CN104941577A - 一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒及其制备方法 - Google Patents

一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒及其制备方法 Download PDF

Info

Publication number
CN104941577A
CN104941577A CN201510191618.5A CN201510191618A CN104941577A CN 104941577 A CN104941577 A CN 104941577A CN 201510191618 A CN201510191618 A CN 201510191618A CN 104941577 A CN104941577 A CN 104941577A
Authority
CN
China
Prior art keywords
parts
banana
active carbon
particles
modified active
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510191618.5A
Other languages
English (en)
Inventor
黄浩
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Hongkun Auto Parts Co Ltd
Original Assignee
Wuhu Hongkun Auto Parts Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Hongkun Auto Parts Co Ltd filed Critical Wuhu Hongkun Auto Parts Co Ltd
Priority to CN201510191618.5A priority Critical patent/CN104941577A/zh
Publication of CN104941577A publication Critical patent/CN104941577A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒，其特征在于，由下列重量份的原料制备制成：羊毛脂2-4、甘油2-4、平平加O 1-2、十二烷基甜菜碱0.8-1.2、硫脲0.8-1、铝矾土5-7、天然胶乳3-5、二氧化硅7-9、芭蕉叶18-24、香蕉皮13-17、椰壳活性炭102-108、硅藻土36-41、氢氧化钾2-3、吸附助剂4-6、水适量；本发明添加芭蕉叶、香蕉皮经过干燥粉碎与活性炭混合，多纤维多孔隙，增加了除尘效果，而且具有一定的抗菌效果；添加吸附助剂，具有特殊多孔性，延长气体与之接触时间；本发明经过粘性物质的添加，制成的颗粒强度大，不易崩解，表面孔洞多，提高了脱硫精度高。

Description

一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒及其制备方法
技术领域
本发明涉及一种脱硫活性炭及其制备方法，特别是一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒及其制备方法。
背景技术
随着社会的迅猛发展，环境污染也日趋严重污水处理、造纸、石油加工、化肥制造、化学纤维制造以及一些化工原料制造行业中排放出大量的硫化氢、二氧化硫，不仅造成环境污染，也容易导致催化剂中毒失活，因此降低工业生产中硫的排放量成为当今世界工业生产中需要解决的几大难题之一。这些吸附剂大多吸附能力有限，需要针对不同的要求研究不同的吸附剂，发挥最好的作用。同时，寻找新的原料，以增强吸附效果，节约成本。
在脱硫的众多方法中，有一种方法是活性炭吸附法，虽然活性炭能够吸附多种酸性气体，但是活性炭价格较高，脱硫效率低，增加了成本。本发明将活性炭与具有特殊多孔的硅藻土结合，通过添加多种功能型物质，制成颗粒状物质，使得脱硫剂容易固定，安全无毒，吸附性能强，增强产品的刚性和强度，延长了活性炭的使用时间，降低了干法脱硫的成本。
巴西圣保罗州大学的研究人员发现，切碎的香蕉皮可有效去除饮用水中有害的铜、铅等重金属。香蕉皮能在水质净化领域发挥重要作用，因为同其他净化方法相比，这一方法不但环保低廉，而且耐用性更好。本发明设想将香蕉皮用于脱硫除尘设备中，也会起到除尘的效果。
发明内容
本发明的目的是提供一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒及其制备方法。
为了实现本发明的目的，本发明通过以下方案实施：
一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒，由下列重量份的原料制备制成：羊毛脂2-4、甘油2-4、平平加O 1-2、十二烷基甜菜碱0.8-1.2、硫脲0.8-1、铝矾土5-7、天然胶乳3-5、二氧化硅7-9、芭蕉叶18-24、香蕉皮13-17、椰壳活性炭102-108、硅藻土36-41、氢氧化钾2-3、吸附助剂4-6、水适量；
所述吸附助剂由以下重量份的原料制成：鹿沼土1.5-2.5、硫酸铝1.5-2.5、 碳酸钠2-3、高岭土12-14、纳米碳2-3、二氧化钛2-3、茶籽壳8-10、莲房13-15；制备方法是将茶籽壳、莲房在100℃-120℃条件下干燥1-1.5小时，粉碎成40-60目粉末，然后加入适量水与除鹿沼土之外的其余剩余成分搅拌均匀，形成泥状物，然后放入400℃-500℃的炭化炉中炭化2-3小时，取出冷却后粉碎成80-100目粉末，用50％-60％的醋酸溶液浸泡1.5-2小时，过滤，取滤渣加鹿沼土、1.5-2倍量的纯水研磨40-50分钟得浆料即可。
本发明所述一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒，由以下具体步骤制成：
(1)将芭蕉叶、香蕉皮在95℃-105℃的条件下烘烤1.5-2.5小时，粉碎成80-100目的干燥粉末与椰壳活性炭、硅藻土一同放入球磨机中球磨1.5-2.5小时，球磨后过150-200目筛，得到混合粉末待用；
(2)将甘油、硫脲、铝矾土、二氧化硅、氢氧化钾中加入适量的水，不断搅拌制成浆料，然后加入除吸附助剂之外的其余剩余成分，搅拌均匀，加热至65℃-80℃，保温研磨1.5-2小时，得混合浆料待用；
(3)将混合粉末、混合浆料、吸附助剂相互搅拌均匀，然后浓缩干燥，送入造粒机中造粒即得。
本发明的有益效果是：本发明添加芭蕉叶、香蕉皮经过干燥粉碎与活性炭混合，多纤维多孔隙，增加了除尘效果，而且具有一定的抗菌效果；添加吸附助剂，具有特殊多孔性，延长气体与之接触时间；本发明经过粘性物质的添加，制成的颗粒强度大，不易崩解，表面孔洞多，提高了脱硫精度高。
具体实施方案
下面通过具体实例对本发明进行详细说明。
一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒，由下列重量份(公斤)的原料制备制成：羊毛脂2、甘油2、平平加O 1、十二烷基甜菜碱0.8、硫脲0.8、铝矾土5、天然胶乳3、二氧化硅7、芭蕉叶18、香蕉皮13、椰壳活性炭102、硅藻土36、氢氧化钾2、吸附助剂4、水适量；
所述吸附助剂由以下重量份(公斤)的原料制成：鹿沼土1.5、硫酸铝1.5、碳酸钠2、高岭土12、纳米碳2、二氧化钛2、茶籽壳8、莲房13；制备方法是将茶籽壳、莲房在100℃-120℃条件下干燥1-1.5小时，粉碎成40-60目粉末， 然后加入适量水与除鹿沼土之外的其余剩余成分搅拌均匀，形成泥状物，然后放入400℃-500℃的炭化炉中炭化2-3小时，取出冷却后粉碎成80-100目粉末，用50％-60％的醋酸溶液浸泡1.5-2小时，过滤，取滤渣加鹿沼土、1.5-2倍量的纯水研磨40-50分钟得浆料即可。
本发明所述一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒，由以下具体步骤制成：
(1)将芭蕉叶、香蕉皮在95℃-105℃的条件下烘烤1.5-2.5小时，粉碎成80-100目的干燥粉末与椰壳活性炭、硅藻土一同放入球磨机中球磨1.5-2.5小时，球磨后过150-200目筛，得到混合粉末待用；
(2)将甘油、硫脲、铝矾土、二氧化硅、氢氧化钾中加入适量的水，不断搅拌制成浆料，然后加入除吸附助剂之外的其余剩余成分，搅拌均匀，加热至65℃-80℃，保温研磨1.5-2小时，得混合浆料待用；
(3)将混合粉末、混合浆料、吸附助剂相互搅拌均匀，然后浓缩干燥，送入造粒机中造粒即得。
本发明样品主要技术参数为：硫容(wt％)：≥19.5％，脱硫精度(ppm)：≤1；利用本发明样品进行废气处理，捕集微尘效率≥99％。

Claims (2)

1.一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒，其特征在于，由下列重量份的原料制备制成：羊毛脂2-4、甘油2-4、平平加O 1-2、十二烷基甜菜碱0.8-1.2、硫脲0.8-1、铝矾土5-7、天然胶乳3-5、二氧化硅7-9、芭蕉叶18-24、香蕉皮13-17、椰壳活性炭102-108、硅藻土36-41、氢氧化钾2-3、吸附助剂4-6、水适量；
所述吸附助剂由以下重量份的原料制成：鹿沼土 1.5-2.5、硫酸铝1.5-2.5、碳酸钠2-高岭土12-14、纳米碳2-3、二氧化钛2-3、茶籽壳8-10、莲房13-15；制备方法是将茶籽壳、莲房在100℃-120℃条件下干燥1-1.5小时，粉碎成40-60目粉末，然后加入适量水与除鹿沼土之外的其余剩余成分搅拌均匀，形成泥状物，然后放入400℃-500℃的炭化炉中炭化2-3小时，取出冷却后粉碎成80-100目粉末，用50%-60%的醋酸溶液浸泡1.5-2小时，过滤，取滤渣加鹿沼土、1.5-2倍量的纯水研磨40-50分钟得浆料即可。
2.根据权利要求1所述一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒，其特征在于，由以下具体步骤制成：
（1）将芭蕉叶、香蕉皮在95℃-105℃的条件下烘烤1.5-2.5小时，粉碎成80-100目的干燥粉末与椰壳活性炭、硅藻土一同放入球磨机中球磨1.5-2.5小时，球磨后过150-200目筛，得到混合粉末待用；
（2）将甘油、硫脲、铝矾土、二氧化硅、氢氧化钾中加入适量的水，不断搅拌制成浆料，然后加入除吸附助剂之外的其余剩余成分，搅拌均匀，加热至65℃-80℃，保温研磨1.5-2小时，得混合浆料待用；
（3）将混合粉末、混合浆料、吸附助剂相互搅拌均匀，然后浓缩干燥，送入造粒机中造粒即得。
CN201510191618.5A 2015-04-22 2015-04-22 一种用于脱硫除尘的香蕉皮改性活性炭硅藻土颗粒及其制备方法 Pending CN104941577A (zh)