CN104932040A - 一种光学薄膜 - Google Patents
一种光学薄膜 Download PDFInfo
- Publication number
- CN104932040A CN104932040A CN201510394400.XA CN201510394400A CN104932040A CN 104932040 A CN104932040 A CN 104932040A CN 201510394400 A CN201510394400 A CN 201510394400A CN 104932040 A CN104932040 A CN 104932040A
- Authority
- CN
- China
- Prior art keywords
- tac
- coating
- layer
- optical thin
- thin film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
材料 | 配比 |
TAC | 100 |
二氯甲烷 | 800 |
甲醇 | 43 |
增塑剂 | 10 |
测试项目 | 测试值 |
PET膜厚 | 10μm |
TAC膜厚 | 30μm |
透光率 | 92% |
雾度 | 1.2% |
材料 | 配比 |
TAC | 100 |
二氯甲烷 | 800 |
甲醇 | 43 |
增塑剂 | 10 |
紫外吸收剂 | 2 |
测试项目 | 测试值 |
PET膜厚 | 25μm |
TAC膜厚 | 10μm |
透光率 | 91% |
雾度 | 1.9% |
紫外吸收率 | 85% |
材料 | 配比 |
TAC | 100 |
二氯甲烷 | 800 |
甲醇 | 43 |
增塑剂 | 10 |
高折光剂 | 5 |
测试项目 | 测试值 |
PET膜厚 | 50μm |
TAC膜厚 | 100μm |
透光率 | 91% |
雾度 | 1.9% |
折光率 | 1.52 |
材料 | 配比 |
TAC | 100 |
二氯甲烷 | 800 |
甲醇 | 43 |
增塑剂 | 10 |
蓝光阻隔剂 | 0.5 |
测试项目 | 测试值 |
PET膜厚 | 200μm |
TAC膜厚 | 50μm |
透光率 | 90% |
雾度 | 2.0% |
蓝光阻隔率 | 32% |
材料 | 配比 |
TAC | 100 |
二氯甲烷 | 800 |
甲醇 | 43 |
增塑剂 | 10 |
测试项目 | 测试值 |
PET膜厚 | 25μm |
TAC膜厚 | 15μm |
透光率 | 92% |
雾度 | 1.3% |
材料 | 配比 |
TAC | 100 |
二氯甲烷 | 800 |
甲醇 | 43 |
增塑剂 | 10 |
测试项目 | 测试值 |
PET膜厚 | 40μm |
TAC膜厚 | 20μm |
透光率 | 92% |
雾度 | 1.3% |
Claims (12)