CN104929338A - High-performance quartzite board and production method - Google Patents
High-performance quartzite board and production method Download PDFInfo
- Publication number
- CN104929338A CN104929338A CN201510273943.6A CN201510273943A CN104929338A CN 104929338 A CN104929338 A CN 104929338A CN 201510273943 A CN201510273943 A CN 201510273943A CN 104929338 A CN104929338 A CN 104929338A
- Authority
- CN
- China
- Prior art keywords
- performance
- slate
- orders
- raw material
- quartz
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a high-performance quartzite board. The high-performance quartzite board comprises a quartzite board body and support cloth which are integrally formed, wherein the support cloth is clamped inside the quartzite board body. The high-performance quartzite board has the advantages that the problem that an existing quartzite board is prone to cracking and poor in pressure resistance is solved; the crack and pressure resistance of the formed quartzite board are increased by the support cloth inside the quartzite board body, the performance of the finished quartzite board is increased evidently, product service life is prolonged, and product use cost is lowered.
Description
Technical field
The present invention relates to building material technical field, particularly relate to high-performance quartzite slate and preparation method.
Background technology
Quartzite slate as conventional constructional materials, under being widely used in the laying occasion on external wall and ground.The technique of existing artificial slabstone raw material and quartz sand powder is first uniformly mixed to carry out upper die forming afterwards, and therefore, in use, volatility is higher for resin, easily unstable properties in forming process, and the caking property of resin is deteriorated.Meanwhile, resin, in mixing, solidification process, by the impact of adding material, is not easily evenly distributed, and then makes shrinkage factor in Integral stone evenly, easily cannot produce local contraction, thus, easily produce areal deformation.Meanwhile, due to the impact of resin-bonded characteristic, the anti-pressure ability of quartzite slate is declined, and easily cause cracking and local shedding.
Summary of the invention
The object of this invention is to provide high-performance quartzite slate and preparation method, thus solve the problem that existing quartzite slate is easy to crack, anti-pressure ability is poor.
In order to achieve the above object, the invention provides following technical scheme:
High-performance quartzite slate, comprises integrated quartz slate and supports cloth, and it is inner that described supports cloth is clamped in described quartz slate.
In a preferred embodiment, described supports cloth is clamped in described quartz slate inside with the direction running through quartz slate longitudinal section.
In a preferred embodiment, the number of plies of described supports cloth is one deck or two-layer.
In a preferred embodiment, the material of described supports cloth is fiberglass gridding cloth, and mesh shape is square, and size of mesh opening is 535mm, and the thickness of described fiberglass gridding cloth is: 1,0.3 and 0.4.
In a preferred embodiment, described quartz slate is prepared by the raw material comprising quartz sand, glass sand and unsaturated-resin.
In a preferred embodiment, described quartz sand comprises: 4 ~ 6 orders, 6 ~ 8 orders, 8 ~ 10 orders, 10 ~ 16 orders, 16 ~ 26 orders, 26 ~ 40 orders, 40 ~ 70 orders, 70 ~ 120 orders and 325 object quartz sands; Described glass sand comprises: 6 ~ 8 orders, 8 ~ 16 orders, 16 ~ 30 object glass sands.
In a preferred embodiment, described 325 object quartz sand consumptions are 25% of stone slab raw material volume, and described glass sand consumption is 20% of stone slab raw material volume, and unsaturated-resin consumption is 9% of stone slab raw material volume.
Meanwhile, present invention also offers a kind of manufacture method of high-performance quartzite slate, wherein, comprising:
Step S101, at mould bottom laid bottom quartz slate raw material;
Step S102, laid supports cloth on the stone slab raw material of described bottom;
Step S103, at laid upper strata, the top of described supports cloth quartz slate raw material.
In a preferred embodiment, also comprise after step S103:
Step S104, flattens the upper surface of the stone slab raw material on upper strata.
In a preferred embodiment, also comprising after step S104: step S105, shaping successively to being equipped with stone slab raw material mould;
Described sizing comprises: press, vacuum, vibration, shaping, dry, cooling, polishing and demoulding step.
Beneficial effect of the present invention is: the present invention is by adding supports cloth in the inside of quartz slate raw material, thus increase quartz slate cracking resistance after shaping and anti-pressure ability, make the end properties of quartzite slate be significantly improved, extend life of product, reduce the use cost of product.
Accompanying drawing explanation
In order to be illustrated more clearly in the embodiment of the present invention or technical scheme of the prior art, be briefly described to the accompanying drawing used required in embodiment or description of the prior art below, apparently, accompanying drawing in the following describes is only some embodiments of the present invention, for those of ordinary skill in the art, under the prerequisite not paying creative work, other accompanying drawing can also be obtained according to these accompanying drawings.
Fig. 1 is in one embodiment of the present invention, the schematic cross section of high-performance quartzite slate.
Detailed description of the invention
Below in conjunction with accompanying drawing of the present invention, be clearly and completely described technical scheme of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
As shown in Figure 1, in embodiments of the present invention, provide a kind of high-performance quartzite slate, comprise integrated quartz slate 10 and supports cloth 20.Supports cloth 20, to run through the direction of quartz slate 10 longitudinal section, is clamped in quartz slate 10 inner.Supports cloth 20 is made to be clamped in quartz slate 10 inner.The number of plies of above-mentioned supports cloth 20 material is one deck or two-layer.Thus increase support degree, according to two-layer supports cloth, can connect in advance in the middle of its two-layer support portion, or mutually be bondd by quartz plate material.The material of supports cloth 20 can be preferably glass fiber grid cloth (middle alkali woven roving).The grid establishment shape of this grid cloth is square, and size of mesh opening is 535mm, and the thickness of described fiberglass gridding cloth is: 1,0.3 and 0.4.Above-mentioned glass fiber grid cloth also can adopt, the network of encryption establishment.The raw material of above-mentioned quartz slate 10 is prepared by the raw material comprising quartz sand, glass sand and unsaturated-resin.Above-mentioned quartz sand comprises: 4 ~ 6 orders, 6 ~ 8 orders, 8 ~ 10 orders, 10 ~ 16 orders, 16 ~ 26 orders, 26 ~ 40 orders, 40 ~ 70 orders, 70 ~ 120 orders and 325 object quartz sands; Glass sand comprises: 6 ~ 8 orders, 8 ~ 16 orders, 16 ~ 30 object glass sands.Wherein, 325 object quartz sand consumptions are 25% of stone slab raw material volume, and glass sand consumption is 20% of stone slab raw material volume, and unsaturated-resin consumption is 9% of stone slab raw material volume.Thus can effectively ensure, quartzite slate has the performance of resistance to compression and cracking resistance.
Meanwhile, present invention also offers a kind of manufacture method of high-performance quartzite slate, comprising:
Step S101, at mould bottom laid bottom quartz slate 10 raw material;
Step S102, laid supports cloth 20 on the stone slab raw material of bottom;
Step S103, at laid upper strata, the top of supports cloth 20 quartz slate 10 raw material.
In a preferred embodiment, also comprise after step S103:
Step S104, flattens the upper surface of the stone slab raw material on upper strata.
In a preferred embodiment, also comprise after step S104:
Step S105, shapes successively to being equipped with stone slab raw material mould; Sizing comprises: press, vacuum, vibration, shaping, dry, cooling, polishing and demoulding step.
The above; be only the specific embodiment of the present invention, but protection scope of the present invention is not limited thereto, is anyly familiar with those skilled in the art in the technical scope that the present invention discloses; change can be expected easily or replace, all should be encompassed within protection scope of the present invention.Therefore, protection scope of the present invention should described be as the criterion with the protection domain of claim.
Claims (10)
1. high-performance quartzite slate, is characterized in that: comprise integrated quartz slate and supports cloth, and it is inner that described supports cloth is clamped in described quartz slate.
2. high-performance quartzite slate according to claim 1, is characterized in that: it is inner that described supports cloth is clamped in described quartz slate with the direction running through quartz slate longitudinal section.
3. high-performance quartzite slate according to claim 2, is characterized in that: the number of plies of described supports cloth is one deck or two-layer.
4. according to the high-performance quartzite slate one of claims 1 to 3 Suo Shu, it is characterized in that: the material of described supports cloth is fiberglass gridding cloth, mesh shape is square, and size of mesh opening is 535mm, and the thickness of described fiberglass gridding cloth is: 1,0.3 and 0.4.
5. according to the high-performance quartzite slate one of claims 1 to 3 Suo Shu, it is characterized in that: described quartz slate is prepared by the raw material comprising quartz sand, glass sand and unsaturated-resin.
6. high-performance quartzite slate according to claim 5, is characterized in that: described quartz sand comprises: 4 ~ 6 orders, 6 ~ 8 orders, 8 ~ 10 orders, 10 ~ 16 orders, 16 ~ 26 orders, 26 ~ 40 orders, 40 ~ 70 orders, 70 ~ 120 orders and 325 object quartz sands; Described glass sand comprises: 6 ~ 8 orders, 8 ~ 16 orders, 16 ~ 30 object glass sands.
7. high-performance quartzite slate according to claim 6, it is characterized in that: described 325 object quartz sand consumptions are 25% of stone slab raw material volume, described glass sand consumption is 20% of stone slab raw material volume, and unsaturated-resin consumption is 9% of stone slab raw material volume.
8. the manufacture method of the high-performance quartzite slate as described in one of claims 1 to 3, is characterized in that, comprising:
Step S101, at mould bottom laid bottom quartz slate raw material;
Step S102, laid supports cloth on the stone slab raw material of described bottom;
Step S103, at laid upper strata, the top of described supports cloth quartz slate raw material.
9. the manufacture method of high-performance quartzite slate according to claim 8, is characterized in that, also comprise after step S103:
Step S104, flattens the upper surface of the stone slab raw material on upper strata.
10. the manufacture method of high-performance quartzite slate according to claim 9, is characterized in that, also comprise after step S104: step S105, shapes successively to being equipped with stone slab raw material mould;
Described sizing comprises: press, vacuum, vibration, shaping, dry, cooling, polishing and demoulding step.