CN104944988B - 垃圾处理水泥回转窑用耐腐蚀红砖以及制备工艺 - Google Patents

垃圾处理水泥回转窑用耐腐蚀红砖以及制备工艺 Download PDF

Info

Publication number
CN104944988B
CN104944988B CN201510359920.7A CN201510359920A CN104944988B CN 104944988 B CN104944988 B CN 104944988B CN 201510359920 A CN201510359920 A CN 201510359920A CN 104944988 B CN104944988 B CN 104944988B
Authority
CN
China
Prior art keywords
corrosion
common brick
rotary kiln
garbage disposal
cement rotary
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201510359920.7A
Other languages
English (en)
Other versions
CN104944988A (zh
Inventor
俞益君
王才军
徐志坚
俞清耀
朱秀芬
吴明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JUNYAO ANTI-WEAR REFRACTORY Co Ltd JIANGSU
Original Assignee
JUNYAO ANTI-WEAR REFRACTORY Co Ltd JIANGSU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JUNYAO ANTI-WEAR REFRACTORY Co Ltd JIANGSU filed Critical JUNYAO ANTI-WEAR REFRACTORY Co Ltd JIANGSU
Priority to CN201510359920.7A priority Critical patent/CN104944988B/zh
Publication of CN104944988A publication Critical patent/CN104944988A/zh
Application granted granted Critical
Publication of CN104944988B publication Critical patent/CN104944988B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种垃圾处理水泥回转窑用耐腐蚀红砖以及制备工艺，属耐火材料领域，由铝矾土熟料、锆英砂，焦宝石，碳化硅、电熔白刚玉颗粒、红柱石微粉等混合经压制成型后经高温烧成。本发明的红砖具有以下优点：1）抵御垃圾焚烧（生活垃圾、工业废弃物、城市污泥）产生的腐蚀性气体、液体对耐火材料的侵蚀，延长使用周期；2）保护或替代分解炉等部位的隔热层耐火材料；3）保护筒体，该耐腐蚀红砖工艺简单，性价比高。

Description

垃圾处理水泥回转窑用耐腐蚀红砖以及制备工艺
技术领域
本发明属于耐火材料行业，尤其指一种垃圾处理水泥回转窑用耐腐蚀红砖，同时指提供这种耐腐蚀红砖的制备工艺。
背景技术
随着城市化发展及环保标准的提高，水泥窑协同处置垃圾成为垃圾无害化、垃圾资源化的发展方向。在协同处置垃圾的水泥窑分解炉、预热器、窑内窑口、过渡带、分解带等部位，普通耐火砖无法满足其抗腐蚀要求，无法有效保护隔热衬里和金属筒体受到的酸性腐蚀，寿命大大缩短。
发明内容
本发明提供一种高性价比的垃圾处理水泥回转窑用耐腐蚀红砖，由铝矾土熟料、锆英砂，焦宝石，碳化硅、电熔白刚玉颗粒、红柱石微粉等混合经压制成型后经高温烧制成耐火砖，在满足节能长寿的同时，明显抵抗由处置垃圾产生的酸性腐蚀，保护金属筒体及隔热衬里，性价比极高。
本发明的技术方案是：
一种垃圾处理水泥回转窑用耐腐蚀红砖，各组份的重量配比为：
外加：
黄糊精 0.3％～0.6％
甲基纤维素 0.3％～0.6％
水 3％～5％
将上述组份混合，于混炼机中制成泥料，压制成砖坯后，烧结成制品。
本发明中，各组份的重量配比为：
外加：
黄糊精 0.3％～0.6％
甲基纤维素 0.3％～0.6％
水 3％～5％
一种垃圾处理水泥回转窑用耐腐蚀红砖的制备工艺，将原料按配比要求进行混合，于混炼机中制成泥料，压制成砖坯后，烧结成制品。
本发明中，在2500吨压力下将泥料压制成砖坯。
本发明中，砖坯在隧道窑中烧结，烧结温度是1570℃-1590℃。
本发明的有益效果：
本发明的产品经珠江水泥、华新武穴、溧阳天山等生产线使用，有效解决了普通耐火砖、隔热衬里受腐蚀膨胀解体和金属筒体受腐蚀锈蚀的难题。对提高设备的运转率、使用周期起到十分积极的作用。
本发明烧制成的耐腐蚀红砖具有以下优点：1)抵御垃圾焚烧(生活垃圾、工业废弃物、城市污泥)产生的腐蚀性气体、液体对耐火材料的侵蚀，延长使用周期。；2)保护或替代分解炉等部位的隔热层耐火材料；3)保护筒体，该耐腐蚀红砖工艺简单，性价比高。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例1，垃圾处理水泥回转窑用耐腐蚀红砖，各组分的重量配比为：
高纯铝矾土熟料：55％
外加：
黄糊精： 0.3％～0.6％
甲基纤维素： 0.3％～0.6％
水: 2％
将上述原料安配比混合，于混炼机中制成泥料，在2500吨压力下成型，砖坯在隧道窑中于1580℃±10℃下烧结。
实施例2，参考实施1，各组分的重量配比为：
高纯铝矾土熟料：52％(其中，铝矾土熟料一22％、铝矾土熟料二30％)
锆英砂：11％
焦宝石：8％
碳化硅：9％
电熔白刚玉颗粒：7％
红柱石微粉：8％
结合粘土：5％
外加：
黄糊精：0.3％～0.6％
甲基纤维素：0.3％～0.6％
水：3％～5％
实施例3，参考实施1，各组分的重量配比为：
高纯铝矾土熟料：60％(其中，铝矾土熟料一25％、铝矾土熟料二35％)
锆英砂：8％
焦宝石：7％
高纯碳化硅:7％：
电熔白刚玉颗粒：8％
红柱石微粉：5％
结合粘土：5％
外加：
黄糊精：0.3％～0.6％
甲基纤维素：0.3％～0.6％
水：3％～5％
本发明的产品有效解决了普通耐火砖、隔热衬里受腐蚀膨胀解体和金属筒体受腐蚀锈蚀的难题，对提高设备的运转率、使用周期起到十分积极的作用。
本发明烧制成的耐腐蚀红砖具有以下优点：1)抵御垃圾焚烧(生活垃圾、工业废弃物、城市污泥)产生的腐蚀性气体、液体对耐火材料的侵蚀，延长使用周期。；2)保护或替代分解炉等部位的隔热层耐火材料；3)保护筒体，该耐腐蚀红砖工艺简单，性价比高。
本发明未涉及部分均与现有技术相同或可采用现有技术加以实现。

Claims (6)

1.一种垃圾处理水泥回转窑用耐腐蚀红砖，其特征在于各组份的重量百分比为：
铝矾土熟料一 1~3mm Al2O3≥88% 20~25%
铝矾土熟料二 3~5mm Al2O3≥88% 25~40%
锆英砂 80~120um ZrO2≥55% 8~12%
焦宝石 0~3mm Al2O3≥44% 10~15%
碳化硅 1~3mm SiC≥97% 10~18%
电熔白刚玉颗粒 1~3mm Al2O3≥99.4% 8~15%
红柱石微粉 3~5mm Al2O3≥60% 10~15%
结合粘土 200um Al2O3≥38% 5~7%
外加：
黄糊精 0.3%~0.6%
甲基纤维素 0.3%~0.6%
水 3%~5%
上述各组份的重量百分比之和为100%，将上述组份混合，于混炼机中制成泥料，压制成砖坯后，烧结成制品。
2.根据权利要求1所述的垃圾处理水泥回转窑用耐腐蚀红砖，其特征是在2500吨压力下将泥料压制成砖坯。
3.根据权利要求1所述的垃圾处理水泥回转窑用耐腐蚀红砖，其特征是砖坯在隧道窑中烧结，烧结温度是1570℃-1590℃。
4.一种制备权利要求1所述的垃圾处理水泥回转窑用耐腐蚀红砖的工艺，其特征在于：将原料按配比要求进行混合，于混炼机中制成泥料，压制成砖坯后，烧结成制品。
5.根据权利要求4所述的制备垃圾处理水泥回转窑用耐腐蚀红砖的工艺，其特征是在2500吨压力下将泥料压制成砖坯。
6.根据权利要求4所述的制备垃圾处理水泥回转窑用耐腐蚀红砖的工艺，其特征是砖坯在隧道窑中烧结，烧结温度是1570℃-1590℃。
CN201510359920.7A 2015-06-25 2015-06-25 垃圾处理水泥回转窑用耐腐蚀红砖以及制备工艺 Active CN104944988B (zh)