
所述冰裂底料所用釉料由以下原料按份数配制而成：
钠长石30-70份
锂辉石5-20份
硼酸14-35份
石英8-40份
双飞5-30份；
所述结晶底料所用釉料由以下原料按份数配制而成配方：
石英砂50-150份
冰晶石6-30份
无水纯碱10-50份
白垩 1-10份
硝石2-15份；
所述流纹底料所用釉料由以下原料按份数配制而成配方：
长石 20-70份
石英 5-50份
石灰石 5-40份
高岭 40-100份
白云石1-12份。
2.如权利要求1所述的一种陶瓷可控窑变釉料，其特征在于：
所述冰裂底料所用釉料由以下原料按份数配制而成：
钠长石50份
锂辉石10份
硼酸28份
石英20份
双飞18份
所述结晶底料所用釉料由以下原料按份数配制而成配方：
石英砂100份
冰晶石18.7份
无水纯碱30份
白垩 4份
硝石 10份；
所述流纹底料所用釉料由以下原料按份数配制而成配方：
长石 43.3份
石英 25.7份
石灰石 17.6份
高岭 70.4份
白云石 6份。
CN201410113008.9A 2014-03-25 2014-03-25 一种陶瓷可控窑变釉料 Active CN104945017B (zh)